Made available in DSpace on 2014-08-20T14:30:11Z (GMT). No. of bitstreams: 1 Tese_Francine_Cardozo_ Madruga.pdf: 29010459 bytes, checksum: 5e3b51088eb6a2939cfc07531186e6a7 (MD5) Previous issue date: 2012-05-18 / In this study the effect of the addition of calcium hydroxide Ca(OH)2 on the pHneutralization and physico-chemical properties of experimental self-adhesive resin cements was investigated. The cements were formulated as two pastes: Paste A, containing UDMA, Bis-GMA, TEGDMA, HEMA, GDMA-P and glass particles; Paste B, composed of UDMA, HEMA, water, photoinitiators and glass particles. The formulation variable tested was concentration of Ca(OH)2, added to paste B at mass fractions of 0% (control), 0.25%, 0.5%, 1%, 2%, and 4%. Equal volumes of pastes A and B were mixed for the analyses, which started by immersion of cement specimens in distilled water and follow up of the pH of the eluate for 24 h. The additional analyses consisted in measurement of degree of C=C conversion by infrared spectroscopy, film thickness, flexural strength, elastic modulus and work-of-fracturei n 3-point bending mode, Knoop hardness, depth of cure, water sorption and solubility after immersion in water for 7 days, and dentin bond strength by shear testing. Statistical comparisons between groups were carried out at a 5% significance level. All Ca(OH)2 concentrations above 0.25% caused pH increase of the eluate at 24 h, although the only concentrations of the compound leading to pH-neutralization were 2% and 4%. Compared with the control cement, the addition of 4% Ca(OH)2 decreased the flexural strength, flexural modulus, work-of-fracture, degree of C=C conversion, and dentin bond strength. In contrast, the physico-chemical properties of the material with 2% Ca(OH)2 were similar to the control material, except for a discreet reduction in mechanical strength and the lower film thickness of the material containing Ca(OH)2. Hardness, depth of cure, and water sorption were not affected by incorporation of Ca(OH)2. The material with 4% Ca(OH)2 had lower solubility and film thickness than the other cements. In conclusion, judicious incorporation of Ca(OH)2 might lead no pH-neutralization of self-adhesive resin cements without negatively interfering with other physico-chemical properties of the material. / Neste estudo investigou-se o efeito da adição de hidróxido de cálcio Ca(OH)2 na neutralização do pH e propriedades físico-químicas de cimentos resinosos autoadesivos experimentais. Os cimentos foram formulados em duas pastas: Pasta A, contendo UDMA, Bis-GMA, TEGDMA, HEMA, GDMA-P e partículas de vidro; Pasta B: composta por UDMA, HEMA, água, fotoiniciadores e partículas de vidro. A variável de formulação testada foi a concentração de Ca(OH)2, adicionado à pasta B nas frações em massa de 0% (controle), 0,25%, 0,5%, 1%, 2% e 4%. Volumes iguais de pasta A e B foram misturados para as análises, que iniciaram pela imersão em água destilada de espécimes de cimento e acompanhamento do pH do eluato por 24 h. As demais análises consistiram em mensuração do grau de conversão de C=C por meio de espectroscopia no infravermelho, espessura de película, resistência à flexão, módulo de elasticidade e trabalho de fratura por meio de teste de flexão por 3 pontos, dureza Knoop, profundidade de polimerização, sorção e solubilidade após imersão em água por 7 dias, e resistência de união à dentina por meio de teste de cisalhamento. Comparações estatísticas estre os grupos foram realizadas em nível de significância de 5%. Todas as concentrações de Ca(OH)2 acima de 0,25% ocasionaram aumento do pH do eluato em 24 h, porém as únicas concentrações do composto que levaram à neutralização do pH foram 2% e 4%. Comparado com o cimento controle, a adição de 4% de Ca(OH)2 reduziu a resistência à flexão, módulo de flexão, trabalho de fratura, grau de conversão de C=C e resistência de união à dentina. Por outro lado, as propriedades físicoquímicas do material contendo 2% de Ca(OH)2 foram similar ao material controle, exceto por discreta redução de propriedades mecânicas e pela menor espessura de película do material contendo Ca(OH)2. Dureza, profundidade de polimerização e sorção de água não foram afetadas pela incorporação de Ca(OH)2. O material com 4% de Ca(OH)2 apresentou menor solubilidade e espessura de película que os demais cimentos. Em conclusão, a incorporação criteriosa de Ca(OH)2 pode levar à neutralização do pH de cimentos resinosos autoadesivos sem interferir de forma negativa em outras propriedades físico-químicas dos materiais.

The purpose of this study is to evaluate the effect of different irrigatins on bond strength of fiber posts cemented with RelyX U200. Eighty single-rooted premolars were sectioned at 14 mm from the apex, prepared with ProTaper Universal system until F3 instrument, and filled with F3 master cone and AH Plus sealer. Root canal filling was partially removed, remaining 4 mm of guta-percha at the apical third. Specimens were randomly divided into 8 groups (n=10), according to the irrigant used during root canal preparation and before fiber post cementation (dentin surface treatment), as described: SS: 0,9% saline solution (control group); CHX: 2% chlorhexidine; 1%NaOCl: 1% sodium hypochlorite; 2,5%NaOCl: 2,5% sodium hypochlorite; 5%NaOCl: 5% sodium hypochlorite; 1%CaOCl: 1% calcium hypochlorite; 2,5%CaOCl: 2,5% calcium hypochlorite; e 5%CaOCl: 5% calcium hypochlorite. For each group, irrigation was performed continuously with 2ml. Exacto N2 glass fiber posts were cemented with RelyX U200. The specimens were sectioned providing 3 slices, one for each root third and the push-out test was performed. Optical microscopy was used to analyze the failure mode. Bond strength means were calculated and ANOVA and Bonferroni tests were used for statistical analysis. SS showed higher mean of bond strength values (11.47MPa), than all NaOCl and CaOCl groups, which showed similar values to CHX (7.56Mpa ± 2:47). Adhesive failures at cement/dentin interface were predominant (58.33%). NaOCl and CaOCl negatively affect the bond strength of fiber posts to root dentine when cemented with sef-adhesive resin cement; however the concentration of NaOCl and CaOCl did not affect this outcome. / Este estudo tem como objetivo avaliar o efeito de diferentes soluções irrigadoras sobre a resistência adesiva de pinos de fibra de vidro, cimentados com cimento autoadesivo RelyX U200. Foram utilizados 80 pré-molares inferiores humanos tiveram a coroa seccionada, padronizando-se o comprimento da raiz em 14 mm. Os condutos foram instrumentados com o sistema rotatório ProTaper até o instrumento F3, obturados com cimento endodôntico AH Plus e cones de guta-percha F3 do mesmo sistema, pela técnica do cone único. Os condutos foram desobturados até 10mm de profundidade, mantendo-se os 4mm apicais da obturação. As raízes foram aleatoriamente distribuídas em 8 grupos (n=10), de acordo com a solução irrigadora utilizada previamente à cimentação dos pinos: SS: solução salina 0,9% (grupo controle); CHX: clorexidina 2%; 1%NaOCl: hipoclorito de sódio 1%; 2,5%NaOCl: hipoclorito de sódio 2,5%; 5%NaOCl: hipoclorito de sódio 5%; 1%CaOCl: hipoclorito de cálcio 1%; 2,5%CaOCl: hipoclorito de cálcio 2,5%; e 5%CaOCl: hipoclorito de cálcio 5%. Para cada espécime, a irrigação foi realizada com 2ml da solução a cada troca de instrumento. Os pinos de fibra de vidro do Sistema Exacto Translúcido n02 foram silanizados e cimentados com o cimento resinoso autoadesivo RelyX U200. As raízes foram seccionadas na máquina de corte, de forma a obter 3 slices por espécime, sendo 1 slice para cada terço radicular. A seguir, os corpos de prova foram submetidos ao teste de push-out na máquina de ensaio universal EMIC. Para análise do padrão de falha, os espécimes foram analisados com microscopia óptica. A média de resistência adesiva de cada espécime foi calculada. Testes ANOVA e Bonferroni foram utilizados para analisar as diferenças entre os grupos. O grupo SS demonstrou a maior média de resistência adesiva, sendo superior aos grupos NaOCl e CaOCl (P <0.05), nos quais apresentaram valores semelhantes ao grupo CHX (7.56Mpa ± 2.47). As falhas adesivas cimento/dentina foram predominantes (58.33%). Concluímos que SS parece ser a solução mais adequada para limpeza do canal radicular previamente à cimentação de pinos de fibra cimentados com cimento autoadesivo RelyX U200. NaOCl e CaOCl diminuíram os valores de resistência adesiva dos pinos de fibra à dentina radicular e suas diferentes concentrações não afetaram este resultado.