Abstract  Aim: To determine the shear bond strength of two commercially available self-adhesive resin cements on four different materials and to analyse the degree of conversion (DC) of those resin cements.  Materials and Methods: A total of 45 embedded specimens made of four different materials were prepared for the notched-edge shear bond strength test. Ten specimens each of resin composite, glass-ionomer, zirconia and 15 of human dentine. Pillars of two different self-adhesive resin cements were luted onto these specimens. Five of the dentine specimens were treated with Katana Cleaner before being luted with Panavia. A single sample from each self-adhesive resin cement was used to determine the DC using ATR-FTIR Spectroscopy. The samples were measured uncured, right after being light cured and 10 min thereafter. Results: The highest shear bond strength values were seen for RelyX, irrespective of the material tested. This difference was statistically significant. No statistically significant difference was seen between the dentine specimens pre-treated with Katana Cleaner and luted with Panavia, compared to no pre-treatment. No statistically significant differences were found regarding DC between Panavia and RelyX.  Conclusion: The bond between the dental materials and the tooth structure is extremely important for the longevity of the restoration. The bond strength of RelyX for all materials tested were 2.1 to 37.5 times higher than that for Panavia and the differences were statistically significant. Panavia had virtually no bonding to the dentine in this study which might be due to the treatment of the dentine. The differences regarding the degree of conversion between the two resin cements were not statistically significant. However, the DC 10 min after curing was 1.3 times higher than directly after curing for both resins.

O objetivo deste estudo foi avaliar a dureza de um cimento resinoso dual autoadesivo (RelyX U200) e um cimento resinoso dual convencional (RelyX ARC) fotoativados sob materiais restauradores indiretos, utilizando unidades fotoativadoras com diferentes comprimentos de ondas (LED Elipar Freelight 2, LED Bluephase, Laser AccuCure 3000TM), por meio de teste de nanoendentação. Para a obtenção dos espécimes foram utilizados incisivos bovinos que após profilaxia, foram submetidos a cortes no limite amelo-cementário para a separação da porção coronária. Após inclusão, os espécimes foram submetidos ao desgaste para exposição de dentina e padronização do substrato. Para simular clinicamente restaurações indiretas foram confeccionadas peças em cerâmica IPS e.max® Press (Ivoclar Vivadent) e em resina composta indireta SR Adoro (Ivoclar Vivadent) que foram cimentadas nas superfícies dentinárias. Os espécimes foram seccionados longitudinalmente em baixa velocidade e constante irrigação e polidos em politriz. Foi estabelecido um grupo controle positivo, no qual o cimento foi fotoativado sem a interposição de material restaurador indireto e um grupo controle negativo, no qual, após a cimentação do material restaurador indireto, a fotoativação foi suprimida, ocorrendo apenas a polimerização química do cimento. Todos os espécimes foram armazenados em água destilada a 37°C durante 7 dias e após esse período, foram submetidos ao teste de nanoendentação na linha de cimentação, com o auxílo do ultra-microdurômetro (Shimadzu Dynamic Ultra Micro Hardness Tester). O ciclo aplicado foi de 100mN. Foram realizadas cinco nanoendentações em cada espécime, cujas médias resultaram nos valores de cada superfície. Os resultados obtidos foram submetidos à Análise de Variância e Teste de Tukey (p<0,05). Podese concluir que o cimento RelyX ARC apresentou maiores valores de dureza do que o RelyX U200 e este foi mais dependente da fotoativação para alcançar uma polimerização adequada. A dureza dos cimentos resinosos avaliados foi influenciada negativamente pela interposição do material restaurador indireto e apenas os LEDs foram capazes de manter o mesmo grau de polimerização dos cimentos quando interposto um material restaurador indireto. / This study aimed to evaluate the hardness of a dual cure self-adhesive resin cement (RelyX U200) and a dual cure conventional resin cement (RelyX ARC) light curing units with different wavelengths (Elipar Freelight 2 LED, Bluephase LED, AccuCure 3000TM Laser) through nanoindentadion test. To obtain the specimens bovine incisors were used after prophylaxis. The tooth were sectioned at the limit amelocement for the separation of the coronal portion. After inclusion, the dentin surface of the specimens were exposed to standardize the substrate. To clinically simulate indirect restorations ceramic pieces were made (IPS e.max® Press/Ivoclar Vivadent) and indirect composite resin (SR Adoro/Ivoclar Vivadent) were cemented on dentin surfaces. The specimens were sectioned longitudinally at low speed with constant irrigation and polished. A positive control group was stablished, in which the cement was light cured without the interposition of indirect restorative material, and a negative control group, in which, after cementation of the indirect restorative material, the light curing was removed, occurring only the chemical polymerization of the cement. All specimens were stored in distilled water at 37°C for 7 days. Nanoindentadion hardness of the cement layer was measured under 100mN load (Shimadzu Dynamic Ultra Micro Hardness Tester). Five nanoindentations in each specimen were obtained, which resulted in the average values of each surface. Data were statistically analyzed using ANOVA and Tukey test (p<0,05). RelyX ARC pesented higher values of hardness than RelyX U200 and this was more dependent on the polymerization. The hardness of the evaluated resin cements was negatively influenced by the interposition of an indirect restorative material and only the LEDs were able to maintain the same degree of polymerization of the cement when an indirect restorative material was used.

Este estudo objetivou analisar o grau de conversão (GC) e a microdureza de um cimento resinoso utilizando diferentes protocolos de ativação, e, caracterizar o cimento quanto à composição monomérica, diâmetro médio das partículas inorgânicas e porcentagem em peso das frações orgânica e inorgânica. Foram preparados quarenta espécimes (8mm de diâmetro, 0,5mm de espessura), sendo metade usada para a determinação do GC e a outra metade usada no teste de microdureza. Os espécimes foram divididos em quatro grupos: GR1 fotoativação realizada diretamente sobre o cimento por 20s, GR2 fotoativação através de um disco de porcelana com 2mm de espessura por 20s, GR3 fotoativação através de um disco de porcelana com 2mm de espessura por 40s, e GR4 fotoativação foi omitida e o material foi polimerizado exclusivamente por seus componentes químicos. A dureza Vickers (HV) e o GC, determinado através de FTIR-ATR, foram realizados imediatamente após a fotoativação (GR1, GR2 e GR3) ou cinco minutos após o início da polimerização (GR4). Após armazenagem em ambiente seco e escuro por 24h, os espécimes foram novamente submetidos aos testes de HV e GC. Para a caracterização do material avaliado, foram realizadas as análises: Termogravimétrica, Espectrometria no Infravermelho, Espectrometria de Ressonância Magnética Nuclear e Microscopia Eletrônica de Varredura. Os resultados foram analisados estatisticamente por ANOVA, teste t e teste de Bonferroni (P&#8804;0,05). Os valores do GC nos períodos imediato e 24h foram, respectivamente: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. Os valores de HV nos períodos imediato e 24h foram, respectivamente: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. A baixa polimerização para o GR4 não permitiu a determinação da dureza inicial e após 24h este valor foi 10.65HV 0.92. O modo de ativação autopolimerizável influenciou negativamente o GC e a HV em relação ao modo de ativação no qual foi utilizada a fotoativação. A restauração simulada de porcelana não influenciou o GC, porém interferiu negativamente na microdureza. O tempo de fotoativação não influenciou os valores do GC e da HV. O GC e microdureza sofreram um aumento significativo após 24h da polimerização inicial, com exceção do GC no período inicial, quando a fotoativação foi realizada através de um disco de porcelana por um tempo de exposição de 20s. Houve uma correlação linear e positiva entre a HV e o GC para o cimento RelyX&#61668; Unicem. Caracterização química: porção orgânica composta por uma mistura de monômeros, tendo o Bis-GMA como monômero-base. Presença de um monômero dimetacrilato contendo hidroxila para se ligar ao ácido fosfórico sob a forma de fosfato. Partículas inorgânicas variando entre 0,4 a 11,2&#61549;m. A fração sólida do material é composta por 96% de partículas inorgânicas. Na fração líquida, a porção orgânica corresponde a 84%. Restou um resíduo incombustível de 16% devido à queima do material em atmosfera de nitrogênio. / The aim of this study was to evaluate the degree of conversion (DC) and the microhardness of a self-adhesive resin cement under different activation protocols, immediately and after 24 hours of the beginning of the polymerization, and, defining cement regarding monomer composition, average diameter of the inorganic fillers and the percentage by weight of the organic and inorganic portions. Forty specimens (8 mm in diameter, 0.5 mm in height) were prepared. Half of them were used to determine DC and the other half were used on the microhardness test. The specimens were divided into four groups: GR1 direct photoactivation for 20s, GR2 photoactivation through 2mm porcelain disc for 20s, GR3 photoactivation through 2 mm porcelain disc for 40 s, and GR4 photoactivation was omitted and curing was reliant on the chemical reaction only. Vickers microhardness (HV) and DC, by FTIR-ATR, were determined immediately after photoactivation (GR1, GR2 e GR3) or after five minutes from the beginning of the polymerization (GR4). After dry storage in the dark, for 24 hours, the samples were submitted to the tests again. In order to define the studied cement, the Thermogravimetric method was applied, as well as the Infrared Spectometry, Nuclear Magnetic Ressonance Spectroscopy and Scanning Electron Microscope. Data were statistically analyzed by one-way ANOVA, t-Test and Bonferroni Test (P&#8804;0,05) and the degree of conversion values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. HV values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. The low DC for GR4 do not permitted to quantify the initial HV value and after 24 hours this values was 10.65HV 0.92. The chemical curing mode showed DC and HV results for both period (initial and after 24 hours), statistically lower than the other groups where the photoactivation was used. The simulated ceramic restoration did not influence monomer conversion, however it negatively influence resin cement hardness. The exposure time did not influence resin cement hardness and monomer conversion. The inical DC and HV were significantly greater than after 24 hours, except for DC for initial period, when the photoactivation was realizded through a porcelain disc for 20s.There was a linear and positive correlation between degree of conversion and microhadness for the self-adhesive resin cement RelyX&#61668; Unicem. Defining the cement: organic portion composed by a mixture of monomers. Bis-GMA is the main monomer. Presence of a dimethacrylate containing hydroxyl to connect to the phosphoric acid as a phosphate. Inorganic fillers raging between 0,4 to 11,2&#61549;m. Powder is composed by 96% of inorganic particles. In liquid fraction, the organic portion corresponds to 84%. There were 16% of waste that did not burn due to nitrogen atmosphere.

Este estudo objetivou analisar o grau de conversão (GC) e a microdureza de um cimento resinoso utilizando diferentes protocolos de ativação, e, caracterizar o cimento quanto à composição monomérica, diâmetro médio das partículas inorgânicas e porcentagem em peso das frações orgânica e inorgânica. Foram preparados quarenta espécimes (8mm de diâmetro, 0,5mm de espessura), sendo metade usada para a determinação do GC e a outra metade usada no teste de microdureza. Os espécimes foram divididos em quatro grupos: GR1 fotoativação realizada diretamente sobre o cimento por 20s, GR2 fotoativação através de um disco de porcelana com 2mm de espessura por 20s, GR3 fotoativação através de um disco de porcelana com 2mm de espessura por 40s, e GR4 fotoativação foi omitida e o material foi polimerizado exclusivamente por seus componentes químicos. A dureza Vickers (HV) e o GC, determinado através de FTIR-ATR, foram realizados imediatamente após a fotoativação (GR1, GR2 e GR3) ou cinco minutos após o início da polimerização (GR4). Após armazenagem em ambiente seco e escuro por 24h, os espécimes foram novamente submetidos aos testes de HV e GC. Para a caracterização do material avaliado, foram realizadas as análises: Termogravimétrica, Espectrometria no Infravermelho, Espectrometria de Ressonância Magnética Nuclear e Microscopia Eletrônica de Varredura. Os resultados foram analisados estatisticamente por ANOVA, teste t e teste de Bonferroni (P&#8804;0,05). Os valores do GC nos períodos imediato e 24h foram, respectivamente: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. Os valores de HV nos períodos imediato e 24h foram, respectivamente: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. A baixa polimerização para o GR4 não permitiu a determinação da dureza inicial e após 24h este valor foi 10.65HV 0.92. O modo de ativação autopolimerizável influenciou negativamente o GC e a HV em relação ao modo de ativação no qual foi utilizada a fotoativação. A restauração simulada de porcelana não influenciou o GC, porém interferiu negativamente na microdureza. O tempo de fotoativação não influenciou os valores do GC e da HV. O GC e microdureza sofreram um aumento significativo após 24h da polimerização inicial, com exceção do GC no período inicial, quando a fotoativação foi realizada através de um disco de porcelana por um tempo de exposição de 20s. Houve uma correlação linear e positiva entre a HV e o GC para o cimento RelyX&#61668; Unicem. Caracterização química: porção orgânica composta por uma mistura de monômeros, tendo o Bis-GMA como monômero-base. Presença de um monômero dimetacrilato contendo hidroxila para se ligar ao ácido fosfórico sob a forma de fosfato. Partículas inorgânicas variando entre 0,4 a 11,2&#61549;m. A fração sólida do material é composta por 96% de partículas inorgânicas. Na fração líquida, a porção orgânica corresponde a 84%. Restou um resíduo incombustível de 16% devido à queima do material em atmosfera de nitrogênio. / The aim of this study was to evaluate the degree of conversion (DC) and the microhardness of a self-adhesive resin cement under different activation protocols, immediately and after 24 hours of the beginning of the polymerization, and, defining cement regarding monomer composition, average diameter of the inorganic fillers and the percentage by weight of the organic and inorganic portions. Forty specimens (8 mm in diameter, 0.5 mm in height) were prepared. Half of them were used to determine DC and the other half were used on the microhardness test. The specimens were divided into four groups: GR1 direct photoactivation for 20s, GR2 photoactivation through 2mm porcelain disc for 20s, GR3 photoactivation through 2 mm porcelain disc for 40 s, and GR4 photoactivation was omitted and curing was reliant on the chemical reaction only. Vickers microhardness (HV) and DC, by FTIR-ATR, were determined immediately after photoactivation (GR1, GR2 e GR3) or after five minutes from the beginning of the polymerization (GR4). After dry storage in the dark, for 24 hours, the samples were submitted to the tests again. In order to define the studied cement, the Thermogravimetric method was applied, as well as the Infrared Spectometry, Nuclear Magnetic Ressonance Spectroscopy and Scanning Electron Microscope. Data were statistically analyzed by one-way ANOVA, t-Test and Bonferroni Test (P&#8804;0,05) and the degree of conversion values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. HV values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. The low DC for GR4 do not permitted to quantify the initial HV value and after 24 hours this values was 10.65HV 0.92. The chemical curing mode showed DC and HV results for both period (initial and after 24 hours), statistically lower than the other groups where the photoactivation was used. The simulated ceramic restoration did not influence monomer conversion, however it negatively influence resin cement hardness. The exposure time did not influence resin cement hardness and monomer conversion. The inical DC and HV were significantly greater than after 24 hours, except for DC for initial period, when the photoactivation was realizded through a porcelain disc for 20s.There was a linear and positive correlation between degree of conversion and microhadness for the self-adhesive resin cement RelyX&#61668; Unicem. Defining the cement: organic portion composed by a mixture of monomers. Bis-GMA is the main monomer. Presence of a dimethacrylate containing hydroxyl to connect to the phosphoric acid as a phosphate. Inorganic fillers raging between 0,4 to 11,2&#61549;m. Powder is composed by 96% of inorganic particles. In liquid fraction, the organic portion corresponds to 84%. There were 16% of waste that did not burn due to nitrogen atmosphere.

O objetivo deste estudo foi avaliar a dureza de um cimento resinoso dual autoadesivo (RelyX U200) e um cimento resinoso dual convencional (RelyX ARC) fotoativados sob materiais restauradores indiretos, utilizando unidades fotoativadoras com diferentes comprimentos de ondas (LED Elipar Freelight 2, LED Bluephase, Laser AccuCure 3000TM), por meio de teste de nanoendentação. Para a obtenção dos espécimes foram utilizados incisivos bovinos que após profilaxia, foram submetidos a cortes no limite amelo-cementário para a separação da porção coronária. Após inclusão, os espécimes foram submetidos ao desgaste para exposição de dentina e padronização do substrato. Para simular clinicamente restaurações indiretas foram confeccionadas peças em cerâmica IPS e.max® Press (Ivoclar Vivadent) e em resina composta indireta SR Adoro (Ivoclar Vivadent) que foram cimentadas nas superfícies dentinárias. Os espécimes foram seccionados longitudinalmente em baixa velocidade e constante irrigação e polidos em politriz. Foi estabelecido um grupo controle positivo, no qual o cimento foi fotoativado sem a interposição de material restaurador indireto e um grupo controle negativo, no qual, após a cimentação do material restaurador indireto, a fotoativação foi suprimida, ocorrendo apenas a polimerização química do cimento. Todos os espécimes foram armazenados em água destilada a 37°C durante 7 dias e após esse período, foram submetidos ao teste de nanoendentação na linha de cimentação, com o auxílo do ultra-microdurômetro (Shimadzu Dynamic Ultra Micro Hardness Tester). O ciclo aplicado foi de 100mN. Foram realizadas cinco nanoendentações em cada espécime, cujas médias resultaram nos valores de cada superfície. Os resultados obtidos foram submetidos à Análise de Variância e Teste de Tukey (p<0,05). Podese concluir que o cimento RelyX ARC apresentou maiores valores de dureza do que o RelyX U200 e este foi mais dependente da fotoativação para alcançar uma polimerização adequada. A dureza dos cimentos resinosos avaliados foi influenciada negativamente pela interposição do material restaurador indireto e apenas os LEDs foram capazes de manter o mesmo grau de polimerização dos cimentos quando interposto um material restaurador indireto. / This study aimed to evaluate the hardness of a dual cure self-adhesive resin cement (RelyX U200) and a dual cure conventional resin cement (RelyX ARC) light curing units with different wavelengths (Elipar Freelight 2 LED, Bluephase LED, AccuCure 3000TM Laser) through nanoindentadion test. To obtain the specimens bovine incisors were used after prophylaxis. The tooth were sectioned at the limit amelocement for the separation of the coronal portion. After inclusion, the dentin surface of the specimens were exposed to standardize the substrate. To clinically simulate indirect restorations ceramic pieces were made (IPS e.max® Press/Ivoclar Vivadent) and indirect composite resin (SR Adoro/Ivoclar Vivadent) were cemented on dentin surfaces. The specimens were sectioned longitudinally at low speed with constant irrigation and polished. A positive control group was stablished, in which the cement was light cured without the interposition of indirect restorative material, and a negative control group, in which, after cementation of the indirect restorative material, the light curing was removed, occurring only the chemical polymerization of the cement. All specimens were stored in distilled water at 37°C for 7 days. Nanoindentadion hardness of the cement layer was measured under 100mN load (Shimadzu Dynamic Ultra Micro Hardness Tester). Five nanoindentations in each specimen were obtained, which resulted in the average values of each surface. Data were statistically analyzed using ANOVA and Tukey test (p<0,05). RelyX ARC pesented higher values of hardness than RelyX U200 and this was more dependent on the polymerization. The hardness of the evaluated resin cements was negatively influenced by the interposition of an indirect restorative material and only the LEDs were able to maintain the same degree of polymerization of the cement when an indirect restorative material was used.

Este estudo comparou a performance de quarto agentes cimentantes com diferentes estratégias adesivas para cimentação de pinos de fibra de vidro em canais radiculares, através do teste de resistência adesiva e avaliando a dureza em diferentes profundidades. Para isto, foram utilizadas 60 raízes bovinas tratadas endodonticamente. Foram cimentados pinos de fibra de vidro Rebilda Post 20 de acordo com os seguintes protocolos divididos nos seguintes grupos: Grupos QM: Adesivo autocondicionante dual Futurabond DC + cimento resinoso dual Bifix QM; Group SE: Cimento resinoso autocondicionante de polimerização dual Bifix SE; Group RB: Adesivo autocondicionante de polimerização dual Futurabond DC + Resina Rebilda; Group XB: aplicação do adesivo autocondicionante de polimerização dual Futurabond DC + resina composta do tipo \"bulk fill\" X-tra Base. As raízes foram cortadas em fatias de 1mm e separadas em terços, sendo obtidos 2 corpos de prova por terço. Foram avaliadas a resistência adesiva (n=10) e a microdureza (n=5), após uma semana e após 4 meses de armazenamento em água. Para o teste de resistência adesiva (push- out) uma fatia de cada terço foi testada depois de uma semana e as outras 3 fatias provenientes do mesmo dente avaliadas após 4 meses. O ensaio de push out foi realizado a uma velocidade de 0,5mm/min até o deslocamento do pino e/ou fratura da interface adesiva. Para o teste de microdureza 20 dentes foram selecionados aleatoriamente e de cada dente foram obtidas seis 6 fatias que foram armazenadas em água destilada por uma semana até a mensuração em microdurômetro, após uma semana e após 4 meses. Os corpos de prova foram submetidos ao teste de microdureza Knoop em microdurômetro HMV-2000 (Shimadzu, Tokyo, Japan), cinco endentações foram realizadas na camada de cimento de cada fatia. Os dados referentes aos testes de resistência adesiva (push- out) e microdureza foram submetidas análise de variância 3 fatores (ANOVA), teste de tukey (p<0,05) e teste de correlação de Person. Os valores de resistência adesiva não apresentaram diferenças estatísticas significantes quando observado os valores de resistência adesiva entre os grupos QM, RB e XB (p>=0.05), porém menores valores de resistência adesiva foram observados no Grupo SE. Quando considerada a variável envelhecimento não foram encontradas diferenças na resistência adesiva medida em uma semana e 4 meses (p>=0.05). Para a microdureza diferenças estatisticamente significantes foram encontradas nos diferentes terços da raiz (p<0.05). Os agentes cimentantes apresentaram diferenças estatísticas significantes na dureza (p<0.05). O grupo XB apresentou os maiores valores seguido por QM, RB e SE. Os grupos SE, RB e XB não apresentaram 80% da dureza máxima nas fatias correspondentes a região apical do canal radicular. O teste de Person mostrou haver correlação positiva linear entre a resistência adesiva e a dureza medidas antes e após o envelhecimento. O uso cimento resinoso dual, associado a uma aplicação anterior do sistema adesivo, ainda é a escolha mais segura, pois apresentou valores de força de adesão elevados, associados a valores de dureza adequados, mesmo em regiões apicais do canal radicular. / This study compared the performance of four cementitious agents with different adhesive strategies for cementing fiberglass pins in root canals, through the adhesive strength test and evaluating the hardness at different depths. For this, 60 endodontically treated bovine roots were used. Rebilda Post 20 fiberglass pins were cemented according to the following protocols divided into the following groups: QM groups: dual self-etching adhesive Futurabond DC + resin cement Bifix QM; Group SE: Dual polymerization resin cement Bifix SE; Group RB: application of self-etching dual-polymerization adhesive Futurabond DC + resin Rebilda; Group XB: application of the self-etching adhesive for dual polymerization Futurabond DC + composite resin of the bulk fill type X-tra Base. The roots were cut into 1mm slices and separated into thirds, obtaining 2 specimens per third. Bond strength (n =10) and microhardness (n = 5) were evaluated after one week and after 4 months of storage in water. For the push-out test one slice of each third was tested after one week and the other 3 slices from the same tooth evaluated after 4 months. The push out test was performed at a speed of 0.5mm / min until the pin displacement and / or fracture of the adhesive interface. For the microtensile test, 20 teeth were randomly selected and six slices were obtained from each tooth, which were stored in distilled water for one week until microdurometer measurement, after one week and after four months. The specimens were submitted to the Knoop microhardness test in HMV-2000 microdurometer (Shimadzu, Tokyo, Japan), five indentations were performed in the cement layer of each slice. The data for the tests of bond strenght (push-out) and microhardness were submitted to analysis of variance 3 factors (ANOVA) and Tukey test (p <0.05) and Person correlation test. The bond strength values did not present significant statistical differences when the adhesive strength values were observed between the groups QM, RB and XB (p>=0.05), but lower values of adhesive strength were observed in the SE Group. When the aging variable was considered, differences in adhesive strength measured at one week and 4 months (p>=0.05) were not found. For microhardness, statistically significant differences were found in the different thirds of the root (p <0.05). The cementing agents presented significant statistical differences in the hardness (p <0.05). The XB group presented the highest values followed by QM, RB and SE. The groups SE, RB and XB did not present 80% of the maximum hardness in the slices corresponding to the apical region of the root canal. The Person test showed a linear positive correlation between the adhesive strength and the hardness measured before and after aging. The use of dual resin cement, combined with a previous application of the adhesive system, is still the safest choice, since it presented high values of bond strength, associated with adequate hardness values, even in apical regions of the root canal.

Objetivos: o presente estudo teve como objetivo determinar a aplicabilidade e eficácia adesiva de diferentes monômeros ácidos quando aplicados em formulações de cimentos resinosos autoadesivos experimentais sob o grau de conversão, propriedades físico-químicas e resistência de união à dentina e à zircônia tetragonal policristalina estabilizada por ítrea (Y-TZP), após um período de 3 meses de armazenamento em água. Material: dois tipos de cimentos do tipo pasta-pasta foram formulados contendo monômeros convencionais UDMA, HEMA, BISGMA, TEGDMA e monômeros ácidos 2MP e GDMAP como matriz orgânica. Um grupo contendo apenas monômeros convencionais foi formulado como grupo controle. Os componentes canforoquinona/EDMAB e peróxido de benzoíla/DHPT foram empregados como sistema de ativação dual. O sal sódico do ácido benzenosulfônico 98% (BAS) foi incorporado nos grupos experimentais. Partículas de carga foram incorporadas na proporção ±55% em peso final. Método: A técnica de espectroscopia no infravermelho (FT-IR) foi empregada para análise do grau de conversão (n=3) imediato e após 24 h. A avaliação do pH (n=3) foi feita através do emprego de um equipamento medidor de pH. Os corpos de provas foram imersos em água destilada e o pH foi analisado de forma imediata e após 5 min, 24 h e 48 h. Os testes de sorção e solubilidade (n=6) e espessura de película (n=5) seguiram as recomendações da ISO 4049. A análise de resistência de união (n=12) foi realizada em dentina e Y-TZP, através do teste de cisalhamento em área reduzida após um protocolo de envelhecimento em água destilada por 3 meses. No caso da Y-TZP, metade dos espécimes receberam um tratamento superficial cojet (30 ?m), associado a aplicação de um agente de união silano. O padrão de fratura foi analisado com o auxílio de um estereomicroscópio. Resultados: O grupo controle (91,7%) e o grupo formulado com 2MP (92%) apresentaram superiores valores de grau de conversão em relação ao grupo GDMAP (77,7%). O pH dos grupos experimentais 2MP e GDMAP se apresentou mais ácido após 48 h em comparação ao grupo controle. Em contrapartida, esses grupos experimentais apresentaram uma maior sorção e solubilidade em relação ao grupo controle. A espessura da película formada foi semelhante em todos os grupos testados (p=0,266). Em dentina o grupo controle (27,0 MPa) e GDMAP (24,1 MPa) não apresentaram diferença estatística após 3 meses de estocagem. O grupo 2MP (13,7 MPa) apresentou resultados inferiores aos demais grupos. O tratamento de superfície empregado não foi capaz de manter ou de elevar os valores de resistência de união à Y-TZP após o período de envelhecimento em água. Todos os grupos experimentais apresentaram falhas precoces ou baixos valores de resistência de união após 3 meses, independente da presença ou não do tratamento de superfície. Conclusão: os grupos experimentais 2MP e GDMAP apresentaram resultados promissores. Entretanto, a adesão dos CRAs experimentais testados em Y-TZP ainda se apresenta frágil e instável. / Objectives: the purpose of this study was to evaluate the applicability and adhesive efficiency of different acid monomers utilized in formulations of experimental self-adhesive resin cement under degree of conversion, physico-chemical properties and bond strength to dentin and Y-TZP after 3 months aging period. Materials: two paste-paste luting agents were formulated containing UDMA, HEMA, BISGMA, TEGDMA and acid adhesive monomers 2MP and GDMAP as organic matrix. The control group was formulated containing only conventional monomers. Camphoroquinone/EDMAB and benzoyl peroxide/DHPT were used as dual activation system. BAS salt was incorporated into the experimental groups. Filler particles were added in a proportion of ±55% final weight. Method: Infrared spectroscopy technique (FTIR) was employed for degree of conversion analysis (n=3) immediately and after 24 hours. The pH assessment (n=3) was made using a pH meter. All the specimens were immersed in distilled water and pH assessment was performed immediately and after 5 min, 24 h and 48 h. Tests for sorption and solubility (n=6) and thickness (n=6) were carried out according to ISO 4049 recommendations. Bond strength analysis (n=12) was performed in dentin and Y-TZP through microshear after an aging 3 months protocol in distilled water. Regarding Y-TZP, half of the specimens were submitted to a cojet surface treatment (30 ?m) in association to silane bonding agent application. Fracture toughness standard was evaluated with the assistance of a stereomicroscope. Results: The control (91,7%) and 2MP (92%) groups presented higher degree of conversion than GDMAP group (77,7%). The 2MP and GDMAP experimental groups showed the highest pH compared to control group. In contrast, experimental groups showed a high hydrolytic degradation. The thickness of the formed film was similar among all the tested groups (p=0,266). Regarding the dentin, control and GDMAP groups had statistically similar bond strength (27,0 and 24,1 MPa respectively) after 3 months storage. While 2MP group (13,7 MPa) showed lower results compared the other groups. The surface treatment employed was not capable to maintain or elevate bond strength to Y-TZP results after the aging period in water. All experimental groups showed low bond strength values and even early failures after 3 months, regardless the surface treatment or its abscence. Conclusion: the experimental groups 2MP and GDMAP presented promising results. However, chemical adhesion to Y-TZP still remains weak and instable.

The current study aimed to evaluate the effect of irrigating and chelating solutions on bond strength of fiber glass posts cemented with RelyX U200. 60 single-rooted premolars were sectioned at 14 mm from the apex, prepared with ProTaper Universal system until F3 instrument and filled with F3 master cone and AH Plus sealer. Root canal filling was partially removed, remaining 4 mm of guta-percha at the apical third. Specimens were randomly divided into 5 experimental groups (n=12), according to the solution used before fiber post cementation (dentin surface treatment), as described: EDTA 17% (EDTA); QMix (QM); SmearClear (SC); NaOCl 2.5% (NaOCl) and saline solution as control group (SS). Ultrasonic activation was performed three times, during 20 seconds each and root canals were dried with paper points. Exacto N2 glass fiber posts were cemented with RelyX U200. Rhodamine B dye was mixed to RelyX U200 in one specimen per group, in order to provide fluorescence for confocal laser scanning microscopy (CLSM) assessment. A cutting machine was used for root s sectioning, providing 3 slices, one for each root third. Next, push-out test was performed. Stereomicroscope and CLSM were used to analyze the failure mode and to illustrate the pattern of distribution of RelyX U200 inside dentinal tubules, respectively. Bond strength mean were calculated and ANOVA and Bonferroni tests were used for statistical analysis. SS showed the higher mean of bond strength values, superior to QM, SC (P < .05). NaOCl presented intermediary bond strength values, similar to EDTA and SS (P > .05). QM and SC showed the lowest mean of bond strength (P < .05). In conclusion, SS and NaOCl associated to ultrasonic activation seems to be adequate solutions for root canal cleaning before fiber post cementation with RelyX U200, while chelating solutions, such as EDTA, QMix and SmearClear, should not be used for dentin pre-treatment when cementing with RelyX U200. / O presente estudo tem por objetivo avaliar o efeito de diferentes soluções irrigantes e quelantes na resistência adesiva de pinos de fibra de vidro cimentados com cimento autoadesivo RelyX U200. 60 pré-molares inferiores extraídos de humanos, padronizados em 14 mm, foram preparados com o sistema ProTaper Universal até o instrumento F3, obturados com cimento AH Plus e cones F3 do mesmo sistema. Os espécimes foram desobturados parcialmente, restando 4 mm apicais de material obturador e realocados em quatro grupos experimentais e um controle (n=12), de acordo com a solução de tratamento de superfície dentinária prévia à cimentação dos pinos: EDTA 17% (EDTA), QMix (QM), SmearClear (SC), Soro Fisiológico (SS) e NaOCl 2,5% (NaOCl). As soluções foram ativadas por ultrassom em três etapas, durante 20 segundos cada e os canais foram secos com pontas de papel absorventes. Os pinos de fibra de vidro do Sistema Exacto Translúcido N2 foram cimentados com RelyX U200. Em um espécime por grupo foi incorporada Rodamina B ao cimento autoadesivo como marcador fluorescente para análise em Microscopia Confocal à laser (MECL). Foram seccionados 3slices por espécime, sendo 1 slice por terço radicular, e submetidos ao teste de push-out na máquina de ensaio universal EMIC. Estereomicroscópio e MECL foram utilizados para analisar o padrão de falha dos espécimes e o padrão de penetração do cimento autoadesivo nos túbulos dentinários, respectivamente. A média de resistência adesiva de cada espécime foi calculada. Testes ANOVA e Bonferroni foram utilizados para analisar as diferenças entre os grupos. SS demonstrou a maior média de resistência adesiva, sendo superior aos grupos QM, SC (P <.05). NaOCl apresentou valores intermediários de resistência adesiva, similares ao EDTA e SS (P > .05). QM e SC apresentaram as menores médias de resistência adesiva (P < .05). Pode-se concluir que o uso de SS e NaOCl parece ser adequado para lavagem do canal prévia à cimentação de pinos de fibra de vidro, com uso de cimento resinoso autoadesivo RelyX U200. O uso de soluções quelantes como EDTA, QM e SC parece interferir negativamente nos valores de resistência adesiva.

Este estudo comparou a performance de quarto agentes cimentantes com diferentes estratégias adesivas para cimentação de pinos de fibra de vidro em canais radiculares, através do teste de resistência adesiva e avaliando a dureza em diferentes profundidades. Para isto, foram utilizadas 60 raízes bovinas tratadas endodonticamente. Foram cimentados pinos de fibra de vidro Rebilda Post 20 de acordo com os seguintes protocolos divididos nos seguintes grupos: Grupos QM: Adesivo autocondicionante dual Futurabond DC + cimento resinoso dual Bifix QM; Group SE: Cimento resinoso autocondicionante de polimerização dual Bifix SE; Group RB: Adesivo autocondicionante de polimerização dual Futurabond DC + Resina Rebilda; Group XB: aplicação do adesivo autocondicionante de polimerização dual Futurabond DC + resina composta do tipo \"bulk fill\" X-tra Base. As raízes foram cortadas em fatias de 1mm e separadas em terços, sendo obtidos 2 corpos de prova por terço. Foram avaliadas a resistência adesiva (n=10) e a microdureza (n=5), após uma semana e após 4 meses de armazenamento em água. Para o teste de resistência adesiva (push- out) uma fatia de cada terço foi testada depois de uma semana e as outras 3 fatias provenientes do mesmo dente avaliadas após 4 meses. O ensaio de push out foi realizado a uma velocidade de 0,5mm/min até o deslocamento do pino e/ou fratura da interface adesiva. Para o teste de microdureza 20 dentes foram selecionados aleatoriamente e de cada dente foram obtidas seis 6 fatias que foram armazenadas em água destilada por uma semana até a mensuração em microdurômetro, após uma semana e após 4 meses. Os corpos de prova foram submetidos ao teste de microdureza Knoop em microdurômetro HMV-2000 (Shimadzu, Tokyo, Japan), cinco endentações foram realizadas na camada de cimento de cada fatia. Os dados referentes aos testes de resistência adesiva (push- out) e microdureza foram submetidas análise de variância 3 fatores (ANOVA), teste de tukey (p<0,05) e teste de correlação de Person. Os valores de resistência adesiva não apresentaram diferenças estatísticas significantes quando observado os valores de resistência adesiva entre os grupos QM, RB e XB (p>=0.05), porém menores valores de resistência adesiva foram observados no Grupo SE. Quando considerada a variável envelhecimento não foram encontradas diferenças na resistência adesiva medida em uma semana e 4 meses (p>=0.05). Para a microdureza diferenças estatisticamente significantes foram encontradas nos diferentes terços da raiz (p<0.05). Os agentes cimentantes apresentaram diferenças estatísticas significantes na dureza (p<0.05). O grupo XB apresentou os maiores valores seguido por QM, RB e SE. Os grupos SE, RB e XB não apresentaram 80% da dureza máxima nas fatias correspondentes a região apical do canal radicular. O teste de Person mostrou haver correlação positiva linear entre a resistência adesiva e a dureza medidas antes e após o envelhecimento. O uso cimento resinoso dual, associado a uma aplicação anterior do sistema adesivo, ainda é a escolha mais segura, pois apresentou valores de força de adesão elevados, associados a valores de dureza adequados, mesmo em regiões apicais do canal radicular. / This study compared the performance of four cementitious agents with different adhesive strategies for cementing fiberglass pins in root canals, through the adhesive strength test and evaluating the hardness at different depths. For this, 60 endodontically treated bovine roots were used. Rebilda Post 20 fiberglass pins were cemented according to the following protocols divided into the following groups: QM groups: dual self-etching adhesive Futurabond DC + resin cement Bifix QM; Group SE: Dual polymerization resin cement Bifix SE; Group RB: application of self-etching dual-polymerization adhesive Futurabond DC + resin Rebilda; Group XB: application of the self-etching adhesive for dual polymerization Futurabond DC + composite resin of the bulk fill type X-tra Base. The roots were cut into 1mm slices and separated into thirds, obtaining 2 specimens per third. Bond strength (n =10) and microhardness (n = 5) were evaluated after one week and after 4 months of storage in water. For the push-out test one slice of each third was tested after one week and the other 3 slices from the same tooth evaluated after 4 months. The push out test was performed at a speed of 0.5mm / min until the pin displacement and / or fracture of the adhesive interface. For the microtensile test, 20 teeth were randomly selected and six slices were obtained from each tooth, which were stored in distilled water for one week until microdurometer measurement, after one week and after four months. The specimens were submitted to the Knoop microhardness test in HMV-2000 microdurometer (Shimadzu, Tokyo, Japan), five indentations were performed in the cement layer of each slice. The data for the tests of bond strenght (push-out) and microhardness were submitted to analysis of variance 3 factors (ANOVA) and Tukey test (p <0.05) and Person correlation test. The bond strength values did not present significant statistical differences when the adhesive strength values were observed between the groups QM, RB and XB (p>=0.05), but lower values of adhesive strength were observed in the SE Group. When the aging variable was considered, differences in adhesive strength measured at one week and 4 months (p>=0.05) were not found. For microhardness, statistically significant differences were found in the different thirds of the root (p <0.05). The cementing agents presented significant statistical differences in the hardness (p <0.05). The XB group presented the highest values followed by QM, RB and SE. The groups SE, RB and XB did not present 80% of the maximum hardness in the slices corresponding to the apical region of the root canal. The Person test showed a linear positive correlation between the adhesive strength and the hardness measured before and after aging. The use of dual resin cement, combined with a previous application of the adhesive system, is still the safest choice, since it presented high values of bond strength, associated with adequate hardness values, even in apical regions of the root canal.

Objetivos: o presente estudo teve como objetivo determinar a aplicabilidade e eficácia adesiva de diferentes monômeros ácidos quando aplicados em formulações de cimentos resinosos autoadesivos experimentais sob o grau de conversão, propriedades físico-químicas e resistência de união à dentina e à zircônia tetragonal policristalina estabilizada por ítrea (Y-TZP), após um período de 3 meses de armazenamento em água. Material: dois tipos de cimentos do tipo pasta-pasta foram formulados contendo monômeros convencionais UDMA, HEMA, BISGMA, TEGDMA e monômeros ácidos 2MP e GDMAP como matriz orgânica. Um grupo contendo apenas monômeros convencionais foi formulado como grupo controle. Os componentes canforoquinona/EDMAB e peróxido de benzoíla/DHPT foram empregados como sistema de ativação dual. O sal sódico do ácido benzenosulfônico 98% (BAS) foi incorporado nos grupos experimentais. Partículas de carga foram incorporadas na proporção ±55% em peso final. Método: A técnica de espectroscopia no infravermelho (FT-IR) foi empregada para análise do grau de conversão (n=3) imediato e após 24 h. A avaliação do pH (n=3) foi feita através do emprego de um equipamento medidor de pH. Os corpos de provas foram imersos em água destilada e o pH foi analisado de forma imediata e após 5 min, 24 h e 48 h. Os testes de sorção e solubilidade (n=6) e espessura de película (n=5) seguiram as recomendações da ISO 4049. A análise de resistência de união (n=12) foi realizada em dentina e Y-TZP, através do teste de cisalhamento em área reduzida após um protocolo de envelhecimento em água destilada por 3 meses. No caso da Y-TZP, metade dos espécimes receberam um tratamento superficial cojet (30 ?m), associado a aplicação de um agente de união silano. O padrão de fratura foi analisado com o auxílio de um estereomicroscópio. Resultados: O grupo controle (91,7%) e o grupo formulado com 2MP (92%) apresentaram superiores valores de grau de conversão em relação ao grupo GDMAP (77,7%). O pH dos grupos experimentais 2MP e GDMAP se apresentou mais ácido após 48 h em comparação ao grupo controle. Em contrapartida, esses grupos experimentais apresentaram uma maior sorção e solubilidade em relação ao grupo controle. A espessura da película formada foi semelhante em todos os grupos testados (p=0,266). Em dentina o grupo controle (27,0 MPa) e GDMAP (24,1 MPa) não apresentaram diferença estatística após 3 meses de estocagem. O grupo 2MP (13,7 MPa) apresentou resultados inferiores aos demais grupos. O tratamento de superfície empregado não foi capaz de manter ou de elevar os valores de resistência de união à Y-TZP após o período de envelhecimento em água. Todos os grupos experimentais apresentaram falhas precoces ou baixos valores de resistência de união após 3 meses, independente da presença ou não do tratamento de superfície. Conclusão: os grupos experimentais 2MP e GDMAP apresentaram resultados promissores. Entretanto, a adesão dos CRAs experimentais testados em Y-TZP ainda se apresenta frágil e instável. / Objectives: the purpose of this study was to evaluate the applicability and adhesive efficiency of different acid monomers utilized in formulations of experimental self-adhesive resin cement under degree of conversion, physico-chemical properties and bond strength to dentin and Y-TZP after 3 months aging period. Materials: two paste-paste luting agents were formulated containing UDMA, HEMA, BISGMA, TEGDMA and acid adhesive monomers 2MP and GDMAP as organic matrix. The control group was formulated containing only conventional monomers. Camphoroquinone/EDMAB and benzoyl peroxide/DHPT were used as dual activation system. BAS salt was incorporated into the experimental groups. Filler particles were added in a proportion of ±55% final weight. Method: Infrared spectroscopy technique (FTIR) was employed for degree of conversion analysis (n=3) immediately and after 24 hours. The pH assessment (n=3) was made using a pH meter. All the specimens were immersed in distilled water and pH assessment was performed immediately and after 5 min, 24 h and 48 h. Tests for sorption and solubility (n=6) and thickness (n=6) were carried out according to ISO 4049 recommendations. Bond strength analysis (n=12) was performed in dentin and Y-TZP through microshear after an aging 3 months protocol in distilled water. Regarding Y-TZP, half of the specimens were submitted to a cojet surface treatment (30 ?m) in association to silane bonding agent application. Fracture toughness standard was evaluated with the assistance of a stereomicroscope. Results: The control (91,7%) and 2MP (92%) groups presented higher degree of conversion than GDMAP group (77,7%). The 2MP and GDMAP experimental groups showed the highest pH compared to control group. In contrast, experimental groups showed a high hydrolytic degradation. The thickness of the formed film was similar among all the tested groups (p=0,266). Regarding the dentin, control and GDMAP groups had statistically similar bond strength (27,0 and 24,1 MPa respectively) after 3 months storage. While 2MP group (13,7 MPa) showed lower results compared the other groups. The surface treatment employed was not capable to maintain or elevate bond strength to Y-TZP results after the aging period in water. All experimental groups showed low bond strength values and even early failures after 3 months, regardless the surface treatment or its abscence. Conclusion: the experimental groups 2MP and GDMAP presented promising results. However, chemical adhesion to Y-TZP still remains weak and instable.