Previous issue date: 2014-08-14 / Este trabalho tem por objetivo avaliar membranas de silicone que envolve o
implante mamário preenchido com gel de silicone, no intuito de verificar a
conformidade das suas propriedades. Como estratégia utilizou-se das técnicas
de caracterização para analisar os parâmetros físico-químicos em três lotes
diferentes de implante mamário. Os resultados experimentais encontrados
foram comparados com valores referenciados em padrões estabelecidos em
norma ou na literatura. Com isso, foi possível analisar alguns atributos que influenciam na qualidade desses implantes. Os resultados de microscopia por
MO e MEV não detectaram anomalias nas superfícies das amostras. Foram
detectados pelo ensaio de espectroscopia por EDS os elementos carbono,
silício e oxigênio, como também identificados os metais ferro, cálcio, níquel e
cromo nas amostras ensaiadas. O teste de alongamento de duas amostras não
atendeu o requisito normativo. Conclui-se, portanto, que a integridade das
membranas de silicone foi comprometida, por conta do seu comportamento
mecânico, em duas das três amostras ensaiadas. / This work aims to evaluate silicon membranes surrounding the breast implant
filled with silicone gel, in order to verify the conformity of its properties. As a
strategy, we used the characterization techniques to analyze the
physicochemical parameters in three different batches of breast implant. The
experimental results were compared with values referenced in standard or
standards established in the literature. Thus, it was possible to analyze some
attributes that influence the quality of these implants. The results of OM and
SEM microscopy did not detect anomalies in the surfaces of the samples. Were detected by testing the EDS spectra of carbon, silicon and oxygen elements,
also identified as metals iron, calcium, nickel and chromium in the test samples.
The stretching test two samples did not meet the regulatory requirement.
Therefore, it is concluded that the integrity of the silicone membranes was
compromised, because its mechanical behavior, in two of the three samples
tested.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/421 |
| Date | 18 April 2018 |
| Creators | CALMON, Walfredo da Silva. |
| Contributors | FOOK, Marcus Vinícius Lia., BARBOSA, Rossemberg Cardoso., FOOK, Sayonara Maria Lia. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.026 seconds