This multi-scale investigation aimed to provide new knowledge and understanding of creep and shrinkage of high performance lightweight concrete (HPLC) by assessing prestress losses in HPLC prestressed members in a large-scale study; by quantifying the effect of the constituent materials and external conditions on creep and shrinkage in a medium-scale study; and by improving the fundamental understanding of creep and shrinkage in a small-scale study.
Creep plus shrinkage prestress losses were between two and eight times lower than those estimated for the design standards and approximately 50% of those measured in similar strength normal weight high performance concrete girders.
The lower creep and shrinkage exhibited by HPLC was found to be caused by a synergy between the pre-soaked lightweight aggregate and the low water-to-cementitious material ratio matrix. That is, the water contained in the lightweight aggregate contributes to enhance hydration by providing an internal moist curing. The water in the aggregate also contributes to maintain a high internal relative humidity which reduces or eliminates autogenous shrinkage. This higher internal relative humidity also reduces creep by preventing load-induced water migration. Finally, lightweight aggregate exhibits a better elastic compatibility with the paste than normal weight aggregate. This improved elastic matching and the enhanced hydration are believed to reduce peak deformations at the ITZ which further decreases creep and shrinkage.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/7531 |
| Date | 22 November 2005 |
| Creators | Lopez, Mauricio |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation |
| Format | 13760283 bytes, application/pdf |
Page generated in 0.0018 seconds