Previous issue date: 2012-04-13 / This work presents a numerical-experimental correlation of the factors that may influence the hardenability of SAE 1045 steel subjected to the Jominy end quench test at austenitizing temperature of 850 ?C. This correlation was made by calculating the heat transfer coefficient and its phase‟s presents during the cooling of the specimen. These calculations were obtained based on thermal analysis of the test, through the cooling rates. A thermocouple was installed near from the edge of the specimen to obtain the cooling temperature curves. Based on these informations were estimated uncertainties of measurement temperature ? 23 ?C for an evaluation of the reproducibility of the process, even an error of ? 10.3 ?C. During the Jominy test, should be considered parameters such as hydraulic pressure suitable austenitizing temperature with a tolerance of ? 6 ?C, temperature and water flow. These parameters change the phase heat transfer, and also the flux density and therefore the heat transfer coefficient of heat. It was determined the variation of the heat transfer coefficient versus time h=f(t), and the average value is close to theorycal value, which is approximately 15.3 kW/m2.K / O trabalho aborda uma correla??o num?rico-experimental dos fatores que podem influenciar a temperabilidade de um a?o SAE 1045 submetido ao Ensaio Jominy em uma temperatura de austenitiza??o de 850?C. Tal correla??o foi feita a partir do c?lculo do coeficiente de transfer?ncia de calor e os modos presentes durante o resfriamento do corpo de prova. Estes c?lculos foram obtidos com base na an?lise t?rmica do ensaio, atrav?s das taxas de resfriamento. Para isso, um termopar foi instalado em uma dist?ncia pr?xima da extremidade do corpo de prova a fim de obter as curvas de resfriamento. Com base nestes dados foi calculada a incerteza de medi??o de temperatura de ? 23 ?C, para uma avalia??o da repetibilidade do processo, chegando ao erro de ? 10,3 ?C. Devem ser levados em considera??o durante o ensaio Jominy par?metros significativos como: press?o hidr?ulica adequada, temperatura de austenitiza??o com toler?ncia de at? ? 6?C, temperatura e vaz?o da ?gua. Estes par?metros alteram as condi??es de transfer?ncia de calor, e tamb?m a densidade de fluxo de calor e por conseq??ncia o coeficiente de transfer?ncia de calor. Foi determinada a varia??o do coeficiente de transfer?ncia de calor em rela??o ao tempo h = f(t), e seu valor m?dio est? de acordo com o valor informado na teoria, que ? de aproximadamente 15,3 kW/m?K
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.pucrs.br:tede/3204 |
| Date | 13 April 2012 |
| Creators | Petersen, Jefferson Ricardo Bilheri |
| Contributors | Santos, Carlos Alexandre dos |
| Publisher | Pontif?cia Universidade Cat?lica do Rio Grande do Sul, Programa de P?s-Gradua??o em Engenharia e Tecnologia de Materiais, PUCRS, BR, Faculdade de Engenharia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS, instname:Pontifícia Universidade Católica do Rio Grande do Sul, instacron:PUC_RS |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -7432719344215120122, 500, 600, -655770572761439785 |
Page generated in 0.002 seconds