The recycled asphalt pavement (RAP) extracted from recovery distresses in highways does not receive the attention and importance it deserves in Brazil. The reuse of this material, which presents as good properties as the virgin aggregate, when applied correctly in the composition of new pavement layers or rehabilitations, is a widely used in European and United States. Besides solving the environmental liabilities of pavement, the reuse of milled material in asphalt mixtures is a sustainable alternative, which decreases consumption of asphalt and virgin aggregate, milled material transportation and allocation costs. This study seeks an alternative to the use of RAP as the base layer in the implementation of new pavements.For this paper, cold recycled mixtures were studied, wich are composed of RAP (granulometrically stabilized with fine aggregate) and RL-1C asphalt emulsion, a bituminous binder that contains added Portland Cement (CP V ARI) in the proportions of 2% to 5% for emulsion and from 0% to 1% of cement, in weight. The proposed mixtures were evaluate through mechanical resistance to single compression (RCS), indirect tensile strength (RT), resilient modulus tests (RM), Complex Modulus (E* and Ф) and Flow Number (FN). After performing these tests, it was observed that the values obtained reveal that the mixtures with proportions varying from 50% to 75% of emulsion, compared to the cement used in the mixtures, show better results. Moreover, the mixtures present resilient modulus results ranging from 1500 MPa to 3000 MPa (excellent values for base layers). The FN test shows that by adding cement to the mixture, the results improved in the form of an increment in the number of cycles, which performed at its best with samples that had 2% and 3% of emulsion. The uniaxial Complex Modulus test allowed access the viscoelastic behavior and the 2S2P1D modeling was used too. It´s possible to confirm that this technique is viable pavement maintenance. / O material fresado extraído de trechos em recuperação não recebe a atenção e importância que merece no Brasil. O reaproveitamento desse material, que apresenta comportamento tão bom quanto os agregados virgens, quando empregado de maneira correta na composição de camadas de pavimentos novos ou restaurações, é uma prática largamente utilizada em países europeus e nos Estados Unidos. Além de resolver o passivo ambiental das empresas, o reemprego do fresado em misturas asfálticas, é uma alternativa sustentável que diminui o consumo de agregados virgens e custos com transporte de fresado e alocação do mesmo. Este trabalho busca uma alternativa para emprego do material fresado como camada de base na execução de pavimentos novos. Foram estudadas misturas recicladas a frio compostas de fresado estabilizado granulometricamente com pó-de-pedra e tendo como ligante betuminoso emulsão asfáltica RL-1C nas proporções de 2% a 5% e de ligante hidráulico CP V ARI de 0% a 1% de cimento. As misturas propostas foram avaliadas por meio de ensaios de resistência à compressão simples (RCS), ruptura por tração por compressão diametral (RT), módulo de resiliência (MR), módulo complexo (IE*I) e FlowNumber (FN). Após a realização dos ensaios, observou-se que os valores obtidos demonstram que as misturas com proporção variando de 50% a 75% de emulsão, em relação ao cimento empregado nas misturas, apresentam melhores resultados. Além disso, as mesmas misturas apresentam valores de módulo resiliente variando entre 1500 MPa e 3000 MPa (valores excelentes para camadas de base). O ensaio de FN mostrou que a adição de cimento na mistura melhora os resultados aumentando o número de ciclos, apresentando como melhores as amostras com 2% e 3% de emulsão. Através do ensaio de módulo dinâmico obteve-se a curva mestra das misturas utilizando a modelo 2S2P1D. Acredita-se que esta será uma alternativa técnica e economicamente viável para destinação do material fresado gerado em abundância pelas obras rodoviárias.

Fundação de Amparo a Pesquisa no Estado do Rio Grande do Sul / The use of recycled materials can become a constructive application with good acceptance in the road sector, and is a great contribution to the sustainability policy. In this scenario, the study of economic and sustainable techniques for execution, construction and maintenance of highways, forces a survey in which they can find alternatives to the use of materials that reduce energy consumption, taking into account also the environmental appeal. Therefore, this is an objective research on the study of a way to use, reuse, and improve the use of the recycled asphalt pavement (RAP) in hot asphalt mixtures. This is possible due to the RAP's recycling process being a viable option to replace conventional pavement materials. Then, the RAP becomes an alternative when someone wishes to improve the properties of a material, called particle size stabilization, aiming at a correct particle size and obtain a material with greater strength, efficiency and lower cost. To achieve the purpose of this study, laboratory tests were made to evaluate the mechanical properties and adhesiveness of mixtures containing 10% addition of RAP, 20% and 30%, compared to a reference mix without the RAP addition. Additionally, the initial use of the Bailey method was an important factor to the formation of the mixtures and selection of the aggregates used to Superpave methodology to design dosage strength and preparing of the samples. For mechanical evaluation were used resilient modulus tests (RM) and to review viscoelastic were used uniaxial dynamic modulus test. In addition, the indirect tensile strength tests were performed (RT) and Flow Number (FN) and damage tests induced moisture through the Modified Lottman test and wear a Cantabro abrasion, for evaluation of the properties of adhesion and cohesion of the mixtures, respectively. So after obtained these results, it was possible to make an analysis of the use of these hot mix asphalt recycling hot pavements, as well as assess how much conventional mixtures can be improved with the inclusion of recycled material, replacing virgin aggregate. Then, it was possible to infer that the mechanical evaluation showed positive results with the addition of RAP compared to a reference blend. It´s possible to reduce the new binder content between 13 and 37%. The results showed that RM stiffness and indirect tensile strength increases with RAP amount. Furthermore, the FN test results showed reductions on permanent deformation and rutting of the RAP´s mixtures. Through the master curve obtained by dynamic module, along with modeling 2S2P1D, it was found that the CAF10 mixture unexpectedly had stiffness greater than the CAF20 mixture, which has 20% more RAP than the previous. / A utilização de materiais provenientes da reciclagem pode se tornar uma aplicação construtiva com boa aceitação no setor rodoviário, além de contribuir na política de sustentabilidade. Com isso, torna-se viável o estudo de técnicas econômicas e sustentáveis para execução, construção e manutenção de rodovias, forçando uma pesquisa em que se possa encontrar alternativas para o uso de materiais que diminuam o consumo de energia, levando em conta, ainda, o apelo ambiental. Por isso, essa pesquisa se objetiva no estudo de uma maneira de utilizar, reutilizar e melhor aproveitar o material fresado em misturas asfálticas a quente. Isto se dá devido ao processo de reciclagem deste material ser uma alternativa de possível substituição aos materiais convencionais naturais de pavimentação como, por exemplo, a pedra britada. Então, o material asfáltico do pavimento deteriorado (fresado) torna-se uma das alternativas quando se deseja melhorar as propriedades de um material, denominada estabilização granulométrica, visando corrigir sua granulometria e obter um material com maior resistência, eficiência e menor custo. Para atingir o objetivo desta pesquisa, foram realizados ensaios laboratoriais que pudessem avaliar as propriedades mecânicas e de adesividade das misturas contendo 10% de adição de fresado, 20% e 30%, comparadas a uma mistura de referência sem adição de agregado reciclado. Além disso, a utilização inicial do Método Bailey foi um fator importante para a formação das misturas e seleção dos agregados, sendo utilizada a metodologia Superpave para dosagem do teor de projeto e moldagem das amostras. Para avaliação mecânica, foram usados ensaios de módulo de resiliência (MR) e, ainda, para avaliação viscoelástica, ensaio de módulo dinâmico uniaxial. Além destes, foram realizados ensaios de resistência à tração indireta (RT) e Flow Number (FN) e, também, ensaios de dano por umidade induzida, através do ensaio de Lottman Modificado, e desgaste por abrasão Cântabro, para avaliação das propriedades de adesividade e coesão das misturas, respectivamente. Assim, após obtidos estes resultados, foi possível efetuar uma análise da utilização destas misturas asfálticas na reciclagem a quente de pavimentos, bem como avaliar o quanto as misturas convencionais podem ser melhoradas com a inserção de material reciclado, em substituição ao agregado virgem. Então, foi possível concluir que a avaliação mecânica apresentou resultados positivos com a adição de fresado, quando comparados a uma mistura de referência. Os resultados de MR mostraram que a rigidez aumenta ao passo que a quantidade de fresado é maior na composição das misturas, o mesmo foi possível verificar através dos ensaios de RT, os quais apresentaram valores crescentes. Além disso, o ensaio de FN comprovou que o fresado aumenta a rigidez das misturas. Através da curva mestra obtida pelo módulo dinâmico, juntamente com a modelagem 2S2P1D, foi possível constatar que a mistura CAF10, inesperadamente, apresentou rigidez maior que a mistura CAF20, a qual tem 20% a mais de fresado que a anterior.