Made available in DSpace on 2017-06-01T17:57:31Z (GMT). No. of bitstreams: 1 dissertacao_clerio_bezerra.pdf: 3171938 bytes, checksum: 2c69909d4369b39648102f2f200d89ec (MD5) Previous issue date: 2011-06-13 / The corrosion by chlorides is considered by a number of researchers the most dangerous pathological manifestation attacking concrete reinforcements. The assessment of the attacks to the structure by sodium chloride is usually done in the laboratory, takes too long and costs too much. The.main reason for this work is to assess the presence of free chlorides in Portland cement concrete and mortar through the silver nitrate aspersion method, which is justified by the fact that Our objective is to evaluate the applicability of the silver nitrate aspersion method in loco, in Portland-cement-based materials as indicators capable of showing the presence or not of contamination by chlorides, avoiding the immediate need for lab tests. So as to give credibility to the test for presence of free chlorides in the samples, these were checked by means of electrochemical tests in parallel with the silver nitrate aspersion. The experimental results of these tests showed that the applicability of the silver nitrate aspersion method seems to be of great relevance in the technical environment, as it is a qualitative method, easily applicable, inexpensive and capable of providing quick information so that professionals can safely diagnose the levels of chloride corrosion in the structures / A corrosão por cloretos é considerada por muitos pesquisadores a mais severa das manifestações patológicas que atacam as armaduras. O objetivo principal deste trabalho é avaliar a presença de cloretos livres em concreto de cimento Portland pelo método de aspersão de solução de nitrato de prata. A verificação de ataque por cloreto na estrutura é normalmente feita através de exames laboratoriais, demorados em que apresentam um custo muito alto. Pesquisando a aplicabilidade do método de aspersão de nitrato de prata in loco, em materiais à base de cimento Portland como indicador com capacidade de informar a presença ou não de contaminação por cloretos, evitando assim de imediato o teste laboratorial. Para que os resultados destes ensaios tivessem credibilidade quanto à presença de cloretos livres nas amostras, foi realizado, paralelamente à aspersão de nitrato de prata, um acompanhamento das amostras através de ensaios eletroquímicos. Observou-se com os resultados experimentais da pesquisa que a aplicabilidade do método de aspersão de solução de nitrato de prata vem a ser de grande relevância para o meio técnico, por ser um método qualitativo, de fácil aplicação, barato e provendo informações rápidas para que os profissionais da área de engenharia possam diagnosticar com segurança as estruturas com corrosão contaminadas por cloreto

Made available in DSpace on 2017-06-01T17:57:32Z (GMT). No. of bitstreams: 1 Ronaldo Pontes.pdf: 4668306 bytes, checksum: 48d4fe1ec07bae512f5d789ae55d9ec8 (MD5) Previous issue date: 2006-03-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Exposing concrete structures to the saline mist, they can suffer chlorides attacks and could cause reinforcement corrosion. The structures parts with faces directed to dominant winds are more susceptible, especially those with great surface in relation to the volume, such as pillars and beams. This work objective is to evaluate the level of marine aggressiveness, in marine edge of Boa Viagem quarter, Recife-PE, in function of the distance to the sea, measuring the value of chloride deposition, using the wet candle method, with the support of the environment management. The results indicate that chloride ions reach surface structure in different levels of concentration, depending on the distance from its origin, in this case, the sea. The conclusion is that chloride deposition decreases, in an exponential relation, when there is an increase of the distance to the sea, and that aggressiveness is significantly as far as 400 m from the marine edge / Diante da exposição à névoa salina, as estruturas em concreto podem sofrer ataques por cloretos, provocando corrosão das armaduras. As peças com faces voltadas aos ventos dominantes estão mais suscetíveis, especialmente aquelas que possuem grande superfície em relação ao volume, como são os casos de pilares e vigas. Este trabalho tem como objetivo avaliar os níveis de agressividade marinha, na orla marítima do Bairro de Boa Viagem, Recife-PE, em função de sua distância em relação ao mar, medindo a taxa de deposição de cloretos, pelo método da vela úmida, tendo como apoio o monitoramento do ambiente. Os resultados indicam que os íons cloreto chegam à superfície das estruturas a distintos níveis de concentração, dependendo da distância em relação à sua fonte geradora, no caso, o mar. Conclui-se que a deposição de cloretos decresce, numa relação do tipo exponencial, à medida que há um aumento do distanciamento em relação ao mar, e que a agressividade é significativa até 400 m da orla marítima

Submitted by Biblioteca Central (biblioteca@unicap.br) on 2018-04-11T18:44:16Z No. of bitstreams: 2 adriana_maria_monteiro_passos.pdf: 4108061 bytes, checksum: 98b74cf5e2d768af7917f11d7e580f90 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-04-11T18:44:16Z (GMT). No. of bitstreams: 2 adriana_maria_monteiro_passos.pdf: 4108061 bytes, checksum: 98b74cf5e2d768af7917f11d7e580f90 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2013-06-03 / Urban concrete or reinforced concrete structures built in saline environments, under either intermittent or continuous sea water exposure, usually present mechanical wear and structure pathology problems that require relentless maintenance care. Currently, Brazil has a large number of civil construction equipment and buildings under direct or near direct contact with the sea and the city of Recife, Pernambuco State capital, for one, figures among the top most exposed cities in terms of number of urban equipment in contact with sea water, including buildings, bridges, mooring sites, footbridges, piers, i.e., design projects that essentially imply concrete structures located under diverse marine exposure conditions such as underwater or partially submersed structures, or structures located in tidal zones or areas under mist or sea water splash environments. Sea water carries rather high chloride ion contents, hence making those exposed structures especially vulnerable. A chloride penetration study was carried out according to ISO TC 71/SC 1 (07/26/2010 release), ISO/WD 1920-11, ISO TC 71/SC 1/WG SII, and Brazilian ABNT NBR 12655 standards. Concrete core samples of several strength levels were kept partially submerged in sea water; chloride ion contents and penetration depths were recorded. Furthermore, a number of chemical analyses have been conducted in order to estimate chloride contents present at several depths in various concrete samples prepared with several W/C ratios, hence with different strength values. According to what one might expect, laboratory assays indicated that the deeper the axial sample taken from the exposed core for analysis and the more concentrated the concrete Water/Cement ratio, the lower the chloride penetration. Therefore, the chloride ion penetration rate indeed decreases as the W/C ratio gets richer, when compared to average and poor W/C ratios for all sampled penetration depths analyzed. / Em cidades que estão sujeitas a essa exposição salina, as construções de concreto ou concreto armado, ora em contato com água do mar ora não, ou à vontade dos mares sempre sofrem patologias e desgastes mecânicos; que exigem permanente manutenção. O Brasil atualmente; possuí vários equipamentos e construções que estão em contato direto ou semidireto com o mar. Recife capital de Pernambuco, é uma das cidades que mais tem equipamentos urbanos em contato com a água do mar. Edifícios, pontes, ancoradouros, passarelas, piers, enfim projetos que determinam estruturas em concreto em ambiente marítimo: ambientes de zona submersa, parcialmente submersa, zona de maré, zona de respingo e zona de névoa. As águas do mar contem elevada quantidade de íons de cloretos; e essa exposição torna mais vulnerável essas estruturas de concreto. Esta dissertação pesquisou e estudou a penetração de cloretos, de acordo com parametros da ISO TC 71/SC 1 de 26/07/2010, ISO/WD 1920-11, ISO TC 71/SC 1/WG SII, e a ABNT NBR 12655, experimentando corpos de prova de concreto, de diferentes resistèncias que ficaram parcialmente imersos em água do mar; verificando quantidade e a profundidade de penetração de íons de cloretos. Portanto, o principal objetivo deste trabalho foi, através de ensaios quimicos, a definição do quantitativo de íons de cloretos em exemplares com concreto de traços de diferentes resistências, à diferentes profundidades. De acordo com as expectativas, verificou-se com os ensaios em laboratórios que quanto e mais rico o traço de concreto, acontece menor quantidade de penetração de íons de cloretos. Portanto se pode dizer que o percentual de penetração de íons cloreto é menor para o traço rico, em relação ao traço médio e o pobre em todas as perfurações feitas nos corpos de prova estudados.

No description available.

No description available.

Rebar corrosion in reinforced concrete structures is a big issue to technical studies, because it has, besides the maintenance costs, indirect costs which affect bridges and building users. Corrosion inhibitors are chemical substances that added to concrete reduce or retard rebar corrosion. In this thesis we described the behavior of sodium molybdate and thiourea used as corrosion inhibitors (CI) for concrete mixes submitted to chloride medium. Calcium hydroxide solution, cement paste, mortar and concrete were used to understand corrosion inhibitors effects on their properties. Dosage study was performed using solutions, with and without the CI, applying cyclic voltammetry and steady-state polarization. Effects on cement paste and concrete were studied using four different dosages of the proposed CI and two commercial products, two different cements and silica fume as supplementary cementitious material. Concretes mixes were tested by workability, compression strength and resistance to chloride penetration, using ASTM C 1202 and ASTM C 1543. ASTM G 109 was used as standard to determine CI efficiency on corrosion inhibition and two techniques were used to determine concrete electrical resistivity: electrochemical impedance spectroscopy and conductivimetry. The proposed inhibitors showed, in 2% sodium molybdate and 0,67% thiourea, slight effects on concrete properties and good effects on improving the resistance to chloride penetration and to corrosion due chloride ions. / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A corrosão de armaduras de concreto armado em pontes, viadutos e edifícios tem preocupado o meio técnico, pois além do custo de manutenção, há o custo indireto devido à quedas de estruturas, interdições e incômodos causados aos usuários. Entre os métodos para minimizar a corrosão, podem ser citados os inibidores de corrosão, os quais são adicionados ao concreto e atuam na interface concreto/aço, diminuindo a taxa de corrosão. Neste trabalho, são relatados os estudos do comportamento de inibidores de corrosão à base de molibdato de sódio e tiouréia, aplicados em concretos submetidos à ação de íons cloreto e comparados a dois inibidores comerciais. Foram realizados estudos em solução e em pastas, argamassas e concretos, com dois cimentos diferentes, sem e com adição de 5 e 10% de sílica ativa. A determinação das dosagens de inibidores foi feita em solução saturada de hidróxido de cálcio, utilizando técnicas eletroquímicas como polarização em estado quase-estacionário e voltametria cíclica. Foram estudados os efeitos dos inibidores propostos, em várias dosagens, e de dois inibidores comerciais, nas propriedades de pastas e concretos sem e com sílica ativa. Além da trabalhabilidade e da resistência à compressão, foi testada a resistência à penetração de cloretos pelos métodos ASTM C 1202 e ASTM C 1543. A avaliação da eficiência frente à corrosão provocada por íons cloreto seguiu a norma ASTM G 109. A resistividade elétrica foi determinada utilizando espectroscopia de impedância eletroquímica e condutivimetria. Os inibidores propostos, nas concentrações de 2% de molibdato de sódio e 0,67% de tiouréia, mostraram resultados bastante promissores, tanto na avaliação quanto à influência sobre as propriedades físicas e mecânicas do concreto, quanto à diminuição da penetração de cloretos e eficiência na inibição da corrosão.

No description available.

The dissertation thesis is focused on practical use of composite material with modified cement matrix. Especially the area of electrical behavior of composite materials in use has been examined, for strain sensing material. The experimental part solves the problematics of corrosion of carbon and metallic materials in alkaline environment of the cement matrix. The physical design of the sensor and its fabrication using functional composite cement material have been described here. The thesis has also discussed defining the influence of temperature change and humidity change on the change of electrical parameters of integrated sensors. An important part of the thesis is the area of evaluating a series of measurements of electrical parameters under dynamic loading. The thesis analyzes designed measurement method in detail, being suitable to determine electrical properties of cement composite materials including the construction of a monitoring system that enables practical application of sensors in complex structures.