Embankment dams is the most common type of dams in operation inSweden today. Due to the nature of embankment dams, seepage throughthem will always occur. If the seepage velocity exceeds a critical velocity,internal erosion is initiated, which could lead to damage in form of pipingand sinkholes. To treat this problem, remedial grouting has beenperformed involving a combination of conventional grouts, i.e. cement andcement-bentonite as well as sodium silicate, which is a chemical grout thatalso known as water glass. Regarding the sodium silicate grout, there isconcern about the long-term permanence.The aim of this thesis has been to study the potential performance ofsodium silicate grouted in embankment dams. The first part of this thesisis a literature review of the general behavior of sodium silicate as a grout,its degradation processes and the factors that could induce degradation.The second part suggests monitoring methods to control and evaluate theperformance of the treated dam and the grout if degradation has occurred.Findings from literature generally indicates a high risk of instability andlow permanence of sodium silicate when grouted in an embankment dam.This type of grout will undergo degradation mainly in two forms: syneresisinduced shrinkage and leaching due to grout erosion or dissolution. As thedegradation has developed, an increase in permeability of the repaireddam core is a potential consequence.How the potential degradation of sodium silicate will affect the treateddams is suggested to be observed by monitoring the permeability of thegrouted core. Applicable monitoring methods for this purpose aremeasurements of pore pressure and temperature using piezometers. Thesecond direct method of monitoring a changed dam behavior is suggestedto be leakage analysis, in order to detect potentially increased leakagebecause of the grout degradation. An indirect way to investigate the damperformance is suggested to be monitoring of the grout state. Measurementof ion concentration of sodium and silicon respectively in leakage waterusing selective-ion electrodes will reveal any increase in ion concentrationdue to the potential grout dissolution or leaching.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-275740 |
Date | January 2019 |
Creators | Fu, Jenny |
Publisher | KTH, Jord- och bergmekanik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | TRITA-ABE-MBT ; 19676 |