The process, structure, and property relationship of PAN fiber as a precursor to carbon fiber was studied. The limitations of stable spinning and property improvement associated with hot draw in solution spinning were found and quantified. Conditions were varied to generated precursor fiber up to the limit of draw, from which actual samples were collected for thermal conversion to carbon fiber. Samples of PAN and subsequent carbon fiber were characterized using tensile testing and x-ray analysis. The effects of draw on modulus and break stress, as well as the orientation of the crystalline structure of both parent precursor and resultant carbon fiber were found and related back to the quantified draw limit.
| Identifer | oai:union.ndltd.org:uky.edu/oai:uknowledge.uky.edu:me_etds-1094 |
| Date | 01 January 2017 |
| Creators | Edrington, Sarah |
| Publisher | UKnowledge |
| Source Sets | University of Kentucky |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations--Mechanical Engineering |
Page generated in 0.002 seconds