No description available.

Impact damage resistance is an essential requirement of lightweight structural components for high-performance applications. The aim of this thesis is to study the impact damage and perforation behaviour of lightweight materials including thin aluminium alloy plates and carbon fibre reinforced epoxy composites. The focus of this investigation is on the stress state and strain rate dependence of failure, and the effect of microstructural modifications on indentation and impact response. The thesis is divided into three parts. In the first part (Chapter 2) the impact response of thin monolithic ductile aluminium alloy plates is investigated. Impact perforation experiments are performed using different projectile nose shapes to span a wide range of stress states at the onset of ductile fracture. Impact perforation behaviour, ballistic limit velocity, energy absorption capability and sensitivity to projectile tip geometry are evaluated. Modes of deformation and failure during impact are assessed experimentally. It is shown that modelling the stress state and strain rate dependence of plasticity and failure is crucial to accurately predict ductile fracture initiation in thin metal plates. In the second part (Chapters 3 and 4), the stress state and strain rate dependent yield and failure behaviour of epoxy resin is investigated. An iterative numerical-experimental approach is shown to be essential to develop a material model capable of predicting the failure behaviour of epoxy for a wide range of stress triaxialities across different regimes of failure. The influence of microstructural modifications in epoxy, through two different toughening strategies, on its failure behaviour is investigated. The effect of increasing the applied strain rate on the stress state dependent response of epoxy is investigated to provide an insight into the impact damage resistance of carbon fibre reinforced epoxy composites. In the third part (Chapter 5), experimental studies are conducted on the quasi-static indentation and impact perforation response of plain weave carbon fibre reinforced epoxy composites to investigate the effect of toughening the epoxy matrix to improve resistance to indentation and impact. The nose shape sensitivity of failure initiation in carbon/epoxy composite targets is assessed by considering indenters with different tip geometries. Conclusions and suggestions for future work are presented in Chapter 6.

Fibre Reinforced Polymer Composites are extensively used in aircraft structures because of its high specific stiffness, high specific strength and tailorability. Though Fibre Reinforced Polymers offer many advantages, they are not free from problems. The damage of different nature, e.g., service mechanical damages, fatigue damage or environmental damage can be observed during operating conditions. Among all the damages, manufacturing or service induced, delamination related damage is the most important failure mechanisms of aircraft-composite structures and can be detrimental for safety. Delamination growth under fatigue loading may take place due to local buckling, growth from free edges and notches such as holes, growth from ply-drops and impact damaged composites containing considerable delamination. Delamination growth can also occur due to interlaminar stresses, which can arise in complex structures due to unanticipated loading. The complex nature of composite failure, involving different failure modes and their interactions, makes it necessary to characterize/identify the relevant parameters for fatigue damage resistance, accumulation and life prediction. An effort has been made in this thesis to understand the fatigue behavior of carbon fibre reinforced epoxy laminates under aircraft wing service loading conditions. The study was made on laminates with different lay-up sequences (quasi-isotropic and fibre dominated) and different geometries (plain specimen, specimen with a hole and ply-drop specimen). The fatigue behaviour of the composite was analyzed by following methods: . Ultrasonic C-Scan was used to characterize the delamination growth. . Dynamic Mechanical Analysis (DMA) was done to study the interfacial degradation due to fatigue loading. In this analysis, the interfacial strength indicator and interfacial damping were calculated. The DMA also provides the storage modulus degradation under fatigue loading. . Scanning electron microscope examination was carried out to understand the fatigue damage mechanisms. . A semi-empirical phenomenological model was also used to estimate the residual fatigue life. This research work reveals that the Carbon Fibre Reinforced Polymer laminates are in the safe limit under service loading conditions, except the specimen with a hole. The specimen with a hole showed delaminations around the hole due to stress concentration and higher interlaminar stresses at the hole edges and this delamination is found to be associated with fibre breakage and fibre pullout. The quasi-isotropic laminate is found to show poorer fatigue behaviour when compared to fibre dominated laminate and ply-drop also shows poor performance due to high stress concentration in the ply-drop region.

Carbon fibre reinforced composites are known for their high specific strength-to-weight ratio and are of great interest to the aerospace industry. Incorporating these materials into the fuselage, like in Boeing's 787 "Dreamliner", offers considerable weight reduction which increases flying efficiency, and reduces the cost of flying. In flight, aircraft are often subject to lightning strikes which, in the case of composites, can result in localized melting given the high resistive nature of the material. Aerospace carbon fibre composites often incorporate a metallic mesh or foil within the composite layers to dissipate the electrical charge through the large aircraft. The damage to the aircraft is minimized but not always eliminated. This research aims to elaborate a practical technique to deposit thin layers of conductive material on the surface of aerospace grade composites. Using Cold Gas Dynamic Spray (CGDS), such coatings could be used to repair damaged components. An experimental research approach was used to develop metallic coated composites. Using the CGDS equipment of Centerline (SST-P), specific parameters (such as gas temperature and stagnation pressure) were determined for each type of metallic coating (tin-based & copper-based). The use of bond coats was explored in order to attain the desired coatings. Once optimized, these coatings were evaluated with respect to their corrosive, adhesive, and electrical properties following industry standards.