Aluminum and aluminum-alumina powder mixtures were used to produce pyramidal fin arrays on aluminum substrates using cold spray as an additive manufacturing process. Using aluminum-alumina mixtures instead of pure aluminum powder could be seen as a cost-effective measure, preventing nozzle clogging. The fin geometries that were produced were observed using a 3D digital microscope to determine the flow passages width and fins geometric details. Heat transfer and pressure tests were carried out using different ranges of appropriate Reynolds numbers for the sought commercial application to compare each fin array and determine the effect of alumina content. It was found that the presence of alumina reduces the fins’ performance when compared to pure aluminum but that they still outperform traditional fins. Numerical simulations were performed and were used to explain the obtained experimental results. The numerical model opens up new avenues in predicting different parameters such as pressure and substrate temperature.
| Identifer | oai:union.ndltd.org:uottawa.ca/oai:ruor.uottawa.ca:10393/33383 |
| Date | January 2015 |
| Creators | Farjam, Aslan |
| Contributors | Jodoin, Bertrand |
| Publisher | Université d'Ottawa / University of Ottawa |
| Source Sets | Université d’Ottawa |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0138 seconds