Previous issue date: 2009 / A proposta deste trabalho foi preparar nanocompósitos de
polipropileno/compatibilizante/bentonita, pelo método de intercalação na fusão, utilizando como carga uma argila sódica comercial Argel, fornecida por uma indústria local, purificada e modificada organicamente com um sal quaternário de amônio empregando diferentes métodos de preparação. Ao longo do trabalho foram utilizadas duas matrizes e dois tipos de compatibilizantes: PP H103, PP H401, Polipropileno modificado com anidrido maleico (PP-g-MA) e Copolímero de etileno e álcool vinílico (EVOH), respectivamente. As argilas foram caracterizadas por difração de raios-X (DRX), espectroscopia de infravermelho (FTIR) e análise termogravimétrica (TG) visando determinar o método de preparação mais eficiente para obtenção das argilas organofílicas. Uma vez determinado o melhor procedimento para organofilização, na segunda parte deste estudo, avaliou-se o efeito do tipo e teor de argila organofílica, bem como o tipo e teor de compatibilizante nas propriedades de filmes de polipropileno. De acordo com os resultados preliminares deste estudo, há uma indicação de que os filmes de nanocompósitos PP/PP-g-MA/argila organofílica, contendo 1% de argila organofílica e 15% de polipropileno modificado com anidrido maléico (PP-g-MA) podem ser promissores
para o mercado de embalagens e poderão em um futuro próximo serem usados como um novo produto por empresas nacionais. / The purpose of this work is to prepare nanocomposites of polypropylene/compatibilizer/bentonite, by melting intercalation, with a commercial sodium clay – Argel – as filler. This clay was organically purified and modified by different methods, with a quaternary ammonium salt. The clays were characterized by X-Ray diffraction (XRD), infrared spectroscopy (FTIR) and thermogravimetric analyses (TG) to determine the most efficient preparation method. Before that, in the second stage of this study, the influence of the type and contend of organoclay in the properties of the polypropylene films was measured; the same was done for the compatibilizer. The preliminary results indicate that the nanocomposites film with 1% of organoclay and 15% of polypropylene grafted with maleic anhydride show promise as packing materials and may be used, in the near future, as a new product by the national industry.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1691 |
| Date | 12 September 2018 |
| Creators | ANDRADE, Daniela de Lourdes Anjos Coutinho Simões. |
| Contributors | CARVALHO, Laura Hecker de., SILVA, Suédina Maria de Lima., RAPÔSO, Claúdia M. O., WELLEN, Renate Maria Ramos., LARANJEIRA, Edilâne., CANEDO, Luis Eduardo. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | RENAMI |
Page generated in 0.0074 seconds