Contactless electroreflectance (CER), a modulation spectroscopy (MS) technique, has been used to study the A and C exciton transitions in A1xGa1-xN layers for a composition range of 0 ≤ x ≤ 0.48 at room temperature. Taking the entire composition range (0 ≤ x ≤ 1) into account by incorporating a previously reported band gap energy for AlN, the dependence of the A-exciton transition on composition showed a downward bowing from linearity. A bowing parameter of b = 1.7 eV was found. Analysis of the lower composition range 0 ≤ x ≤ 0.48 resulted in a linear fit, as did the trend for the detectable C exciton transitions. The slope of the linear trendlines for the A and C exciton were practically the same.
| Identifer | oai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-2001 |
| Date | 01 January 2006 |
| Creators | McGlinchey, Laura C. |
| Publisher | VCU Scholars Compass |
| Source Sets | Virginia Commonwealth University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | © The Author |
Page generated in 0.0019 seconds