Orientador: Jose Roberto Lovadino / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T20:06:01Z (GMT). No. of bitstreams: 1
Fragoso_LarissaSilveiradeMendonca_M.pdf: 745321 bytes, checksum: 11d0220042f028180b3a2d86a37f5f8b (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo in vitro foi avaliar a influência de selantes de superfície na microinfiltração em dentes restaurados com resina composta; Foram utilizados 45 fragmentos de dentes incisivos bovinos onde foram realizados preparos cavitários do tipo Classe V. Os preparos foram restaurados com resina composta Z250, em seguida, foram armazenados em água destilada e mantidos em estufa a 37°C por 24 horas, e então, realizado acabamento e polimento. Após este procedimento, as restaurações foram divididas aleatoriamente em três grupos: grupo I (sem selamento) - controle; grupo II - as restaurações foram condicionadas e o sei ante de superfície Fortify (Bisco) foi aplicado na superfície da restauração; grupo m - as restaurações foram condicionadas e o selante de superfície Biscover (Bisco) foi aplicado na superfície da restauração. Em seguida as amostras foram armazenadas em água destilada por mais 12 horas a 37°C e submetidas à termociclagem. Para avaliar a infiltração marginal, as restaurações foram imersas em corante tamponado de azul de metileno 2%, por 4 horas. O método utilizado para a avaliação foi o qualitativo, por meio de um Estereomicroscópio onde três observadores calibrados avaliaram o nível de infiltração do corante na interface dente/material restaurador de acordo com os seguintes escores: 0= nenhuma infiltração do corante; 1= infiltração do corante na interface dente/restauração, até a metade da parede gengival; 2= infiltração do corante na interface dente/restauração, além da metade da parede gengival, sem atingir a parede axial; 3= infiltração do corante ao longo da interface dente/restauração até a parede axial ou além dela. Os resultados obtidos foram submetidos à análise estatística (Testes de Kappa e Kruskal-Wallis). Foi demonstrado que os selantes de superfície Fortify (Grupo lI) e Biscover (Grupo III), apresentaram as menores médias de infiltração marginal, diferindo estatisticamente do grupo controle (Grupo I). Desta forma, concluiu-se que o uso de selantes de superfície foi eficaz na diminuição da infiltração marginal / Abstract: The aim of this "in vitro" study was to evaluate the influence of sealants on the microleakage of teeth restored with composite. Class V cavity preparations were performed in 45 bovine incisive fragments. The cavities were filled with composite resin Z250. They were then stored in distilled water and placed in a incubator at 37°C for 24 hours followed by finishing and polishing. After this procedure, the samples were randomly divided into 3 groups: Group I (no sealant) - control; Group II- Samples were etched and the surface sealant Fortify (Bisco) was applied over the filling's surface; Group m- Samples were conditioned and Biscover (Bisco) was applied over the filling's surface. In a second moment, the fillings were stored once more in distilled water for 12 hours at 37°C and then were submitted to thermocyc1ing. To evaluate marginal infiltration, the samples were immersed in 2% methylene blue dye (pH 7,0), for 4 hours. The method used for evaluation was qualitative, through the manipulation of an Estereomicroscope where three observes analyzed the infiltration leveI of the pigment within the tooth/filling according the following scores: 0= no infiltration; 1= infiltration within tooth/material interface, beyond half of the gingival wall; 2 = infiltration within tooth/material interface, beyond half of the gingival wall, but not reaching the axial wall; 3 = infiltration within tooth/material interface up to or beyond axial wall. The results obtained were submitted to statistical analysis (Kruskal-Wallis Test). 1t was demonstrated that the surfaces sealantes Fortify (group II) and Biscover(group m) presented the lowest averages of marginal infiltration, and these results were statistically significant in relation to group control (group I). 1t can be conc1uded that the use of surface sealant was eficient on reducting the microinfiltration / Mestrado / Dentística / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289471 |
| Date | 07 January 2005 |
| Creators | Fragoso, Larissa Silveira de Mendonça |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Lovadino, José Roberto, 1953-, Aguiar, Flávio Henrique Baggio, Martins, Luís Roberto Marcondes |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 81f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds