Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0
Previous issue date: 2013-08-28Bitstream added on 2014-06-13T20:44:04Z : No. of bitstreams: 1
souzafilho_mp_dr_guara.pdf: 3300858 bytes, checksum: 28f848b21612cf810bf7d4ab1078db03 (MD5) / Neste trabalho estudou-se as vitrocerâmicas obtidas a partir de vidro base do sistema SiO2-Al2O3-MgO-Li2O com adição de ZrO2, como agente nucleante e do B2O3, que tem a função de reduzir a viscosidade do sistema durante o processo de fusão. Os vidros precursores foram obtidos por fusão na temperatura de 1650 ºC, em cadinhos de mulita-zirconia. Os vidros fundidos foram vertidos em molde de grafite para obtenção das amostras monolíticas, e em água para obtenção do material particulado. Este material foi moído e passou por processo de prensagem uniaxial e isostática, antes da sinterização. Para produção das vitrocerâmicas foram realizados tratamentos térmicos em duas condições diferentes. Na primeira as amostras foram aquecidas até 1100 ºC, com taxa de 10 ºC/min, e, na segunda, aquecimento inicial até a temperatura de 780 ºC, com taxa de 10 ºC/min e, em seguida, aquecimento até 1100 ºC, com taxa de 1ºC/min. Sobre os vidros foram feitas análises de dureza indicando valores em torno de 7,0 GPa. Com relação às vitrocerâmicas, os maiores valores de dureza, em torno de 9,2 ± 0,5 GPa, foram verificados nas amostras monolíticas cristalizadas no volume e que estiveram sob tratamento térmico com duas taxas de aquecimento (10 ºC/min até 780 ºC e 1 ºC/min até 1100 ºC) / This work presents the results of the study with glass-ceramics obtained from base glass of the MgO-Al2O3-SiO2-Li2O system with addition of ZrO2 as nucleating agent and B2O3, which has the function to reduce the viscosity of the system during the melting process. The parent glasses were obtained by fusing at the temperature of 1650 ºC in crucible zirconia-mullite. The molten glasses were poured into a graphite mold to obtain the monolithic samples and also in water in order to obtain particulate material. Such material was grinded and then pressed by the uniaxial and isostatic pressing method before being sintered. Both the monolithic and pressed samples were performed under two different conditions of heat treatment for their nucleation and crystallization. In the first one the samples were heated to 1100 ºC with a heating rate of 10 ºC/min In the second one there was an initial heating rate of 10 ºC/min until reaching 780 ºC. Such temperature was kept for 5 minutes. After that, the samples were heated to 1100 ºC at a rate of 1 ºC/min microhardness analysis showed that base glass presented values around 7.0 GPa. The glass-ceramics obtained from the sintering powder had microhardness values smaller than those obtained from the monolithic samples. The highest hardness values were obtained in samples that were treated (10 ºC/min to 780 ºC and 1 ºC/min to 1100 ºC) which reached values around 9.2 ± 0.5 GP
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/103730 |
| Date | 28 August 2013 |
| Creators | Souza Filho, Manoel Pereira de [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Campos, Elson de [UNESP], Melo, Francisco Cristóvão Lourenço de [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 117 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |