Avaliação do diagrama de fases Ni-Al-Nb e obtenção da estrutura eutetica NiAl-NiAlNb

Orientador: Rubens Caram Junior / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-02T03:27:07Z (GMT). No. of bitstreams: 1
GarciaUrrutiaAraujo_FernandoLuis_M.pdf: 12841097 bytes, checksum: 7616bc4cce13fb5a7d3b91a7272ba131 (MD5)
Previous issue date: 2002 / Resumo: A solidificação de uma liga eutética permite produzir duas ou mais fases sólidas, que crescem de forma cooperativa. Tal fato toma esse tipo de liga atraente na obtenção de compósitos do tipo in situo Um compósito in situ exibe propriedades distintas das propriedade das fases que o constituem, o que pode resultar em um material com características interessantes no tocante a propriedades mecânicas, elétricas, magnéticas ou ópticas. O objetivo do presente trabalho é avaliar ligas do sistema Ni-Al-Nb, contendo a estrutura eutética formadas pelas fases NiAl e NiAlNb. A primeira parte do presente estudo consistiu na obtenção das ligas no estado bruto de fusão, em atmosfera inerte, e sua respectiva caracterização por microscopia óptica, eletrônica de varredura, fluorescência de raios-X, análise térmica diferencial e difração de raios-X. Em seguida, ligas eutéticas desse sistema foram processadas pela técnica de solidificação direcional em fomo de aquecimento indutivo do tipo Bridgman. As amostras obtidas foram caracterizadas da mesma maneira elaborada com as amostras no estado bruto de fusão. Com o objetivo de avaliar a estabilidade da microestrutura em altas temperaturas, ligas solidificadas direcionalmente foram submetidas a tratamento térmico. Finalmente, amostras no estado bruto de fusão e solidificadas direcionalmente foram ensaiadas através de teste de microdureza Vickers. Os resultados obtidos permitiram compreender o modo de crescimento do eutético estudado, sua morfologia, seu comportamento em altas temperaturas e alguns aspectos preliminares de seu comportamento mecânico / Abstract: The solidification of an eutectic alloy results in two or more solid phases, which grow in cooperative form. Such phenomenon makes this type of alloy interesting for obtainment of in situ composites. An in situ composite shows different properties than the individual component phases, that can result in a material with interesting features with regards to mechanical, electric, magnetic or optical properties. The aim of the present work is to evaluate alloys in the Ni-Al-Nb system, containing the eutectic structure formed by NiAl and NiAlNb phases. The first part of the present study consisted of the obtainment of cast eutectic structure in an electric arc furnace under inert atmosphere, and their characterization by optical and electronic microscopy, thermal analysis technique, X-rays fluorescence and X-rays diffraction. After that, the eutectic alloys were processed by directional solidification in a Bridgman type inductive furnace. The directionally solidified samples were characterized in the same way as the cast samples. In addition, the high temperature stability of the directionally solidified samples was evaluated. Finally, cast and directionally solidified samples were evaluated through microhardeness Vickers testing. The results allowed to understand the NiAl-NiAlNb eutectic growth, its morphology, its behavior in high temperatures and some preliminary aspects of its mechanical properties / Mestrado / Materiais e Processos / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263168
Date14 March 2002
CreatorsGarcia Urrutia Araujo, Fernando Luis
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Caram Junior, Rubens, 1958-, Junior, Rubens Caram, Ierardi, Maria Clara Filippini, Ranieri, Izilda Marcia
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format86f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds