Previous issue date: 1995 / Resumo: o objetivo deste trabalho foi avaliar a resistência à fadiga das ligas do sistema Co-Cr (Steldent, Dentorium e Biosil), utilizadas na condição de novas e refundidas, submetidas ou não ao procedimento de soldagem convencional. Para cada uma das ligas avaliadas, quarenta amostras cilíndricas com diâmetro de 1,7 mm foram obtidas por fundição odontológica, utilizando maçarico à oxigênio e acetileno . Vinte amostras foram obtidas com liga nova e outras vinte pela mistura de partes iguais de liga nova e liga previamente fundida. O procedimento de soldagem foi realizado em vinte amostras de cada uma das ligas, dez novas e dez refundidas. No processo, foi utilizada liga de solda à base de Co-Cr, fundida por meio de maçarico à oxigênio e gás (G.L.P.). Foi padronizada uma distância de 0,3 mm entre as extremidades das amostras a serem soldadas, as quais foram usinadas para obtenção de geometria cônica (ponta de lápis). O ensaio de resistência à fadiga foi conduzido numa máquina de cargas cíclicas AMSLER (Alfred J. Amsler & Co. - Shaffuausen - Schaweis Switzerland), regulada com carregamento constante de tração de 1 kg, com as amostras solicitadas à flexão por ciclo osciliatório de 2° para cada lado. Após a fratura, o número de ciclos era registrado e a superficie de fratura analisada sob microscoJ?ia eletrônica de varredura (M.E. V.). Com base nos resultados obtidos, verificamos que: l-Na condição de novas, a liga Biosil mostrou-se superior .estatisticamente às ligas Steldent e Dentorium, as quais foram semelhantes estatisticamente entre si; 2- Para as três ligas ensaiadas na condição de novas, as amostras submetidas ao procedimento de soldagem , foram estatisticamente semelhantes e inferiores às livres de solda; 3-Quando refundidas, a liga Steldent foi semelhante estatisticamente às ligas Dentorium e Biosil, a qual mostrou superioridade estatística em relação à liga Dentorium; 4- Para as três ligas ensaiadas na condição refundidas, as amostras submetidas ao procedimento de soldagem foram estatisticamente semelhantes e inferiores às livres de solda; 5-Não houve diferenças estatisticamente significantivas entre as amostras obtidas pela fusão de partes iguais de liga nova e liga refundida e aquelas oriundas exclusivamente de liga nova, soldadas ou não / Abstract: The aim of this study was to evaIuate the fatigue strength of Steldent, Dentorium and Biosil partiaI denture framework Co-Cr based alloys, as new and in mixture of new and previously casted alloy, submitted or not to convencional soldering procedure. Forty rods with 1,7mm in diameter were casted with oxi-acetilene torch for each of the alloys tested. Half specimens were obtained with new alloy and the others, as a misture ofhaIfnew and ha1fpreviously casted alloy. The soldering procedme was conducted in twenty specimens of each alIoy, half new and half refused alloy. The joints were obtained by Co-Cr welding rods and gas-oxygen torch. The solder gap selected was 0,3 mm and the segments were machined until a conicaI shaped end was achieved. The fatigue strength was conducted in a AMSLER (Alfred 1. Amsler & Co. - Shaflhausen - Schaweis - Switzerland) fatigue testing machine and the specimens were sujected to a tensile load of I kg and a ciclic stress amplitude of 2° . Afier failure, the cycles were registered and the fracture surface was examined with scannig electron microscope (S.E.M.) Related to fatigue strength, the results of this study indicated the folIowing: l-As new, Biosil was statistically stronger than Steldent and Dentori~ aIloys; 2-As new, there were no significant differences among soldered specimens, however all were statisticaIly weaker than the intact ones; 3-when refused, there were . 'no significant differences between Steldent and Dentorium and between Steldent and Biosil, however Biosil was statisticaIly stronger than Dentorium alloy; 4-As refused, the data of soldered specimens were statistically the same, but weaker than the intact ones; 5-there were no significant differences between new and refused specimens, soldered or not / Doutorado / Protese / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290101 |
| Date | 30 November 1995 |
| Creators | Henriques, Guilherme Elias Pessanha, 1968- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Silva, Frederico Andrade e, Domitti, Saide Sarckis, Rollo, Joao Manoel Domingos de Almeida, Dinelli, Wellington |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 128f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds