The Digitization Centre has determined that page 49 was not published with the original copies of this thesis. / The validity of current theories of precipitate morphology is dependent on the microscopic nature of the precipitate-matrix interface. It is the purpose of this thesis to investigate, by electron microscopy interfacial structure and mobility in precipitation reactions pertaining to these theories. In particular the B->a Widmanstatten reaction in 60:40 brass is investigated and compared with the B->y reaction in a Cu-Zn-Sn alloy. / Thesis / Master of Science (MS)