Previous issue date: 1983 / Resumo: É analisada a eficiência de refino de estruturas de alumínio EC (Electrical Conductor) pela adição dos sais K2NbF7, K2ZrF6 e K2TiF6 em diferentes condições de concentração (0,01, 0,04, 0,07 e 0,10%At Nb, Ti, Zr), temperatura de inoculação/retenção (750 e 850ºC) e tempos de retenção (5, 60 e 120 minutos), às temperaturas indicadas, do líquido após inoculação. Um eficiente efeito de refino e obtido para a adição de teores de Nb acima de 0,04%At, sendo este efeito mantido constante independentemente do aumento posterior de tal teor, da temperatura de inoculação/retenção e tempo de retenção. Uma menor potência de refino para a maioria das condições verificadas, é obtida para outros dois elementos analisados, sendo ainda seu efeito reduzido pelo aumento do tempo de retenção e temperatura de inoculação. São ainda analisados os efeitos do refino da estrutura no limite de resistência à tração e alongamento do fundido, bem como resistência à tração e condutibilidade elétrica de fios obtidos de tais estruturas, no estado encruado e recristalizado. Um aumento em smax e %A é obtido pela redução do tamanho de grão do fundido, independentemente do tipo de elemento e teor adicionado. Não se observa efeito da presença de Nb, Zr e Ti no smax de fios tanto no estado encruado quanto recuperado, até o teor de 0,10%At adicionado. Uma drástica e crescente redução da condutibilidade elétrica é provocada pela adição de Ti em teores crescentes, enquanto a adição de Nb reduz menos significativamente tal propriedade; tal redução é mantida inalterada com o aumento do teor de Nb. / Abstract: It was analysed the possibility of grain refinement of Aluminium EC (Electrical Conductor) when K2NbF7, K2ZrF7 and K2TiF6 salts were added to liquid, in different amounts (0,01, 0,04, 0,07 and 0,10% At Nb, Ti, Zr), inoculation temperature (750, 850ºC) and retention time (5,60,120 minutes) previously to he pouring. An efficient effect was obtained for Nb additions higher than 0,04%At; this effect was kept constant with increasing amount, inoculation/retention temperature and time to pouring. An efficient effect was kept constant with increasing waiting time and inoculation/retention temperature. Changes in ultimate tensile strength (UTS) and elongation (%E) in as-casted structure, and also UTS and electrical conductivity of wires obtained form the initial inoculated ingots, promoted by Nb, Zr and Ti additions, were analysed. In the wires case, tests were made in the hardened structure and after heat treatment for recovery and recristalization. And increase in UTS and %E was observed when grain size decreases, in the as-casted structures, independent of type of element and amount added. It was not observed effect in UTS of wire, with or without heat treatment, due to Nb and Ti presence in the matrix, for amount less than 0,10%At. A serious and increasing reduction of electrical conductivity was observed with increasing Ti amounts; while Nb additions till 0,20%At provoked less dangerous reductions. This effect is mainteined fixed with increasing Nb amount from 0,04 to 0,10%At. / Doutorado / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265510 |
| Date | 15 July 2018 |
| Creators | Robert, Maria Helena, 1953- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Coppini, Nivaldo Lemos, 1944-, Cupini, Nivaldo Lemos |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Campinas |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 351f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds