No description available.

Friction Bit Joining (FBJ) is a recently developed spot joining technology capable of joining dissimilar metals. A consumable bit cuts through the upper layer of metal to be joined, then friction welds to the lower layer. The bit then snaps off, leaving a flange. This research focuses on FBJ using DP980 or DP590 steel as the lower layer, AZ31 magnesium alloy as the top layer, and 4140 or 4130 steel as the bit material. In order to determine optimal settings for the magnesium/steel joints, experimentation was performed using a purpose-built computer controlled welding machine, varying factors such as rotational speeds, plunge speed, cutting and welding depths, and dwell times. It was determined that, when using 1.6 mm thick coupons, maximum joint strengths would be obtained at a 2.03 mm cutting depth, 3.30 mm welding depth, and 2500 RPM welding speed. At these levels, the weld is stronger than the magnesium alloy, resulting in failure in the AZ31 rather than in the FBJ joint in lap shear testing.

Friction Bit Joining (FBJ) is a new technology that can be used to join dissimilar materials together. This ability makes it a good candidate for creating lightweight structures for the automotive industry by combining lightweight materials such as aluminum to stronger materials like advanced high-strength steels. The automotive industry is putting significant effort into interest in reducing vehicle structure weight to increase fuel efficiency and reduce greenhouse gas emissions. Joining of dissimilar materials is a challenge they face in the light weighting the body of the vehicle. The purpose of the current research is to employ FBJ in the joining of a very challenging material combination: GA DP 1180 to AA 7085-T71. In accomplishing this purpose, the goal is to move FBJ toward a more production ready process by better understanding the effects of tooling, bit design, and process parameters on joint strength and reliability as they relate to load profiles captured during the joining process. It was found that the joint strength variation was influenced strongly by the hardness and the geometric consistency of the consumable bits. Bit hardness below 45 HRC led to joint strength that was less than the required specification (5kN in lap shear tension, and 1.5kN in cross-tension and T-peel). Variation in bit height and diameter also led to excessive scatter in joint strength values, where it was not possible to meet the standard for 10 consecutive specimens (for each of the three tests). Implementation of high-speed data acquisition (1000Hz) enabled the capture of load curve profiles generated during FBJ. Load curve profiles were correlated with destructive testing results to discover the impact of process parameter combinations. Analysis of load curve profiles led to improvements in parameter selections of spindle speeds (revolutions per minute) and spindle feed-rates (inches per minute). Process parameters of 5000 RPM and 15 IPM reduced variation in load-curve profiles and destructive testing. Satisfactory joint strength was achieved in lap shear tension, cross-tension, and T-peel testing configurations with values of 10.1 kN, 4.1 kN, and 1.8 kN, respectively. The presence of wet adhesive had little impact on joint performance. Finally, the analysis of a load-curve profiles resulted in a criterion that allowed for distinguishing "good" welds from "bad" ones, where a threshold load of 6kN, or higher, during the dwell phase of welding was required in order to meet joint strength standards.

No description available.

No description available.

No description available.

This thesis is a critical evaluation of the content, form and technique of traditional and modern praise poetry in Northern Sotho. Chapter 1 presents the aim of the study and the method of research and defines the concepts of poetry and praise poetry. Praise poetry is viewed from a traditional and modern perspective. Chapter 2 deals with the content and technique of praise poetry. Content consists of oral praise poetry lauding the heroic deeds of men in battles and casual encounters. Modern praise poetry comments on current events. Devices for rapid composition of the praises are discussed. Techniques differ between poets and according to time, place and occasion. Chapter 3 covers the traditional praises of chiefs, warriors, initiates, animals, birds, divining bones and totem praises, examining them from the perspective of content and form. The praises extol human achievements, peculiar animal characteristics and the interpretation of "mawa" of divining bones. Chapter 4 deals with the development and transition from traditional to modern form as well as the reciprocal influence. The content and form of modern praises of chiefs, academics, community leaders, animals, birds, divining bones, man-made objects and some natural phenomena are discussed. Many modern poets have also written praises of fictional characters. Chapter 5 compares oral and written praise poetry by concentrating on the similarities and differences between traditional and modern praise poetry. This study shows that there are differences in of theme, rhyme, beginning and ending, sentence length and significant emphasis on man-made objects such as cars and locomotives as exceptional modes of transport for commuters. Chapter 6 concludes the study and proves that praise poetry is a living or dynamic entity which will continue to exist. Praise poetry highlights persons, interpersonal relationships, attitudes and values derived from an African conceptions of the universe. / African Languages / D.Litt. et Phil (African Languages)

Neste trabalho foram determinadas as condições para a soldagem de chapas grossas de aço carbono ASTM A36 com aço baixo-liga temperado e revenido ASTM A514 Grau Q empregando-se o processo arame tubular. Para tanto foram soldadas diversas peças de testes com o intuito de se avaliar as condições mais adequadas de preparação e soldagem de juntas dissimilares destes materiais. A preparação foi realizada por meio de corte térmico. A temperatura de preaquecimento foi determinada através de modelos matemáticos, pelas recomendações das normas AWS D1.1 e DIN EN 1011-2 sendo posteriormente avaliada por intermédio do teste de soldabilidade tipo CTS Controlled Thermal Severity. Os parâmetros de soldagem foram determinados a partir da qualificação de um procedimento de soldagem, conforme a norma AWS D1.1. Foram avaliadas as consequências do emprego do tratamento térmico de alívio de tensões após soldagem (TTAT), pelos testes de dureza Vickers e impacto Charpy. A caracterização microestrutural foi realizada por meio de microscopia óptica e microscopia eletrônica de varredura. A caracterização das superfícies oxicortadas evidenciou os efeitos da descarbonetação e também da carbonetação. A temperatura de pré-aquecimento de 160°C determinada por meio da metodologia recomendada pelas normas AWS D1.1 e DIN EN 1011-2 mostrou-se satisfatória nos testes de soldabilidade. Foi possível a qualificação do procedimento de soldagem (EPS) com requisitos de impacto na condição \"como soldado\", porém na condição \"após TTAT\", os baixos valores de tenacidade obtidos no metal de solda, inferiores a 27J, não permitiram a qualificação de uma EPS com requisitos de impacto. Foi observada a ausência de trincas intergranulares tanto na zona afetada pelo calor quanto no metal de base ASTM A514, porém foi revelada a presença de microfases frágeis no metal de solda na condição \"como soldado\", especificamente na região da raiz, intensificadas pelo efeito da diluição. O aumento do teor de carbono na raiz, a presença de microfases frágeis, a grande fração de grãos colunares e de ferrita proeutetóide combinados com a baixa fração de ferrita acicular no metal de solda contribuíram para os baixos valores de tenacidade encontrados na condição \"como soldado\". Após o TTAT observou-se uma queda acentuada da tenacidade, inferior a 27J, do metal de solda devido à fragilização provocada pela precipitação e coalescimento de carbonetos de ferro. / In this work it was determined the conditions for welding thick plate of ASTM A36 carbon steel with quenched and tempered low-alloy steel ASTM A514 Grade Q employing the Flux Cored Arc Welding (FCAW) process. For that several coupons of tests were welded in order to evaluate the most appropriate conditions for preparation and welding of these dissimilar materials. The preparation was carried out by means of thermal cutting. The preheat temperature was determined by mathematical models, the recommendations of standards AWS D1.1 and DIN EN 1011-2 being further evaluated using the CTS type weldability test - Controlled Thermal Severity. The welding parameters were determined by qualifying a welding procedure (WPS), according to AWS D1.1. The effects of post weld heat treatment (PWHT) were evaluated by Vickers hardness tests and Charpy. Microstructural characterization was performed by optical microscopy and scanning electron microscopy. The characterization of oxi-fuel cut surfaces showed the effects of decarburization and also carburization. The preheating temperature of 160 °C determined by calculation and the methodology recommended by the standards was satisfactory in weldability tests. It was possible qualification of welding procedure (WPS) with impact requirements in the condition \"as welded\" but the condition \"after PWHT\" low toughness values obtained in the weld metal, less than 27J, did not allow to qualify a WPS with toughness requirements. The absence of intergranular cracking was observed in both the heat affected zone as the base metal ASTM A514, but the presence of fragile microphase in the weld metal was revealed in the weld metal in the condition \"as welded\" specifically in the root region, intensified by the effect of dilution. The carbon increase at root, the presence of fragile microphase, the large fraction of columnar grains and proeutectoid ferrite combined with the low fraction of acicular ferrite in the weld metal contributed to the low toughness values found in the condition \"as welded \". After PWHT there was a sharp drop in toughness, less than 27J, in the weld metal due to embrittlement caused by precipitation and coarsening of iron carbides.

O processo de soldagem por fricção e mistura (FSW) tem despertado grande interesse nos últimos anos e tornou-se uma alternativa para unir materiais de baixa soldabilidade, como as ligas de alumínio das séries 2XXX e 7XXX, as quais são empregadas na estrutura das aeronaves, por possuírem elevada relação resistência/peso. O processo FSW, todavia, causa mudanças microestruturais nos materiais soldados, particularmente na zona misturada (ZM) e nas zonas termicamente (ZTA) ou termomecanicamente (ZTMA) afetadas. Estas mudanças geralmente interferem no desempenho frente à corrosão das ligas soldadas. No presente estudo, a resistência à corrosão das ligas de alumínio 2024-T3 e 7475-T761, unidas pelo processo FSW foi investigada em solução 10 mM de NaCl. Ensaios de visualização em gel ágar-ágar e de imersão associados a técnicas microscópicas foram realizados para investigar o efeito do acoplamento galvânico na corrosão das diferentes regiões da junta soldada. Os resultados do ensaio de visualização em gel mostraram que, quando acopladas, a liga 2024 atua como cátodo e a 7475 como ânodo. Os ensaios de imersão revelaram acoplamento galvânico entre as ligas na zona misturada (ZM). A região mais afetada pela corrosão foi a ZTMA da liga 7475, com corrosão intergranular desde as primeiras horas de imersão. A influência do processo de soldagem na resistência à corrosão das duas ligas de alumínio foi investigada por ensaios eletroquímicos. Os ensaios eletroquímicos adotados foram medidas de potencial de circuito aberto (PCA) em função do tempo de exposição ao meio corrosivo, espectroscopia de impedância eletroquímica (EIE) e curvas de polarização potenciodinâmica. Os ensaios de polarização mostraram elevada atividade eletroquímica na zona de mistura indicada pelos altos valores de densidade de corrente em comparação com as demais zonas testadas. Os resultados de EIE globais mostraram que nas primeiras horas de exposição ao eletrólito o processo de corrosão foi predominantemente controlado pela liga 7475; todavia, com o tempo de exposição ao eletrólito, a corrosão passou a ser controlada pela liga 2024. / Friction stir welding (FSW) has roused great interest in recent years and it is now an alternative for joining materials of low weldability, such as the aluminum alloys of the 2XXX and 7XXX series, used in the aircrafts structure due to their high strength /weight ratio. However, FSW causes material microstructural changes, mainly in the stir zone (SZ), the heat affected zone (HAZ) or thermomechanically (TMAZ) affected zones of the materials welded. These generally interfere with the corrosive performance of the welded joint. In the present study, the corrosion resistance of the 2024-T3 and 7475-T761aluminum alloys, joined by FSW was investigated in 10 mM NaCl electrolyte. Agar-agar gel and immersion tests associated with microscopic techniques were performed to investigate the effect of galvanic coupling between the welded materials. Results from this test showed that, when galvanically coupled, the 2024 alloy acts as cathode and the 7475 as anode. Immersion tests revealed galvanic coupling between the alloys in the SZ. The zone most susceptible to corrosion was the TMAZ of the 7475. Intergranular corrosion was observed in this zone since the first hours of immersion. The influence of the welding process on the corrosion resistance of the alloys was also evaluated by electrochemical tests. The electrochemical tests adopted were open circuit potential measurements (OCP) as a function of time of exposure to the electrolyte, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. The polarization tests showed high electrochemical activity in the stir zone indicated by the high current densities measured comparatively to the other tested zones. The global EIS results indicated that in the first few hours of exposure to the electrolyte the corrosion process was predominantly controlled by the 7475 alloy; however, with time of exposure to the electrolyte, the corrosion was controlled by alloy 2024.

Tendo em vista a tendência mundial de se buscar a diminuição de peso de estruturas metálicas de veículos, o desenvolvimento de aços de resistência mecânica superior apresenta-se como um importante fator para a competitividade e sustentabilidade da indústria brasileira, além da segurança do usuário. No setor automobilístico, as reduções no peso e no consumo de combustível requerem não somente a pesquisa de novos aços, mas também a utilização de componentes híbridos, resultantes, entre outros, da união entre os aços austeníticos inovadores de alta liga e baixo custo (TRIP) e aços ferríticos comerciais (ARBL). Na presente dissertação foram investigadas as propriedades mecânicas microestruturais, antes e após o processo de soldagem TIG, dos aços TRIP e ARBL utilizados pela indústria automotiva. O principal objetivo do trabalho foi avaliar possíveis estruturas e modificações nas propriedades das juntas soldadas de acordo com parâmetros de soldagem pré-determinados. Primeiramente, verificaram-se as extensões da zona termicamente afetada dos corpos de prova soldados. Os perfis de microdureza indicaram que não houve uma alteração significativa de dureza na zona termicamente afetada do aço de efeito TRIP, enquanto que para o aço ARBL observa-se um considerável aumento. Os limites de escoamento determinados pelos ensaios de tração realizados permitiram a obtenção dos níveis de resistência mecânica das juntas soldadas. Através dos ensaios de microscopia eletrônica de varredura e microscopia ótica foi possível observar a influência do aporte térmico na zona termicamente afetada do aço ARBL. A análise de EDX nas juntas dissimilares permitiu observar a presença de zonas parcialmente diluídas na zona fundida do lado do metal de base ARBL, a caracterização da composição química nas interfaces entre os metais de base e o metal de solda e prever a microestrutura destas regiões. As fases presentes nos metais de base e na zona fundida foram caracterizadas também pela difração de raios x. Por meio da estereologia quantitativa caracterizou-se as fases presentes na zona fundida e determinou-se suas proporções em função do aporte térmico. / In view of the global trend of searching for the weight reduction of metal frames in vehicles, the development of superior mechanical resistance steels presents itself as an important factor for the competitiveness and sustainability of the Brazilian industry, as well as to user safety. In the automotive industry, the reductions in vehicle weight and fuel consumption not only require research of new types of steel but also the use of hybrid components, which result, amongst other things, between the union of austenitic innovative high alloy and low cost (TRIP) with commercial ferritic steels (HSLA). This dissertation analyses the microstructural mechanical properties before and after the TIG welding process, the TRIP steel, and HSLA used by the automotive industry. The main objective of this study was to evaluate possible phase changes in steel structures and transformation in the properties of the welded joints according to pre-determined welding parameters by analyzing extensions of the heat-affected and melted zones of welded specimens. The micro hardness profiles showed no significant changes in hardness in the heat affected HSLA steel, while the TRIP steel showed considerable increase. Additionally, the yield point determined by the traction tests performed, allowed the obtainment of the mechanical resistance levels of the welded joints. Through the tests of scanning electron and optical microscopy was observed the influence of heat input on heat affected zone of HSLA steel. EDX analysis allowed us to observe the presence of molten zones partially diluted in the side of the base metal HSLA, characterization of the chemical composition at the interface of the base metal and weld metal and predicting the microstructure in these regions. The phases present in the base metal and weld zone were characterized too by x-ray diffraction. By quantitative stereology characterized by the phases present in the weld zone and their proportions were determined as a function of heat input.