Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-08T12:27:59Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_ColagemJuntaMadeira.pdf: 1519438 bytes, checksum: 1c0964555dba5dcc59129a15491e26ac (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-17T14:19:01Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_ColagemJuntaMadeira.pdf: 1519438 bytes, checksum: 1c0964555dba5dcc59129a15491e26ac (MD5) / Made available in DSpace on 2014-06-17T14:19:01Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_ColagemJuntaMadeira.pdf: 1519438 bytes, checksum: 1c0964555dba5dcc59129a15491e26ac (MD5)
Previous issue date: 2010 / Este trabalho tem como objetivo confeccionar, testar e comparar juntas coladas de topo, biselada e encaixada de espécies de madeira de diferentes densidades. A
colagem da madeira possibilita o reaproveitamento de aparas e sobras de madeiras que normalmente são descartadas, podendo minimizar o corte de muitas árvores,seja da natureza ou de plantio planejado. A metodologia de fabricação das juntas foi estabelecida com base em indicações descritas em normas brasileiras. Foi realizada observação macroscópica da madeira, para confirmação de suas espécies. Depois
de estabelecida à dimensão das juntas foram confeccionados corpos de prova, utilizando o adesivo Compound Adesivo de base epóxi e as madeiras Angelimpedra, Jatobá e Tauari, adquiridas em depósito de madeira na cidade de Ananindeua-Pa. Quanto à caracterização do adesivo, foi verificado através do ensaio de tração, que tem boa resistência mecânica. Após a colagem das juntas foi realizado ensaio de tração a fim de determinar a resistência das juntas coladas O desempenho dessas juntas foi avaliado em função da relação entre os valores de resistência à tração da madeira sólida e os valores de resistência à tração com madeira colada e modo de ruptura. De acordo com os resultados observou-se que as juntas coladas biseladas apresentaram excelente resistência à tração, bem próxima da resistência da madeira sólida; notou-se também a boa aceitação de colagem da madeira Jatobá. Com relação à qualidade da adesão, as juntas coladas de topo e encaixada apresentaram ruptura adesiva. Os resultados experimentais obtidos indicam uma boa concordância entre os modelos teóricos para avaliar a resistência à tração e a qualificação das juntas coladas. / This work has as objective of making, to test and to compare the glued joints of butt,
scarf and finger with three species of wood of different densities. The collage of the
wood makes possible the use of pieces and surpluses of wood that are usually
discarded, could minimize the cut of a lot of trees, be of the nature or of planned
planting. The methodology of production of the joint, it was established with base in
indications described in Brazilian norms. Macroscopic observation of the wood it was
accomplished, for confirmation of your species. After established the dimension of
the joints they were made bodies of proof, using the adhesive Compound Adhesive
of epoxy base and wood Angelim-pedra, Jatobá and Tauari, acquired in wood
deposit in the city of Ananindeua-Pa. With relationship the characterization of the
adhesive, it was verified through the traction tests that has good mechanical
resistance. After collages of the joints it was accomplished traction tests to
determining the resistance of the glued joints. The glued joints performance it was
evaluated in function of the relationship among the values of resistance to traction of
the solid wood and the values of resistance to traction with glued wood and rupture
way. In agreement with the results it was observed that the glued joints scarf they
presented excellent resistance to traction, very close of the resistance of the solid
wood; it was also noticed the good acceptance of collage of the wood Jatobá. With
relationship the quality of the adhesion, the glued joints of butt and finger, therefore
they presented adhesive rupture. The experimental results obtained indicate a good
agreement among the theoretical models to evaluate the resistance to the traction
and the qualification of the glued joints.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5086 |
| Date | 08 February 2010 |
| Creators | CARNEIRO, Ruth Pereira |
| Contributors | FUJIYAMA, Roberto Tetsuo |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds