Orientador : Luiz Andre Freire Pimenta / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T21:06:54Z (GMT). No. of bitstreams: 1
Castro_AnaKarinaBarbieriBedrande_M.pdf: 3358547 bytes, checksum: f08d2334343db4f45a8c783fca6a268f (MD5)
Previous issue date: 2001 / Resumo: O objetivo deste trabalho, "in vitro", foi avaliar qualitativamente, através da penetração de corante, dois sistemas restauradores, e o efeito de uma camada intermediária de resina composta de baixa viscosidade. Foram selecionados 90 dentes bovinos, os quais tiveram parte da coroa seccionada a fim de padronizar comprimento de 4 mm no sentido ocluso-gengival. Em seguida, foram realizados preparos cavitários padronizados, nas faces mesial e distal, simulando classe II tipo "slot" vertical, com término em dentina, totalizando 180 preparos. As cavidades foram aleatoriamente divididas em 6 grupos (n=30): Gl- sistema adesivo Etch & Prime 3.0 (EP) (Oegussa) + resina "compactável" Oefinite (OEF) (Oegussa); G2- sistema adesivo Prime & Bond NT (PB) (Oentsply) + OEF; G3- EP + resina "flow" Wave (W) (SOl) + OEF; G4- PB + resina composta TPH Spectrum (TPH) (Oenstply); G5- EP + TPH; G6- PB + W + TPH. Após o acabamento e polimento, os espécimes foram submetidos a 1500 ciclos térmicos em banhos de 5 :t 2°C e 55 :t 2°C, com duração de 60 segundos para cada banho. Após ciclagem térmica, os dentes foram vedados com esmalte de unha e imersos em solução de azul de metileno a 2%, durante 4 horas. Em seguida, foram realizados seccionamentos ao meio das restaurações e analisadas qualitativamente em lupa estereoscópica (45X), seguindo um padrão de escores em dentina (O a 4). Também foi avaliado o padrão de infiltração (adesivo ou dentinário) dos espécimes que infiltraram. Os dados foram submetidos ao Teste Kappa de reprodutibilidade interexaminadores, e a média dos escores dos 3 examinadores foi analisada pelo Teste não-paramétrico de Kruskall-Wallis e Teste não-paramétrico de Comparação Múltipla com p<0,05. O padrão de infiltração foi analisado pelo Teste Exato de Fisher. Os postos médios dos grupos foram dispostos em ordem crescente dos valores: G4-6723(a). G3- 7258 (ab). G6- 7843 (ab). G5- 93 19 (be). G2- 11297 (e). Gl- 11352 (e) Conclui-se que nenhum dos sistemas utilizados foi capaz de impedir a microinfiltração, e o uso de uma resina "flow" reduziu os valores de infiltração para a resina OEF. O padrão de infiltração para os grupos que utilizaram PB foi dentinário, apresentando-se predominantemente adesivo para EP / Abstract: The purpose of this study was to evaluate the "in vitro", marginalleakage, with dye penetration, of two restorative systems and the application of a flowable composite resin as an intermediate layer. Ninety bovine teeth were selected and had part of the crown sectioned allowing a standardization of 4 mm of height from ocluso-gengival proximal margins. Standardized cavities preparations simulating class 11 type box were design with gingival margin at dentin, on mesial e distal faces. The cavities were randomly divided in 6 groups (n=30): G1- adhesive system Etch & Prime 3.0 (EP) (Oegussa) + Oefinite composite resin (OEF) (Oegussa); G2- adhesive system Prime & Bond NT (PB) (Oentsply) + OEF; G3- EP + Wave flowable resin (W) (501) + DEF; G4- PB + TPH Spectrum composite resin (TPH) (Oenstply); G5- EP + TPH; G6- PB + W + TPH. After finishing and polishing, the specimens were subjected to 1500 thermal cycles in bath of 5 :i: 2°C e 55 :i: 2°C with 60 seconds dwell time each bath. After thermocycling, the specimens were sealed with nail vamish and immersed for 4 hours in a 2% solution of methylene blue. Than the specimens were sectioned longitudinally through the center of the restoration and qualitatively evaluated by stereomicroscopy (45X), following a ranked score for dentin margin (O a 4). The leakage partem (adhesive or dentin) was also evaluated for those specimens that had leakage. The data were subjected to a reproducibility Kappa T est and the mean of the 3 examiners scores were analyzed by Kruskall-Wallis non-parametric Test and multiple comparison non-parametric Test (p<0.05). For leakage partem Fisher Exact Test was used. The ranked values of the groups were expressed in decreasing order: G4- 67.23 (a); G3- 72.58 (ab); G6- 78.43 (ab); G5- 93.19 (be); G2- 112.97 (e); G1- 113.52 (e). It was concluded that all systems used were not able to impede the microleakage, and the use of a flowable resin decrease the values of leakage for the resin OEF. The partem of leakage for the groups that used PB was at dentin, showing mostly adhesive to EP / Mestrado / Dentística / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289749 |
| Date | 29 March 2001 |
| Creators | Castro, Ana Karina Barbieri Bedran de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Pimenta, Luiz Andre Freire, 1965-, Baron, Giselle Maria Marchi, Mauro, Silvio Jose |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 99p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds