Orientador: João Sinézio de Carvalho Campos / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-20T20:46:43Z (GMT). No. of bitstreams: 1
Lopes_SelmaAparecida_M.pdf: 4679717 bytes, checksum: b44b60b38798f2147b5fd6fe7eacc78f (MD5)
Previous issue date: 2012 / Resumo: O material polimérico denominado não tecido de polipropileno (NTPP), após receber adequado tratamento químico, tem sido largamente utilizado na indústria têxtil para confecção de produtos de higiene pessoal, fraldas e absorventes descartáveis. Neste sentido o presente trabalho analisa os efeitos das técnicas de descarga corona (atmosfera ambiente) e plasma por radiofrequência (atmosferas de oxigênio (O2), nitrogênio (N2) e argônio (Ar) causados nas propriedades de superfície de amostras de NTPP em função do tempo de tratamento e nas respectivas atmosferas citadas. Recortam-se amostras de NTPP com geometria retangular (10x30mm) e espessura média de 40?m. Após tratamentos por corona e plasma submetem-se as amostras ás técnicas de medidas de ângulo de contato (método da gota séssil), de espectrometria em infravermelho (FTIR/ATR), de microscopia eletrônica exploratória (SEM) e de calorimetria diferencial exploratória (DSC); as quais têm por objetivo caracterizar a superfície do material em relação à molhabilidade, a formação de grupos polares, alterações morfológicas e comportamento de volume, respectivamente. Realizaram-se as medidas em quintuplicatas e dentre os resultados pode-se destacar que (i) o ângulo de contato tende a diminuir com o aumento do tratamento tanto corona quanto plasma, indicando que está ocorrendo aumento da molhabilidade do material, assim como comprovado por cálculos de energia livre de superfície (por exemplo: sem tratamento 18 mN/m e após tratamento 87 mN/m); (ii) as espectrometrias em infravermelho indicam a formação de grupos polares (hidroxílicos e carboxílicos); (iii) os termogramas em DSC indicam que não há alterações entre amostras com e sem tratamento, preservando assim propriedades de volume do material (estabilidade térmica de 0 á 135ºC e Tm=162ºC). Cabe ressaltar que realizaram-se medidas sobre a durabilidade do tratamento corona e os resultados mostram satisfatória durabilidade até 4 dias / Abstract: The polymeric material known as non-woven polypropylene (NTPP) upon receiving suitable chemical treatment has been widely used in the textile industry for the manufacture of personal hygiene products, diapers and disposable absorbent. In this sense the present paper analyzes the effects of corona discharge techniques (ambient atmosphere) and plasma radiofrequency (atmospheres of oxygen (O2), nitrogen (N2) and argon (Ar) caused the surface properties of samples as a function NTPP treatment time and the respective atmospheres cited. Samples were cut out NTPP rectangular geometry (10x30mm) and an average thickness of 40?m. After corona treatment and plasma samples were subjected techniques measures the contact angle (sessile drop method), infrared spectrometry (FTIR/ATR), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC) which are intended to characterize the material surface with respect to wettability, the formation of polar groups, and morphological behavior volume, respectively. There were measures in quintuplicatas and among the results can be noted that (i) the contact angle tends to decrease with the increase in both corona treatment and plasma, indicating that it is an increase of the wettability of the material, as evidenced by calculations of surface free energy (for example, untreated 18 mN/m after treatment 87 mN/m; (ii) infrared spectroscopy indicated the formation of polar groups (hydroxyl and carboxyl); (iii) the DSC thermograms show no charges between treated and untreated samples, thus maintaining properties of the material volume (thermal stability of 0 to 135ºC and Tm=162ºC). It should be noted that measurements were performed on the stability of the corona treatment and the results show satisfactory stability up to 4 days / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266705 |
| Date | 20 August 2018 |
| Creators | Lopes, Selma Aparecida, 1974- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Campos, João Sinézio de Carvalho, 1955-, Ravagnani, Sergio Persio, Giordano, João Batista |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 115 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds