Previous issue date: 2017-12-07 / O objetivo deste estudo foi avaliar o efeito da aplicação de primers
experimentais à base de flavonoides na resistência de união, nanodureza,
módulo de elasticidade e micromorfologia da interface adesiva criada em
dentina hígida e dentina afetada por cárie utilizando um adesivo universal
aplicado em modo convencional. Superfícies planas de dentina foram expostas
em 182 molares permanentes. Noventa e um molares foram armazenados em
água, enquanto os outros 91 foram imersos em uma solução de BHI/Sacarose
(pH 4.0) e cepas de Streptococcus mutans por 14 dias para induzir lesões
artificiais de cárie em dentina. Quarenta e nove dentes foram aleatoriamente
alocados em 7 grupos (n=7) de acordo com o primer experimental usado em
cada tipo de substrato (hígido ou afetado por cárie): Controle, sem aplicação de
primer (CON), Placebo solução hidroalcoólica com tensoativo (PLA),
Proantocinidina (PRO), Quercetina (QER), Naringina (NAR), Rutina (RUT), e
Hesperidina (HES). Após o condicionamento, lavagem e secagem das
superfícies de dentina, os primers foram ativamente aplicados por 1 min para
reumedecer a dentina. Após serem restaurados, os espécimes foram
seccionados no seu longo eixo até obter palitos retangulares (0,9 mm2) que
foram testados em tração com velocidade de 1 mm/min, tanto após 24 h quanto
após 25.000 ciclos em uma máquina de ciclagem térmica (5 ºC / 55 ºC). Para
os testes de nanodureza e módulo de elasticidade (n=3), os espécimes foram
cortados longitudinalmente até obter duas fatias planas (1,2 mm) e foram
analisados em um nanoindentador com uma ponta Berkovich tanto após 24 h
quanto após 25.000 ciclos térmicos. Para a análise qualitativa de
microinfiltração, 21 dentes (n=3) assistida por corantes em Microscópio
confocal (CSLM), o adesivo e a resina composta foram misturados com 0,2%
de Rhodamina B (massa) antes dos procedimentos restauradores e duas fatias
planas foram obtidas para análise após 24 h e 25.000 ciclos térmicos. As fatias
foram imersas em uma solução de Fluoresceína (0,1%) por 4 horas. Quatro
imagens da interface adesiva de cada dente foram obtidas em cada momento
experimental (24 h ou 25.000 ciclos) a 5 e 10 μm de profundidade. Os
resultados foram analisados usando uma análise de variância de medidas
repetidas e pós-teste de Bonferroni (= 0,05). Resultados: Os grupos PLA e
RUT mostraram os valores mais altos de μTBS em dentina hígida em ambos
intervalos (p > 0,05). Na dentina afetada por cárie os grupos RUT e NAR
apresentaram os valores mais altos em ambos intervalos. As imagens de
CSLM mostraram sinais de infiltração em todos os grupos. PLA, RUT, NAR e
PRO mostraram áreas sem infiltração em ambos intervalos e tipo de substrato.
As nanopropriedades foram influenciadas pelos grupos experimentais em
profundidade dependendo do flavonoide usado. Conclusão: O uso de
flavonoides poderia ser uma alternativa terapêutica em dentina hígida e afetada
por cárie para melhorar as propriedades e longevidade da interface adesiva. / The aim of this study was to evaluate the effect of experimental flavonoid
primers on bond strength, nanohardness, elastic modulus, and
micromorphology of bonding interfaces created on sound and caries-affected
dentin using one commercially available universal bonding agent applied in the
etch-and-rinse mode. Flat midcoronal dentin surfaces were exposed in 182
permanent molars. Ninety-one molars were stored in water while the other 91
molars were kept in a BHI/Sucrose solution (pH 4.0) with Streptococcus mutans
strain for 14 days to induce artificial caries-affected dentin. Forty-nine teeth
were randomly assigned to 7 groups (n=7) according to the experimental primer
applied to each dentin surface condition (sound or caries-affected dentin):
Control, in which no primer was applied (CON), Hydroalcoholic solution with
surfactant Placebo (PLA), Proanthocianidin (PRO), Quercetin (QER), Naringin
(NAR), Rutin (RUT) and Hesperidin (HES). After etching, rinse and drying the
dentin surfaces, the primers were actively applied for 1 min to rewet the dentin
surface. After bonding and restorative procedures, specimens were sectioned in
the long axis to obtain rectangular sticks (0.9 mm2) that were subjected to
microtensile tests (μTBS) at a crosshead speed of 1 mm/min, either 24 h or
after 25.000 cycles in a thermocycling machine (5ºC / 55ºC). For nanohardness
and elastic modulus (n=3), the specimens were longitudinally sectioned to
obtain 2 flat silces (1,2 mm) and were analyzed in a nanohardness device with
a Berkovich indenter either after 24 h or after 25.000 (5 ºC / 55 ºC) thermal
cycles. For the dye assisted microinfiltration qualitative analysis 21 teeth (n=3)
was performed with a Confocal Scanning Laser Microscope (CSLM), both
adhesive system and resin composite were mixed with 0.2% (weight)
Rhodamine B prior to the restorative procedure and two flat slices were
obtained for analysis in 24 h and after 25.000 thermal cycles. The bonding
interfaces were immersed in a 0,1%. Fluorescein solution for 4 hours. Four
images of bonding interface per specimen where obtained in each experimental
time (24 h and 25.000 cycles) at 5 and 10 m depth. The data were analyzed
using two-way repeated measures ANOVA and Bonferroni post-hoc test ( =
0.05). Results. PLA and RUT showed the highest TBS values in sound teeth
at both intervals (24h and ageing) (p>0.05), while RUT and NAR showed the
highest TBS values in carious teeth in both stages. CLSM analysis showed
signs of microinfiltration for all groups. PLA, RUT, NAR and PRO showed areas
of no infiltration in both experiments and intervals. Nanomechanical properties
were influenced by experimental groups in deep, dependending on the
flavonoid used. Conclusion: The use of flavonoids may be an alternative for
therapeutic substances in sound or carious dentin to improve their properties
and longevity in the adhesive interphase.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2423 |
| Date | 07 December 2017 |
| Creators | Sánchez, Carlos Andrés Dávila |
| Contributors | Arrais, Cesar Augusto Galvão, Loguercio, Alessandro Dourado, Fernandez, Eduardo, Stanislawczuk, Rodrigo, Chibinski, Ana Cláudia, Gomes, João Carlos |
| Publisher | Universidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Odontologia, UEPG, Brasil, Departamento de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0059 seconds