none

Corrosion is a common issue which must be accounted for when designing all metal products in our society. Many factors need to be considered when new alloys are created, and further knowledge of the corrosion process would be of great use for companies worldwide. The purpose of this thesis was to investigate if X-ray Photoelectron Spectroscopy, XPS, can be used to characterise and quantify corrosion products. With the goal to develop a method that can be used for further studies to increase our understanding of the corrosion process. Aluminium alloy AA3003 was subjected to an immersion corrosion test in an acidified salt solution for different periods of time and the produced chemical compounds were characterised using XPS. The results revealed a direct connection between corrosion time and formed product, which after characterisation proved to be aluminium hydroxide, Al(OH)3. It was concluded that XPS can be used for corrosion studies and is a method that shows great potential and should be further developed. / I metallindustrin är korrosion ett ständigt förekommande problem som måste tas i beaktande vid design av metallprodukter. Många faktorer är avgörande när nya legeringar utvecklas och en djupare kunskap om korrosionsprocessen och dess mekanismer är av stort värde för företag världen över. Syftet med detta examensarbete var att undersöka huruvida röntgen-fotoelektron-spektroskopi, XPS, kan användas för att kvalitativt och kvantitativt karakterisera de korrosionsprodukter som bildas vid korrosion. Med målet att presentera en metod som kan användas för att vidare undersöka och öka vår förståelse för korrosionsprocessen. Aluminiumlegering AA3003 utsattes för accelererad korrosion i en surgjord saltlösning under varierande tid och korrosionsprodukter karakteriserades med XPS. Resultatet påvisade direkt korrelation mellan korrosionstid och mängd produkt. Korrosionsprodukten visade sig vara aluminiumhydroxid, Al(OH)3, och med det i åtanke kunde slutsatsen dras att XPS kan användas vid studier av korrosion. Den utvärderade metoden visar stor potential och detta examensarbete öppnar upp för vidare forskning som kan komma att öka förståelsen för korrosionsprocessen och hur den kan kontrolleras.

Recrystallisation is an important topic in the metal industry since the process may drastically alter the properties of the materials subjected to it. By controlling the recrystallisation process, the material properties can be adjusted as desired, which could lead to stronger materials and hence lighter constructions, decreasing our material consumption. This is currently regulated using softening curves complied from tensile tests, a method which does not show the degree of recrystallisation of a metal. This thesis work therefore explores the possibility to characterise the recrystallisation process using in situ X-ray diffraction, XRD, during heating.The method proposed is using in situ heat treatments of aluminium samples combined with XRD measurements. The results show that it is possible to follow the recrystallisation process of rolled aluminium alloy AA3003 by using in situ XRD during heating, a discovery that could facilitate development and understanding of new materials. Nevertheless, further investigations of the subject is required before the method will be profitable. / Rekristallisation är ett viktigt ämne inom metallindustrin, detta eftersom materialegenskaper drastiskt kan förändras under rekristallisationsprocessen. Genom att kontrollera rekristallisationsprocessen kan materialegenskaper skräddarsys efter applikation. Även starkare material kan tillverkas och därav kan lättare strukturer konstrueras och på så vis minskar även materialåtgången. Idag regleras rekristallisation med hjälp av mjukningskurvor sammanställda genom dragprov, en metod som inte kan visa rekristallisationsgraden av en metall. Detta examensarbete utforskar möjligheten att karaktärisera rekristallisationsprocessen genom att använda in situ röntgendiffraktion, XRD, under värmningsprocessen.Den framtagna metoden inkluderar in situ värmebehandlingar av aluminiumprover i kombination med XRD-mätningar. De erhållna resultaten från experimenten visar på att det är fullt möjligt att följa rekristallisationsprocessen av aluminiumlegering AA3003 med in situ XRD, en upptäckt som kan komma att underlätta vid utveckling och förståelse av legeringar och nya material. Dock krävs fortsatta studier i ämnet innan metoden kan anses vara lönsam.

No description available.

No description available.