There are two main goals of this thesis: to investigate the flow-induced crystallization behaviour of Polybutene-1 (PB-1 samples, and to study the effects of molecular parameters on the crystallization behaviour While flow-induced crystallization is not a new area in polymer research, well-defined experimental methods that allow access to high flow rate range comparable to that encountered in real processing are still lacking. Two types of flow are considered: shear and uniaxial elongational. Regarding the second aim, several molecular parameters considered are: molecular weight, molecular weight distribution, isotacticity, presence of nucleating agents, and copolymer content. For this purpose an array of PB-1 samples were used. It is found that each of these parameters can have significant effect on the crystallization behaviour. Mainly rheological methods were utilized to conduct the flow-induced crystallization experiments. Crystallization onset time is define d from the change in viscosity or other related parameters. The experiments begin with low shear rate range, to ensure that the results are comparable with literature data. In this range we encounter the quasi-quiescent onset time at very small. shear rates, which draws an interesting comparison with another physical parameter, the gel time. Beyond a critical flow rate a decrease in the onset time is seen, and a plateau-and-slope trend is evident for a curve of onset time vs. shear rate. Using a combination of three experimental methods, shear rates ranging from Q0001 - 500 s-1 are successfully achieved, and a good agreement between these methods is observed. Furthermore, a normalization procedure is introduced, which yields temperature-invariant curves for the mentioned range of shear rate. For the uniaxial elongation flow, the Elongational Viscosity Fixture (EVF) is employed, with the strain rate ranging from 0.0001 - 10 s'. A greater reduction in onset time as compared to shear (at the same shear/strain r ate) is observed, and the difference in the onset times for shear and elongation already reaches more than one decade for a flow rate of 10 5. This quantitative comparison is particularly important; since not so many data on elongation-induced crystallization are available in the literature. Finally, the thesis compares several flow induced crystallization models that can be useful as prediction tools and selects one of these models to be compared with the experimental data. A qualitative agreement is found, however, for better quantitative prediction the model still needs to be.
| Identifer | oai:union.ndltd.org:ADTP/210233 |
| Date | January 2007 |
| Creators | Hadinata, Chitiur, chitiurh@yahoo.com.au |
| Publisher | RMIT University. Civil, Environmental and Chemical Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://www.rmit.edu.au/help/disclaimer, Copyright Chitiur Hadinata |
Page generated in 0.0013 seconds