<p>Hydrogenated amorphous silicon (a-Si:H) is second only to crystalline silicon in volume manufacturing of solar cells due to its attractive characteristics for solar panel manufacturing. These are lower manufacturing costs, and the fact that it can be deposited on any surface, and in any shape even on flexible substrates. The metal induced crystallization of hydrogenated amorphous silicon has been the subject of intense scrutiny in recent years. By combining the technology of hydrogenated amorphous silicon thin films with the superior characteristics of c-Si material, it is hoped that more efficient solar cells can be produced. In this thesis we report on the metal-mediated-thermally induced changes of the structural and optical properties of hydrogenated amorphous silicon deposited by hot-wire CVD, where aluminium and nickel were used to induce crystallization. The metal-coated amorphous silicon was subjected to a thermal annealing regime of between 150 and 520° / C. The structural measurements, obtained by Raman spectroscopy, show partial crystallization occurring at 350 ° / C. At the higher annealing temperatures of 450° / C and 520° / C complete crystallization occurs. Reflection and transmission measurements in the UV-visible range were then used to extract the optical properties. By adopting the effective medium approximation a single optical model could be constructed that couldsuccessfully model material that was in different structural phases, irrespective of metal contamination. Changes in the absorption of the material in various stages of transition were confirmed with a directly measured absorption technique, and the modelled absorption closely followed the same trends This study forms part of the larger overall solar cell research project, of which the primary aim is to eventually develop a silicon solar panel that optimises the characteristics for best performance.</p>
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:uwc/oai:UWC_ETD:http%3A%2F%2Fetd.uwc.ac.za%2Findex.php%3Fmodule%3Detd%26action%3Dviewtitle%26id%3Dgen8Srv25Nme4_2308_1280954238 |
| Date | January 2009 |
| Creators | Muller, Theophillus Frederic George |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis and dissertation |
| Format | |
| Coverage | ZA |
| Rights | Copyright: University of the Western Cape |
Page generated in 0.0023 seconds