Previous issue date: 2015 / Objetivos: Avaliar a fluência por microindentação de materiais restauradores à base de polímeros como, resina composta para uso direto e resina composta para uso indireto. Material e Método: Discos de resinas compostas foram confeccionados em uma matriz metálica, de forma circular com 1mm de altura e 16mm de diâmetro. Estes espécimes foram divididos em quatro grupos de acordo com o material utilizado: Grupo I ( Empress Direct, Esmalte A2); Grupo II (Filtek Z350 XT, Esmalte A2); Grupo III (Signum Ceramis, Esmalte A2); Grupo IV (SR Adoro, A2) e subdivididos em dois grupos (n=20) de acordo com a armazenagem e controle de umidade, temperatura e tempo: SG I: armazenagem em água destilada 23oC; SG II: armazenagem à seco 23oC, controlado por ar-condicionado; Os períodos de avaliação foram após 24h, 1, 3, e 6 meses de armazenagem. Após o polimento, a lisura, a planificação e o paralelismo entre as superfícies dos discos de resinas compostas foram analisados, para garantir a planificação e o paralelismo entre as faces superior e inferior do disco de resina composta, foram levados ao microdurômetro e submetidos ao teste de fluência em um microdurômetro HMV-2, Micro Hardness Tester, (Shimadzu). Foram realizadas duas endentações, uma inicial e outra final. A carga de endentação utilizada foi de 100gf. O tempo de cada endentação foi 30s e o tempo de relaxação entre cada endentação também de 30s. Os períodos de avaliação foram 24h, 1 mês, 3 meses e 6 meses após a confecção dos espécimes. Para cada espécime foi realizado cinco leituras, uma no centro e em cada quadrante do disco, e então realizada uma média entre esse valores. Resultados; As resinas compostas indiretas apresentarem menos valores de deformação por fluência que as resinas compostas diretas, sendo que todas apresentaram deformação permanente maior quando armezenadas em água e por período de 6 meses., diminuindo a cada período. Conclusão: As resinas compostas indiretas são mais resistentes à fluência que as resinas compostas diretas, a armazenagem em água diminui a resistência de todos os materiais aqui testados, assim como o tempo de armazenagem.<br> / Abstract : Objectiv: Evaluate fluency by microindentação of restorative materials to the polymer base as composite resin for direct use and indirect composite resin for use. Methods: composite resin discs were prepared using a metal matrix, circular in shape with 1 mm high and 16mm in diameter. These specimens were divided into four groups according to the material used: Group I (Empress Direct Enamel A2); Group II (Filtek Z350 XT, Enamel A2); Group III (Signum Ceramis, Enamel A2); Group IV (SR Love, A2) and subdivided into two groups (n = 20) in accordance with the storage and humidity control, temperature and time: I GS: storing in distilled water 23 ° C; SG II: dry storage at 23 ° C, controlled air conditioning; The evaluation periods were after 24 hours, 1, 3, and 6 months of storage. After polishing, the smoothness, the planning and the parallelism between the surfaces of the composite resin discs were analyzed to ensure the planning and the parallelism between the upper and lower faces of the composite disc were taken and subjected to the test microhardness fluency in a HMV-2 microdurometer, Micro Hardness Tester (Shimadzu). Two indentations, initial and another final were held. The indentation load was 100gf used. The time of each indentation was 30s and the relaxation time between each indentation also 30s. The evaluation periods were 24, 1 month, 3 months and 6 months after the making of the specimens. For each specimen was performed five readings, one in the center and in each quadrant of the disc, and then held an average of these values. Results; The indirect composite resins exhibiting less creep strain values that direct composites, which all showed higher permanent deformation when armezenadas in water and for a period of 6 months., Decreasing each period. Conclusion: The indirect composite resins are more resistant to creep than the direct composites, storage decreases in water resistance of all materials tested here, as well as the storage time.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/160791 |
| Date | January 2015 |
| Creators | Martins, Marceli Vieira |
| Contributors | Universidade Federal de Santa Catarina, Maia, Hamilton Pires, Araújo, Élito |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 87 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds