The X-band FMR has been employed to investigate the angular variation of resonance Fields of DC sputtered Co-Cr Films with different substrate temperatures. This angular variation has been Fitted with the classical uniaxial anisotropy crystal model and yields the values of 2K₁/M-4πM=-4∼-7 KOe, 4K₂ =-0.8∼0.8 KOe and g-factor = 2.3~2.8. The FMR measurments of the first anisotropy constant are quite different from the counterparts measured with VSM. This discrepancy is interpreted as a result of the formation of two ferromagnetic phases. With this simple model, the substrate temperature dependence of First anisotropy is explained and it is predicted that a lower substrate temperature will improve the Co-Cr Films for their potential application in perpendicular magnetic recording devices. The angular dependence of the FMR linewidth is discussed. / Science, Faculty of / Physics and Astronomy, Department of / Graduate

A longevidade da prótese e a saúde bucal de usuário de Prótese Parcial Removível (PPR) são muito dependentes de higiene apropriada. O objetivo deste estudo foi comparar o efeito de soluções de Ricinus communis, em diferentes concentrações, com soluções de peróxido alcalino e cloreto de cetilpiridínio, em relação à liga metálica de Cobalto Cromo (Co-Cr) que compõe a estrutura de PPR. A amostra do experimento foi composta por 55 espécimes de Co-Cr, confeccionados a partir de padrões de cera circulares (12 mm x 3 mm) obtidos a partir de uma matriz metálica. Os padrões foram fundidos, numerados aleatoriamente e divididos em 5 grupos de imersão: H2O- água deionizada (controle) (15 minutos); Rc 2%- Ricinus communis 2% (20 minutos), Rc 10% -Ricinus communis 10% (20 minutos), PA- peróxido alcalino (15 minutos) e CCP- cloreto de cetilpiridínio 0,500 mg (10 minutos). Os espécimes foram avaliados quanto à rugosidade de superfície (n=10) no início e após a simulação de 6 meses, 1, 2, 3, 4 e 5 anos tanto pelo microscópio confocal a laser (Sa, &micro;m), como também pelo rugosímetro de superfície (Ra, &micro;m). Um espécime de cada grupo foi analisado quanto à topografia de superfície (Microscopia Eletrônica de Varredura, MEV) e Espectrometria de Energia Dispersiva de Raios-X (EDS) antes e após simulação de uso por 5 anos. De acordo com os resultados obtidos (&alpha;=0,05) pela microscopia confocal (Sa), não houve diferença para o fator solução (Kruskal-Wallis); para o fator tempo (Friedman) houve diferença estatística em Rc 2% entre T0 e T1, T3, T4 e T6 (p<0,001) e em Rc 10% de T2 para T3 (p=0,007), com diminuição da rugosidade. Com o rugosímetro (Ra), houve diferença estatística (Kruskal- Wallis) para CCP que apresentou menor rugosidade em relação à Rc 10% em T1 (p=0,048) e T6 (p=0,013). Em relação ao tempo (Friedman), a água propiciou diminuição da rugosidade superficial (Ra) de T0 para T2 (p=0,013). Na análise de MEV e EDS podese verificar que as soluções não apresentaram efeitos deletérios sobre as superfícies. Conclui-se que embora tenha sido encontrada diferença estatística para a rugosidade, os resultados são clínicamentes aceitáveis. Deste modo, todas as soluções podem ser utilizadas com segurança pelo período de 5 anos. / Denture longevity and oral health of Removable Partial Denture (RPD) user are highly dependent on proper hygiene. The aim of this study was to compare the effect of solutions of Ricinus communis, in different concentrations, with solutions of alkaline peroxide and cetylpyridinium chloride 0.500 mg, in relation to the Cobalt Chromium (Co-Cr) alloy that composes the structure of RPD. The sample of the experiment consisted of 55 specimens of Co-Cr, made from circular wax patterns (12 mm x 3 mm) obtained in a metal matrix. The patterns were cast, randomly enumerated and divided into 5 immersion groups: H2Odeionized water (control) (15 minutes); Rc 2%- Ricinus communis 2% (20 minutes), Rc 10% -Ricinus communis 10% (20 minutes), PA-alkaline peroxide (15 minutes) and CCPcetylpyridinium chloride 0.500 mg (10 minutes). The specimens were evaluated for surface roughness (n = 10) at the beginning and after the simulation of 6 months, 1, 2, 3, 4 and 5 years by the laser confocal microscope (Sa, &micro;m) and by the rugosimeter of surface (Ra, &micro;m). One specimen from each group was analyzed for surface topography (Scanning Electron Microscopy, SEM) and Energy-dispersive X-ray spectroscopy (EDS) befofe and after simulation of use for 5 years. According to the results obtained (&alpha;= 0.05) by confocal microscopy (Sa), there was no difference for the solution factor (Kruskal- Wallis); For the time factor (Friedman) there was a statistical difference in Rc 2% in T0 to T1, T3, T4 and T6 (p <0.001) and Rc 10% in T2 to T3 (p = 0.007), with decrease in roughness. With the the rugosimeter (Ra), there was a statistical difference (Kruskal- Wallis) for CCP that presented less roughness in relation to the Rc 10% in T1 (p = 0.048) and T6 (p = 0.013). In relation to the time, (Friedman) the water caused a reduction of surface roughness (Ra) between T0 and T2 (p = 0.013). In the analysis of SEM and EDS it can be verified that the solutions did not present deleterious effects on the surfaces. It was concluded that although a statistical difference was found for roughness, the results are clinically acceptable. Thus, all solutions can be safely used for a period of 5 years.

Made available in DSpace on 2014-12-17T14:07:01Z (GMT). No. of bitstreams: 1 HarrisonAD.pdf: 3488100 bytes, checksum: 805801db06d21e5667735d16a5799fe2 (MD5) Previous issue date: 2008-05-30 / The cobalt-chromium alloy is extensively used in the Odontology for the confection of metallic scaffolding in partial removable denture. During the last few years, it has been reported an increasing number of premature imperfections, with a few months of prosthesis use. The manufacture of these components is made in prosthetic laboratories and normally involves recasting, using parts of casting alloy and parts of virgin alloy. Therefore, the objective of the present study was to analyze the mechanical properties of a commercial cobalt-chromium alloy of odontological use after successive recasting, searching information to guide the dental prosthesis laboratories in the correct manipulation of the cobalt-chromium alloy in the process of casting and the possible limits of recasting in the mechanical properties of this material. Seven sample groups were confectioned, each one containing five test bodies, divided in the following way: G1: casting only with virgin alloy; G2: casting with 50% of the alloy of the G1 + 50% of virgin alloy; G3: casting with 50% of the alloy of the G2 + 50% of virgin alloy; G4: casting with 50% of the alloy of the G3 + 50% of virgin alloy; G5: 50% of alloy of the G4 + 50% of virgin alloy; G6: 50% of alloy of the G5 + 50% of virgin alloy and finally the G7, only with recasting alloy. The modifications in the mechanical behavior of the alloy were evaluated. Moreover, it was carried the micro structural characterization of the material by optic and electronic scanning microscopy, and X ray diffraction.and fluorescence looking into the correlatation of the mechanical alterations with structural modifications of the material caused by successive recasting process. Generally the results showed alterations in the fracture energy of the alloy after successive recasting, resulting mainly of the increasing presence of pores and large voids, characteristic of the casting material. Thus, the interpretation of the results showed that the material did not reveal significant differences with respect to the tensile strength or elastic limit, as a function of successive recasting. The elastic modulus increased from the third recasting cycle on, indicating that the material can be recast only twice. The fracture energy of the material decreased, as the number of recasting cycles increased. With respect to the microhardness, the statistical analyses showedno significant differences. Electronic scanning microscopy revealed the presence of imperfections and defects, resulting of the recasting process. X ray diffraction and fluorescence did not show alterations in the composition of the alloy or the formation of crystalline phases between the analyzed groups. The optical micrographs showed an increasing number of voids and porosity as the material was recast. Therefore, the general conclusion of this study is that the successive recasting of of Co-Cr alloys affects the mechanical properties of the material, consequently leading to the failure of the prosthetic work. Based on the results, the best recommendadition is that the use of the material should be limited to two recasting cycles / Ligas cobalto-cromo s?o extensivamente utilizadas na Odontologia para a confec??o de arma??es met?licas em pr?teses parciais remov?veis. Durante os ?ltimos anos, tem sido reportado um n?mero crescente de falhas prematuras, com poucos meses de utiliza??o das pr?teses. A fabrica??o desses componentes ? feita em laborat?rios prot?ticos e normalmente envolve a refundi??o, utilizando partes de liga fundida e partes de liga virgem. Portanto, o objetivo do presente estudo foi analisar as propriedades mec?nicas de uma liga comercial de cobalto-cromo de uso odontol?gico ap?s sucessivas refundi??es, buscando informa??es no sentido de orientar os laborat?rios de pr?tese dent?ria na correta manipula??o dessa liga no processo de fundi??o e nos poss?veis limites de refundi??o desse material. Foram confeccionados sete grupos de amostras, cada um contendo cinco corpos de prova, divididos da seguinte maneira: G1: fundi??o apenas com liga virgem; G2: fundi??o com 50% da liga do G1 + 50% de liga virgem; G3: fundi??o com 50% da liga do G2 + 50% de liga virgem; G4: fundi??o com 50% da liga do G3 + 50% de liga virgem; G5: 50% de liga do G4 + 50% de liga virgem; G6: 50% de liga do G5 + 50% de liga virgem e finalmente o G7, s? com liga refundida. Foram avaliadas as principais modifica??es ocorridas no comportamento mec?nico dessa liga por meio de ensaios de tra??o e microdureza. Al?m disso, foi realizada a caracteriza??o microestrutural do material por meio de microscopia ?ptica e eletr?nica de varredura, difra??o e fluoresc?ncia de raios X procurando correlacionar as altera??es mec?nicas com modifica??es estruturais do material ocasionadas pelos sucessivos processos de refundi??o. De forma geral os resultados mostraram altera??es na plasticidade e energia de fratura da liga ap?s sucessivas refundi??es, decorrentes principalmente da crescente presen?a de poros e vazios, defeitos caracter?sticos da fundi??o do material. A interpreta??o dos resultados permitiu concluir que o material n?o apresentou diferen?as significativas em rela??o ? resist?ncia ? tra??o ou ao limite el?stico, em fun??o das sucessivas refundi??es. A energia de fratura do material mostrou tend?ncia ? diminui??o, ? medida que o material foi refundido. Em rela??o ? microdureza, as an?lises estat?sticas mostraram n?o haver diferen?as significativas. A microscopia eletr?nica revelou a presen?a de falhas e defeitos, resultantes dos processos de refundi??es. A an?lise por fluoresc?ncia e difra??o de raios X n?o mostrou altera??es na composi??o da liga ou na forma??o de fases cristalinas entre os grupos analisados. As micrografias ?pticas mostraram um crescente n?mero de vazios e aumento da porosidade ? medida que o material foi refundido. Assim, a conclus?o geral do trabalho ? que as sucessivas refundi??es em ligas de Co-Cr comprometem as propriedades mec?nicas do material, o que pode levar a falhas e consequentemente, ao fracasso do trabalho prot?tico. Com base nos resultados, o mais recomendado ? a utiliza??o de no m?ximo duas refundi??es, para que as propriedades do material n?o sejam comprometidas

A longevidade da prótese e a saúde bucal de usuário de Prótese Parcial Removível (PPR) são muito dependentes de higiene apropriada. O objetivo deste estudo foi comparar o efeito de soluções de Ricinus communis, em diferentes concentrações, com soluções de peróxido alcalino e cloreto de cetilpiridínio, em relação à liga metálica de Cobalto Cromo (Co-Cr) que compõe a estrutura de PPR. A amostra do experimento foi composta por 55 espécimes de Co-Cr, confeccionados a partir de padrões de cera circulares (12 mm x 3 mm) obtidos a partir de uma matriz metálica. Os padrões foram fundidos, numerados aleatoriamente e divididos em 5 grupos de imersão: H2O- água deionizada (controle) (15 minutos); Rc 2%- Ricinus communis 2% (20 minutos), Rc 10% -Ricinus communis 10% (20 minutos), PA- peróxido alcalino (15 minutos) e CCP- cloreto de cetilpiridínio 0,500 mg (10 minutos). Os espécimes foram avaliados quanto à rugosidade de superfície (n=10) no início e após a simulação de 6 meses, 1, 2, 3, 4 e 5 anos tanto pelo microscópio confocal a laser (Sa, &micro;m), como também pelo rugosímetro de superfície (Ra, &micro;m). Um espécime de cada grupo foi analisado quanto à topografia de superfície (Microscopia Eletrônica de Varredura, MEV) e Espectrometria de Energia Dispersiva de Raios-X (EDS) antes e após simulação de uso por 5 anos. De acordo com os resultados obtidos (&alpha;=0,05) pela microscopia confocal (Sa), não houve diferença para o fator solução (Kruskal-Wallis); para o fator tempo (Friedman) houve diferença estatística em Rc 2% entre T0 e T1, T3, T4 e T6 (p<0,001) e em Rc 10% de T2 para T3 (p=0,007), com diminuição da rugosidade. Com o rugosímetro (Ra), houve diferença estatística (Kruskal- Wallis) para CCP que apresentou menor rugosidade em relação à Rc 10% em T1 (p=0,048) e T6 (p=0,013). Em relação ao tempo (Friedman), a água propiciou diminuição da rugosidade superficial (Ra) de T0 para T2 (p=0,013). Na análise de MEV e EDS podese verificar que as soluções não apresentaram efeitos deletérios sobre as superfícies. Conclui-se que embora tenha sido encontrada diferença estatística para a rugosidade, os resultados são clínicamentes aceitáveis. Deste modo, todas as soluções podem ser utilizadas com segurança pelo período de 5 anos. / Denture longevity and oral health of Removable Partial Denture (RPD) user are highly dependent on proper hygiene. The aim of this study was to compare the effect of solutions of Ricinus communis, in different concentrations, with solutions of alkaline peroxide and cetylpyridinium chloride 0.500 mg, in relation to the Cobalt Chromium (Co-Cr) alloy that composes the structure of RPD. The sample of the experiment consisted of 55 specimens of Co-Cr, made from circular wax patterns (12 mm x 3 mm) obtained in a metal matrix. The patterns were cast, randomly enumerated and divided into 5 immersion groups: H2Odeionized water (control) (15 minutes); Rc 2%- Ricinus communis 2% (20 minutes), Rc 10% -Ricinus communis 10% (20 minutes), PA-alkaline peroxide (15 minutes) and CCPcetylpyridinium chloride 0.500 mg (10 minutes). The specimens were evaluated for surface roughness (n = 10) at the beginning and after the simulation of 6 months, 1, 2, 3, 4 and 5 years by the laser confocal microscope (Sa, &micro;m) and by the rugosimeter of surface (Ra, &micro;m). One specimen from each group was analyzed for surface topography (Scanning Electron Microscopy, SEM) and Energy-dispersive X-ray spectroscopy (EDS) befofe and after simulation of use for 5 years. According to the results obtained (&alpha;= 0.05) by confocal microscopy (Sa), there was no difference for the solution factor (Kruskal- Wallis); For the time factor (Friedman) there was a statistical difference in Rc 2% in T0 to T1, T3, T4 and T6 (p <0.001) and Rc 10% in T2 to T3 (p = 0.007), with decrease in roughness. With the the rugosimeter (Ra), there was a statistical difference (Kruskal- Wallis) for CCP that presented less roughness in relation to the Rc 10% in T1 (p = 0.048) and T6 (p = 0.013). In relation to the time, (Friedman) the water caused a reduction of surface roughness (Ra) between T0 and T2 (p = 0.013). In the analysis of SEM and EDS it can be verified that the solutions did not present deleterious effects on the surfaces. It was concluded that although a statistical difference was found for roughness, the results are clinically acceptable. Thus, all solutions can be safely used for a period of 5 years.