Thesis (Ph.D.) - Carleton University, 2007. / Includes bibliographical references (p. 128-137). Also available in electronic format on the Internet.

Thesis (M.App.Sc.) - Carleton University, 2007. / Includes bibliographical references (p. 82-92). Also available in electronic format on the Internet.

Thesis (M.App.Sc.) - Carleton University, 2007. / Includes bibliographical references (p. 105-109). Also available in electronic format on the Internet.

Thesis (M.S.)--Ohio University, March, 2009. / Title from PDF t.p. Includes bibliographical references.

Thesis (Ph. D.)--Ohio State University, 2005. / Title from first page of PDF file. Document formatted into pages; contains xxiii, 261 p.; also includes graphics. Includes bibliographical references (p. 256-261). Available online via OhioLINK's ETD Center

Thesis (Ph. D.)--University of Texas at Austin, 2004. / Supervisor: Ray T. Chen. Vita. Includes bibliographical references.

Thesis (M.A.)--Baylor University, 2009. / Includes bibliographical references (p. 108-117).

Th.--Électronique--Toulouse--I.N.P., 1978. N°: 36.

Um dos problemas da fabricação de protótipos de dispositivos fotônicos esta no controle dos vários parâmetros de construção. A utilização do laser de femtosegundo para a fabricação de dispositivos óticos esta cada vez mais comum devido as suas qualidades e propriedades. Com a utilizaçãao das instruções de programação e do laser de femtosegundo foi possível a alteração do índice de refração dos substratos de sodocálcico e de sílica fundida, tornando viável o guiamento em estruturas planas. Com estas estruturas de guiamento devidamente produzidas e caracterizadas, permitiu construir um acoplador direcional, mostrando a possibilidade de controle para fabricação de diversos dispositivos. / One of the problems of manufacturing prototypes of photonic devices that control the various parameters of construction. The utilization of the femtosecond laser for the fabrication of optical devices is increasingly common due to their qualities and properties. With the utilization of the instructions for programming and femtosecond laser was possible alteration of the index of refraction of the substrates of soda-lime and fused silica, making viable guiding in planar structures. With these guiding structures properly produced and characterized, it was possible to build a directional coupler, showing the possibility of control for the manufacture of various devices.

Submitted by Claudia Rocha (claudia.rocha@udesc.br) on 2018-03-14T16:47:07Z No. of bitstreams: 1 PGCA16MA205.pdf: 2376420 bytes, checksum: 7adb5710821c906867f36fd27eb356b4 (MD5) / Made available in DSpace on 2018-03-14T16:47:07Z (GMT). No. of bitstreams: 1 PGCA16MA205.pdf: 2376420 bytes, checksum: 7adb5710821c906867f36fd27eb356b4 (MD5) Previous issue date: 2016-07-06 / PROMOP / CAPES / This study aimed to analyze and compare different combinations of biocements in relation to osteoinductive and osseocondutive potential, applied by growth guides in rabbit calvaria. We used 14 New Zealand male rabbits, with 6 months of age and average weight of 3.28 ± 0.44 kg, proved healthy through physical examination and hematologic analysis. After performing anesthesia, the animals underwent periosteal bone exposure of the calvaria and each rabbit were attached four cylindrical polyamide guides with stainless steel bolt. Of these guides, three were filled with materials in the form of biocement consisting of: hydroxyapatite 100% (HA 100%), Hydroxyapatite 95% plus Alumina 5% (HA95% + Al5%) and Hydroxyapatite 99% plus Mg 1% (HA99% + Mg1%) and one with autologous blood clot (control). The animals were randomly assigned into two groups: M60 (n = 07) and M90 (n = 07) who were euthanized at 60 and 90 days postoperativelyand the calvaria was removed and wrapped in formaldehyde for 15 days. After, the calvaria was sectioned in four squares, each containing the biomaterial or control and is maintained in buffered formaldehyde for 15 days for histological evaluations and scanning electron microscopy (SEM). Analyzing the images and histological micrographs obtained with the SEM the control samples showed no significant bone growth. The biocements formed by HA100% and HA99% + Mg1% proved promising, leading to an important exoskeletal bone growth (osteoinduction), since the base and the apex of the samples (osseoconduction) and showed no rejection indicated by small amount of fibrous tissue and inflammatory cells. Samples containing HA99% + Mg1% provided greater bone growth at an early stage as compared those containing HA100%. Samples composed of hydroxyapatite 95% + Alumina 5% did not obtain satisfactory results, leading to tiny bone formation and showing signs of rejection. Based on these, the biociment composed of HA100% and the composite formed by HA99% and Mg1% are promising and likely to be used as bone neocresciment promoters / O presente estudo objetivou analisar e comparar diferentes combinações de biocimentos em relação ao seu potencial osseoindutivo e osseocondutivo, quando plicados através de guias de crescimento na calvária de coelhos. Foram utilizados 14 coelhos da raça Nova Zelândia, machos, com 6 meses de idade e peso médio de 3,28 ± 0,44 kg, comprovadamente hígidos através de exame físico e análise hematológica. Após realização de anestesia e em adequado plano cirúrgico, os animais foram submetidos à exposição óssea periosteal da região da calvária, onde, em cada coelho, foram fixados com parafuso de aço inoxidável, quatro guias cilíndricas de poliamida. Destas guias, três foram preenchidas com materiais na forma de biocimento, compostos por: Hidroxiapatita a 100% (HA 100%), Hidroxiapatita 95% + Alumina 5% (HA95% + Al5%) e Hidroxiapatita 99% + Magnésio 1% (HA99% + Mg1%) e uma com coágulo sanguíneo autólogo (controle). Os animais foram distribuídos aleatoriamente em dois grupos: M60 (n=07) e M90 (n=07), que foram eutanasiados com 60 e 90 dias de pós-operatório, respectivamente, sendo a calvária removida e acondicionada em formaldeído por 15 dias. Após, a calvária foi seccionada na forma de quatro quadrados, cada qual contendo o biomaterial ou o controle, sendo mantidos em formaldeído tamponado por mais 15 dias e então encaminhados para avaliações histológicas e para a realização de microscopia eletrônica por varredura (MEV). Analisando as imagens histológicas e as micrografias obtidas com a MEV, observou-se que as amostras controle não apresentaram crescimento ósseo expressivo. Os biocimentos formados por HA100% e HA99% + Mg1% se mostraram bastante promissores, levando a um importante crescimento ósseo exoesqueletal (osseoindução), desde a base quanto ao ápice das amostras (osseocondução) e apresentaram ausência de rejeição, indicada pela pequena quantidade de tecido fibroso e células inflamatórias. As amostras contendo HA99% + Mg1% proporcionaram maior crescimento ósseo em uma fase inicial quanto comparada as que continham HA100%. As amostras compostas por hidroxiapatita 95% + Alumina 5% não obtiveram resultados satisfatórios, levando à ínfima neoformação óssea e apresentando sinais de rejeição. Frente ao exposto, o biocimento composto por HA 100% e o compósito formado por HA99% e Mg1% são promissores e passíveis de serem utilizados como promotores de neocrescimento ósseo