Orientador: Elisa Maria Aparecida Giro / Banca: Carlos Alberto de Souza Costa / Banca: João Eduardo Gomes Filho / Resumo: Para que um material seja indicado como retrobturador, é desejável que apresente várias propriedades, entre elas, intensa atividade antibacteriana e aceitável biocompatibilidade. O presente trabalho teve como objetivo avaliar, in vitro, o efeito antibacteriano e citotóxico do Agregado de Trióxido Mineral (MTA-Branco, Angelus® Indústria de Produtos Odontológicos Ltda., Londrina, PR, Brasil), associado à solução de clorexidina (CHX) em diferentes concentrações. Para a análise da atividade antibacteriana foi empregado o método de difusão em ágar Müller-Hinton e foram utilizados os microrganismos Staphylococcus aureus (ATCC - 25923), Pseudomonas aeruginosa (ATCC - 27853), Escherichia coli (ATCC - 25922) e Enterococcus faecalis (ATCC - 29262). Em placas de Petri contendo a suspensão bacteriana com meio de cultura, foram preparados poços com 4 mm de diâmetro e 5 mm de profundidade, os quais foram preenchidos com o cimento MTA preparado com água destilada estéril (G1-controle) ou com solução de CHX nas concentrações de 0,06% (G2), 0,12% (G3), 0,2% (G4) e 1% (G5). As placas foram incubadas em condições de aerobiose a 37ºC por 24 horas e os halos de inibição do crescimento bacteriano foram medidos em milímetros. Para avaliar a citotoxicidade do MTA associado às diferentes concentrações de CHX, o metabolismo e a morfologia celular foram avaliados por meio do teste do MTT e da análise da microscopia eletrônica de varredura, respectivamente. Corpos de prova de 4 mm de diâmetro e 2 mm de espessura foram preparados com as associações de materiais e imersos em 1,1 mL de meio de cultura (DMEM) por 24 horas ou por 7 dias para obtenção dos extratos. DMEM completo (grupo controle - G6) e os extratos de cada grupo foram aplicados sobre cultura de fibroblastos do ligamento periodontal de camundongos, os quais foram incubados... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: An ideal root-end filling material should present several properties, including antibacterial activity and biocompatibility. The aim of this in vitro study was to investigate the antibacterial and cytotoxic effects of Mineral Trioxide Aggregate (MTA-White, Angelus® Indústria de Produtos Odontológicos Ltda., Londrina, PR, Brasil) mixed with different concentrations of chlorhexidine (CHX). For antibacterial activity analysis diffusion method on Müller-Hinton agar was employed. The bacterial strains used were Staphylococcus aureus (ATCC - 25923), Pseudomonas aeruginosa (ATCC - 27853), Escherichia coli (ATCC - 25922) e Enterococcus faecalis (ATCC - 29262). In Petri plates containing culture medium with bacterial suspension, wells were made measuring 4 mm in diameter and 5 mm in depth. The wells were completely filled with MTA mixed with sterile distilled water (G1) or with different concentrations of CHX: 0.06 % (G2), 0.12% (G3), 0.2% (G4) and 1% (G5). The plates were incubated in aerobic conditions at 37ºC for 24 hours, and then the diameters of the zones of bacterial inhibition were measured. To evaluate the cytotoxicity of the MTA mixed with different concentrations of CHX, the cell metabolism and cells morphology were evaluated by the MTT assay and scanning electron microscopy, respectively. Round-shaped samples measuring 4 mm in diameter and 2 mm in thickness were prepared with the association of materials and immersed in 1.1 mL of culture medium (DMEM) and incubated for 24 hours or 7 days. The extracts from every sample and pure DMEM (control group - G6) were applied on mouse periodontal ligament fibroblast cells culture and incubated at 37ºC with 5% CO2 and 95% air for 24 hours. The addition of CHX 1% to MTA increased the antibacterial activity of the cement against S. aureus (p <0.05). There was no statistically significant difference... (Complete abstract click electronic access below) / Mestre

Orientador: Marcelo Ferrarezi de Andrade / Banca: Hugo Henrique Alvim / Banca: Victor Humberto Orbegoso Flores / Banca: Edson Alves de Campos / Banca: José Roberto Cury Saad / Resumo: O presente trabalho propõe avaliar a utilização de clorexidina e laser de Er,Cr:YSGG no processo de adesão em cavidades mistas hígidas e afetadas por cárie em relação a adaptação externa de restaurações classe V submetidas a ciclagem térmica. Foram realizados preparos cavitários mistos de classe V vestibular em 36 molares humanos, dos quais metade foram induzidos artificialmente à cárie. Foi feita a remoção da cárie com broca esférica em baixa rotação, permanecendo a dentina afetada. Os dentes foram subdivididos em 6 grupos, cavidade hígida: sem tratamento prévio, utilização de clorexidina e utilização de laser de Er,Cr:YSGG e cariados: sem tratamento prévio, utilização de clorexidina e utilização de laser de Er,Cr:YSGG. Foi empregado o sistema adesivo e restaurador da resina a base de silorano Filtek P90 (3M ESPE, St. Paul, MN, EUA). Os espécimes foram submetidos a 5000 ciclos térmicos (5-55° C em banhos de 60 minutos). Para caracterização da adaptação externa foram obtidas réplicas de epóxi pela impressão da superfície das restaurações. Foi realizada a análise quantitativa da adaptação externa, tanto em dentina hígida quanto afetada, por meio de réplicas de epóxi, utilizando Microscopia Eletrônica de Varredura. Os valores médios em porcentagem de margen não-adaptadas foram 5,41% em esmalte e 6,49% em dentina antes da termociclagem e 25% e 33,7% respectivamente após. As amostras do grupo com cavidade cariada que foram irradiados com laser apresentaram os maiores valores de margem não-contínua. A clorexidina não afetou os resultados na adaptação marginal / Abstract: This study evaluates the use of chlorhexidine and laser Er,Cr:YSGG in the adesion in cavities mixed healthy and carie affected, in relation to external adaptation on class V restorations subjected to thermal cycling. Cavity preparations were performed mixed class V buccal 36 human molars, half of which were artificially carie induced. Was removed from the cavity with round bur at low speed, the remaining affected dentin. The teeth were divided into 6 groups, cavity healthy: without previous treatment, use of chlorhexidine and the use of Er,Cr:YSGG and carie afected: no previous treatment, use of chlorhexidine and the use of Er,Cr:YSGG. We used adhesive system and restorative resin-based silorano Filtek P90 (3M ESPE, St. Paul, MN, USA). The specimens were subjected to 5000 thermal cycles (5-55° C 60 minutes). To characterize the external adaptation of epoxy replicas were obtained by printing the surface of the restorations. We performed quantitative analysis of external adaptation, both in healthy female and affected dentin, using epoxy replicas, using SEM. The average percentage of non-adapted were 5.41% and 6.49% in enamel dentine before thermal cycling and 25% and 33.7% respectively after. And the group they were carious cavity laser irradiated showed higher non-continuous margin. The clorexidine does not affected the result / Doutor

Orientador: Edson Alves de Campos / Banca: Milton Carlos Kuga / Banca: Marco Antonio Húngaro Duarte / Resumo: O objetivo deste estudo foi avaliar, por meio de ensaio push-out, a resistência de união de pinos de fibra de vidro cimentados com cimento resinoso empregando-se diferentes protocolos de tratamento da dentina, com clorexidina e etanol. Cinqüenta dentes caninos humanos extraídos por motivos periodontais, tratados endodonticamente tiveram suas raízes preparadas para receber pino de fibra de vidro. As raízes foram aleatoriamente divididas em cinco grupos (n=10), de acordo com o tratamento da dentina condicionada: Grupo 1 (controle): água destilada; Grupo 2: solução aquosa de diacetato de clorexidina a 1% ; Grupo 3: solução alcoólica de diacetato de clorexidina a 1%; Grupo 4: etanol a 99% e Grupo 5: solução de digluconato de clorexidina 2%. Após o tratamento da dentina condicionada, aplicou-se o sistema adesivo e pino de fibra foi cimentado com cimento resinoso. Todos os espécimes foram armazenados em água destilada por 24 h. Após este tempo, foram obtidas secções horizontais de cada um dos terços da raiz e o teste push-out foi realizado para avaliação da resistência de união. Os resultados foram obtidos (em MPa) e os dados analisados com ANOVA e teste de Tukey (P < 0,05). Os padrões de falha foram classificados em adesiva, coesiva ou mista. Em todos os terços, G3 e G4 apresentaram valores médios de resistência de união similares, mas maior que os outros grupos. G1, G2 e G5 foram semelhantes entre si. Independentemente dos terços da raiz, G3 e G4 exibiram mais incidência de falhas mista. O tratamento da dentina radicular com etanol, isolado ou associado com diacetato de clorexidina a 1% aumentou a resistência de união do pino de fibra cimentado com cimento resinoso, em comparação com o tratamento da dentina radicular com água destilada ou diacetato de clorexidina a 1% ou 2%, em curto prazo / Abstract: The aim of this study was to evaluate if radicular dentine pretreatment with various protocols using chlorhexidine and/or ethanol improves the push-out bond strength of fiber posts luted with resin cement. A total of 50 space post prepared in endodontically-treated extracted human canine roots were randomly divided into five groups (n = 10), according to dentine pretreatment: Group 1 (control): distilled water; Group 2: 1% chlorhexidine diacetate solution; Group 3: chlorhexidine diacetate + 99% ethanol; Group 4: 99% ethanol, and Group 5: 2% chlorhexidine digluconate solution . After pretreatment, an adhesive system was applied into radicular dentine and fiber post was luted with resin cement. All specimens were stored in distilled water for 24 h. After this time, horizontal slices were obtained from each root thirds and push-out bond strength was assessment. The results were obtained (in MPa) and data analyzed with ANOVA and Tukey tests (P = 0.05). Failure modes were classified in adhesive, cohesive or mixed. At all thirds, G3 and G4 presented similar push-out bond strength values (P > 0.05), but higher than other groups (P < 0.05). G1, G2 and G5 were similar (P > 0.05). Regardless the root thirds, G3 and G4 exhibited more mixed failures incidence. The radicular dentine pretreatment with ethanol, alone or associated with chlorhexidine diacetate increased the bond strength of fiber post luted with resin cement, in comparison to radicular dentine pretreatment with distilled water, 2% chlorhexidine digluconate solution or 1% chlorhexidine diacetate solution, independently of root thirds, when evaluated in short-time / Mestre

Made available in DSpace on 2014-11-15T01:01:45Z (GMT). No. of bitstreams: 1 000462638-Texto+Completo-0.pdf: 1440576 bytes, checksum: 4bcbd45daf2312b27e7e80da0fe9fc8e (MD5) Previous issue date: 2014 / This thesis had the purpose to evaluate the action of a new irrigant, QMix, on bacterial endotoxins as well as the effect of its combination with sodium hypochlorite on the root canal walls. Having the main purpose to evaluate its action on bacterial endotoxins, 50 extracted human teeth were contaminated in vitro with endotoxins and irrigated with QMix, EDTA, chlorhexidine (CHX) and sodium hypochlorite (NaOCl). It was used a Limulus Amebocyte Lysate (LAL) assay to quantify the remaining endotoxins after the irrigation. The results of this first study showed that QMix reduced the endotoxins level when compared to the other irrigant solutions that were tested. The second study from this thesis had the purpose to observe in scanning electron microscopy (SEM) the formation of precipitate on the root canal walls due to the concomitant use of NaOCl and QMix. The results from this study showed that despite the presence of CHX in the composition of QMix, its use after the chemical mechanical preparation of the canal with NaOCl did not result in the formation of a precipitate on the root canal walls. On the contrary, the images in SEM showed clean walls with exposed dentinal tubules. Once it is a new product there are still few studies about QMix. Although, according to the results presented on this study, it can be concluded that QMix is effective on the elimination of bacterial endotoxins from the root canal, not showing any precipitate formation when used concomitantly with NaOCl. / Este trabalho teve o objetivo de avaliar a ação de um novo irrigante, o QMix, sobre endotoxinas bacterianas, bem como o efeito da sua combinação com hipoclorito de sódio sobre as paredes do canal radicular. Com a finalidade de avaliar sua ação sobre endotoxinas bacterianas, 50 dentes humanos extraídos foram contaminados in vitro com endotoxinas, e preenchidos com QMix, EDTA, clorexidina (CHX) e hipoclorito de sódio (NaOCl). Foi utilizado um teste de Lisado de Amebócito de Limulus (LAL) para quantificação de endotoxinas remanescentes após a irrigação. Os resultados deste primeiro estudo demonstraram que o QMix reduziu os níveis de endotoxinas quando comparado com as outras soluções irrigadoras testadas. O segundo estudo da presente tese teve o propósito de observar em Microscopia Eletrônica de Varredura (MEV) a formação de precipitado sobre as paredes do canal decorrente do uso concomitante de NaOCl e QMix. Os resultados deste estudo demonstraram que, apesar da presença de CHX na composição do QMix, seu uso após o preparo químico mecânico do canal com NaOCl não resultou na formação de precipitado sobre as paredes do canal. Muito pelo contrário, as imagens em MEV apresentaram paredes limpas com túbulos dentinários expostos. Por se tratar de um produto novo, ainda existem poucos estudos sobre o QMix. Porém, de acordo com os resultados apresentados neste trabalho, pode-se concluir que o QMix é eficaz na eliminação de endotoxinas bacterianas do interior do canal radicular, e seu uso concomitante com NaOCl não resulta na formação de precipitado sobre as paredes do canal.

Introdução: O objetivo do presente estudo foi correlacionar o efeito antimicrobiano residual e a substantividade da solução de clorexidina a 2%, em dentina humana de dentes extraídos e contaminada com E. faecalis, por 48 horas, 7 e 30 dias. Metodologia: Cento e vinte e três dentes humanos extraídos foram utilizados para esse estudo. As amostras foram divididas em quatro grupos conforme a solução irrigadora utilizada (CHX 2% ou soro fisiológico) e na presença ou ausência do biofilme de Enterococcus faecalis. As amostras foram mantidas em contato com a respectiva solução durante 5 minutos. Cada grupo foi distribuído aleatoriamente em 3 subgrupos de acordo com o período de avaliação (n=10). A quantidade de CHX presente foi avaliada através de cromatografia líquida de alta eficiência (HPLC) e a viabilidade bacteriana foi analisada através de microscópio confocal a laser (CLSM). A análise estatistica foi feita através dos testes de Kruskal-Wallis e Mann-Whitney U (P<.05) e teste de correlação de Spearman (P<.01). Resultados: Houve uma correlação negativa entre o percentual de células viáveis e a quantidade de CHX remanescente (P = .000). A CHX reduziu significativamente o percentual de células viáveis em relação ao soro após 48 horas (P = .007). A diferença foi mantida no período de 7 dias (P = .001). Após 30 dias, o grupo CHX apresentou um aumento da viabilidade bacteriana tornando-se semelhante ao soro (P = .623). Simultaneamente, a quantidade de CHX reduziu significativamente após 30 dias (P = .000). Conclusão: Os resultados do presente estudo indicam que a CHX a 2% foi detectada nos periodos de 48 horas e 7 dias, mantendo reduzido o percentual de células viáveis. A presença de microrganismos na dentina humana não alterou a quantidade de CHX residual. / Introduction: The aim of this study was to correlate the bacterial viability and the presence of 2% chlorhexidine (CHX) on dentin by means of confocal laser scanning microscope (CLSM) and high-performance liquid chromatography (HPLC) for 48 hours, 7 and 30 days. Methods: One hundred twenty three extracted human teeth were used. Samples were divided into 4 groups according to the solution (CHX or saline) and the presence of Enterococus faecalis biofilm. Samples were kept in contact with 5mL of the solution for 5 minutes. Each group was divided into 3 subgroups according to the evaluation period (n = 10). Statistical analysis was performed by using the Kruskal- Wallis, Mann-Whitney U tests (P < .05) and Spearman’s Rank Correlation Coefficient (P < .01). Results: There was a negative correlation between the percentage of live cells and the amount of remaining CHX (P = .000). CHX significantly reduced the percentage of viable cells compared to saline after 48 hours (P = .007). Differences were maintained in the 7-day evaluation (P = .001). After 30 days, CHX group presented an increase of viable cells, thereby becoming similar to saline (P = .623). Simultaneously, remaining CHX significantly reduced in the 30-day specimens (P = .000). Conclusion: The results of this study indicate that 2% CHX solution was detected for 48 hours and 7 days, keeping a low percentage of viable cells. The presence of microorganisms on human dentin did not affect 2% chlorhexidine maintenance.

Introdução: O objetivo do presente estudo foi correlacionar o efeito antimicrobiano residual e a substantividade da solução de clorexidina a 2%, em dentina humana de dentes extraídos e contaminada com E. faecalis, por 48 horas, 7 e 30 dias. Metodologia: Cento e vinte e três dentes humanos extraídos foram utilizados para esse estudo. As amostras foram divididas em quatro grupos conforme a solução irrigadora utilizada (CHX 2% ou soro fisiológico) e na presença ou ausência do biofilme de Enterococcus faecalis. As amostras foram mantidas em contato com a respectiva solução durante 5 minutos. Cada grupo foi distribuído aleatoriamente em 3 subgrupos de acordo com o período de avaliação (n=10). A quantidade de CHX presente foi avaliada através de cromatografia líquida de alta eficiência (HPLC) e a viabilidade bacteriana foi analisada através de microscópio confocal a laser (CLSM). A análise estatistica foi feita através dos testes de Kruskal-Wallis e Mann-Whitney U (P<.05) e teste de correlação de Spearman (P<.01). Resultados: Houve uma correlação negativa entre o percentual de células viáveis e a quantidade de CHX remanescente (P = .000). A CHX reduziu significativamente o percentual de células viáveis em relação ao soro após 48 horas (P = .007). A diferença foi mantida no período de 7 dias (P = .001). Após 30 dias, o grupo CHX apresentou um aumento da viabilidade bacteriana tornando-se semelhante ao soro (P = .623). Simultaneamente, a quantidade de CHX reduziu significativamente após 30 dias (P = .000). Conclusão: Os resultados do presente estudo indicam que a CHX a 2% foi detectada nos periodos de 48 horas e 7 dias, mantendo reduzido o percentual de células viáveis. A presença de microrganismos na dentina humana não alterou a quantidade de CHX residual. / Introduction: The aim of this study was to correlate the bacterial viability and the presence of 2% chlorhexidine (CHX) on dentin by means of confocal laser scanning microscope (CLSM) and high-performance liquid chromatography (HPLC) for 48 hours, 7 and 30 days. Methods: One hundred twenty three extracted human teeth were used. Samples were divided into 4 groups according to the solution (CHX or saline) and the presence of Enterococus faecalis biofilm. Samples were kept in contact with 5mL of the solution for 5 minutes. Each group was divided into 3 subgroups according to the evaluation period (n = 10). Statistical analysis was performed by using the Kruskal- Wallis, Mann-Whitney U tests (P < .05) and Spearman’s Rank Correlation Coefficient (P < .01). Results: There was a negative correlation between the percentage of live cells and the amount of remaining CHX (P = .000). CHX significantly reduced the percentage of viable cells compared to saline after 48 hours (P = .007). Differences were maintained in the 7-day evaluation (P = .001). After 30 days, CHX group presented an increase of viable cells, thereby becoming similar to saline (P = .623). Simultaneously, remaining CHX significantly reduced in the 30-day specimens (P = .000). Conclusion: The results of this study indicate that 2% CHX solution was detected for 48 hours and 7 days, keeping a low percentage of viable cells. The presence of microorganisms on human dentin did not affect 2% chlorhexidine maintenance.

Orientador: Regina Maria Puppin-Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T08:50:32Z (GMT). No. of bitstreams: 1 Sacramento_PatriciaAlmada_D.pdf: 3198869 bytes, checksum: 35adfba6168c7cf3012e88e5e9c2c3c5 (MD5) Previous issue date: 2010 / Resumo: Os objetivos nesta tese, apresentada em dois capítulos, foram avaliar o efeito da clorexidina-CHX e do monômero antibacteriano 12-metacriloxidodecilpiridíneo-MDPB na resistência e degradação da união resina/dentina desmineralizada por até doze meses de armazenamento. Capítulo 1: O objetivo deste estudo in vitro foi avaliar o efeito da CHX e/ou de diferentes sistemas adesivos na penetração dos monômeros na dentina desmineralizada, na formação e espessura da camada híbrida utilizando a técnica de Microscopia Confocal de Varredura a Laser (MCVL). Foram utilizados 3 sistemas adesivos: Clearfil SE Bond- SE (Kuraray), Clearfil Protect Bond - PB (Kuraray) e Adper Single Bond 2- SB (3M/ESPE) e um agente antimicrobiano: solução de digluconato de clorexidina 2% (FGM) preconizado para a limpeza da cavidade. Trinta terceiros molares hígidos foram distribuídos aleatoriamente em 6 grupos de acordo com os sistemas adesivos SE, PB e SB, com ou sem aplicação prévia da CHX. A dentina média foi exposta e desmineralizada artificialmente com gel ácido de carboximetilcelulose previamente ao procedimento de união. Os dados de MCVL foram analisados pelo teste estatístico Análise de Variância e teste de Tukey (P<0,05). A CHX e os sistemas adesivos não interferiram com a penetração dos monômeros na dentina desmineraliza. Todas as amostras apresentaram formação de camada híbrida, sendo mais espessa e menos homogênea nos grupos do SB, independente do uso da CHX. Concluiu-se que a CHX e os diferentes sistemas adesivos não afetaram a penetração dos monômeros em dentina desmineralizada. Somente o sistema adesivo interferiu com a espessura e homogeinidade da camada híbrida. Capítulo 2: O objetivo deste estudo in vitro foi: avaliar a influência CHX, do MDPB e o tempo de armazenamento na resistência e degradação da união resina/dentina desmineralizada através do teste de microcisalhamento (µSBS) e análise da nanoinfiltração. Foram utilizados 2 sistemas adesivos: Clearfil SE Bond- SE (Kuraray), Clearfil Protect Bond - PB (Kuraray). Cento e vinte terceiros molares hígidos foram distribuídos aleatoriamente em 12 grupos de acordo com os sistemas adesivos SE e PB, com ou sem aplicação prévia da CHX na superfície de união e tempo de armazenamento de 24 horas, 6 e 12 meses. A dentina média foi exposta e desmineralizada artificialmente. Após 24 horas de armazenamento o SE apresentou os menores valores de µSBS, não havendo diferença após 6 e 12 meses de armazenamento. A CHX não afetou os valores de µSBS. O modo de falha e a avaliação da nanoinfiltração foram analisados de forma descritiva. A nanoinfiltração da interface resina/dentina foi verificada em todos os grupos, havendo maior penetração da prata nos grupos de CHX. Um aumento no depósito de prata e decréscimo nos valores de µSBS foi notado em todos os grupos após 6 meses de armazenamento. A CHX e o MDPB não foram capazes de inibir a nanoinfiltração e o decréscimo na resistência de união. Conclui-se que a CHX não afetou a penetração dos sistemas adesivos na dentina desmineralizada, afetou a formação da camada híbrida, porém, não afetou os valores de resistência de união imediatos, que foram alterados pelo tempo de armazenamento, bem como a nanoinfiltração da prata na interface adesiva, após 6 e 12 meses. / Abstract: The objective of this Thesis, presented in two chapters, was to evaluate the effect of chlorhexidine-CHX and the antibacterial monomer 12-metacriloxydodecylpiridinium-MDPB on the bond strength and bonding degradation of the resin/demineralized dentin interface over twelve months of storage time. Chapter 1: The objective of this in vitro study was to evaluate the effect of CHX and/or different adhesive systems, in the penetration of monomers in demineralized dentin, as well as on the formation and thickness of the hybrid layer using Confocal Laser Scanning Microscopy (CLSM). Three adhesive systems were used: Clearfil SE Bond- (Kuraray), Clearfil Protect Bond - PB (Kuraray) and Adper Single Bond 2 - SB (3M/ESPE), and an antibacterial agent: 2% chlorhexidine solution (FGM) used for cavity disinfectant. Thirty sound third molars were randomly distributed into 6 groups according the adhesive systems SE, PB and SB, with or without previous CHX application. The middle dentin was exposed and the artificial caries lesion was developed with a carboxymethylcellulose acid gel previously the bonding procedure. CLSM images were analysed by the Analysis of Variance and Tukey's post hoc tests (P<0.05). The CHX and the MDPB did not interfere with the penetration of the adhesive systems in demineralized dentin. All the groups presented a hybrid layer formation, with significantly thicker and lower homogeneity in the SB groups, regardless of the CHX application. It was concluded that the CHX and the different adhesive system did not affect the penetration of monomers in the demineralized dentin. Only the adhesive system affected the thickness and homogeneity of hybrid layer. Chapter 2: The objective of this in vitro study was to evaluate the influence of CHX, MDPB and storage time in regard to the bond strength and the bonding degradation of resin/demineralized dentin interface by microshear (µSBS) and nanoleakage evaluation.Two adhesive systems were used: Clearfil SE Bond- SE (Kuraray), Clearfil Protect Bond- PB (Kuraray). One hundred twenty sound third molars were randomly distributed into 12 groups according to the adhesive systems, SE and PB, with or without previous CHX application on the bonding surface, and storage time of 24h, 6 and 12 months. The middle dentin was exposed and a artificial caries lesion was developed artificially. After 24h of storage, the SE groups presented the lower µSBS values, but they did not have statistical significant differences after 6 and 12 months of storage. The failure mode and the nanoleakage were evaluated descripitivelly. The nanoleakage of the resin/dentin interface was verified in all the groups, having a greater silver deposit in the CHX groups. An increase in the silver deposit and decrease in the µSBS values were noticed in all the groups after 6 months of storage. The CHX and the MDPB were not able to inhibit the nanoleakage and a decrease in bond strength. It was concluded that the CHX did not affect the penetration of the adhesive systems in the demineralized dentin, affected the hybrid layer formation, but it did not affect the imediate values of the bond strength, which were modified with the storage time, as was the nanoleakage in bonding interface, after 6 and 12 months. / Doutorado / Odontopediatria / Doutor em Odontologia

Orientador: Caio Cezar Randi Ferraz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T21:47:13Z (GMT). No. of bitstreams: 1 Santos_IvanaLins_M.pdf: 4446919 bytes, checksum: 906c2bb88c7bbc1591d2d43d0c214552 (MD5) Previous issue date: 2005 / Resumo: O presente trabalho avaliou, in vitra, a capacidade de remoção da smear layer das paredes dos canais radiculares após o preparo químico-mecânico realizado com diferentes substâncias químicas auxiliares. Selecionou-se 54 dentes humanos unirradiculares, com canais retos e ápices formados, divididos em grupos seguindo o protocolo de irrigação: G1: NaOCI 5,25% + EDTA 17%; G2: solução fisiológica 0,9%; G3: clorexidina (CLX) gel 2% pH neutro + solução fisiológica 0,9%; G4: CLX gel 2% pH neutro + solução fisiológica 0,9% + EDTA 17%; G5: CLX gel a 2% pH ácido + solução fisiológica 0,9% e G6: CLX gel a 2% pH ácido + solução fisiológica 0,9% + EDTA 17%. Os grupos foram instrumentados utilizando técnica manual híbrida, sendo analisadas quatro áreas distintas em cada terço do canal radicular: apical, médio e cervical, através do microscópio eletrônico de varredura (MEV) atribuindo escores de 0 a 3 de acordo com Gaberogllio & Becce (1994), considerando a capacidade de limpeza de cada substância. A análise estatística utilizou o software SPSS (Statistical Package for Social Sciences) e o teste não paramétrico de Mann-Whitney. Concluímos que a combinação das soluções de NaOCI a 5,25% e irrigação final com EDTA a 17% foi mais efetiva na remoção da smear layer das paredes dos canais radiculares quando comparado com as demais soluções testadas (p<0,05). O uso do gluconato de clorexidina gel a 2% com pH ácido + EDTA a 17% foi mais efetivo apenas quando comparado com a solução fisiológica e o gel de gluconato de clorexidina a 2% com pH neutro + solução fisiológica (p<0,05). A clorexidina gel neutra + solução fisiológica foi a que apresentou pior condição de limpeza das paredes dos canais radiculares. O terço apical apresentou condições de limpeza estatisticamente inferiores, independente das soluções testadas / Abstract: This in vitro study evaluted the effects of 2% chlorhexidine gel with acid pH on smear layer removal after chemomechanical debridement as endodontic irrigating solution. Fifty-four single-root extracted of human teeth were separated into six groups: G1: 5.25% NaOCI + 17% EDTA; G2: saline solution; G3: 2% chlorhexidine gel (CHX) neutral pH + saline solution; G4: 2% CHX gel neutral pH + saline solution + EDTA 17%; G5: 2% CHX gel acid pH + saline solution and G6: 2% CHX gel acid pH + Saline solution + EDTA 17%. After instrumentation using the respective irrigants, the root canais were examined by scanning electron microscopy in four differents areas in each third of the canal: apical, middle and carona!. The areas photographed were evaluated according to the rating system developed by Gaberoglio & Becce (1994). The data were analyzed using the Mann-Whitney test to determine whether there was any significant difference in the ability of the irrigating regimens to remove the smear layer. In the coronal and middle thirds, 5.25% NaOCI + 17% EDTA effectively removes the smear layer when compared with the others substances (p<0.05).In the coronal third, the 2% CHX gel acid pH + EDTA 17% were statistically more effective in removing the smear layer than with saline solution; 2% CHX gel neutral; 2% CHX gel acid pH (p<0.05). In the midlle third, this irrigant had the same result, except when compared with the 2% CHX gel acid pH alone. In the apical third, the difference was significant and better to the group flushed with 5.25% NaOCI + 17% EDTA compared with saline solution and 2% CHX gel neutral pH + saline solution / Mestrado / Endodontia / Mestre em Clínica Odontológica

Orientador: Alexandre Augusto Zaia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:37:13Z (GMT). No. of bitstreams: 1 Machado_JoseLecio_M.pdf: 638995 bytes, checksum: e590348fae76b970939ad0028be1c3d7 (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar radiograficamente a obturação de canais laterais artificialmente confeccionados em dentes humanos instrumentados com diferentes substâncias auxiliares e obturados pela técnica da condensação lateral. Dois canais laterais foram confeccionados no terço médio e no terço apical de 40 dentes com uma lima #10. Condensação lateral e o cimento AH Plus foram usados para a obturação dos canais radiculares e radiografias vestíbulo-linguais foram feitas. Diferentes soluções foram usadas para irrigar o canal: Gluconato de Clorexidina gel, Hipoclorito de Sódio, EDTA e Solução salina. Os resultados obtidos não demonstraram diferenças estatísticas. Concluímos que o uso de diferentes substâncias auxiliares no preparo químico-mecânico não influencia a obturação de canais laterais artificialmente confeccionados em dentes humanos quando avaliados radiograficamente / Abstract: The aim of this study was to evaluate if the presence of smear layer interfere the filling of artificial lateral canals. Two lateral canals were produced in the medium and apical third of 40 teeth roots with #10 files. Lateral condensation and AH-Plus sealer were used to fill the root canals and buccolingual radiographs were performed. Different solutions were used to irrigate the canal: Chlorhexidine Gluconate Gel; Sodium Hypochlorite, EDTA and Saline solution. The results did not show any statistical difference. It was concluded that no differences were found among the different substances in used the lateral condensation on the ability to obturated lateral canals artificially in human teeth, in same third or in same groups radiographically / Mestrado / Endodontia / Doutor em Clínica Odontológica

Orientador: Caio Cezar Randi Ferraz / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T21:19:10Z (GMT). No. of bitstreams: 1 Dametto_FabioRoberto_D.pdf: 5792903 bytes, checksum: e96494d5cbd4bb4a015b8039b5411709 (MD5) Previous issue date: 2006 / Resumo: Grande parte dos insucessos da terapia endodôntica está diretamente relacionada com a ausência ou confecção de uma inadequada restauração, propiciando assim, microinfiltração coronária e recontaminção do sistema de canais radiculares. Desta forma, este trabalho teve como objetivo avaliar a influência de substâncias químicas auxiliares ao tratamento endodôntico na resistência de união de um sistema adesivo à dentina profunda da câmara pulpar. Molares íntegros tiveram as coroas dentais seccionadas transversalmente 3mm acima da junção cemento-esmalte, expondo o assoalho da câmara pulpar. Os dentes foram divididos em 6 grupos e submetidos ao tratamento variando-se as substâncias químicas auxiliares, G1- Soro fisiológico, G2- EDTA 17%, G3- NaOCl 5,25%, G4- NaOCl 5,25% + EDTA 17%, G5- Clorexidina gel 2% e G6- Clorexidina líquida 2%, nas quais os espécimes foram mantidos imersos pelo período de 30 minutos. Posteriormente, 4mm da câmara pulpar foram preenchidos utilizando o sistema adesivo Single BondÒ (3M, St. Paul, MN, USA) e a resina composta Z250Ò cor B2 (3M, St. Paul, MN, USA). Vinte dentes de cada grupo foram submetidos a cortes seriados no sentido mésio-distal obtendo-se fatias de 1,0mm. Estas fatias foram divididas para confecção de entalhes na dentina do assoalho da câmara pulpar ou na interface de união dentina-resina do assoalho, obtendo-se uma constrição em forma de ampulheta, com área de aproximadamente 1,0mm2. Os espécimes foram submetidos ao ensaio de microtração para avaliação da alteração na resistência coesiva em dentina e resistência de união dentina-resina. Dez dentes foram submetidos ao teste de nanoinfiltração coronária com nitrato de prata. Os resultados foram avaliados estatisticamente e demonstraram não haver diferença significativa entre os grupos quanto a resistência coesiva da dentina. No entanto, a resistência de união dentina-resina foi menor (p<0,05) para os grupos que utilizaram EDTA 17%. Todos os grupos apresentaram um padrão de fratura tipicamente mista. O teste de nanoinfiltração não apresentou padrões diferentes entre os grupos avaliados em MEV, tendo a infiltração ocorrida apenas no trajeto dos túbulos que ficaram expostos ao agente traçador, não havendo também uma correlação entre a resistência de união e a nanoinfiltração. Conclui-se assim, que as substâncias químicas auxiliares testadas, com exceção do EDTA 17%, não promoveram alterações na resistência de união dentina-resina no assoalho da câmara pulpar / Abstract: Most of the endodontic treatment failure cases are directly related to inadequate or absent restoration, which leads to coronal microleakage and root canal system recontamination. Hence, the aim of this research was to evaluate the influence of chemical substances auxiliary to the endodontic treatment on the adhesive system adherence to the deep pulp chamber dentin. Crowns of intact molars were transversally sectioned at 3 mm above the enamel-cement junction, so that the pulp chamber floor was exposed. The teeth were divided in 6 groups according to the auxiliary chemical substance used during the treatment, G1- physiologic solution, G2 17% EDTA, G3 5.25%NaOCl, G4- 5.25% NaOCl + 17% EDTA, G5- 2% Chlorhexidine gel and G6- 2% Chlorhexidine solution. All specimens of all groups were immersed in the respective chemical substance for 30 minutes. Afterwards, 4 mm of the pulp chamber were filled with adhesive system Single Bond® (3M, St. Paul, MN, USA) and the compound resin Z250® B2 shade (3M, St. Paul, MN, USA). Twenty teeth of each group were serially cut from mesial to distal into 1.0 mm slices. These slices were trimmed to an hourglass shape cuts with a cross-sectional area of 1.0 mm2 on the dentin of the pulp chamber floor or in the dentin-resin bond interface of the pulp chamber floor. Microtensile tests were used on the slices to evaluate cohesive resistance alterations on dentin and resistanc e of the dentin-resin bond. Ten teeth were submitted to coronary nanoleakage tests with silver nitrate. The results were statistically analyzed and showed that there are no statistical significant differences between groups regarding the cohesive resistance of the dentin. However, the dentinresin bond was lower (p<0.05) in the 17% EDTA group. All groups showed a typically mixed fracture pattern. The nanoleakage test did not show different patterns between groups evaluated on the SEM, as the infiltration occurred only on the pathways of tubules exposed to the marker. Moreover, there was no correlation between union resistance and nanoleakage. In conclusion, the auxiliary chemical substances tested, except the 17% EDTA, did not influence the dentin-resin bond mechanism on the pulp chamber floor / Doutorado / Endodontia / Doutor em Clínica Odontológica