Previous issue date: 2012-03-09 / Soil improved with the addition of cement have been utilized as an alternative to the
construction of various types of geotechnical works, almost always present economic
and environmental advantages. This paper presents a study on the usage of cement
in the improvement of mechanical properties of sandy soils, characteristic of the
region of Natal, collected from its dunes. This research was made in order to analyze
the influence of cement content, voids, and also including water immersion
and confining pressure. Samples molded from cement-soil mixtures were tested for
unconfined compression tests and triaxial tests. The samples had the percentage of
cement mixed in 2.5%, 5% and 10% by weight. The cement agent used was the
Portland Cement of High Early strength(CPV-ARI), which promoted agility to the
experimental procedure for presenting a rapid gain in strenght. The void ratio used
ranged from 0.7 (more compact), 0,9 and 1,1(softer). The soil under study can be
considered as pure sand. In general, it can be stated that the larger the amount of
cement added to the sand studied is, the greater ultimate strength will be. Likewise,
as more compact the soil is, the less void ratio and more resistant it will be present.
The confining pressure tends to increase the resistance of the specimens. The
cementing adopted grades showed that the use of different criteria for failure did not
significantly alter the stress-strain parameters for the sand studied. The angle of
friction values were found within the typical range of medium and compact sands.
Cementing acted in the sand providing an intercepted cohesion which increased
enhancing the potential cementation. In triaxial compression tests, the sand with void
ratio is equal to 0.7 and showed the expected behavior for a compact sand while the
stress-strain behavior of the same sand with the void ratio of 0.9 tended to be
expected for the soft sand as well / Solos melhorados com adi??o de cimento t?m sido bastante utilizados como
alternativa na constru??o de diversos tipos de obras geot?cnicas, quase sempre por
apresentar vantagens econ?micas e ambientais. Este trabalho apresenta um estudo
sobre a utiliza??o de cimento no melhoramento das propriedades mec?nicas de
solos arenosos caracter?sticos da regi?o de Natal, coletados em dunas. Foi avaliada
a influ?ncia do teor de cimento, do ?ndice de vazios, da inunda??o e da tens?o
confinante. Corpos-de-prova moldados a partir de misturas de solo-cimento foram
submetidos a ensaios de resist?ncia ? compress?o simples e ? compress?o triaxial
convencional. Nas amostras as porcentagens de cimento foram variadas em 2,5%,
5% e 10% em peso. O agente cimentante utilizado foi o Cimento Portland de Alta
resist?ncia inicial (CP-V ARI), que promoveu agilidade ao procedimento experimental
por apresentar um processo de cura mais r?pido.Os ?ndices de vazios utilizados
variaram de 0,7 (mais compacto), 0,9 e 1,1(mais fofo). O solo estudado pode ser
considerado como uma areia pura. De uma forma geral, pode-se afirmar que quanto
maior a quantidade de cimento adicionado ? areia estudada, maior a sua resist?ncia
final. Da mesma forma, quanto mais compacto estiver esse solo, isto ?, quanto
menor o ?ndice de vazios, mais resistente ele se apresentar?. A tens?o confinante
tende a aumentar a resist?ncia dos corpos de prova. Nos graus de cimenta??o
adotados, a utiliza??o de diferentes crit?rios de ruptura n?o alterou
significativamente os par?metros tens?o-deforma??o para a areia estudada. Os
valores de ?ngulo de atrito encontrados estavam dentro dos valores t?picos para
areias m?dias e compactas. A cimenta??o agiu na areia de modo a proporcionar um
intercepto de coes?o que aumentou com o incremento da cimenta??o. Nos ensaios
de compress?o triaxial, a areia com ?ndice de vazios igual a 0,7 apresentou o
comportamento esperado para uma areia compacta, enquanto o comportamento
tens?o deforma??o da mesma areia com ?ndice de vazios de 0,9 tendeu ao
esperado para a areia fofa
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/14840 |
| Date | 09 March 2012 |
| Creators | Lopes, Francisco Mateus Gomes |
| Contributors | CPF:35816384449, http://lattes.cnpq.br/1573496204231636, Danziger, Bernadete Ragoni, CPF:40599337753, http://lattes.cnpq.br/2006272256799450, Costa, Yuri Daniel Jatob?, CPF:92610927487, http://lattes.cnpq.br/6737841388506901, Severo, Ricardo Nascimento Flores, CPF:36957194000, http://lattes.cnpq.br/8346360266500368, Santos J?nior, Olavo Francisco dos |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Engenharia Civil, UFRN, BR, MEC?NICA DAS ESTRUTURAS, ESTRUTURAS DE CONCRETO E ALVENARIA E MATERIAIS E PROCESSOS CONSTRUTIVOS |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds