Made available in DSpace on 2014-06-12T23:16:46Z (GMT). No. of bitstreams: 2 arquivo9061_1.pdf: 1262061 bytes, checksum: 0bfd347b9846f529fcaa1f09fbfd75f9 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2005 / Com objetivo de determinar as características de atenuação do minério sulfato de bário (BaSO4) e do vidro cristal utilizados como blindagem contra as radiações ionizantes X e gama, em instalações radiográficas, foi realizado um estudo de atenuação com argamassa e concreto de barita, usados, respectivamente, no revestimento de paredes e em blocos; e com o vidro cristal usado em biombos e janelas. Para isso, foram analisadas 10 placas de argamassa de barita, 3 placas de concreto de barita, com área média útil de 900 cm2 e espessura média de 1 a 5 cm, e 3 placas de vidro cristal, com área útil de 323 cm2, com espessuras de 1, 2 e 4 cm. As amostras foram irradiadas com raios-X, com potenciais de 60, 80,110 e 150 quilovolts, e raios gama do 60Co. As respostas de atenuação (mGy/mAmin) e (mGy/h) ambos a 1 metro, em função da espessura, resultaram na obtenção das curvas de atenuação e de transmissão. Além disso, foram determinadas as espessuras equivalentes das camadas semi e deciredutoras, tanto para o vidro cristal, como para a argamassa e o concreto de barita

Orientador: Frab Norberto Boscolo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-14T02:20:12Z (GMT). No. of bitstreams: 1 Souza_JoaoGeraldoMartinsde_M.pdf: 1939298 bytes, checksum: db33f1f8c25e3f28983e120355828c46 (MD5) Previous issue date: 1992 / Resumo: O presente estudo teve o propósito de determinar a proporção ideal do mineral barita em argamassa de revestimento. E a espessura necessária e equivalente à espessura de chumbo para barrar ou absorver raios-X de aproximadamente 30keV de energia efetiva, para blindagens em clinicas de radiologia odontológica. Foram confeccionados blocos de argamassa baritada com 150x150mm e espessuras de 1.4 a 15.1mm. Foi utilizado como fonte de radiação um a aparelho GE 100 modelo A0061. Os feixes incidentes e emergentes de radiação, foram medidos por meio de dosimetros termoluminescentes de Fluoreto de Litio 700, e por câmara de ionização e eletrometro Victoreen modelos 600-4 e 600 respectivamente, e ainda foi feito um cálculo teórico a partir dos elementos componentes da argamassa, para uma comparação com os resultados nos testes. Os resultados evidenciaram que a barita, numa proporção de 60%, em relação aos demais componentes da argamassa estudada, para raios-X de aproximadamente 30keV de energia efetiva (93.7 kVp), foi obtido por meio de um fator de conversão de 5.6 da espessura da argamassa para espessura necessária de chumbo. A camada semi-redutora (HVL) da argamassa baritada foi de 1.24mm e a camada semi-redutora (HVL) do chumbo foi de O.22mm. Assim sendo, para cada milímetro de chumbo seria necessário 5.6mm da argamassa de revestimento para uma proteção eficiente / Abstract: The present paper has the aim of determine the ideal portion of baryte mineral in plaster and the necessary equivalent thickness of plumbum to absorb or stop x-rays in nearly 30keV effective energy, in isolating odontological clinics. Baryte plaster boards were made at 150x150mm and from 1.4 to 15.1mm of thick. As a radiation source, a GE 100, model A0061 device was used. The incidental and emergent radiadion beams were measured with Lithium Fluoride 700 dosimeter and ionization chamber and Victoreen electrometer models 600-4 and 600 respectively. A theo cal calculus was also done from the plaster compound elements for a testing result comparison. The results highlighted that baryte in 60% portion related to the other studied plaster compounds for x-rays nearly 30keV effective energy (93.7kVp) was obtained through a convertion factor of 5.6 in the plaster thickness for the plumbum necessary thickness. The baryte plaster half-value-layer (HVL) was 1.24mm and the plumbum half-value-layer was 0.22mm. Hence, for each plumbum milimeter it would be necessary 5.6mm of plaster for an efficient protection / Mestrado / Radiologia / Mestre em Odontologia

Made available in DSpace on 2014-12-17T14:07:02Z (GMT). No. of bitstreams: 1 PriscyllaCAGpdf.pdf: 2221940 bytes, checksum: 25a80df63d59147dc3816d52fcd0e65b (MD5) Previous issue date: 2009-08-21 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / This work main objective is to study the use of bricks in barium X-rays rooms in order to contribute to the optimization of shielding rooms diagnosis. The work was based on experimental measurements of X-ray attenuation (40 to 150 kV), using ceramic seal bearing the incorporation of barium sulfat (BaSO4). Different formulations were studied in three different firing temperatures and evaluated for incorporation in the ceramic body. The composition of 20% of barite processed at a temperature of 950 ? C showed better physical and mechanical properties, is considered the most suitable for the purpose of this work. Were produced bricks sealing composition formulated based on that presented the best technological features. These blocks were tested physically as a building material and wall protective barrier. Properties such as visual, deviation from the square, face flatness, water absorption and compressive strength were evaluated for all the blocks produced. The behavior of this material as attenuator for X-rays was investigated by experimental results which take into account mortar manufacturers barium through the different strains and compared with the reference material (Pb). The simulation results indicated that the ceramic block barium shows excellent properties of attenuation equivalence lead taking into account the energy used in diagnostic X-ray / Este trabalho tem por finalidade principal estudar a utiliza??o de blocos cer?micos baritados em salas de radia??o X, visando contribuir para a otimiza??o da blindagem de salas de diagn?stico. O trabalho foi baseado em medidas experimentais de atenua??o da radia??o X (40 a 150 kV), empregando material cer?mico de veda??o contendo a incorpora??o de sulfato de b?rio (BaSO4). Diferentes formula??es foram estudadas em tr?s temperaturas de queima diferentes e avaliadas as incorpora??es na massa cer?mica. A composi??o de 20% de barita processada a temperatura de 950?C, apresentou melhores propriedades f?sicas e mec?nicas, sendo considerada a mais adequada para a proposta deste trabalho. Foram produzidos blocos cer?micos de veda??o baseados na composi??o formulada que apresentou melhores caracter?sticas tecnol?gicas. Estes blocos foram testados fisicamente como material construtivo de parede e barreira protetora. Propriedades como caracter?sticas visuais, desvio com rela??o ao esquadro, planeza das faces, absor??o de ?gua e resist?ncia ? compress?o foram avaliadas para todos os blocos produzidos. O comportamento deste material como atenuador para a radia??o X foi investigado por meio de resultados experimentais que levaram em considera??o fabricantes de argamassas baritadas atrav?s das diferentes tens?es e comparado com o material de refer?ncia (Pb). Os resultados obtidos nas simula??es indicaram que o bloco cer?mico baritado demonstra ?timas propriedades de atenua??o em equival?ncia ao chumbo levando-se em conta as energias usadas em raios X diagn?stico

Made available in DSpace on 2016-03-15T19:36:37Z (GMT). No. of bitstreams: 1 Jademir Jesus Pirapora de Almeida.pdf: 6328511 bytes, checksum: a6b516ba7f4098781189faf6cc895d92 (MD5) Previous issue date: 2012-03-30 / Universidade Presbiteriana Mackenzie / In this work were studied the action of ionizing radiation on the physical-mechanical properties in elastomeric compounds based on styrene-butadiene rubber (SBR) filled with barite, opening way for application of these composites in the protection and shield against high-energy radiation, in the form of aprons. These aprons come to substitute the elastomeric ones with lead filler in ergonomic and economically advantageous conditions. The effect of high-energy radiation was studied on SBR compounds filled with barite at 50, 75, 100, 125, and 150phr (phr = parts per hundred rubber) of barite concentrations, exposed to ionizing radiation at 0, 100, 200, 500 and 1000kGy doses. The samples were characterized by physic-mechanical tests as rheometry, tensile strength, resilience, hardness, wear resistance, oil absorption, permanent deformation under compression (compression set) and dynamic mechanical thermal analysis. The morphological characteristics were determined by scanning electron microscopy. The results showed that the radiation causes an increase in tensile strength and elongation, the tear strength and hardness, and a decrease in fluid absorção and deformation under compression. / Neste trabalho foi estudada a ação da radiação ionizante nas propriedades físico-mecânicas nos compostos elastoméricos a base de estireno-butadieno (SBR) carregados com barita, abrindo caminho para aplicação destes compostos na proteção e blindagem contra a radiação alta energia, na forma de aventais, vindo substituir os aventais a base de elastômero carregado com chumbo em condições ergonômicas e economicamente vantajosas. Foi estudado o efeito da radiação ionizante em compostos a base de SBR carregado com barita nas concentrações de 50, 75, 100, 125, e 150phr (phr = partes por cem de borracha) de barita expostos à radiação ionizante nas doses de 0, 100, 200, 500 e 1000kGy. As amostras foram caracterizadas por meio de ensaios físico-mecânicos de reometria, de resistência à tração, resiliência, dureza, resistência ao rasgo, absorção de óleo, deformação permanente sob compressão (compression set) e ensaios de análise térmica dinâmico-mecânica. As características morfológicas dos compositos foram determinadas por meio de microscopia eletrônica de varredura. Os resultados mostraram que a radiação provoca um aumento da resistência à tração, do alongamento sob tração, da resistência ao rasgamento e da dureza; e um decréscimo na absorção de fluido e na deformação sob compressão.

Made available in DSpace on 2016-04-18T21:35:57Z (GMT). No. of bitstreams: 2 Graziella Ferecini Bueno Amaral1.pdf: 4073691 bytes, checksum: 8ff4dce433de3d6c54c6320e248c3e74 (MD5) Graziella Ferecini Bueno Amaral2.pdf: 2731324 bytes, checksum: 8a0dac7da8171451384cd27ab251102c (MD5) Previous issue date: 2011-03-17 / Fundo Mackenzie de Pesquisa / In this study it was studied the physical-mechanical properties of elastomers based on styrenebutadiene rubber (SBR) with the addition of barite, for application of these compounds in protecting in the shielding against radiation X, for the substitution of aprons form based on elastomer fillered with lead in ergonomic and economically advantageous conditions. Elastomeric compounds were studied with different barite concentrations [50, 75, 100, 125 and 150 phr (parts for hundred of rubber)]. The studied properties were: tensile strength, tensile modulus, tear strength, permanent deformation in compression, hardness, absorption of fluid, resilience, measure of rheology, morphological analysis and characterization of attenuating materials to radiation X. Results showed that all compositions exhibit good dispersion of the filler in the matrix. It was observed that with the increase barite concentration there is an increase in hardness beyond not causing significant alteration in the tensile strenght, in the elasticity, as well as in the resistance to the tearing of the material. / Neste trabalho foram estudadas as propriedades físico-mecânicas de elastômeros a base de borracha de estireno-butadieno (SBR) com a adição de barita, para aplicação destes compostos na proteção de blindagem contra a radiação X, para a substituição de aventais a base de elastômeros carregados com chumbo em condições ergonômicas e economicamente vantajosas. Foram estudados compostos elastoméricos com diferentes concentrações de barita [50, 75, 100, 125 e 150 phr (partes por cem de borracha)]. Entre as propriedades estudadas destacam-se: resistência à tração, módulo sob tração, resistência ao rasgo, deformação permanente à compressão, dureza, absorção de fluido, resiliência, medida de reologia, análise morfológica e caracterização de materiais atenuadores à radiação X. Os resultados mostraram que todas as composições apresentam uma boa dispersão da carga na matriz. Observou-se que com o aumento da concentração de barita há um aumento na dureza além de não causar alteração significativa na resistência à tração, na elasticidade, bem como na resistência ao rasgamento do material.

Made available in DSpace on 2016-03-15T19:36:30Z (GMT). No. of bitstreams: 1 Jessica Rodrigues Camara.pdf: 4063408 bytes, checksum: d160fbb4a019fe268fcee175023d69fd (MD5) Previous issue date: 2011-03-18 / In this work, it was studied the physical-mechanical properties of elastomers based on ethylene-propylene-diene monomer copolymer (EPDM) with barite addition, witch is a filler in powder form, opening way for application of these composites in the protection and shield against X radiation, in the form of aprons. These aprons come to substitute the elastomeric ones with lead filler in ergonomic and economically advantageous conditions. Elastomeric composites with different barite concentrations were studied: 50, 75, 100, 125 and 150phr (parts per hundred of ruber). Among the studied properties are distinguished: tensile strength, module strength, tear strength, compression set, hardness, fluid absorption, morphologic analysis, X-ray attenuation and equivalent thickness of attenuation in Pb. The results showed that all the compositions present a good dispersion of the filler in the matrix. It was observed that the increase of the barite concentration provokes an increase in the X-ray attenuation, equivalent thickness of attenuation in Pb, hardness, tensile strength, elasticity module, tear strength and in the compression set of composites, as well as a decrease in the oil absorption. / Neste trabalho estudou-se as propriedades dos elastômeros a base do copolímero de etilenopropileno-dieno monômero (EPDM) com a adição de barita, que é uma carga em pó, abrindo caminho para aplicação destes compostos na proteção e blindagem contra a radiação X, na forma de aventais, em substituição dos aventais a base de elastômero carregado com chumbo em condições. Foram estudados compostos elastoméricos com diferentes concentrações de barita: 50, 75, 100, 125 e 150phr (partes por 100 partes de borracha). Entre as propriedades estudadas destacam-se: resistência à tração, módulo sob tração, resistência ao rasgo, deformação permanente à compressão, dureza, absorção de fluído, análise morfológica, atenuação de raios X e espessura equivalente de atenuação em Pb. Os resultados mostraram que todas as composições apresentam uma boa dispersão da carga na matriz. Observou-se que com o aumento da concentração de barita há um aumento na atenuação de raios X, na espessura equivalente de atenuação em Pb, na dureza, na resistência à tração, no módulo de elasticidade, na resistência ao rasgo, na deformação permanente sob compressão dos compostos, bem como um decréscimo na absorção de óleo.