Previous issue date: 2014 / O objetivo deste estudo foi avaliar in vitro a influência da espessura de resina composta para esmalte, baseadas ou não na escala vita clássica nos parâmetros de luminosidade e translucidez. Um dispositivo de resina epóxica foi criado e confeccionado pelo método de estereolitografia para possibilitar a confecção de espécimes de resina composta em forma de um incisivo central superior que apresentavam as camadas de esmalte palatal, dentina e variação de três espessuras de esmalte vestibular: 0,4mm; 0,8mm e 1,2mm. Os materiais testados foram os compósitos, Filtek Z350 XT(3M ESPE), Miris 2(Coltène) e Ena HRi (Micerium). Foram feitas três leituras de cor para cada espécime utilizando o espectrofotômetro Vita Easy Shade (Vita Zahnfabrik). Pela análise estatística foram calculadas as médias das leituras e os parâmetros de translucidez e luminosidade. Os resultados mostram diferenças significativas entre os compósitos e entre as espessuras, sendo os maiores valores de luminosidade e menores graus de translucidez para o compósito Ena HRi e maiores valores de translucidez para o compósito Miris 2. Pode se concluir que os parâmetros de cor dependem do compósito utilizado e ainda da espessura utilizada.<br> / Abstract: The aim of this study was to evaluate in vitro the translucency parameter and lightness using enamel composite resin with different thicknesses, based or not on the Vita Classical shade guide. An epoxic resin device was developed and built by stereolithography process to enable the manufacture of specimens with the shape of an upper central incisor using composite resin. The specimens had layers of palatal enamel, dentin, and three diferente thicknesses of buccal enamel: 0.4mm, 0.8mm and 1.2mm. The composites tested were Filtek Supreme Ultra (3M ESPE), Miris 2 (Coltène) and Ena HRi (Micerium). The spectrophotometer Vita Easy Shade Vita Zahnfabrik) was used to perform three color measurements of each specimen. Measurement means were calculated and through statistical analysis translucency parameter and lightness were also calculated. The results showed significant differences between the composites used and their thicknesses. The values of lightness were higher for lightness and the translucency was higher for the composite Miris 2. It can be concluded that the color parameters evaluated depend on the composite used and their thickness.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/128628 |
| Date | January 2014 |
| Creators | Almeida, Adriano Gondim |
| Contributors | Universidade Federal de Santa Catarina, Monteiro Júnior, Sylvio, Baratieri, Luiz Narciso |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 112 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0056 seconds