This study presents results of selective laser melting (SLM), powder metallurgy (PM), and casting technologies applied for producing Ti–TiB composites from Ti–TiB₂ powder. Diffraction patterns and microstructural investigations reveal that chemical reaction occurred between Ti and TiB₂ during all the three processes, leading to the formation of Ti–TiB composites. The ultimate compressive strength of SLM-processed and cast samples are 1421 and 1434 MPa, respectively, whereas the ultimate compressive strengths of PM-processed 25%, 29%, and 36% porous samples are 510, 414, and 310 MPa, respectively. The Young’s moduli of porous composite samples are 70, 45, and 23 GPa for 25%, 29%, and 36% porosity levels, respectively, and are lower than those of SLM-processed (145 GPa) and cast (142 GPa) samples. Fracture analysis of the SLM-processed and cast samples shows shear fracture and microcracks across the samples, whereas failure of porous samples occurs due to porosities and weak bonds among particles.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:39023 |
| Date | 11 June 2020 |
| Creators | Attar, H., Bönisch, M., Calin, M., Zhang, L. C., Zhuravleva, K., Funk, A., Scudino, S., Yang, C., Eckert, J. |
| Publisher | Cambridge University Press |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:article, info:eu-repo/semantics/article, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 0884-2914, 2044-5326, 10.1557/jmr.2014.122 |
Page generated in 0.0045 seconds