Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-01-26T17:36:30Z
No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-01-27T21:54:39Z (GMT) No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5) / Made available in DSpace on 2016-01-27T21:54:39Z (GMT). No. of bitstreams: 1
ThiagoVictorRodriguesDeMedeiros_DISSERT.pdf: 3828773 bytes, checksum: a71182f41a89dc6ac4d09bef70dac843 (MD5)
Previous issue date: 2014-11-20 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico - CNPq / A nitreta??o por plasma vem sendo utilizada nas aplica??es industriais e
tecnol?gicas em larga escala por apresentar uma melhora nas propriedades mec?nicas,
tribol?gicas, dentre outras. A fim de solucionar problemas decorrentes na nitreta??o
convencional, como por exemplo, os an?is de restri??o (efeito de borda), foram
desenvolvidos t?cnicas com catodos diferenciados. No presente trabalho, estudou-se
superf?cies de tit?nio comercialmente puro (Grau II), modificadas por tratamento de
nitreta??o a plasma atrav?s de diferentes configura??es de c?todos (catodo oco, gaiola
cat?dica com uma gaiola e gaiola cat?dica com duas gaiolas) variando a temperatura em
350, 400 e 430oC, com o objetivo de obter uma otimiza??o da superf?cie para aplica??es
tecnol?gicas, avaliando de forma geral qual o tratamento mostrou melhores resultados
no substrato. As amostras foram caracterizadas atrav?s das t?cnicas de ensaios de
Microscopia de For?a At?mica (AFM), Espectroscopia Raman, Microdureza, Difra??o
de Raios-X (DRX), al?m de uma an?lise macrosc?pica. Desta forma, puderam-se
avaliar propriedades do tratamento como rugosidade, topografia, presen?a de elementos
intersticiais, dureza, homogeneidade, uniformidade e espessura da camada nitretada.
Observou-se que todas as amostras expostas a nitreta??o foram modificadas em rela??o
? amostra padr?o (sem tratamento), logo, apresentando aumento da dureza superficial,
presen?a de TiN constatadas tanto por DRX como por Raman, e uma altera??o
significativa na rugosidade das amostras tratadas. Constatou-se que o tratamento em
c?todo oco, apesar de apresentar o menor valor de microdureza entre as amostras
tratadas, foi o que apresentou a menor rugosidade superficial, apesar de nessa
configura??o as amostras sofrerem uma agressividade f?sica maior do tratamento. / The plasma nitriding has been used in industrial and technological applications
for large-scale show an improvement in the mechanical, tribological, among others. In
order to solve problems arising in the conventional nitriding, for example, rings
constraint (edge effect) techniques have been developed with different cathodes. In this
work, we studied surfaces of commercially pure titanium (Grade II), modified by
plasma nitriding treatment through different settings cathodes (hollow cathode, cathodic
cage with a cage and cathodic cage with two cages) varying the temperature 350, 400
and 430oC, with the goal of obtaining a surface optimization for technological
applications, evaluating which treatment generally showed better results under the
substrate. The samples were characterized by the techniques of testing for Atomic Force
Microscopy (AFM), Raman spectroscopy, microhardness, X-ray diffraction (XRD), and
a macroscopic analysis. Thus, we were able to evaluate the processing properties, such
as roughness, topography, the presence of interstitial elements, hardness, homogeneity,
uniformity and thickness of the nitrided layer. It was observed that all samples were
exposed to nitriding modified relative to the control sample (no treatment) thus having
increased surface hardness, the presence of TiN observed by XRD as per both Raman
and a significant change in the roughness of the treated samples . It was found that
treatment in hollow cathode, despite having the lowest value of microhardness between
treated samples, was presented the lowest surface roughness, although this
configuration samples suffer greater physical aggressiveness of treatment
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/19663 |
| Date | 20 November 2014 |
| Creators | Medeiros, Thiago Victor Rodrigues de |
| Contributors | 21514160463, http://lattes.cnpq.br/3246869695770169, Feitor, Michelle Cequeira, 00981350402, http://lattes.cnpq.br/4011909474871656, Costa, Tharsia Cristiany de Carvalho, 02682732437, http://lattes.cnpq.br/4222594679769828, Costa, Thercio Henrique de Carvalho, 03396191471, http://lattes.cnpq.br/3647710047561421, Sousa, R?mulo Ribeiro Magalh?es de |
| Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM CI?NCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds