Previous issue date: 2000 / Resumo: O propósito deste estudo foi avaliar a resistência ao cisalhamento de bráquetes fixados à cerâmica dental, utilizando as variáveis: materiais para colagem, tratamento superficial e aplicação do silano. Foram confeccionados 192 discos de cerâmica (Duceram) com 5 mm de diâmetro por 2 mm de espessura. Os discos foram embutidos com resina acrílica ativada quimicamente em tubos de P.V.C. e divididos em 4 grupos de 48 discos de acordo com o tratamento de superfície: Grupo I - condicionamento com ácido fosfórico 37%, por 30 segundos; Grupo 11 - condicionamento com ácido hidrofluorídrico a 10%, por 2,0 minutos; Grupo 111 - jateado com óxido de alumínio por 4 segundos; e, Grupo IV submetido apenas a profilaxia com pedra pomes e água por 30 segundos. Vinte e quatro corpos-de-prova de cada grupo receberam aplicação de silano e vinte e quatro não. Três materiais para colagem Transbond XT, Concise e Fuji Ortho LC foram utilizados para fixação dos bráquetes à cerâmica para cada grupo (com e sem silano) perfazendo um total de 64 fixações por material. Todas as amostras foram armazenadas em água destilada a 37° C, por 24 horas. Em seguida, as amostras foram submetidas ao teste de resistência ao cisalhamento numa máquina Instron a velocidade de 1,0 mm/min. Os resultados foram submetidos a análise de variância e ao teste de Tukey 5% de significância. Os resultados mostraram que independente do tratamento superficial da cerâmica e silanização o Transbond XT mostrou valores de resistência ao cisalhamento superiores em relação ao Concise e Fuji Ortho LC (p<0,05); o tratamento superficial da cerâmica com ácido hidrofluorídrico mostrou valores de resistência ao cisalhamento superiores em relação ao jateamento com óxido de alumínio, com condicionamento com ácido fosfórico e profilaxia com pedra pomes e água, independente do material para colagem e silanização (p<O,O5); e, a aplicação do silano aumentou a resistência da união cerâmicalbráquete para os três materiais e tratamentos superficiais, exceto para os bráquetes fixados na cerâmica com o Concise em superfícies submetidas à profilaxia com pedra pomes e água / Abstract: The purpose of this study was to evaluate the shear bond strength of brackets fixed on dental ceramic using three different materials with or without silane. One hundred ninety two specimens with 5 mm in diameter and 2 mm thickness were made with ceramic (Duceram). The specimens were divided into four groups according to surface treatments: Group I - acid etching with 37% phosphoric acid for 30 seconds; Group 11 - acid etching 10% hydrofluoridric acid for 2,0 minutes; Group 111 - Sandblasting with aluminum oxide for 4 seconds; and, Group IV - cleaned with pumice slurry. Twenty-four specimens of each group was treated with silane agents and twenty-four remained untreated. The brackets were bonded to ceramic with Transbond XT, Concise and Fuji Ortho LC. Ali specimens were stored in distilled water 37° C for 24 hours. After that the specimens were submitted to shear bond strength in an Instron at a crosshead speed of 1,0 mm/min. The results were submitted to variance analyses and Tukey's test (p<0.05). The date indicated that the Transbond XT showed higher values of shear bond strength than Concise and Fuji Ortho LC independent of the treatment on ceramic surface (p<0.05); the ceramic etching with hydrofluoridric acid of the ceramic showed higher values shear bond strength than the others three treatments for ali specimens (p<0.05); and the treatement with silane increased the shear bond strength of ceramic/bracket interface for ali materials, except Concise cleaned with pumice slurry on surface ceramic / Mestrado / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289584 |
| Date | 12 June 2000 |
| Creators | Borges, Gilberto Antonio |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Pfeifer, Jesuania Maria Guardiero Azevedo, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 131p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds