Discontinuity surfaces generally consist of undulations termed as roughness. It is well known that surface roughness plays an important role on the shear strength and shear behavior of discontinuities. However, the effect of roughness will not be the same when the direction of shearing changes. This effect causes variation of shear strength with shearing direction or in other words anisotropy on shear strength. In this thesis, an experimental study was performed to investigate the effect of roughness and anisotropy on shear strength. For this purpose, joint samples were prepared using a model material and direct shear tests were conducted at different normal stress levels and shearing directions.

Thesis (Ph. D.)--Carleton University, 2003. / Includes bibliographical references (p. 138-146). Also available in electronic format on the Internet.

Thesis (M.App.Sc.) - Carleton University, 2006. / Includes bibliographical references (p. 151-155). Also available in electronic format on the Internet.

Thesis (M.S.)--University of Alabama at Birmingham, 2009. / Title from PDF title page (viewed on Sept. 3, 2009). Includes bibliographical references (p. 32-37).

Submitted by TAYANE WESTERMANN LOPES CASTILHO null (tayanewest@uol.com.br) on 2018-01-26T16:12:01Z No. of bitstreams: 1 Dissertação Tayane Westermann Lopes Castilho.pdf: 4997047 bytes, checksum: c0457ac97bc5e87fd929dbe70703dd0d (MD5) / Approved for entry into archive by Maria Marlene Zaniboni null (zaniboni@bauru.unesp.br) on 2018-01-26T18:07:08Z (GMT) No. of bitstreams: 1 castilho_twl_me_bauru.pdf: 4997047 bytes, checksum: c0457ac97bc5e87fd929dbe70703dd0d (MD5) / Made available in DSpace on 2018-01-26T18:07:08Z (GMT). No. of bitstreams: 1 castilho_twl_me_bauru.pdf: 4997047 bytes, checksum: c0457ac97bc5e87fd929dbe70703dd0d (MD5) Previous issue date: 2017-12-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este trabalho avaliou a influência da inclusão de fibras recicladas extraídas de garrafas constituídas de politereftalato de etileno (PET) na resistência ao cisalhamento de solos arenoso e argiloso. Por meio de ensaios de compressão simples das amostras dos solos e misturas desses com diferentes teores e comprimentos de fibras, obteve-se que a combinação de 1,5% de fibras, em relação à massa de solo seco, com comprimento de 20 mm levou a um aumento de 92,8% na resistência não confinada para a amostra de solo arenoso, e de 10,5% para a de solo argiloso. Ensaios de cisalhamento direto foram realizados com essa dosagem, em duas diferentes condições de compactação, e revelam o ganho de 66,4% no intercepto de coesão para o solo arenoso com grau de compactação de 100%, e de 55,5% com grau de compactação de 95%, em relação ao solo sem fibra. Enquanto os ângulos de atrito interno praticamente não se alteraram. A mesma dosagem para o solo argiloso promoveu reduções de coesão de 7,6% e 5,4%, respectivamente, para os graus de compactação de 100% e de 95% e aumentos relativos de 2,9% e 7,3% no ângulo de atrito interno. Esses resultados aplicados em dois casos hipotéticos, capacidade de carga de fundações em sapatas e estabilidade de taludes de aterros, demonstram o efeito da inclusão de fibras na melhoria da estimativa da capacidade de carga para ambos os solos e o aumento do fator de segurança para o solo arenoso. O trabalho oferece uma alternativa tecnicamente viável para a melhoria dos solos e que prioriza o reuso de garrafas PET, colaborando para preservação ambiental, mas não só, pois a atividade promove ainda benefícios sociais e econômicos. / This study presents an analysis of the influence of the inclusion of polyethylene terephthalate (PET) fibers, extracted from waste plastic bottles, in the shear strength of sandy and clayey soils. Simple compression tests were performed with soil samples and mixtures of these with different fiber contents and lengths. The combination of 1,5% of fibers in relation to the dry soil mass with a length of 20 mm led to a 92.8% increase in the unconfined resistance for the sandy soil sample and 10.5% for the clayey soil sample. Direct shear tests were carried out with this dosage, with two different compaction conditions, showing the gain of 66.4% in the cohesion intercept for sandy soil with 100% compaction degree, and 55.5% with the degree of 95%, in relation to the soil without fiber. While the angles of internal friction remained almost constant. The same dosage for clayey soil promoted cohesion reductions of 7.6% and 5.4%, respectively, for compaction degrees of 100% and 95% and relative increases of 2.9% and 7.3% in the angle of internal friction. These results, applied in two hypothetical cases, load capacity of an isolated footing foundation and slope stability of landfills, demonstrate the effect of the inclusion of fibers in improving the estimation of the load capacity for both soils and the increase of the safety factor for the sandy soil. The study offers a technically feasible alternative for the improvement of soils, and that prioritizes the reuse of PET bottles, collaborating for environmental preservation, but not only, since the activity also promotes social and economic benefits.

Made available in DSpace on 2014-06-11T19:28:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-03-31Bitstream added on 2014-06-13T20:18:32Z : No. of bitstreams: 1 abirached_fo_me_arafo.pdf: 762282 bytes, checksum: bf4b7b544331c76ec042fed619402110 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O titânio, em virtude de suas atrativas propriedades, foi introduzido na área de reabilitação oral podendo ser indicado para a confecção de restaurações metalocerâmicas dento- ou implanto-suportadas. No entanto, apresenta dificuldade de união com materiais resinosos, o que poderia comprometer a longevidade dessas restaurações, considerando a importância da qualidade de união na interface metal/cimento. Para contornar este problema, pode-se lançar mão de tratamentos de superfície do titânio, empregados isoladamente ou em associação. Este estudo avaliou a eficácia de diferentes tratamentos de superfície na resistência ao cisalhamento (RC) da união do cimento ionomérico modificado por resina RelyX Luting 2 e dos cimentos resinosos RelyX ARC e RelyX U100 ao titânio comercialmente puro (Ti cp). Duzentos e quarenta discos (9 x 3 mm) foram fundidos em Ti cp, incluídos em tubos de PVC e regularizados com lixas de carbeto de silício (150, 400 e 600) em politriz. Os espécimes foram divididos aleatoriamente em oito grupos (n=30), os quais receberam um dos seguintes tratamentos de superfície: (1) Al2O3 50 μm; (2) Al2O3 120 μm; (3) Al2O3 250 μm; (4) Al2O3 50 μm + silano; (5) Al2O3 120 μm + silano; (6) Al2O3 250 μm + silano; (7) Cojet Sand (30 μm) + silano; (8) Al2O3 120 μm + Rocatec (110 μm) + silano. Os cimentos (1) RelyX Luting 2; (2) RelyX ARC; (3) RelyX U100 foram aplicados às superfícies tratadas do Ti cp (n=10). Os espécimes foram termociclados (5.000 ciclos, 5 e 55 °C, 30 segundos de imersão) e, então, submetidos ao ensaio de cisalhamento (0,5 mm/min). O modo de fratura foi avaliado em estereomicroscópio (x20). Os dados foram analisados por ANOVA 2 fatores e teste de Tukey (α=0,05). Os cimentos RelyX Luting 2 e RelyX U100 apresentaram comportamento semelhante com relação ao tratamento de superfície... / Titanium was introduced in the field of oral rehabilitation because of its attractive properties, as it can be indicated for fabricating tooth- or implant-supported metal ceramic restorations. However, difficulties have been shown to exist as regards the bond between resin-based materials and titanium, which could compromise the longevity of these restorations, considering the importance of the bond quality at the metal/cement interface. To overcome this problem, titanium surface treatments can be applied alone or they can be combined with each other. This study evaluated the efficacy of different surface treatments on the shear bond strength (SBS) of RelyX Luting 2 resin-modified glass ionomer cement, RelyX ARC and RelyX U100 resin cements to commercially pure titanium (CP Ti). Two hundred and forty discs (9 x 3 mm) were cast from CP Ti, embedded in PVC tubes and smoothed with silicon carbide papers (150, 400 and 600) using a polisher. Specimens were randomly divided into 8 groups (n=30), which received one of the following surface treatments: (1) 50 μm Al2O3; (2) 120 μm Al2O3; (3) 250 μm Al2O3; (4) 50 μm Al2O3 + silane; (5) 120 μm Al2O3 + silane; (6) 250 μm Al2O3 + silane; (7) Cojet Sand (30 μm) + silane; (8) 120 μm Al2O3 + Rocatec (110 μm) + silane. The luting cements (1) RelyX Luting 2; (2) RelyX ARC; (3) RelyX U100 were applied to the treated CP Ti surfaces (n=10). Specimens were thermal cycled (5,000 cycles, 5 and 55 °C, 30-second dwell time), and afterwards submitted to SBS testing (0.5 mm/min). Failure mode was evaluated under a stereomicroscope (x20). Data were analyzed using 2-way ANOVA and Tukey’s test (α=0.05). The RelyX Luting 2 and RelyX U100 luting cements exhibited similar behavior regards to the surface treatment. For both, only the group abraded with 50 μm Al2O3 particles promoted lower SBS than the other groups (P>.05)... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:28:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-02-24Bitstream added on 2014-06-13T18:58:04Z : No. of bitstreams: 1 azevedo_a_me_arafo.pdf: 1794729 bytes, checksum: de3688df34dcd910d44637e0076e7e4c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Este estudo avaliou o efeito da armazenagem prolongada em água sobre a resistência de união entre uma resina acrílica para base de prótese (Lucitone 550) e quatro resinas para reembasamento (Kooliner - K, New Truliner - NT, Tokuso Rebase - TR e Ufi Gel Hard - UGH). Além disso, a resistência de união ao cisalhamento de corpos-de-prova reembasados com a resina acrílica para base de prótese L foi avaliada para comparação. Cilindros (20 mm X 20 mm) de resina acrílica L foram polimerizados (em água a 70°C por 90 minutos, e por 30 minutos à temperatura de ebulição) de acordo com instruções do fabricante e imersos em água destilada (37 l 1°C por 48 l 2 horas). As superfícies de união foram polidas com lixa de granulação 240, escovadas com detergente (20 segundos), limpas com água destilada e secas com papel absorvente. As superfícies foram, então, preparadas por meio da aplicação do monômero da resina L (180 segundos) para a resina K e com os agentes de união (20 segundos) para as demais resinas. Uma fita adesiva com orifício (3,5 mm) foi fixada sobre a superfície tratada para padronizar a área de união. Cada cilindro foi acoplado a uma matriz metálica bipartida com um orifício central (3,5 mm X 5,0 mm). Os materiais para reembasamento foram manipulados, inseridos na matriz e polimerizados de acordo com as instruções dos fabricantes. Após a polimerização, os corpos-de-prova de cada material reembasador foram divididos em cinco grupos (n=8) e submetidos aos testes de cisalhamento (velocidade = 0,5 mm/min). Para o grupo controle (G1), os testes foram realizados imediatamente após a polimerização, para as resinas de reembasamento, e após os corpos-de-prova terem sido imersos em água (37 l 1° C) por 48 l 2 horas para a resina de base L. Os corpos-de-prova relativos aos Grupos 2, 3 e 4 foram testados após terem sido armazenados em água (37 l 1° C)... / This study evaluated the effect of long-term water storage on the shear bond strength between one heat-polymerizing denture base acrylic resin (Lucitone 550-L) and four autopolymerizing reline resins (Kooliner- K, New Truliner-NT, Tokuso Rebase-TR, Ufi Gel Hard -UGH). Also, the shear bond strength of specimens relined with the denture base resin L was evaluated, for comparison. Cylinders (20mm x 20mm) of the resin L were processed (in water at 70°C for 90 minutes, and 30 minutes at boiling temperature), according to the manufacturer's instructions, and stored in distilled water (37 l 1° C for 48 l 2 hours). The surfaces to be bonded were ground with 240-grit silicon carbide paper, brushed with detergent (20 s), washed in distilled water, and blot-dried. The bonding sites were prepared by painting the surfaces with L monomer (180 seconds) for resin K, and with the bonding agents (30 seconds) for the other resins. A tape with a circular opening (3.5 mm) was placed on the treated surfaces to provide a uniform bonding area. Each cylinder was placed in a stainless steel split mold with a center hole (3.5x5.0 mm). The reline materials were mixed, applied to the mold, and polymerized according to the manufacturers' instructions. After polymerization, specimens of each reline material were divided into 5 groups (n=8), and submitted to shear tests (at a 0.5 mm/min cross-head speed). For control group (G1), the tests were performed immediately after processing for the reline resins, and after the specimens had been stored in water (37 l 1° C) for 48 l 2 hours for the denture base resin L. Groups G2, G3 and G4 specimens were tested after being stored in water (37 l 1° C) for 7 days, 3 months, and 6 months, respectively. The fractured surfaces were examined using scanning electron microscope and an image analysis system to determine the percentage surface area that remained...(Complete abstract click elctronic access below)

Made available in DSpace on 2014-06-11T19:28:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-03-23Bitstream added on 2014-06-13T18:58:02Z : No. of bitstreams: 1 marra_j_me_arafo.pdf: 564454 bytes, checksum: ccab0b66e3c9fe8f4225ae09cf3fc905 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O estudo avaliou a resistência de união entre dentes artificiais e resinas acrílicas para base protética e o efeito da termociclagem. Para isso foram utilizadas três marcas comerciais de dentes artificiais de resina acrílica (Biotone, Trilux e Ivoclar) e quatro de resinas acrílicas para base protética, sendo duas termopolimerizáveis por banho de água quente (Lucitone 550 e QC-20), uma polimerizada por meio da energia de microondas (Acron MC) e uma fotopolimerizável (Versyo.com). Vinte espécimes foram confeccionados para cada combinação de dente artificial e resina acrílica e divididos em 2 grupos (n=10) nas seguintes condições experimentais: sem a ação da termociclagem (grupo controle) e com a ação da termociclagem. Os espécimes dos grupos com termociclagem foram submetidos 5000 ciclos com temperatura variando entre 4º e 60ºC e tempo de imersão de 30 segundos em cada. Em seguida, os espécimes foram submetidos ao ensaio mecânico de cisalhamento em máquina universal a uma velocidade de 1mm/min. Os dados foram submetidos à análise de variância a três fatores seguida pelo teste de Bonferroni para comparações múltiplas (a=0,05). Os resultados demonstraram que a termociclagem reduziu significantemente os valores médios de resistência de união da resina acrílica Lucitone 550 quando associada aos dentes Biotone e Trilux e com a resina Versyo.com e os dentes Ivoclar P<0,05). E que as médias de resistência de união das resinas acrílicas Acron MC e Lucitone 550 quando associadas aos dentes Ivoclar aumentaram significantemente após a ação da termociclagem (P<0,05). Conclui-se que algumas combinações de dente artificial e resina acrílica podem ser mais afetadas pela ação da termociclagem, e esses efeitos variam de acordo com os materiais selecionados. / The purpose of this in vitro study was to evaluate the bond strength of denture base resins to acrylic denture teeth and the effect of the thermocycling. Three acrylic denture teeth (Biotone, Trilux and Ivoclar) were chosen for bonding to four denture base resins: one microwave-polymerized (Acron MC), two heat-polymerized (Lucitone 550 and QC-20) and one light-polymerized (Versyo.com). Twenty specimens were produced for each denture base/acrylic denture tooth combination and were divided into 2 groups (n=10) as follows: without thermocycling (control groups) and thermocycled groups that were submitted to 5,000 cycles between 4º and 60ºC with a dwell time of 30 seconds in each bath. Shear strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 1 mm/min until fracture. Statistical analysis of the results was carried out with 3-way ANOVA and Bonferroni's multiple comparisons post hoc analysis for test groups (a=.05). A significant interaction between denture base resin, acrylic denture teeth and thermocycling (P<.001) was observed. The shear bond strengths of Lucitone 550/Biotone, Lucitone 550/Trilux and Versyo.com/Ivoclar specimens were significantly decreased by thermocycling compared with the corresponding control groups (P<.05). The shear bond strengths of Acron/Ivoclar and Lucitone/Ivoclar specimens significantly increased after thermocycling (P<.05). Some acrylic tooth/denture base resin combinations can be more affected by thermocycling; the effects vary based upon the materials used.

Made available in DSpace on 2014-06-11T19:28:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-12-01Bitstream added on 2014-06-13T20:37:52Z : No. of bitstreams: 1 santos_jg_me_arafo.pdf: 726799 bytes, checksum: ba399d198e118a915d5001ecb642c403 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O reparo em próteses metalocerâmicas é um procedimento útil em determinadas situações clínicas. Recentemente surgiram no mercado alguns materiais designados para tal finalidade que, segundo seus fabricantes, são promissores. Neste trabalho foi avaliada a resistência ao cisalhamento de determinados sistemas de reparo para metalocerâmicas. Foram confeccionadas amostras cilíndricas em liga de NiCr (Vera Bond II) e em porcelana feldspática (Noritake). Após inclusão destas em anel de PVC, suas superfícies foram lixadas (320) e, com auxílio de matriz bi-partida (5 mm diâmetro e 2 mm altura), receberam um dos seguintes tratamentos (n=10): 1) sistema Clearfil SE Bond/Clearfil AP-X (Kuraray), 2) sistema Bistite II DC/Palfique (Tokuyama), 3) sistema Cojet Sand/Z100 (3M-ESPE), 4) jateamento com Al2O3 e sistema Scotchbond Multi Uso Plus/Z100 (3M-ESPE) (grupo controle), e 5) jateamento com Cojet Sand e sistema Scotchbond Multi Uso Plus/Z100. Os corpos-de-prova foram armazenados por 24 horas em água destilada a 37ºC, termociclados (1.000 ciclos - 5º a 55ºC) e, então, deixados nas condições descritas acima por mais 8 dias. O ensaio foi realizado em máquina MTS 810 com velocidade de 0,5 mm/min. Os valores originais foram submetidos à análise de variância (ANOVA) e teste de Tukey. No metal, as médias de resistência dos grupos de 1 a 5 foram respectivamente de 18,40 MPa (B), 8,57 MPa (D), 25,24 MPa (A), 16,26 MPa (BC) e de 13,11 MPa (C) (valor crítico 3,2). Em porcelana, foram de 16,91 MPa (B), 18,04 MPa (AB), 19,54 MPa (AB), 21,05 MPa (A) e de 16,18 MPa (B) (valor crítico 3,7). A melhor opção mediante exposição em metal foi o sistema Cojet Sand. Em porcelana, os sistemas Scotchbond Multi Uso Plus associado ao jateamento com Al2O3, Cojet Sand e Bistite II DC apresentaram os melhores resultados. / Fracture of porcelain in metal-ceramic restorations is a common clinical problem and sometimes the repair is a useful solution. Recently some new repair materials with promising results according to their manufactures are available. The aim of this study was to evaluate the shear bond strengths of porcelain repair systems. Fifty disks in NiCr alloy (Vera Bond II) and in feldspatic porcelain (Noritake) were made. The specimens were included in acrylic resin and the surfaces were ground with 320-grit silicon carbide paper. Metal and porcelain specimens were divided into five groups of ten each and the bonding sites received one of the following treatments: 1) Clearfil SE Bond/Clearfil AP-X (Kuraray), 2) Bistite II DC/Palfique (Tokuyama), 3) Cojet Sand System/Z100 (3M-ESPE), 4) air-abrading with Al2O3 and Scotchbond Multi Purpose/Z100 (3M-ESPE) (control group) and 5) air-abrading with Cojet Sand and Scotchbond Multi Purpose/Z100. After storage for 24 hours in distilled water at 37°C, thermocycling (1.000 cycles - 5º and 55ºC) and storage for more 8 days at the same conditions above, the shear bond strength test was performed in a testing machine MTS 810 at a crosshead speed of 0.5mm/min until fracture. Statistical analysis of the data was accomplished by analysis of variance (ANOVA) and Tukey's test. In metal, the bond strengths of groups 1 to 5 were, respectively 18,40 MPa (B), 8,57 MPa (D), 25,24 MPa (A), 16,26 MPa (BC) and 13,11 MPa (C). In porcelain, the bond strengths of the five groups were 16,91 MPa (B), 18,04 MPa (AB), 19,54 MPa (AB), 21,05 MPa (A) and 16,18 MPa (B). The best option when occurs metal exposure is Cojet Sand System. In porcelain, air-abrading with Al2O3 and Scotchbond Multi Purpose, Cojet Sand System and Bistite II DC showed the best results.

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-06-23Bitstream added on 2014-06-13T19:16:56Z : No. of bitstreams: 1 landim_kt_me_sjc.pdf: 2945410 bytes, checksum: dc611c58884c00b0e53c9d1dcae05bbe (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo avaliou a influência da ciclagem mecânica na resistência de união ao cisalhamento entre cerâmicas infiltradas por vidro para infra-estrutura (In-Ceram Alumina - Vita Zahnfabrik e In-Ceram Zircônia - Vita Zahnfabrik) e uma cerâmica vítrea de recobrimento (VITA VM7 - Vita Zahnfabrik). Foram preparadas vinte e quatro amostras cilíndricas nas dimensões de 4mm de diâmetro por 5mm de altura para cada cerâmica de infra-estrutura. Posteriormente, a cerâmica de recobrimento estético foi aplicada, resultando em corpos-de-prova com 4mm de diâmetro e 9mm de altura, os quais foram divididos em 4 grupos: ICA; ICAM; ICZ e ICZM. Os grupos ICAM e ICZM receberam ciclagem mecânica, com força de 50N, freqüência de 1Hz, durante 20000 ciclos. O ensaio de cisalhamento foi realizado em máquina de ensaio universal (modelo DL - 1000, EMIC - Equipamentos e Sistemas LTDA., São José dos Pinhais - PR - Brasil) com velocidade de 0,5mm/min e as amostras carregadas até a fratura. As interfaces das amostras pós-fratura foram analisadas em estereomicroscópio (20x) e microscopia eletrônica de varredura. As médias e desvios padrão obtidos foram: ICA (30,04 l 11,74); ICAM (32,17 l 9,59); ICZ (44,33 l 11,47); ICZM (43,52 l 8,33). Os dados obtidos (MPa) foram analisados estatisticamente por meio de análise de variância (ANOVA) dois fatores e teste de Tukey (P<0,05). Os resultados mostraram diferença estatisticamente significante entre os grupos In-Ceram Alumina e In-Ceram Zircônia, porém a ciclagem mecânica não influenciou na resistência de união entre as cerâmicas de infra-estrutura e de recobrimento estético estudadas / This study evaluated the influence of cyclic loading on shear bond strength between two glass-infiltrated ceramics for substructure (In-Ceram Alumina - Vita Zahnfabrik and In-Ceram Zirconia - Vita Zahnfabrik) and one glass veneer ceramic (VITA VM7 - Vita Zahnfabrik). Twenty four cylindrical samples with 4mm diameter per 5mm high was to prepare for each ceramics for substructure. Subsequently, the venner ceramic was applied to ceramic substructure, resulting in 4mm diameter per 9mm high specimens. They were divided in four groups ICA; ICAM; ICZ and ICZM. The groups ICAM and ICZM where cyclic loadind from 50N, 1Hz during 20000 cycles. Shear bond testing was performed in a universal testing machine (DL - 1000 model, EMIC - Equipamentos e Sistemas LTDA., São José dos Pinhais - PR - Brasil), with crosshead speed of 0,5mm/min and the specimens were loaded until failure. The interfaces of representative fractured specimens of each group were examined with microscopy (20x) and scanning electron microscopy. The mean values and standard deviations were: ICA (30,04 l 11,74); ICAM: (32,17 l 9,59); ICZ: (44,33 l 11,47); ICZM: (43,52 l 8,33). Data for shear bond strength (MPa) where statistically analysed by variance analysis (ANOVA) two factors and Tukey's test (P<0,05). The results showed statistically significant differences between the groups In-Ceram Alumina and In-Ceram Zirconia, however the cyclic loading effect was not influenced on bond strength between ceramics for substructure and veneer ceramic studied