Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2016. / Made available in DSpace on 2016-09-20T04:09:59Z (GMT). No. of bitstreams: 1
339547.pdf: 935632 bytes, checksum: 0c1932dbf4e0ef6b94fad38425d1a04e (MD5)
Previous issue date: 2016 / Objetivo: avaliar o efeito do clareamento intracoronário e do tempo de espera pós-clareamento, com ou sem o uso da pasta de hidróxido de cálcio (Ca (OH)2), na resistência de união (RU) de pinos de fibra de vidro à dentina radicular. Metodologia: quarenta incisivos centrais bovinos foram submetidos ao tratamento endodôntico. Após a obturação dos canais, um tampão cervical com 2 mm de espessura foi confeccionado 2 mm abaixo da junção cemento-esmalte utilizando cimento de óxido de zinco/ sulfato de zinco (Citodur). Após 1 semana, os dentes foram distribuídos aleatoriamente em quatro grupos (n=10): G1 (grupo controle) ? sem clareamento, cimentação imediata do pino; G2 ? clareamento intracoronário e cimentação imediata do pino; G3 ? clareamento intracoronário, curativo temporário com Ca (OH)2 por 7 dias e, na sequência, cimentação do pino; G4 ? clareamento intracoronário, tempo de espera de 7 dias e, na sequência, cimentação do pino. Nos grupos G2, G3 E G4 o clareamento foi realizado com peróxido de hidrogênio a 35% na câmara pulpar por 45 min. No G3 as amostras tiveram a câmara pulpar preenchida com pasta de Ca(OH)2 . Em todos os grupos os pinos (Whitepost DC nº 3) foram cimentados com cimento resinoso dual (Relyx ARC). Após 24 h, as raízes foram seccionadas, transversalmente, em uma máquina de cortes (Isomet 1000). Foram obtidas duas secções de 1 mm de espessura para cada região (cervical, média e apical) do pino. As amostras foram submetidasao teste de push-out (0,5 mm/min, Instron 4444). As falhas após desunião foram avaliadas em esteromicroscópio. Os dados foram analisados pelos testes ANOVA e Tukey (a=5%). Resultados: não houve diferença estatisticamente significativa na RU (MPa) entre os grupos avaliados. No G1 o terço cervical apresentou RU significativamente maior do que o terço apical (p<0,05). A RU foi semelhante entre os grupos para cada região do pino/dentina (p=0,44). Os modos de falhas mais frequentes foram: adesiva entre cimento/dentina (50,84%) (G1); coesiva do pino (35,38%) (G2); coesiva do pino (40,90%) (G3) e adesiva mista (40,67%) (G4). Conclusão: a realização do clareamento intracoronário e o tempo de espera pós-clareamento para a cimentação do pino, com ou sem utilização do Ca(OH)2, não influenciaram a RU de pinos de fibra de vidro à dentina radicular.<br> / Abstract : Aim: to evaluate the effect of intracoronary bleaching and post-bleaching time with or without the use of calcium hydroxide paste (Ca(OH)2) on fiberglass posts bond strength (BS) to root dentin. Methodology: forty bovine central incisors were submitted to endodontic treatment. After canal filling, a cervical plug with 2 mm thickness was made 2 mm below the cementum-enamel junction using a zinc oxide / zinc sulfate cement (Citodur). One week later, the teeth were randomly divided into four groups (n=10): G1 (control group): no bleaching, and immediate fiberglass post cementation; G2: intracoronary bleaching and immediate post cementation; G3: intracoronary bleaching, temporary dressing with Ca(OH)2 for 7 days and post cementation; G4: intracoronary bleaching, standby time of 7 days and subsequently, post cementation. In groups G2, G3 and G4 bleaching was carried out with 35% hydrogen peroxide in the pulp chamber for 45 min. G3 samples had the pulp chamber filled with Ca(OH)2 paste. In all groups, the posts (White Post DC #3) were cemented with a dual resin cement (Relyx ARC). After 24 h the roots were transversely sectioned in a cutting machine (Isomet 1000). There were obtained two sections of 1mm thickness for each post region (cervical, middle and apical). The samples were submitted to push-out test (0.5 mm/min Instron 4444). After dislodgments, the failures were evaluated in stereomicroscope. Datawere analyzed by ANOVA and Tukey tests (a= 5%) Results: there was no statistically significant difference in the BS (MPa) between the groups. In G1, BS of the cervical third showed significantly higher means values than the apical third (p< 0.05). The BS results were similar among the groups for each of the post/dentin region (p = 0.44). The most frequent failures modes were adhesive cement/dentine (50.84%) (G1); cohesive at the post (35.38%) (G2); cohesive at the post (40.90%), (G3) and mixed adhesive (40.67%) (G4). Conclusions: intracoronary bleaching as well as the time past between bleaching and post cementation, with or without the use of Ca(OH)2, had no influence on fiberglass post BS to root dentin.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/167680 |
| Date | January 2016 |
| Creators | Silva, Iane Souza Nery |
| Contributors | Universidade Federal de Santa Catarina, Teixeira, Cleonice da Silveira |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 58 p.| grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |