(FAPESB). / Defeitos ósseos críticos, representam um problema clínico recorrente. Nestas
situações a capacidade de reparo ósseo torna-se limitada e suscetível a falhas. No
caso supracitado sçao utilizados biomateriais a base de hidroxiapatita, em função de
sua composição química, morfologia porosa tridimensional e alta similaridade com o
osso humano. A alta resolução das técnicas de imagem por μCT,permitem a
avaliação de massa óssea e na morfologia dos espécimes excisados, e traz como
vantagens: a medição direta da morfologia trabecular em três dimensões e um
volume significativamente maior de amostra é analisada. O objetivo deste estudo foi
realizar um estudo comparativo imaginológico por microtomografia computadorizada
(µCT) e a análise histomorfológica, do reparo ósseo, associado ao uso de
biomateriais. Para a realização deste estudo, foi utilizada uma amostra de vinte
ratos, Rattus Novergicus, wistar, para a comparação de quatro grupos distribuídos
aleatoriamente, avaliados nos ponto biológico de 15 dias. Dois grupos com defeito
crítico preenchidos com os biomateriais: compósitos de hidroxiapatita com 1% de
alginato e gelatina (1%) (HAAlgeGel) e BioOss® (HA), um grupo com o mesmo
defeito sem implante de biomaterial e um grupo com a calvária integra. Os animais
foram sacrificados, as calvárias foram submetidas à aquisição de imagens por μCT.
Tal etapa foi realizada em algumas etapas: “Scanning”, reconstrução e análise em
3D, executada pelos programas “N Recon”, “Data Viewer” e “CTan”. Em seguida os
seguimentos anteriores foram descalcificados e os cortes histológicos foram
analisados pelas técnicas de Hematoxilina (HE) e Eosina, Picrossírios (PIFG)
vermelho e Tricromo de masson Goldner e avaliado em microscópio de luz comum.
Conclui-se que através da aquisição de imagens por µTC e análise histomorfológica,
foi possível quantificar o reparo ósseo de defeitos críticos sem implantação de
biomateriais e nos grupos HA e HAAlgGel. / Critical defects, represent a recurring medical problem. In these situations the bone
repair capacity becomes limited and susceptible to failure. In the above case are
biomaterials used hydroxyapatite base, due to its chemical composition, threedimensional
porous morphology and high similarity with human bone. The high
resolution of the image by μCT techniques allow the assessment of bone mass and
morphology of specimens excised, and has as advantages: the direct measurement
of trabecular morphology in three dimensions and a significantly larger volume of
sample is analyzed. The objective of this study was to conduct a comparative study
imaginologic computed microtomography (μCT) and the histomorphological analysis,
bone repair, associated with the use of biomaterials. For this study, a sample of
twenty rats, Rattus Novergicus was used, Wistar, to compare four groups, at random,
biologically evaluated in 15 days. Two groups of critical defect filled with biomaterial:
hydroxyapatite composites with 1% alginate and gelatin (1%) (HAAlgeGel) and
BioOss® (HA), a group with the same defect without biomaterial implant and a group
of the calvaria integrates. The animals were sacrificed, the calvaria were subjected to
image acquisition by μCT. This step was performed in a few steps, "Scanning",
reconstruction and analysis in 3D, performed by the programs "N Recon", "Viewer
Data" and "AWC". Then the previous segments were decalcified and histological
sections were analyzed by hematoxylin techniques (HE) and eosin, Picrossisius
(PIFG) red and Trichrome Masson Goldner and evaluated in light microscope
common. It follows that by acquiring images per μTC and histomorphological analysis
was performed to quantify the bone repair of critical defects without implantation of
biomaterials and HA and HAAlgGel groups.
| Identifer | oai:union.ndltd.org:IBICT/oai:192.168.11:11:ri/17936 |
| Date | January 2014 |
| Creators | Cunha, Anderson de Souza |
| Contributors | Rosa, Fabiana Paim, Rosa, Fabiana Paim, Cirelli, Joni Augusto, Campos, Paulo Sérgio Flores |
| Publisher | Instituto de Ciências da Saúde, Processos Interativos dos Órgãos e Sistemas, ICS, brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFBA, instname:Universidade Federal da Bahia, instacron:UFBA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds