Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2016 / Made available in DSpace on 2017-05-23T04:16:55Z (GMT). No. of bitstreams: 1
345499.pdf: 1757540 bytes, checksum: cdc92546900f0a8658c1960068edf81c (MD5)
Previous issue date: 2016 / Para alcançar estética satisfatória em próteses confeccionadas com zircônia tetragonal policristalina (3Y-TZP), tratamentos laboratoriais, tais como a imersão em líquidos de pigmentação e/ou fluorescentes, podem ser realizados. É importante conhecer a influência desses tratamentos na resistência desse material, assim como a influência do envelhecimento nas propriedades mecânicas de zircônia pigmentadas e/ou fluorescentes. O objetivo deste estudo foi avaliar a resistência mecânica de uma 3Y-TZP tratada com líquidos de pigmentação e/ou fluorescência antes e após protocolo de envelhecimento acelerado. Oitenta discos de zircônia (Prettau Zirkon, Zirkonzahn, Itália) com 14x2,5mm foram usinados, divididos em quatro grupos (N=20) de acordo com o tratamento laboratorial: ZN (sem tratamento); ZC (imersão em líquido de pigmentação A2); ZF (imersão em líquido fluorescente); ZFC (imersão em líquido fluorescente e de pigmentação A2) e sinterizados. Dez discos de cada grupo foram submetidos a um protocolo de envelhecimento acelerado em autoclave por 5 horas. Após, os discos foram submetidos ao teste de resistência flexural (Ball-on-three-balls test). Os valores de resistência obtidos foram analisados pelos testes ANOVA a dois critérios e Tukey?s HSD (p<0,05). O módulo de Weibull (??) foi utilizado para analisar a probabilidade de fratura. O conteúdo de fases tetragonal e monoclínica foi observado por DRX e a visualização da microestrutura, por MEV. Houve um aumento significativo da resistência dos discos após o envelhecimento (p<0,001); porém, quando os tratamentos laboratoriais empregados foram avaliados, nenhuma diferença foi observada (p=0,27). Na análise de DRX, os discos submetidos ao envelhecimento acelerado apresentaram 30% de conteúdo monoclínico, enquanto as amostras não-envelhecidas não apresentaram essa fase. O aumento da resistência flexural dos grupos submetidos ao envelhecimento acelerado por 5 horas, sugere que o aumento do conteúdo monoclínico concentrado na superfície gerou tensões compressivas que fortaleceram o material. Em relação aos tratamentos laboratoriais, não houve diferença significativa da resistência flexural, demonstrando que o uso de agentes de pigmentação e fluorescência não influencia na resistência mecânica da 3Y-TZP estudada.<br> / Abstract : In order to achieve satisfactory aesthetic in yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP), laboratory treatments such as immersion in coloring and/or fluorescent liquids, can be used. It is important to know the influence of such treatments on the strength of the material as well as the influence of aging on mechanical properties of pigmented and/or fluorescent zirconia. The aim of this study was to evaluate the mechanical strength of a pigmented and/or fluorescent 3Y-TZP before and after accelerated aging protocol. Eighty zirconia discs (Prettau Zirkon, Zirkonzahn, Italy) of 14x2,5mm were machined and divided into groups (N=20) according to the laboratory treatment: ZN (no treatment); ZC (immersion in coloring liquid); ZF (immersion in fluorescent liquid); ZFC (immersion in coloring and fluorescent liquid) and sintered. Ten disks of each group were subjected to accelerated aging protocol in an autoclave for 5 hours. All discs were subjected to flexural strength testing (Ball-on-three-balls test). The resistance values obtained were analyzed by two-way ANOVA and Tukey?s HSD (p<0.05). The Weibull modulus (??) was used to analyze the probability of fracture. The content of tetragonal and monoclinic phase was observed by XRD and the microstructure observation was made by SEM. There was a significant increase in resistance of the discs after aging (p<0.001), however, when the laboratory treatments employed were evaluated, no difference was observed (p=0.27). At XRD analysis, the discs subjected to accelerated aging showed the presence of monoclinic content of 30%, while the non-aged samples did not show this phase. The increase in the flexural strength of the groups subjected to accelerated aging for 5 hours suggests that the increase of the monoclinic content concentrated on the surface generated compressive stresses that strengthened the material. Regarding laboratory treatments, there was no significant difference in flexural strength, demonstrating that the use of coloring and fluorescence agents did not influence the mechanical resistance of 3Y-TZP studied.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/175858 |
| Date | January 2016 |
| Creators | Engler, Madalena Lucia Pinheiro Dias |
| Contributors | Universidade Federal de Santa Catarina, Volpato, Cláudia Ângela Maziero, Henriques, Bruno |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 91 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |