Spelling suggestions: "subject:"accelerated artificial aging"" "subject:"accelerated artificial nging""
1 |
Alteração de cor e rugosidade superficial de resina composta clareada após envelhecimento em função do tempo / Color change and surface roughness of composite resin cleared after accelerated artificial aging as a function of timeFreitas, Daniela de Biagi 30 July 2010 (has links)
O presente trabalho teve como objetivo analisar “in vitro” a alteração de cor e a rugosidade superficial de uma resina composta (Charisma®) submetidas a tratamento clareador com agente clareador Lase Peroxide Sensy® (CC) e grupo controle sem tratamento clareador (SCL), após envelhecimento (EAA) em função do tempo, realizando-se avaliação superficial complementar por meio de Microscopia Eletrônica de Varredura (MEV) e EDX. Os corpos-de-prova (n=15) foram confeccionados com o auxílio de uma matriz de Teflon nas dimensões de 11x2,0mm, polidos com discos Soft Lex®, na seqüência de abrasividade decrescente e armazenados em saliva artificial a 37ºC (±1ºC), até os momentos de serem submetidos aos tratamentos propostos e à realização das leituras de alteração de cor e rugosidade superficial, nos tempos: 24 horas após a confecção (T0), após envelhecimento artificial acelerado (T1), 24 horas após clareamento (T2), 7dias (T3) e 1 mês após clareamento (T4). As leituras de alteração de cor foram obtidas com o auxílio do aparelho Espectrofotômetro (PCB6807BYK GARDNER) e para as leituras de rugosidade superfícial foi utilizado o Rugosímetro Mitutoyo SJ201P. Os dados foram submetidos à Análise de Variância ANOVA (p≤0,05). Os resultados obtidos foram: a) o fator Tempo teve efeito estatisticamente significante sobre as variáveis ΔE* (T1=T2=T3; T1=T4), L* (T0<T1=T2=T3=T4), a* (T0>T1=T2; T1=T3=T4; T4>T2), b* (T0>T1=T2=T3; T4=T3=T1; T2<T4) e rugosidade superficial (μm) (T0<T1,T2,T3,T4; T1=T2; T1<T3=T4; T2=T3=T4; b) para o fator tratamento com relação a ΔE* e fator L*(CC>SCL), para os fatores a* e b*(CC<SC), c) a interação Tratamento x Tempo não apresentou diferença estatisticamente significante para as variáveis ΔE*, L*, a*, b* e rugosidade superficial, d) as superfícies após EAA apresentaram alterações d) não houve mudanças no EDX antes e após os tratamentos. Conclui-se que a resina Charisma®, apresentou alteração de cor (ΔE*>3,3) e uma estabilidade na rugosidade superficial a partir de T2. / The current study in vitro evaluated the color change and surface roughness of the composite resin Charisma® cleared with Lase Peroxide Sensy® (CCL) and control without bleaching (SCL) after accelerated artificial aging (EAA) as a function of time, performing additional surface evaluation by scanning electron microscopy (MEV) and EDX. To obtain the color change and surface roughness a Spectrophotometer (PCB 6807 BYK GARDNER) and rugosimeter (Mitutoyo SJ- 201P) were employed respectively. Measurements were carried out at five times: 24 hours after preparation (T0), after artificial accelerated aging (T1), 24 hours after bleaching (T2), 7days (T3) and 1 month after bleaching (T4). The specimens (n=15) were prepared with aid of a Teflon (10-mmin diameter and 2mm thick). The specimens were polished with discs Soft Lex®, following abrasiveness decreased, being stored in artificial saliva at 37ºC (±1ºC) until the time of undergoing the proposed treatments and the measurements. The data obtained were submitted to ANOVA parametric test (p ≤ 0.05). The results were: a) time factor had a statistically significant effect on the variables ΔE* (T1 = T2 = T3, T1 = T4), L*(T0 <T1 = T2 = T3 = T4), a* (T0 > T1 = T2; T1=T3 =T4, T4>T2), b* (T0> T1=T2=T3, T4=T3=T1; T2<T4) and roughness(μm) (T0<T1,T2, T3,T4; T1 = T2; T1<T3=T4; T2=T3=T4), b) for treatment factor ΔE* and L* (CC> SCL) for the factors a*and b* (CC <SC), c) Treatment x Time interaction showed no statistically significant difference for the variables ΔE*, L*, a*, b* and surface roughness, d) after EAA the surfaces change d) before and after EAA dont have changes. It is concluded that the resin Charisma®, presented color change (ΔE *> 3.3) and surface roughness stability from T2.
|
2 |
Resistência ao cisalhamento de bráquetes ortodônticos após envelhecimento artificial acelerado / Shear bond strength of orthodontic brackets after accelerated artificial agingDrubi Filho, Brahim 09 December 2011 (has links)
O propósito deste estudo foi comparar a resistência ao cisalhamento (RC) e o índice de remanescente adesivo (IRA) após Envelhecimento Artificial Acelerado (EAA) de bráquetes ortodônticos metálicos fixados com compósitos autopolimerizável (Concise Ortodôntico - CS, 3M Unitek) e fotoativado (Transbond Plus Color Change - TPCC, 3M Unitek) com diferentes tratamentos de superfície do esmalte. Foram selecionados 60 pré-molares humanos recém extraídos, que tiveram suas raízes embutidas em resina acrílica ativada quimicamente de forma que a face vestibular ficasse perpendicular ao plano horizontal. Estas foram limpas com pedra pomes e água por 10 segundos, lavadas e secas. Os dentes foram separados aleatoriamente em 5 grupos (n=12), segundo o tipo de tratamento de superfície do esmalte, e do compósito utilizado para fixação dos bráquetes: Grupo I - ácido fosfórico a 37% (Dental Gel, Dentsply) e CS; Grupo II - ácido fosfórico a 37% + Primer e CS; Grupo III - ácido fosfórico a 37% e TPCC; Grupo IV - ácido fosfórico a 37% + XT Primer (3M Unitek) e TPCC; e Grupo V Transbond Plus Self Etching Primer - SEP (3M Unitek) e TPCC. Após 24h da colagem dos bráquetes, metade das amostras de cada grupo (n=6) foi submetida ao EAA por 960 horas. Todas as amostras foram submetidas ao ensaio de resistência ao cisalhamento com cinzel em máquina universal de ensaios (DL 200, EMIC) na velocidade de 0,5 mm/min. Após a descolagem dos bráquetes, causada pelo teste de resistência ao cisalhamento, o IRA foi avaliado em lupa (10X) e quantificado a partir de escore (0-3). Os dados foram analisados estatisticamente (2-way ANOVA, Bonferroni, p<0,05) e verificou-se que não houve diferença estatisticamente significante entre os Grupos em função do EAA (p>0,05). Quando comparados os sistemas adesivos utilizados, verificou-se que o Grupo II sem EAA, apresentou a maior média de RC, resultado estatisticamente significante (p<0,05) em relação aos grupos III e V, que apresentou a menor média de RC. Quanto ao IRA, todos os grupos sem EAA apresentaram maior frequência do índice 3. Com EAA, houve aumento de frequência dos índices 1 e 2. Concluiu-se que o EAA não influenciou a RC de bráquetes ao dente, mas diminuiu a área de remanescente adesivo sobre o dente. / The purpose of this study was to compare the shear bond strength (SBS) and the adhesive remnant index (ARI) after Accelerated Artificial Aging (AAA) of metal orthodontic brackets bonded with self-polymerizing (Concise Ortodôntico - CS, 3M Unitek) and light activated (Transbond Plus Color Change - TPCC, 3M Unitek) composites, to enamel with different surface treatments. Sixty recently-extracted human premolars were selected. Their roots were embedded in chemically activated acrylic resin so that the vestibular face was perpendicular to the horizontal plane. They were cleaned with pumice stone and water for 10 seconds, washed and dried. The teeth were randomly separated into 5 groups (n=12), according to the type of enamel surface treatment, and composite used for bracket bonding: Group I - 37% phosphoric acid (Dental Gel, Dentsply) and CS; Group II - 37% phosphoric acid + Primer and CS; Group III - 37% phosphoric acid and TPCC; Group IV - 37% phosphoric acid + XT Primer (3M Unitek) and TPCC; and Group V Transbond Plus Self Etching Primer - SEP (3M Unitek) and TPCC. Twenty-four hours after bracket bonding, half the samples from each group (n=6) were submitted to AAA for 960 hours. All the samples were submitted to shear bond strength testing with a chisel, in a Universal Test Machine (DL 200, EMIC) at a speed of 0.5 mm/min. After bracket debonding caused by the shear bond strength test, the ARI was evaluated under a loupe (10X) and quantified according to a score (0-3). Data were statistically analyzed (2-way ANOVA, Bonferroni, p<0.05) and it was verified that there was no statistically significant difference among Groups as a function of AAA (p>0.05). When comparing the adhesive systems used, it was verified that Group II without AAA showed the highest mean SBS, a statistically significant result (p<0.05) in comparison with Groups III and V, which showed the lowest mean SBS. As regards ARI, all the groups without AAA showed higher frequency of Index 3. With AAA, there was increased frequency of indexes 1 and 2. It was concluded that AAA did not influence SBS of brackets to the tooth, but diminished the area of adhesive remnant on the tooth.
|
3 |
Resistência ao cisalhamento de bráquetes ortodônticos após envelhecimento artificial acelerado / Shear bond strength of orthodontic brackets after accelerated artificial agingBrahim Drubi Filho 09 December 2011 (has links)
O propósito deste estudo foi comparar a resistência ao cisalhamento (RC) e o índice de remanescente adesivo (IRA) após Envelhecimento Artificial Acelerado (EAA) de bráquetes ortodônticos metálicos fixados com compósitos autopolimerizável (Concise Ortodôntico - CS, 3M Unitek) e fotoativado (Transbond Plus Color Change - TPCC, 3M Unitek) com diferentes tratamentos de superfície do esmalte. Foram selecionados 60 pré-molares humanos recém extraídos, que tiveram suas raízes embutidas em resina acrílica ativada quimicamente de forma que a face vestibular ficasse perpendicular ao plano horizontal. Estas foram limpas com pedra pomes e água por 10 segundos, lavadas e secas. Os dentes foram separados aleatoriamente em 5 grupos (n=12), segundo o tipo de tratamento de superfície do esmalte, e do compósito utilizado para fixação dos bráquetes: Grupo I - ácido fosfórico a 37% (Dental Gel, Dentsply) e CS; Grupo II - ácido fosfórico a 37% + Primer e CS; Grupo III - ácido fosfórico a 37% e TPCC; Grupo IV - ácido fosfórico a 37% + XT Primer (3M Unitek) e TPCC; e Grupo V Transbond Plus Self Etching Primer - SEP (3M Unitek) e TPCC. Após 24h da colagem dos bráquetes, metade das amostras de cada grupo (n=6) foi submetida ao EAA por 960 horas. Todas as amostras foram submetidas ao ensaio de resistência ao cisalhamento com cinzel em máquina universal de ensaios (DL 200, EMIC) na velocidade de 0,5 mm/min. Após a descolagem dos bráquetes, causada pelo teste de resistência ao cisalhamento, o IRA foi avaliado em lupa (10X) e quantificado a partir de escore (0-3). Os dados foram analisados estatisticamente (2-way ANOVA, Bonferroni, p<0,05) e verificou-se que não houve diferença estatisticamente significante entre os Grupos em função do EAA (p>0,05). Quando comparados os sistemas adesivos utilizados, verificou-se que o Grupo II sem EAA, apresentou a maior média de RC, resultado estatisticamente significante (p<0,05) em relação aos grupos III e V, que apresentou a menor média de RC. Quanto ao IRA, todos os grupos sem EAA apresentaram maior frequência do índice 3. Com EAA, houve aumento de frequência dos índices 1 e 2. Concluiu-se que o EAA não influenciou a RC de bráquetes ao dente, mas diminuiu a área de remanescente adesivo sobre o dente. / The purpose of this study was to compare the shear bond strength (SBS) and the adhesive remnant index (ARI) after Accelerated Artificial Aging (AAA) of metal orthodontic brackets bonded with self-polymerizing (Concise Ortodôntico - CS, 3M Unitek) and light activated (Transbond Plus Color Change - TPCC, 3M Unitek) composites, to enamel with different surface treatments. Sixty recently-extracted human premolars were selected. Their roots were embedded in chemically activated acrylic resin so that the vestibular face was perpendicular to the horizontal plane. They were cleaned with pumice stone and water for 10 seconds, washed and dried. The teeth were randomly separated into 5 groups (n=12), according to the type of enamel surface treatment, and composite used for bracket bonding: Group I - 37% phosphoric acid (Dental Gel, Dentsply) and CS; Group II - 37% phosphoric acid + Primer and CS; Group III - 37% phosphoric acid and TPCC; Group IV - 37% phosphoric acid + XT Primer (3M Unitek) and TPCC; and Group V Transbond Plus Self Etching Primer - SEP (3M Unitek) and TPCC. Twenty-four hours after bracket bonding, half the samples from each group (n=6) were submitted to AAA for 960 hours. All the samples were submitted to shear bond strength testing with a chisel, in a Universal Test Machine (DL 200, EMIC) at a speed of 0.5 mm/min. After bracket debonding caused by the shear bond strength test, the ARI was evaluated under a loupe (10X) and quantified according to a score (0-3). Data were statistically analyzed (2-way ANOVA, Bonferroni, p<0.05) and it was verified that there was no statistically significant difference among Groups as a function of AAA (p>0.05). When comparing the adhesive systems used, it was verified that Group II without AAA showed the highest mean SBS, a statistically significant result (p<0.05) in comparison with Groups III and V, which showed the lowest mean SBS. As regards ARI, all the groups without AAA showed higher frequency of Index 3. With AAA, there was increased frequency of indexes 1 and 2. It was concluded that AAA did not influence SBS of brackets to the tooth, but diminished the area of adhesive remnant on the tooth.
|
4 |
Alteração de cor e rugosidade superficial de resina composta clareada após envelhecimento em função do tempo / Color change and surface roughness of composite resin cleared after accelerated artificial aging as a function of timeDaniela de Biagi Freitas 30 July 2010 (has links)
O presente trabalho teve como objetivo analisar “in vitro” a alteração de cor e a rugosidade superficial de uma resina composta (Charisma®) submetidas a tratamento clareador com agente clareador Lase Peroxide Sensy® (CC) e grupo controle sem tratamento clareador (SCL), após envelhecimento (EAA) em função do tempo, realizando-se avaliação superficial complementar por meio de Microscopia Eletrônica de Varredura (MEV) e EDX. Os corpos-de-prova (n=15) foram confeccionados com o auxílio de uma matriz de Teflon nas dimensões de 11x2,0mm, polidos com discos Soft Lex®, na seqüência de abrasividade decrescente e armazenados em saliva artificial a 37ºC (±1ºC), até os momentos de serem submetidos aos tratamentos propostos e à realização das leituras de alteração de cor e rugosidade superficial, nos tempos: 24 horas após a confecção (T0), após envelhecimento artificial acelerado (T1), 24 horas após clareamento (T2), 7dias (T3) e 1 mês após clareamento (T4). As leituras de alteração de cor foram obtidas com o auxílio do aparelho Espectrofotômetro (PCB6807BYK GARDNER) e para as leituras de rugosidade superfícial foi utilizado o Rugosímetro Mitutoyo SJ201P. Os dados foram submetidos à Análise de Variância ANOVA (p≤0,05). Os resultados obtidos foram: a) o fator Tempo teve efeito estatisticamente significante sobre as variáveis ΔE* (T1=T2=T3; T1=T4), L* (T0<T1=T2=T3=T4), a* (T0>T1=T2; T1=T3=T4; T4>T2), b* (T0>T1=T2=T3; T4=T3=T1; T2<T4) e rugosidade superficial (μm) (T0<T1,T2,T3,T4; T1=T2; T1<T3=T4; T2=T3=T4; b) para o fator tratamento com relação a ΔE* e fator L*(CC>SCL), para os fatores a* e b*(CC<SC), c) a interação Tratamento x Tempo não apresentou diferença estatisticamente significante para as variáveis ΔE*, L*, a*, b* e rugosidade superficial, d) as superfícies após EAA apresentaram alterações d) não houve mudanças no EDX antes e após os tratamentos. Conclui-se que a resina Charisma®, apresentou alteração de cor (ΔE*>3,3) e uma estabilidade na rugosidade superficial a partir de T2. / The current study in vitro evaluated the color change and surface roughness of the composite resin Charisma® cleared with Lase Peroxide Sensy® (CCL) and control without bleaching (SCL) after accelerated artificial aging (EAA) as a function of time, performing additional surface evaluation by scanning electron microscopy (MEV) and EDX. To obtain the color change and surface roughness a Spectrophotometer (PCB 6807 BYK GARDNER) and rugosimeter (Mitutoyo SJ- 201P) were employed respectively. Measurements were carried out at five times: 24 hours after preparation (T0), after artificial accelerated aging (T1), 24 hours after bleaching (T2), 7days (T3) and 1 month after bleaching (T4). The specimens (n=15) were prepared with aid of a Teflon (10-mmin diameter and 2mm thick). The specimens were polished with discs Soft Lex®, following abrasiveness decreased, being stored in artificial saliva at 37ºC (±1ºC) until the time of undergoing the proposed treatments and the measurements. The data obtained were submitted to ANOVA parametric test (p ≤ 0.05). The results were: a) time factor had a statistically significant effect on the variables ΔE* (T1 = T2 = T3, T1 = T4), L*(T0 <T1 = T2 = T3 = T4), a* (T0 > T1 = T2; T1=T3 =T4, T4>T2), b* (T0> T1=T2=T3, T4=T3=T1; T2<T4) and roughness(μm) (T0<T1,T2, T3,T4; T1 = T2; T1<T3=T4; T2=T3=T4), b) for treatment factor ΔE* and L* (CC> SCL) for the factors a*and b* (CC <SC), c) Treatment x Time interaction showed no statistically significant difference for the variables ΔE*, L*, a*, b* and surface roughness, d) after EAA the surfaces change d) before and after EAA dont have changes. It is concluded that the resin Charisma®, presented color change (ΔE *> 3.3) and surface roughness stability from T2.
|
5 |
Efeito do envelhecimento artificial acelerado na estabilidade de cor de cimentos resinosos para cimentação de laminados cerâmicos / Effect of accelerated artificial aging on color stability of resin cements for luting ceramic laminatesSilame, Francisca Daniele Jardilino 10 April 2013 (has links)
O objetivo deste estudo foi avaliar a estabilidade de cor de cimentos resinosos para fixação de restaurações cerâmicas em diferentes espessuras submetidas ao envelhecimento artificial acelerado (EAA). Foram utilizados 60 molares humanos hígidos, cujas porções radiculares foram incluídas em matriz de PVC (15 mm de diâmetro) com resina acrílica e as faces oclusais foram planificadas, 30 em esmalte e 30 até dentina, sendo que 10 dentes de cada substrato foram considerados gruposcontrole para os dentes restaurados. Foram obtidos 40 corpos de prova em cerâmica (IPS e-max Ceram, Ivoclar Vivadent), com 0,5 mm e 1,0 mm, que foram separados aleatoriamente em dois grupos (n=10) segundo o tipo de cimento resinoso dual utilizado para fixação: convencional (Variolink II, Ivoclar/Vivadent) ou auto-adesivo (Rely-X Unicem, 3M ESPE). Além desses, foram obtidos 10 corpos de prova de cada cimento resinoso (0,5mm), considerado grupo-controle para os materiais. Todas as amostras foram mantidas em estufa a 37ºC por 24h, após o qual foram realizadas as leituras de cor iniciais (Vita EasyShade, VITA). Em seguida, foram submetidas ao EAA por 580 horas, após o qual novas leituras de cor foram realizadas. Foi avaliada estabilidade de cor e a luminosidade. Os dados de estabilidade de cor (ΔE) e luminosidade (ΔL) obtidos foram submetidos a análise estatística (2-way ANOVA, Bonferroni, p<0,05) e a comparação dos materiais com os grupos controles foi realizada utilizando 1-way ANOVA e teste de Tukey (p<0,05). O cimento dual convencional apresentou maior alteração de cor e luminosidade quando sob a restauração de 0,5mm, diferente estatisticamente (p<0,05) de restaurações de 1,0mm. Não houve diferença estatisticamente significante (p>0,05) quando comparados os materiais. Quando analisadas a estabilidade de cor e luminosidade dos grupos com restaurações em relação aos grupos-controle, verificou-se que ambos os cimentos apresentaram maiores alterações, diferente estatisticamente (p<0,05) dos demais grupos, com exceção ao grupo de 0,5mm em relação ao Grupo esmalte quando analisado o cimento dual convencional (p>0,05). Concluiu-se que quanto menor a espessura da restauração, maior a alteração de cor e de luminosidade do cimento dual convencional. As alterações do cimento autoadesivo não dependem da espessura da restauração. / The aim of this study was to evaluate the color stability of resin cements for luting ceramic restorations with different thicknesses submitted to accelerated artificial aging (AAA). Sixty sound human molars had their root portions embedded in PVC rings (15-mm diameter) with acrylic resin. Their occlusal surfaces were flattened according two substrates: 30 surfaces until enamel and 30 until dentin. Then, 10 teeth of each substrate were considered as control groups for restored teeth. Forty specimens of ceramic (IPS e-max Ceram, Ivoclar Vivadent) were obtained with two different thicknesses (0.5 mm and 1.0 mm) and were randomly separated into two groups (n = 10) according to the type of the Dual resin cement used for luting: conventional (Variolink II, Ivoclar / Vivadent) or self-adhesive (Rely-X Unicem, 3M ESPE). Also, 10 specimens (0.5 mm) of each cement were obtained to be considered as control groups for materials. All specimens were stored at 37º C for 24 hours, and initial color readings (Vita Easyshade, VITA) were performed. Then, they were submitted to AAA for 580 hours, and final color readings were taken. Color stability and brightness were evaluated. Data of color stability (ΔE) and brightness (ΔL) were statistically analyzed (2- way ANOVA, Bonferroni, p<0.05) and the comparison of materials with control groups was performed using one-way ANOVA and Tukeys test (p<0.05). The conventional dual cement showed the greatest change in color and brightness when under restorations of 0.5 mm, statistically different (p<0.05) to restorations of 1.0 mm. There was no statistically significant difference (p>0.05) when comparing materials. When analyzing the color stability and brightness of restorations groups compared to control groups, both cements showed greater changes, statistically different (p<0.05), than other groups, except for the group of 0.5 mm in relation to enamel group when the dual conventional cement was analyzed (p>0.05). It was concluded that the smaller the thickness of the restoration, the greater the color and brightness changes of the dual conventional cement. Changes of the self-adhesive cement do not depend on the thickness of the restoration.
|
6 |
Efeito do envelhecimento artificial acelerado na estabilidade de cor de cimentos resinosos para cimentação de laminados cerâmicos / Effect of accelerated artificial aging on color stability of resin cements for luting ceramic laminatesFrancisca Daniele Jardilino Silame 10 April 2013 (has links)
O objetivo deste estudo foi avaliar a estabilidade de cor de cimentos resinosos para fixação de restaurações cerâmicas em diferentes espessuras submetidas ao envelhecimento artificial acelerado (EAA). Foram utilizados 60 molares humanos hígidos, cujas porções radiculares foram incluídas em matriz de PVC (15 mm de diâmetro) com resina acrílica e as faces oclusais foram planificadas, 30 em esmalte e 30 até dentina, sendo que 10 dentes de cada substrato foram considerados gruposcontrole para os dentes restaurados. Foram obtidos 40 corpos de prova em cerâmica (IPS e-max Ceram, Ivoclar Vivadent), com 0,5 mm e 1,0 mm, que foram separados aleatoriamente em dois grupos (n=10) segundo o tipo de cimento resinoso dual utilizado para fixação: convencional (Variolink II, Ivoclar/Vivadent) ou auto-adesivo (Rely-X Unicem, 3M ESPE). Além desses, foram obtidos 10 corpos de prova de cada cimento resinoso (0,5mm), considerado grupo-controle para os materiais. Todas as amostras foram mantidas em estufa a 37ºC por 24h, após o qual foram realizadas as leituras de cor iniciais (Vita EasyShade, VITA). Em seguida, foram submetidas ao EAA por 580 horas, após o qual novas leituras de cor foram realizadas. Foi avaliada estabilidade de cor e a luminosidade. Os dados de estabilidade de cor (ΔE) e luminosidade (ΔL) obtidos foram submetidos a análise estatística (2-way ANOVA, Bonferroni, p<0,05) e a comparação dos materiais com os grupos controles foi realizada utilizando 1-way ANOVA e teste de Tukey (p<0,05). O cimento dual convencional apresentou maior alteração de cor e luminosidade quando sob a restauração de 0,5mm, diferente estatisticamente (p<0,05) de restaurações de 1,0mm. Não houve diferença estatisticamente significante (p>0,05) quando comparados os materiais. Quando analisadas a estabilidade de cor e luminosidade dos grupos com restaurações em relação aos grupos-controle, verificou-se que ambos os cimentos apresentaram maiores alterações, diferente estatisticamente (p<0,05) dos demais grupos, com exceção ao grupo de 0,5mm em relação ao Grupo esmalte quando analisado o cimento dual convencional (p>0,05). Concluiu-se que quanto menor a espessura da restauração, maior a alteração de cor e de luminosidade do cimento dual convencional. As alterações do cimento autoadesivo não dependem da espessura da restauração. / The aim of this study was to evaluate the color stability of resin cements for luting ceramic restorations with different thicknesses submitted to accelerated artificial aging (AAA). Sixty sound human molars had their root portions embedded in PVC rings (15-mm diameter) with acrylic resin. Their occlusal surfaces were flattened according two substrates: 30 surfaces until enamel and 30 until dentin. Then, 10 teeth of each substrate were considered as control groups for restored teeth. Forty specimens of ceramic (IPS e-max Ceram, Ivoclar Vivadent) were obtained with two different thicknesses (0.5 mm and 1.0 mm) and were randomly separated into two groups (n = 10) according to the type of the Dual resin cement used for luting: conventional (Variolink II, Ivoclar / Vivadent) or self-adhesive (Rely-X Unicem, 3M ESPE). Also, 10 specimens (0.5 mm) of each cement were obtained to be considered as control groups for materials. All specimens were stored at 37º C for 24 hours, and initial color readings (Vita Easyshade, VITA) were performed. Then, they were submitted to AAA for 580 hours, and final color readings were taken. Color stability and brightness were evaluated. Data of color stability (ΔE) and brightness (ΔL) were statistically analyzed (2- way ANOVA, Bonferroni, p<0.05) and the comparison of materials with control groups was performed using one-way ANOVA and Tukeys test (p<0.05). The conventional dual cement showed the greatest change in color and brightness when under restorations of 0.5 mm, statistically different (p<0.05) to restorations of 1.0 mm. There was no statistically significant difference (p>0.05) when comparing materials. When analyzing the color stability and brightness of restorations groups compared to control groups, both cements showed greater changes, statistically different (p<0.05), than other groups, except for the group of 0.5 mm in relation to enamel group when the dual conventional cement was analyzed (p>0.05). It was concluded that the smaller the thickness of the restoration, the greater the color and brightness changes of the dual conventional cement. Changes of the self-adhesive cement do not depend on the thickness of the restoration.
|
7 |
Efeito da escovação e do envelhecimento artificial acelerado sobre a alteração superficial de materiais restauradores estéticos / Effect of simulated toothbrushing and accelerated artificial aging on surface degradation of aesthetic restorative materialsRoselino, Lourenço de Moraes Rego 11 April 2012 (has links)
O objetivo desse estudo foi avaliar sistematicamente o efeito da escovação simulada e do envelhecimento artificial acelerado (EAA) sobre estabilidade de cor e rugosidade de superfície de compósitos odontológicos de nanopartículas (Z350 - 3M ESPE) e híbrido (Tetric N-Ceram - Ivoclar Vivadent). Foram confeccionados 24 corpos-de-prova (12mm de diâmetro X 2mm de espessura) para cada compósito e uma cerâmica de revestimento (IPS e.max Ceram - Ivoclar Vivadent) como controle. Após sua confecção, os corpos-de-prova foram polidos com lixas d‘água em abrasividades decrescentes (compósitos = 600, 1200 e 2000 e cerâmica = 100, 320, 1200 e 2000). Em seguida, foram realizadas leituras iniciais de cor (Espectrofotômetro PCB 6807) e rugosidade de superfície (Rugosímetro Surfcorder SE 1700 - Kosakalab). As amostras foram separadas em 3 grupos (n=8), segundo o tratamento a que foram submetidas: Grupo 1: EAA; Grupo 2: escovação mecânica com dentifrício RDA* 68 (Colgate); e Grupo 3: escovação mecânica com dentifrício RDA* 180 (Colgate Total Plus Whitening). Após 480 horas de EAA e em intervalos de 41 minutos de escovação (=14.600 ciclos) até 205 minutos novas leituras de cor e rugosidade de superfície foram realizadas. Amostras inicialmente submetidas a EAA (n=4) receberam escovação mecânica com dentifrício RDA* 68 e 180, conforme metodologia descrita anteriormente e novas leituras de cor e rugosidade foram obtidas. Os dados (antes e após os testes) foram analisados estatisticamente (2-way ANOVA análises repetidas, Bonferroni, p<0,05) e verificou-se que houve maior alteração de cor dos compósitos quando submetidos a EAA com diferença estatisticamente significante (p<0,05) em relação à escovação mecânica. Não houve diferença estatisticamente significante (p>0,05) na estabilidade de cor dos materiais quando comparadas as abrasividades dos dentifrícios, porém esse fator foi significante para a alteração de rugosidade de superfície (p<0,05), sendo maior quando os materiais foram escovados com RDA* 180. Quanto ao tempo de escovação, não houve diferença estatisticamente significante (p>0,05) para a alteração de cor e de rugosidade de superfície dos materiais, o mesmo ocorrendo para amostras escovadas após EAA. Conclui-se que o EAA interfere na estabilidade de cor e a escovação simulada nas alterações de rugosidade de superfície dos compósitos, independente do tempo de utilização do dentifrício, sendo maior para dentifrícios mais abrasivos. Além disso, a abrasividade e o tempo de utilização do dentifrício não alteram a capacidade de remoção do manchamento e a rugosidade de superfície de compósitos. / The purpose of this study was to evaluate the effect of simulated toothbrushing and accelerated artificial aging (AAA) on color stability and surface roughness of nanofill (Z350 - 3M ESPE) and hybrid (Tetric N-Ceram - Ivoclar Vivadent) composites. Twenty-four diskshaped specimens (12mm in diameter X 2 mm thick) were made for each composite and one feldspatic ceramic (IPS e.max Ceram - Ivoclar Vivadent) as a control. The specimens were polished with decreasing abrasiveness sandpapers (composites = 600, 1200, 2000 and ceramic = 100, 320, 1200, 2000). Then, initial readings were taken on color (Spectrophotometer PCB 6807) and surface roughness (Rugosimeter Surfcorder SE 1700 - Kosakalab). The samples were separated in 3 groups (n=8) according to the submitted treatments: Group 1: AAA; Group 2: mechanical brushing with dentifrice RDA* 68 (Colgate); and Group 3: mechanical brushing with dentifrice RDA* 180 (Colgate Total Plus Whitening). New readings on color and surface roughness were taken after 480 hours of AAA and in intervals of 41 minutes of brushing (=14.600 cycles) until 205 minutes. The samples initially submitted to AAA (n=4) received mechanical brushing with dentifrice RDA* 68 and 180, according to previously described methodology and new readings on color and roughness were taken. Data (before and after tests) were statistically analyzed (2- way ANOVA repeated measures, Bonferroni, p<0,05) and it was observed a higher composite color alteration compared with mechanical brushing when submitted to AAA with a statistically significant difference (p<0,05) between them. There was no statistically significant difference (p>0,05) on color stability of materials when the dentifrices abrasiveness were compared, but it was significant for surface roughness degradation (p<0,05), higher when materials were brushed with RDA* 180. Regarding time brushing, there was no statistically significant difference (p>0,05) for color alteration and roughness surface of materials and the same occurred for samples brushed after AAA. It was concluded that AAA interferes on color stability and the simulated brushing on surface roughness degradation of composites regardless the time of used dentifrice, but it was higher for more abrasive dentifrices. Moreover, abrasiveness and time of used dentifrice do not alter the capacity of staining removal and the surface roughness of composites.
|
8 |
Efeito da escovação e do envelhecimento artificial acelerado sobre a alteração superficial de materiais restauradores estéticos / Effect of simulated toothbrushing and accelerated artificial aging on surface degradation of aesthetic restorative materialsLourenço de Moraes Rego Roselino 11 April 2012 (has links)
O objetivo desse estudo foi avaliar sistematicamente o efeito da escovação simulada e do envelhecimento artificial acelerado (EAA) sobre estabilidade de cor e rugosidade de superfície de compósitos odontológicos de nanopartículas (Z350 - 3M ESPE) e híbrido (Tetric N-Ceram - Ivoclar Vivadent). Foram confeccionados 24 corpos-de-prova (12mm de diâmetro X 2mm de espessura) para cada compósito e uma cerâmica de revestimento (IPS e.max Ceram - Ivoclar Vivadent) como controle. Após sua confecção, os corpos-de-prova foram polidos com lixas d‘água em abrasividades decrescentes (compósitos = 600, 1200 e 2000 e cerâmica = 100, 320, 1200 e 2000). Em seguida, foram realizadas leituras iniciais de cor (Espectrofotômetro PCB 6807) e rugosidade de superfície (Rugosímetro Surfcorder SE 1700 - Kosakalab). As amostras foram separadas em 3 grupos (n=8), segundo o tratamento a que foram submetidas: Grupo 1: EAA; Grupo 2: escovação mecânica com dentifrício RDA* 68 (Colgate); e Grupo 3: escovação mecânica com dentifrício RDA* 180 (Colgate Total Plus Whitening). Após 480 horas de EAA e em intervalos de 41 minutos de escovação (=14.600 ciclos) até 205 minutos novas leituras de cor e rugosidade de superfície foram realizadas. Amostras inicialmente submetidas a EAA (n=4) receberam escovação mecânica com dentifrício RDA* 68 e 180, conforme metodologia descrita anteriormente e novas leituras de cor e rugosidade foram obtidas. Os dados (antes e após os testes) foram analisados estatisticamente (2-way ANOVA análises repetidas, Bonferroni, p<0,05) e verificou-se que houve maior alteração de cor dos compósitos quando submetidos a EAA com diferença estatisticamente significante (p<0,05) em relação à escovação mecânica. Não houve diferença estatisticamente significante (p>0,05) na estabilidade de cor dos materiais quando comparadas as abrasividades dos dentifrícios, porém esse fator foi significante para a alteração de rugosidade de superfície (p<0,05), sendo maior quando os materiais foram escovados com RDA* 180. Quanto ao tempo de escovação, não houve diferença estatisticamente significante (p>0,05) para a alteração de cor e de rugosidade de superfície dos materiais, o mesmo ocorrendo para amostras escovadas após EAA. Conclui-se que o EAA interfere na estabilidade de cor e a escovação simulada nas alterações de rugosidade de superfície dos compósitos, independente do tempo de utilização do dentifrício, sendo maior para dentifrícios mais abrasivos. Além disso, a abrasividade e o tempo de utilização do dentifrício não alteram a capacidade de remoção do manchamento e a rugosidade de superfície de compósitos. / The purpose of this study was to evaluate the effect of simulated toothbrushing and accelerated artificial aging (AAA) on color stability and surface roughness of nanofill (Z350 - 3M ESPE) and hybrid (Tetric N-Ceram - Ivoclar Vivadent) composites. Twenty-four diskshaped specimens (12mm in diameter X 2 mm thick) were made for each composite and one feldspatic ceramic (IPS e.max Ceram - Ivoclar Vivadent) as a control. The specimens were polished with decreasing abrasiveness sandpapers (composites = 600, 1200, 2000 and ceramic = 100, 320, 1200, 2000). Then, initial readings were taken on color (Spectrophotometer PCB 6807) and surface roughness (Rugosimeter Surfcorder SE 1700 - Kosakalab). The samples were separated in 3 groups (n=8) according to the submitted treatments: Group 1: AAA; Group 2: mechanical brushing with dentifrice RDA* 68 (Colgate); and Group 3: mechanical brushing with dentifrice RDA* 180 (Colgate Total Plus Whitening). New readings on color and surface roughness were taken after 480 hours of AAA and in intervals of 41 minutes of brushing (=14.600 cycles) until 205 minutes. The samples initially submitted to AAA (n=4) received mechanical brushing with dentifrice RDA* 68 and 180, according to previously described methodology and new readings on color and roughness were taken. Data (before and after tests) were statistically analyzed (2- way ANOVA repeated measures, Bonferroni, p<0,05) and it was observed a higher composite color alteration compared with mechanical brushing when submitted to AAA with a statistically significant difference (p<0,05) between them. There was no statistically significant difference (p>0,05) on color stability of materials when the dentifrices abrasiveness were compared, but it was significant for surface roughness degradation (p<0,05), higher when materials were brushed with RDA* 180. Regarding time brushing, there was no statistically significant difference (p>0,05) for color alteration and roughness surface of materials and the same occurred for samples brushed after AAA. It was concluded that AAA interferes on color stability and the simulated brushing on surface roughness degradation of composites regardless the time of used dentifrice, but it was higher for more abrasive dentifrices. Moreover, abrasiveness and time of used dentifrice do not alter the capacity of staining removal and the surface roughness of composites.
|
9 |
Avaliação da influência do envelhecimento artificial acelerado e armazenamento em fluorfosfato acidulado a 1,23% na rugosidade superficial e na alteração de cor de cerâmicas odontológicas de ultra-baixa fusão para titânio comercialmente pur / Evaluation of the influence of the accelerated artificial aging and storage in 1.23% acidulated phosphate fluoride over superficial roughness and color stability of two low-fusing dental ceramics to commercially pure titaniumJanisse Martinelli Borges de Oliveira 20 December 2007 (has links)
O objetivo do trabalho foi avaliar a influência do envelhecimento artificial acelerado e do fluorfosfato acidulado a 1,23% sobre a rugosidade superficial e alteração de cor de duas cerâmicas odontológicas de ultra-baixa fusão para titânio (Triceram- Dentaurum, e Noritake Ti22- Noritake), livre de metal ou com subestrutura em titânio comercialmente puro (Tritan- Dentaurum). A partir de uma matriz cilíndrica em teflon foram confeccionados, ao todo, 80 corpos-de-prova, com 15mm de diâmetro e 2,5mm de espessura, sendo 40 para cada cerâmica, 20 amostras livre de metal e 20 metalocerâmicas, que foram divididas em dois grupos de 10 amostras cada, sendo submetidas ao envelhecimento artificial acelerado (Sistema Acelerado de Envelhecimento para não-metálicos C-UV - Comexim Matérias Primas Ltda, São Paulo, Brasil) ou ao armazenamento em fluorfosfato acidulado a 1,23%. A rugosidade superficial foi realizada em rugosímetro SJ - 201P (Mitutoyo, Tokyo, Japão) em dois momentos: inicial (R1) foi aquela mensurada logo após obtidos os corpos-de-prova e a rugosidade superficial final (R2) aquela obtida após o envelhecimento artificial acelerado ou armazenamento em fluorfosfato acidulado a 1,23%. Para verificar as alterações de cor ocorridas nas cerâmicas odontológicas utilizou-se o Espectrofotômetro PCB 6807 BYK GARDNER (Columbia, Estados Unidos). Foram feitas leituras antes e após as etapas de envelhecimento artificial acelerado e armazenamento em fluorfosfato acidulado a 1,23%. Os resultados médios e desvios padrão para os corpos-de-prova livre de metal com envelhecimento artificial acelerado foram: a) rugosidade superficial: Triceram antes 0,390 ± 0,097, após 0,431 ± 0,100; Noritake Ti 22 antes 0,299 ± 0,075, após 0,312 ± 0,076; b) alteração de cor: Triceram 0,28 ± 0,14; Noritake Ti 22 0,33 ± 0,22; e para os corpos-de-prova submetidos ao armazenamento em fluorfosfato acidulado a 1,23% foram: a) rugosidade superficial: Triceram antes 0,325 ± 0,036 , após 2,199 ± 0,889; Noritake Ti 22 antes 0,317 ± 0,094, após 2,760 ± 0,833; b) alteração de cor: Triceram 5,39 ± 1,61; Noritake Ti 22 7,31 ± 0,71. Para as amostras metalocerâmicas com envelhecimento artificial acelerado foram: a) rugosidade superficial: Triceram antes 0,282 ± 0,06, após 0,315 ± 0,095; Noritake Ti 22 antes 0,269 ± 0,062, após 0,290 ± 0,075; b) alteração de cor: Triceram 0,57 ± 0,11; Noritake Ti 22 0,41 ± 0,08; e para os corpos-de-prova submetidos ao armazenamento em fluorfosfato acidulado a 1,23% foram: a) rugosidade superficial: Triceram antes 0,137 ± 0,026, após 2,560 ± 0,377; Noritake Ti 22 antes 0,125 ± 0,34, após 3,174 ± 0,565; b) alteração de cor: Triceram 7,56 ± 1,21; Noritake Ti 22 7,69 ± 1,26. Os resultados obtidos mostraram que o envelhecimento artificial acelerado simulando dez anos de uso clínico da restauração não afetou a rugosidade superficial de nenhuma das cerâmicas avaliadas, em nenhum grupo; que apenas o grupo da cerâmica Triceram com subestrutura em titânio comercialmente puro revelou valores de ΔE estatisticamente maiores que os demais, revelando que o envelhecimento artificial acelerado influenciou a coloração desse grupo. Entretanto, a alteração de cor apresentou-se menor que um, sendo considerada clinicamente indetectável; que após o armazenamento em fluorfosfato acidulado foi observado aumento de rugosidade superficial semelhante estatisticamente para ambas as cerâmicas estudadas, tanto em amostras livres de metal quanto metalocerâmicas; que a alteração total de cor, após armazenamento em fluorfosfato acidulado, todos os grupos revelaram valores inaceitáveis clinicamente (ΔE > 3,3) / The purpose of this study was to evaluate the influence of accelerated artificial aging and of 1.23% acidulated phosphate fluoride over superficial roughness and color stability of two low-fusing dental ceramics for titanium (Triceram- Dentaurum, and Noritake Ti22- Noritake), metal-free or metalceramics using commercially pure titanium (Tritan- Dentaurum). 80 cylindrical samples, with 15mm of diameter and 2.5mm of thickness, being 40 for each ceramic, 20 metal free and 20 metal-ceramics, which were divided into two groups of 10 samples, being submitted to the accelerated artificial aging (System Accelerated of Aging for not-metallic C-UV - Comexim Raw materials Ltda, São Paulo, Brazil) or storage in 1.23% acidulated phosphate fluoride. Superficial roughness was accomplished by roughness tester SJ - 201P (Mitutoyo, Tokyo, Japan) in two moments: initial measured after obtained the samples and final superficial roughness after the accelerated artificial aging or storage in 1.23% acidulated phosphate fluoride. Color changes were analyzed by a spectrophotometer PCB 6807 BYK GARDNER (Columbia, United States). The average results and standard deviations for the metal free over accelerated artificial aging were: a) superficial roughness: Triceram before 0.390 ± 0.097, after 0.431 ± 0.100; Noritake Ti22 before 0.299 ± 0.075, after 0.312 ± 0.076; b) color evaluation: Triceram 0.28 ± 0.14; Noritake Ti22 0.33 ± 0.22; and for samples submitted to the storage in 1.23% acidulated phosphate fluoride were: a) superficial roughness: Triceram before 0.325 ± 0.036, after 2.199 ± 0.889; Noritake Ti22 before 0.317 ± 0.094, after 2.760 ± 0.833; b) Color evaluation: Triceram 5.39 ± 0.61; Noritake Ti22 7.31 ± 0.71. The data were submitted to ANOVA and Duncan statistics analysis to p ≤ .05. The obtained results showed that the accelerated artificial aging simulating ten years of clinical use of the restoration did not affect the superficial roughness of none of the evaluated ceramics, in no group; which only the group of the Triceram with substructure in commercially pure titanium revealed values statistically greater than the rest, revealing that the accelerated artificial aging influenced the color of this group. However, the values of color alteration was smaller than 1, being considered clinically acceptable ; which after the storage in 1.23% acidulated phosphate fluoride was observed increased values of superficial roughness with significant difference between both studied ceramics, as in metal-free samples as in metal-ceramics; which the color alteration, after storage in 1.23% acidulated phosphate fluoride, revealed to all the groups evaluated unacceptable values clinically (ΔE > 3.3).
|
10 |
Avaliação da influência do envelhecimento artificial acelerado e armazenamento em fluorfosfato acidulado a 1,23% na rugosidade superficial e na alteração de cor de cerâmicas odontológicas de ultra-baixa fusão para titânio comercialmente pur / Evaluation of the influence of the accelerated artificial aging and storage in 1.23% acidulated phosphate fluoride over superficial roughness and color stability of two low-fusing dental ceramics to commercially pure titaniumOliveira, Janisse Martinelli Borges de 20 December 2007 (has links)
O objetivo do trabalho foi avaliar a influência do envelhecimento artificial acelerado e do fluorfosfato acidulado a 1,23% sobre a rugosidade superficial e alteração de cor de duas cerâmicas odontológicas de ultra-baixa fusão para titânio (Triceram- Dentaurum, e Noritake Ti22- Noritake), livre de metal ou com subestrutura em titânio comercialmente puro (Tritan- Dentaurum). A partir de uma matriz cilíndrica em teflon foram confeccionados, ao todo, 80 corpos-de-prova, com 15mm de diâmetro e 2,5mm de espessura, sendo 40 para cada cerâmica, 20 amostras livre de metal e 20 metalocerâmicas, que foram divididas em dois grupos de 10 amostras cada, sendo submetidas ao envelhecimento artificial acelerado (Sistema Acelerado de Envelhecimento para não-metálicos C-UV - Comexim Matérias Primas Ltda, São Paulo, Brasil) ou ao armazenamento em fluorfosfato acidulado a 1,23%. A rugosidade superficial foi realizada em rugosímetro SJ - 201P (Mitutoyo, Tokyo, Japão) em dois momentos: inicial (R1) foi aquela mensurada logo após obtidos os corpos-de-prova e a rugosidade superficial final (R2) aquela obtida após o envelhecimento artificial acelerado ou armazenamento em fluorfosfato acidulado a 1,23%. Para verificar as alterações de cor ocorridas nas cerâmicas odontológicas utilizou-se o Espectrofotômetro PCB 6807 BYK GARDNER (Columbia, Estados Unidos). Foram feitas leituras antes e após as etapas de envelhecimento artificial acelerado e armazenamento em fluorfosfato acidulado a 1,23%. Os resultados médios e desvios padrão para os corpos-de-prova livre de metal com envelhecimento artificial acelerado foram: a) rugosidade superficial: Triceram antes 0,390 ± 0,097, após 0,431 ± 0,100; Noritake Ti 22 antes 0,299 ± 0,075, após 0,312 ± 0,076; b) alteração de cor: Triceram 0,28 ± 0,14; Noritake Ti 22 0,33 ± 0,22; e para os corpos-de-prova submetidos ao armazenamento em fluorfosfato acidulado a 1,23% foram: a) rugosidade superficial: Triceram antes 0,325 ± 0,036 , após 2,199 ± 0,889; Noritake Ti 22 antes 0,317 ± 0,094, após 2,760 ± 0,833; b) alteração de cor: Triceram 5,39 ± 1,61; Noritake Ti 22 7,31 ± 0,71. Para as amostras metalocerâmicas com envelhecimento artificial acelerado foram: a) rugosidade superficial: Triceram antes 0,282 ± 0,06, após 0,315 ± 0,095; Noritake Ti 22 antes 0,269 ± 0,062, após 0,290 ± 0,075; b) alteração de cor: Triceram 0,57 ± 0,11; Noritake Ti 22 0,41 ± 0,08; e para os corpos-de-prova submetidos ao armazenamento em fluorfosfato acidulado a 1,23% foram: a) rugosidade superficial: Triceram antes 0,137 ± 0,026, após 2,560 ± 0,377; Noritake Ti 22 antes 0,125 ± 0,34, após 3,174 ± 0,565; b) alteração de cor: Triceram 7,56 ± 1,21; Noritake Ti 22 7,69 ± 1,26. Os resultados obtidos mostraram que o envelhecimento artificial acelerado simulando dez anos de uso clínico da restauração não afetou a rugosidade superficial de nenhuma das cerâmicas avaliadas, em nenhum grupo; que apenas o grupo da cerâmica Triceram com subestrutura em titânio comercialmente puro revelou valores de ΔE estatisticamente maiores que os demais, revelando que o envelhecimento artificial acelerado influenciou a coloração desse grupo. Entretanto, a alteração de cor apresentou-se menor que um, sendo considerada clinicamente indetectável; que após o armazenamento em fluorfosfato acidulado foi observado aumento de rugosidade superficial semelhante estatisticamente para ambas as cerâmicas estudadas, tanto em amostras livres de metal quanto metalocerâmicas; que a alteração total de cor, após armazenamento em fluorfosfato acidulado, todos os grupos revelaram valores inaceitáveis clinicamente (ΔE > 3,3) / The purpose of this study was to evaluate the influence of accelerated artificial aging and of 1.23% acidulated phosphate fluoride over superficial roughness and color stability of two low-fusing dental ceramics for titanium (Triceram- Dentaurum, and Noritake Ti22- Noritake), metal-free or metalceramics using commercially pure titanium (Tritan- Dentaurum). 80 cylindrical samples, with 15mm of diameter and 2.5mm of thickness, being 40 for each ceramic, 20 metal free and 20 metal-ceramics, which were divided into two groups of 10 samples, being submitted to the accelerated artificial aging (System Accelerated of Aging for not-metallic C-UV - Comexim Raw materials Ltda, São Paulo, Brazil) or storage in 1.23% acidulated phosphate fluoride. Superficial roughness was accomplished by roughness tester SJ - 201P (Mitutoyo, Tokyo, Japan) in two moments: initial measured after obtained the samples and final superficial roughness after the accelerated artificial aging or storage in 1.23% acidulated phosphate fluoride. Color changes were analyzed by a spectrophotometer PCB 6807 BYK GARDNER (Columbia, United States). The average results and standard deviations for the metal free over accelerated artificial aging were: a) superficial roughness: Triceram before 0.390 ± 0.097, after 0.431 ± 0.100; Noritake Ti22 before 0.299 ± 0.075, after 0.312 ± 0.076; b) color evaluation: Triceram 0.28 ± 0.14; Noritake Ti22 0.33 ± 0.22; and for samples submitted to the storage in 1.23% acidulated phosphate fluoride were: a) superficial roughness: Triceram before 0.325 ± 0.036, after 2.199 ± 0.889; Noritake Ti22 before 0.317 ± 0.094, after 2.760 ± 0.833; b) Color evaluation: Triceram 5.39 ± 0.61; Noritake Ti22 7.31 ± 0.71. The data were submitted to ANOVA and Duncan statistics analysis to p ≤ .05. The obtained results showed that the accelerated artificial aging simulating ten years of clinical use of the restoration did not affect the superficial roughness of none of the evaluated ceramics, in no group; which only the group of the Triceram with substructure in commercially pure titanium revealed values statistically greater than the rest, revealing that the accelerated artificial aging influenced the color of this group. However, the values of color alteration was smaller than 1, being considered clinically acceptable ; which after the storage in 1.23% acidulated phosphate fluoride was observed increased values of superficial roughness with significant difference between both studied ceramics, as in metal-free samples as in metal-ceramics; which the color alteration, after storage in 1.23% acidulated phosphate fluoride, revealed to all the groups evaluated unacceptable values clinically (ΔE > 3.3).
|