Previous issue date: 2014-08-28 / Capes / Os polímeros derivados do petróleo têm provocado impactos ambientais devido
ao descarte inadequado. Uma alternativa para esse problema é a utilização de
polímeros biodegradáveis ou a produção de blendas a partir destes polímeros.
Neste trabalho, foram preparadas blendas de poli (ácido lático) - PLA, poli (caprolactona)
- PCL, com três copolímeros diferentes: EMA, E-GMA e o EMAGMA
que são copolímeros de etileno-acrilato de metila, etileno-metacrilato de
glicidila e o terpolímero etileno-acrilato de metila-metacrilato de glicidila,
respectivamente. As composições utilizadas para as blendas foram as
seguintes: PLA/PCL (90/10), PLA/PCL (80/20), PLA/Copolímeros (90/10) e
PLA/PCL/Copolímeros (80/10/10). Estas foram preparadas por fusão em uma
extrusora de rosca dupla corrotativa e, em seguida, moldadas por injeção sob a
forma de corpos de prova de tração, impacto e HDT. Todas as composições
foram caracterizadas por: ensaios mecânicos de tração e impacto, temperatura
de distorção térmica - HDT, calorimetria exploratória diferencial - DSC, difração
de raios X - DRX, análise térmica dinâmica-mecânica - DMTA, espectroscopia na região do infravermelho por transformada de Fourier - FTIR, microscopia
eletrônica de varredura - MEV, reometria de torque, ensaio reológico e
reometria capilar. As propriedades mecânicas apresentaram redução nos
valores do módulo e da resistência à tração e um aumento no alongamento e
na resistência ao impacto para todas as composições quando comparadas com
o PLA puro, com destaque para as composições que continham o copolímero
EMA-GMA. A HDT não apresentou mudanças significativas para as diferentes
composições em comparação com o PLA puro. O comportamento térmico e
termomecânico foi avaliado por DSC e por DMTA e foi possível observar a
transição térmica das blendas. Por DRX foi possível observar as fases
cristalinas das blendas de PLA. A morfologia da superfície de fratura observada
por MEV ilustrou que ocorreram mudanças significativas em função da
composição. Os resultados de reometria de torque não apresentaram mudanças significativas no comportamento do PLA, enquanto que os
resultados obtidos no ensaio reológico ilustraram aumento no módulo de
armazenamento em todas as composições. A partir do ensaio de reometria
capilar foi visto que houve redução da viscosidade aparente e da tensão de
cisalhamento sob altas taxas de cisalhamento para todas as composições. / The polymers derived from petroleum have caused environmental impacts due
to improper disposal. An alternative to this problem is the use of biodegradable
polymers or blends production from these polymers. In this work, blends of poly
(lactic acid) - PLA, poly (-caprolactone) - PCL, were prepared with three
different copolymers: EMA, E-GMA and EMA-GMA are copolymers the
ethylene-methyl acrylate, ethylene-glycidyl methacrylate and terpolymer
ethylene-methyl acrylate-glycidyl methacrylate respectively. The compositions
used in the blends were as follows: PLA/PCL (90/10) PLA/PCL (80/20) PLA/
Copolymer (90/10) and PLA/PCL/Copolymer (80/10/10). These were prepared
by melting in an extruder twin screw co-rotating and then injection molded in the
form of specimens tensile, impact and HDT. All compositions were
characterized by: mechanical tensile and impact , heat distortion temperature -
HDT, differential scanning calorimetry - DSC, X-ray diffraction - XRD, dynamic
mechanical thermal analysis – DMTA, spectroscopy in the infrared region by
transform Fourier - FTIR, scanning electron microscopy - SEM, torque
rheometer, rheological testing and capillary rheometer. The mechanical
properties showed reduced values of modulus and tensile strength and an
increase in elongation and impact resistance for all compositions when
compared with pure PLA, especially for compositions containing copolymer
EMA-GMA. The HDT showed no significant changes for the different
compositions compared with pure PLA. The thermal and thermomechanical
behavior was evaluated by DSC and DMTA and it was possible to observe the
thermal transition of the blends. XRD was possible to observe the crystalline
phases of the blends of PLA. The morphology of the fracture surface was
observed by SEM illustrated that significant changes as a function of
composition. The torque rheometer results showed no significant change in the
behavior of PLA, while the rheological test results illustrate the increase in
storage modulus in all compositions. From the test capillary rheometer was seen that there was a reduction in the apparent viscosity and shear stress at
high shear rates for all compositions.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/343 |
| Date | 06 April 2018 |
| Creators | SILVA, Taciana Regina de Gouveia. |
| Contributors | MELO, Tomás Jeferson Alves de., ARAÚJO, Edcleide Maria., BRITO, Gustavo de Figueiredo., ANDRADE, Daniela de Lourdes Anjos Coutinho Simões., CAVALCANTE, Wilma Sales., AGRAWAL, Pankaj. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds