21 |
Posouzení degradace opakovaně opravovaných střižných a tvářecích nástrojů / Examination of degradation frequently repaired shearing and forming toolsIzák, Josef January 2021 (has links)
The diploma thesis is focused on the renovation of forming tools made of tool steel, their weldability and assessment of the quality of tool repairs. The damaged tool was a part of the cutter from the progressive cutting tool made of Caldie steel. We used micro TIG technology to repair the damage. A total of three types of additional materials were used and investigated to restore the geometry of the damaged edge. One of the main purposes was to evaluate the possibility of extending the life of tools and reducing the implementation of already inefficient repairs. A number of destructive tests were performed for the assessment - macrostructure, microstructure, hardness measurement and EDS analysis.
|
22 |
Svařování galvanicky pozinkovaných plechů pomocí hybridní technologie Laser-TIG / Welding of galvanized sheets using hybrid Laser-TIG technologyAntes, Jiří January 2021 (has links)
ANTES, Jiří: Welding of galvanized sheets using hybrid Laser-TIG technology This master thesis deals with the welding of zinced deep drawing steel using Laser-TIG technology. The first section of the thesis describes the topic from the theoretical point of view, which includes analysis of welding technologies, influence of used material and application of diagnostic methods. The second part of the thesis is focused on monitoring of welding current impact for weld quality of two types of joints.
|
23 |
Gas Tungsten Arc Welding of 304L and 21-6-9 Austenitic Stainless Steel with Penetration Enhancing CompoundsFaraone, Kevin Michael 02 June 2014 (has links)
No description available.
|
24 |
Framtagning av reparationsmetod för LMS100, Strut IPT frameClar, Helen, Karlsson, Anna January 2005 (has links)
No description available.
|
25 |
Framtagning av reparationsmetod för LMS100, Strut IPT frameClar, Helen, Karlsson, Anna January 2005 (has links)
No description available.
|
26 |
Microtexture and Mechanical Properties of Electron Beam or Tungsten Inert Gas Arc Welded Mg AlloysWu, Hsin-Hui 13 August 2003 (has links)
none
|
27 |
Estudo dos efeitos da polaridade na soldagem com corrente contínua e alternada pelos processos TIG e MIG/MAGCirino, Luciano Machado January 2009 (has links)
Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-graduação em Engenharia Mecânica / Made available in DSpace on 2012-10-24T15:10:55Z (GMT). No. of bitstreams: 1
263087.pdf: 10723418 bytes, checksum: b7eb13bffddce582c25a6f4e8f10d08b (MD5) / Este trabalho abrange o estudo do efeito da polaridade sobre alguns aspectos da soldagem com os processos TIG e MIG/MAG. Os experimentos foram agrupados conforme o processo de soldagem e o aspecto a ser estudado, bem como do procedimento experimental empregado. O primeiro grupo de experimentos visou analisar o efeito do tempo de duração da polaridade positiva sobre as dimensões dos cordões de solda, limpeza catódica e comportamento da tensão no processo TIG CA com formato de onda retangular aplicado ao alumínio. No aspecto dimensões do cordão de solda, os resultados mostraram situações onde um aumento na penetração de solda e nas áreas fundidas foi verificado à medida que maiores tempos de polaridade positiva eram aplicados. Este comportamento difere do que é comumente encontrado na literatura corrente sobre processos de soldagem com eletrodos não-consumíveis, que infere uma diminuição na penetração de solda com o aumento do tempo de atuação da polaridade positiva. O segundo grupo verificou o efeito da intensidade da corrente positiva no mesmo processo. Os resultados também se mostraram distintos ao que é comumente apresentado na literatura corrente, que sugere que a intensidade da corrente durante a polaridade positiva tem um papel menor na capacidade de fusão do processo TIG CA aplicado ao alumínio, sendo apenas efetiva para a realização da remoção de óxidos. O aumento da intensidade de corrente positiva causou um aumento de penetração de solda e área fundida. No terceiro grupo de experimentos, foram investigados aspectos concernentes à influência da polaridade no processo MIG/MAG. A maior parte das informações divulgadas na literatura se confirmou. No entanto, características associadas à condição CC- (polaridade negativa) como repulsão de gota e geração de respingos não foram constatadas pela observação do arco voltaico e análise dos cordões de solda. Isto pode ter sido motivado pela corrente utilizada (260 A), típica de transferência goticular, associada à utilização de um mistura de Ar + 2% O2, o que permitiu uma soldagem satisfatoriamente estável em ambas as polaridades. No último grupo, experimentos foram realizados para avaliar o desempenho do sistema MIG Pulsado na condição CC+ e CA na soldagem de juntas de alumínio em filete. Uma mistura especial de Ar + 0,2% O2 foi testada durante estes ensaios para a condição CC+. A expectativa estava em minimizar a oscilação de comprimento de arco que ocorre durante a soldagem MIG do alumínio. Porém, o resultado não foi atingido conforme o esperado. Uma melhoria foi notada, mas de forma bastante limitada e longe da condição ideal. Na condição CA, o processo mostrou-se mais estável para este tipo de aplicação, porém, problemas de falta de robustez (baixa repetividade) foram constatados para as duas variantes deste processo.
|
28 |
Um estudo da eficiência e produtividade dos principais processos de soldagem a arcoSchwedersky, Mateus Barancelli January 2011 (has links)
Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2011 / Made available in DSpace on 2012-10-26T05:07:49Z (GMT). No. of bitstreams: 1
298665.pdf: 4465108 bytes, checksum: 28d8d0a4d1eaff0b0b21b2a761484bec (MD5) / A busca por processos de soldagem a arco de elevada produtividade, que proporcionem maior velocidade de operação e menor custo é o caminho lógico que vem sendo seguido em todo o mundo. Apesar disso, observa-se que no Brasil o setor industrial é extremamente conservador. Nesse contexto, o presente trabalho trata de diferentes questões ligadas à análise da produtividade dos principais processos de soldagem a arco. Primeiramente, foi realizada uma análise da literatura no tocante ao significado de termos inerentes à eficiência de transferência de calor. Os índices denominados eficiência do arco e eficiência de fusão, muitas vezes, não são interpretados de maneira adequada. O principal problema relacionado à esse tipo de análise é que não existe um valor único dos coeficientes para cada processo, fato que nem sempre é considerado por muitos profissionais da área de soldagem. Para os processos com eletrodos não consumíveis, a eficiência térmica varia de forma acentuada conforme os parâmetros usados, podendo apresentar valores baixos, ou tão elevados quanto o processo MIG/MAG. Com relação ao TIG, que geralmente é considerado de baixa produtividade, foi realizado um estudo dos fatores que limitam a velocidade de soldagem do processo. A principal conclusão mostra que o desempenho do processo quando se busca elevada produção está ligado ao gás de proteção que está sendo usado, pois este influi de forma acentuada sobre a eficiência ao gerar fusão. A adição de pequenos percentuais de hidrogênio ao argônio proporciona aumento de rendimento do processo possibilitando a soldagem TIG em maiores velocidades. Usando esses fundamentos são apresentados desenvolvimentos de procedimentos de soldagem TIG autógeno com elevada velocidade de soldagem. Os exemplos mostram que os processos considerados tradicionalmente de baixa produtividade podem atingir níveis de desempenho idênticos aos considerados mais produtivos se aplicados de maneira mais bem estudada / The search for high productivity arc welding processes, providing higher travel speed and lower cost is the logical path that has been followed worldwide. Nevertheless, it is observed that the industrial sector in Brazil is extremely conservative. In this context, this work deals with different issues related to productivity analysis of the main arc welding processes. An analysis of the literature regarding the meaning of terms related to heat transfer efficiency was performed. Often, arc efficiency and melting efficiency index are not properly interpreted. The main problem with this type of analysis is that there is not a unique value for the coefficients for each process, a fact that is not considered by many professionals in the welding area. For processes with non-consumable electrodes, the thermal efficiency varies dramatically according to the used parameters, and may present really low values, or values as high as processes such as MIG/MAG. A study was conducted about the factors that limit the speed of TIG welding, which is generally considered a low productivity process. The main conclusion shows that the performance of this process aiming high production capacity is linked to the shielding gas that was used, because it dramatically affects the melting efficiency. The addition of small percentages of hydrogen to argon provides increased efficiency of the process allowing TIG welding at higher speeds. Using these fundamentals, this work presents developments for autogenous TIG welding procedures with high productivity. The examples show that the processes traditionally considered of low productivity can reach performance levels similar to those considered to be more productive if applied with a more refined technique
|
29 |
An?lise n?o-linear do campo de temperaturas desenvolvidas durante a soldagem do tipo TIG cont?nuo em placas delgadasSantos, Tadeu F?lix dos 02 September 2015 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-04-25T21:03:05Z
No. of bitstreams: 1
TadeuFelixDosSantos_DISSERT.pdf: 1188872 bytes, checksum: 47b34679279af1fc33a4e33479484fde (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-04-27T19:21:27Z (GMT) No. of bitstreams: 1
TadeuFelixDosSantos_DISSERT.pdf: 1188872 bytes, checksum: 47b34679279af1fc33a4e33479484fde (MD5) / Made available in DSpace on 2016-04-27T19:21:27Z (GMT). No. of bitstreams: 1
TadeuFelixDosSantos_DISSERT.pdf: 1188872 bytes, checksum: 47b34679279af1fc33a4e33479484fde (MD5)
Previous issue date: 2015-09-02 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Este estudo oferece uma abordagem anal??tica que visa determinar o campo de temperaturas
desenvolvido durante a soldagem TIG DC sobre uma placa fina de Alum??nio.
As caracter??sticas n?ao-lineares do fen?omeno, tais como a depend?encia das propriedades
termof??sicas e mec?anicas do material com a temperatura, s?ao consideradas nesse estudo.
Al?em do processo de troca de calor por condu?c?ao, s?ao levadas em considera?c?ao as trocas
por convec?c?ao natural e radia?c?ao. Uma an?alise transiente foi realizada a fim de se avaliar
o comportamento temporal do campo de temperatura. Tamb?em uma modelagem tridimensional
para a fonte de calor foi discutida. Com a finalidade de validar os resultados
obtidos atrav?es do modelo anal??tico, foi feito o confronto destes com aqueles obtidos experimentalmente
e os dispon??veis na literatura. As respostas anal??ticas obtidas apresentam
uma boa correla?c?ao com as experimentais dispon??veis na literatura, comprovando assim
a viabilidade e efici?encia deste m?etodo anal??tico na simula?c?ao do ciclo t?ermico para este
tipo de soldagem. / This study offers an analytical approach in order to provide a determination of the temperature
field developed during the DC TIG welding of a thin plate of aluminum. The
non-linear characteristics of the phenomenon, such as the dependence of the thermophysical
and mechanical properties with temperature were considered in this study. In addition
to the conductive heat exchange process, were taken into account the exchange by natural
convection and radiation. A transient analysis is performed in order to obtain the temperature
field as a function of time. It is also discussed a three-dimensional modeling of
the heat source. The results obtained from the analytical model were be compared with
the experimental ones and those available in the literature. The analytical results show a
good correlation with the experimental ones available in the literature, thus proving the
feasibility and efficiency of the analytical method for the simulation of the heat cycle for
this welding process.
|
30 |
Soldagem A-TIG em Aço Inoxidável Ferrítico / A-TIG welding in Ferritic Stainless SteelAzevedo, Alessandra Gois Luciano de January 2011 (has links)
O uso de fluxo ativo no processo de soldagem TIG pode ser uma alternativa para
aumentar a velocidade de soldagem do processo, pois esta técnica permite o aumento da profundidade de penetração do cordão de solda mantendo os mesmo parâmetros
empregados no TIG convencional. A principal desvantagem desta técnica reside principalmente na propensão à formação de uma camada oxidada sobre o cordão de solda
o que pode também acarretar num acabamento superficial ruim. Uma forma de tirar proveito
desta técnica garantindo um bom acabamento do cordão é aplicar o fluxo de tal maneira
que, ao invés de uma camada que cubra toda a superfície da chapa, sejam feitas duas
faixas de fluxo, separadas por uma distância predeterminada, definida como parâmetro “a”.
Esta técnica é chamada neste trabalho de Técnica da Constrição Controlada (TCC). Desta
forma, a camada de fluxo isola eletricamente certas regiões da superfície da peça
direcionando a região de incidência do arco e, como a diluição do fluxo na poça de solda é menor, alia-se a vantagem do aumento de penetração com o bom acabamento do cordão de
solda. O objetivo desta pesquisa é verificar e analisar a influência do uso da Técnica da
Constrição Controlada com o processo A-TIG na soldagem do aço inoxidável ferrítico;
identificar e quantificar os principais fenômenos envolvidos como, aumento da penetração, alterações no arco voltaico e as possíveis modificações nas propriedades mecânicas e metalúrgicas do aço ferrítico. Para isso, realizou-se a soldagem do aço inoxidável ferrítico empregando a técnica da constrição controlada variando-se a largura do parâmetro “a”, a distância eletrodo-peça, a corrente de soldagem e a velocidade de soldagem. Foi possível observar que a geometria do cordão de solda sofre modificações como redução na largura e
aumento da penetração do cordão de solda para todos os casos em que se empregou o
fluxo ativo. Porém, não foi possível um aumento da velocidade de soldagem com os
parâmetros empregados. Quando empregada a Técnica da Constrição Controlada em uma
junta desalinhada, os dados comprovaram que é possível conseguir resultados de desvios
satisfatórios no arco, ou seja, direcioná-lo para a borda da junta, com a utilização de fluxo ativo e a modificação tanto do parâmetro “a” quanto do desalinhamento na tocha (dt). A aplicação desta técnica não provocou alterações nem na tenacidade nem na microestrutura da zona fundida._________________________________________________________________________________________ ABSTRACT: The use of active flux in TIG process can be an alternative to increase the productivity since this technique increases the depth of penetration of weld bead maintaining the same parameters of conventional TIG welding. The results obtained indicate that the use of the traditional way of flux application tend to produce slag, which is hard to remove. In
order to avoid this problem, are approach is by applying two flux strips alongside the joint, separated by a predetermined distance, defined as parameter "a". This technique is called Contraction Controlled Technique (CCT). The result with this methodology was satisfactory, allowing increasing the depth of penetration and ensuring a good weld bead surface finish.
The objective of this research is to verify and analyze the influence of the use of Contraction Controlled Technique with the A-TIG process in the welding of ferritic stainless steel. It also aims to identify and quantify the main phenomena involved such as increase of the penetration, the changes in the arc, and changes in mechanical and metallurgical properties
of the ferritic steel. For this purpose, it were done welding of ferritic stainless steels surfaces using the Contraction Controlled Technique, varying the width of the parameter "a", the distance between the piece and the electrode, the electrical current and welding speed. It was observed that the geometry of the weld beads has suffered modifications such as reduction in width and increased of the penetration of the weld beads for all cases where the
active flux was used. The use of the active flux in TIG welding process is a technique that allows the increased of penetration depth of weld maintain keeping the same parameters used in the conventional TIG. However, it was not possible to increase the speed of the welding within the parameters used. When it was employed the technique of controlled contraction in a disalignment joint, the data showed that it is possible to improve results of arc direction, direct it to the edge of the board, using active flux and modifing both the parameter "a" and the deviation of the torch (dt). The application of this technique did not
cause changes in the toughness or in the microstructure of the fusion zone the ferritic stainless steel.
|