Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T01:41:39Z (GMT). No. of bitstreams: 1 Pacheco_JoaoFelipeMota_D.pdf: 4282811 bytes, checksum: 41703a5d88ddb80855223eb94057a90b (MD5) Previous issue date: 1997 / Resumo: O objetivo deste estudo foi avaliar a influência de diferentes tratamentos na superfície do polímero de vidro Artglass (HERAEUS, Kulzer - Germany). Foi verificado também o efeito do agente de silanização (Porcelain Primer - BISCO, lnc. ltasca IL), do ativador superficial de compósitos (Composite Activator BISCO, lnc. ltasca IL) e do líquido para reparos do sistema Artglass na resistência à tração com o sistema adesivo All Bond 2 (BISCO, lnc. ltasca IL) associado ao cimento Choice Porcelain Venner System (BISCO, lnc. ltasca IL). Foram confeccionadas duzentos e quarenta amostras e divididas em 12 grupos com 20 amostras cada. Cada grupo foi submetido aos seguintes tratamentos: grupo 1 - jateamento com óxido de alumínio; grupo 2 - jateamento com óxido de alumínio e aplicação do Porcelain Primer; grupo 3 jateamento com óxido de alumínio e aplicação do Composite Activator; grupo 4 - jateamento com óxido de alumínio e aplicação do Artglass Liquid; grupo 5 - condicionamento com ácido fosfórico; grupo 6 - condicionamento com ácido fosfórico e aplicação do Porcelain Primer; grupo 7 - condicionamento com ácido fosfórico e aplicação do Composite Activator; grupo 8 condicionamento com ácido fosfórico e aplicação do Artglass Liquid; grupo 9 - condicionamento com ácido fluorídrico; grupo 10 - condicionamento COIIJ ácido fluorídrico e aplicação do Porcelain Primer; grupo 11 - condicionamento com ácido fluorídrico e aplicação do Composite Activator; grupo 12 - condicionamento com ácido fluorídrico e aplicação do Artglass Liquid. Após o tratamento, as amostras foram unidas em pares com auxílio do sistema adesivo e do cimento resinoso manipulados de acordo com as instruções do fabricante. Em seguida, os corpos-de-prova foram armazenados a 37 'GRAUS'C com umidade relativa do ar em 100%, durante 24 horas e, logo após, foram submetidos a 500 ciclos térmicos ajustados às temperaturas de 5'GRAUS'C, 37°C e 60°C, com duração de 30 segundos cada. Decorrido o período de 48 horas, os corpos-de-prova foram submetidos ao ensaio de tração em uma máquina de ensaio universal (Otto Wolpert Werke, Germany), a uma velocidade de 6 mm/minuto. As médias dos resultados obtidos foram: grupo 1 - 11,46 MPa; grupo 2 - 12,28 MPa; grupo 3 - 9,45 MPa, grupo 4 - 11,53 MPa; grupo 5 - 3,83 MPa; grupo 6 - 4,84 MPa; grupo 7 - 3,94 MPa; grupo 8 - 5,67 MPa; grupo 9 - 6,51 MPa; grupo 10 - 6,36 MPa; grupo 11 - 7,86 MPa; grupo 12 - 8,34 MPa. A seguir os resultados foram submetidos análise de variância e ao Teste de Tukey. Após os testes de resistência à tração as amostras foram examinadas em lupa estereoscópica com aumento de 16 vezes, onde foi verificado predomínio de fraturas coesivas do polímero de vidro para os grupos tratados com jateamento com óxido de alumínio. O efeito dos tratamentos de superfície foi analisado com auxílio de um microscópio eletrônico de varredura (Zeiss DSM 960, Germany). Os resultados indicaram que o maior valor de resistência de união foi obtido através do jateamento com óxido de alumínio associado ao agente de silanização. Nos demais grupos onde também foi realizado o jateamento com óxido de alumínio os valores de resistência de união foram superiores e diferentes estatisticamente, quando comparados aos outros grupos, com exceção da associação do ácido fluorídrico com o Composite Activator, que não diferiu do grupo 3. A análise através de M.E.V. das superfícies tratadas demonstrou um padrão morfológico mais favorável ao imbricamento micromecânico produzido com o jateamento com óxido de alumínio / Abstract: The purpose of this study was to evaluate the influence of different superficial treatment of glass polymeric material Artglass (Heraeus, Kulzer). The effect of the silane agent application (Porcelain Primer - Bisco, lnc., ltasca, IL), a superficial Composite activator mixture (Composite Activator - Disco, Inc., ltasca, lL) and also the Artglass Liquid was verified in the tensile strength with adhesive system AllBond 2 (Bisco, lnc., !tasca, lL) associated with the resin cement Choice Porcelain Venner System (Bisco, lnc., !tasca, IL). Two hundred and torty samples were made and divided into 12 groups. Each group contained 20 samples submitted to treatments: Group 1 sandblasting with aluminum oxide; Group 2 - sandblasting with aluminum oxide and Porcelain Primer application; Group 3 - sandblasting with aluminum oxide and Composite Activator application; Group 4 - sandblasting with aluminum oxide and Artglass liquid application; Group 5 - acid etching with phosphoric acid; Group 6 - acid etching with phosphoric acid and Porcelain Primer application; Group 7 - acid etching with phosphoric acid and Composite Activator application; Group 8 acid etching with phosphoric acid and Artglass Liquid application; Group 9 acid etching with hydrofluoridric acid; Group 10 - acid etching with hydrofluoridric acid and Porcelain Primer application; Group 11 - acid etching with hydrotluoridric acid and Composite Activator application; Group 12 - acid etching with. hydrofluoridric acid and Artglass Liquid application. Following the treatment, the samples were bonded into pairs with the adhesive system and the resin cement, applied according with the manufacturer's instructions. Then, the samples were stored in 37° with a relative humidity of 100% during 24 hours. Submitted into 500 thermal circles, adjusted to 5 'DEGREE'C, 37 'DEGREE'C and 60'DEGREE'C, lasting 30 second each. After 48 hours, the samples were submitted to a tensile strength test in a Universal test machine (Otto Wolpert Werke, Germany) with a crosshead speed 6 mm / minute. The average results were : Group 1 - 11,46 MPa; Group 2 - 12,28 MPa; Group 3 - 9,45 MPa; Group 4 - 11,53 MPa; Group 5 - 3,83 MPa; Group 6 - 4,84 MPa; Group 7 - 3.94 MPa; Group 8 - 5,67 MPA; Group 9 - 6,51 MPA; Group 10 6,36 MPa; Group 11 - 7,86 MPa; Group 12 - 8,34 MPa. ThereFore, the results were submitted to Anova and Tukey Test. Then the samples were examined in a stereoscopic magnifying glass (x16), where it was verified the prevailing of cohesive rupture of the Glass Polymer in the groups treated with aluminum oxide sandblasting. The efFect of the superficial treatments was analyzed by a Scanning Electron Microscopy. The results indicated that sandblasting with aluminum oxide associated with the silane agent attained the biggest value of the bond strength. ln groups where the aluminum oxide sandblasting was performed the values presented were higher and statistically significant comparing with the others groups, except the association between hydrotluoridric acid and Composite Activator, which did not differ from group 3. The analysis of the treated surface was made using the Scanning Electron Microscopy and showed a more suitable morphologic pattem to the micromechanic retention produced with aluminum oxide sandblasting / Doutorado / Doutor em Materiais Dentários

Orientador: Vitor Antonio Ducatti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-04T21:28:54Z (GMT). No. of bitstreams: 1 Coelho_RivaldoTeodoro_M.pdf: 3250291 bytes, checksum: b2bb15d8a20d152e3701aa42810cff85 (MD5) Previous issue date: 2005 / Resumo: O principal objetivo desta dissertação foi a determinação das principais propriedades mecânicas de um compósito à base de cimento Portland CP-V-ARI (alta resistência inicial) tendo como agregado os grãos reciclados aglutinados de polipropileno (GRAP). A escolha do plástico se deve ao fato de que é um dos principais materiais utilizados pela indústria em geral sendo descartado em média na proporção de 7% do peso e 25% do volume do lixo urbano metropolitano e índice de reciclagem de 17,5%. No caso específico do polipropileno a proposta de seu uso deveu-se ao fato dele ser um dos três plásticos mais consumidos e descartados no Brasil, tornando-se oportuno o desenvolvimento de alternativas para a reciclagem deste material como material para a construção civil como agregado para o concreto. Neste estudo, foram realizados ensaios com base nas normas da ABNT ¿ Associação Brasileira de Normas Técnicas, para a caracterização do concreto no estado endurecido, principalmente para a determinação das resistências à compressão axial e diametral, resistência à tração na flexão e módulo de elasticidade secante. Os resultados obtidos em ensaios com misturas com e sem agregados minerais (substituição) foram satisfatórios permitindo o desenvolvimento de vários concretos com resistência à compressão axial (fcj) adequado para a produção de elementos pré-fabricados, concretos porosos adequados para drenagens e enchimento de lajes, painéis, blocos de concreto e grãos de polipropileno mineralizados com a pasta de cimento, dentre outras aplicações. Houve uma redução superior a 30% do peso final do concreto por meio da redução da massa específica. O novo concreto também se mostrou extremamente dúctil, adequado para especificações de absorção de impactos. Através dos resultados desta pesquisa pôde-se concluir que é perfeitamente viável o uso do concreto com grãos de polipropileno em substituição aos agregados minerais na construção civil / Abstract: The main objective of this dissertation was the determination of the main mechanical properties of a composite based on Portland cement CP-V-ARI (high initial resistance) tends as aggregate the grains recycled agglutinated of polypropylene (GRAP). The choice of the plastic is due to the fact that it is one of the main materials used by the industry in general being discarded on average in the proportion of 7% of the weight and 25% of the volume of the metropolitan urban garbage and index of recycling of 17,5%. In the specific case of the polypropylene the proposal of his use was due to his fact to be one of the three plastics more consumed and discarded in Brazil and that indicators reveal the need to develop alternatives for the recycling of this material in the engineering and in the building site as an aggregate for the concrete seeking the partial or total substitution of minerals aggregates. In this study, rehearsals were accomplished with base in the norms of ABNT - Brazilian Association of Technical Norms, for the characterization of the concrete in the hardened state, mainly for the determination of the resistances to the axial and diametrical compression, resistance to the traction in the flexing and module of drying elasticity. The results obtained in rehearsals with mixtures with and without aggregates minerals (substitution) they were satisfactory allowing the development of several concretes with resistance to the axial compression (fcj), through appropriate mixtures to the production of prefabricated elements, an appropriate porous concrete for drainages and stuffing of flagstones and polypropylene grains mineralized with the cement paste, among other applications. There was a superior reduction to 30% of the final weight of the concrete through the reduction of the specific mass. The new concrete was also shown extremely ductile, appropriate for specifications of absorption of impacts. Through the results of this research it could be concluded that it is perfectly viable the use of the concrete with polypropylene grains in substitution to the mineral aggregates in the building site / Mestrado / Edificações / Mestre em Engenharia Civil