This diploma thesis is focused on the study of electric and dielectric properties of transistors based on ionic liquids. The measurements were performed on organic electrochemical transistors with a semiconducting channel made of PEDOT:PSS, which were firstly prepared on ITO substrates, later they were printed using 3D print. Ionic liquid NO4 (1-butyl-3-methylimidazolium hydrogensulfate) was used for measuring of the properties. Electrical properties were determined by measuring volt-ampere characteristics, dielectric properties were measured by impedance spectroscopy.

L’objectif de ce mémoire de maîtrise est de caractériser une Décharge à Barrière Diélectrique (DBD) à la pression atmosphérique dans l’azote en régime homogène. L’objectif est d’une part de mettre en évidence les différents paramètres fondamentaux de ces décharges (température électronique, densité électronique, densité d’espèces excitées et métastables) mais aussi leurs évolutions spatio-temporelles. Dans ce contexte une électrode fractionnée a été réalisée afin de caractériser la décharge le long du flux de gaz et des mesures de spectroscopie d’émission optique résolues spatialement et temporellement ont été utilisées afin d’étudier la physico-chimie de ces décharges. Des variations de tension de claquage et de courant de décharge ont pu être observées entre l’entrée et la sortie du réacteur plasma. Cette variation a pu être reliée à une modification de la population de métastables d’azote N2(A) le long du flux de gaz. De plus, aucune variation significative de la température électronique n’a été relevé. Dans ce travail, des effets d’étalement de la décharge de Townsend ont été mis en évidence grâce à une méthode simple et rapide d'estimation de la surface de décharge. La décharge s’initie d’abord en sortie à cause d’une plus forte population d’espèces énergétiques par rapport à l’entrée. Les mauvaises estimations de surface de décharge conduisent à de mauvaises estimations des valeurs des capacités du circuit équivalent et donc à des paramètres électriques tels que le courant de décharge et la tension appliquée au gaz erronés. Ceci peut donner lieu à de mauvaises interprétations de la physique des DBD. La méthode proposée peut s’appliquer avec ou sans électrode fractionnée ainsi qu’en présence d’espèces réactives appropriées pour le dépôt de couches minces fonctionnelles et multifonctionnelles. / The objective of this master thesis is to characterize a Dielectric Barrier Discharge (DBD) at atmospheric pressure in nitrogen gas in a homogeneous regime. The objective is on the one hand to highlight the different fundamental parameters of these discharges (electronic temperature, electronic density, density of excited and metastable species) but also their spatio-temporal evolutions. In this context a structured electrode was made to characterize the discharge along the gas flow lines as well as optical emission spectroscopy measurements to study the physical chemistry of these discharges. Variations in breakdown voltage and discharge current could be observed between the entrance and the exit of the plasma reactor. This variation could be related to a change in the metastable population of nitrogen N2(A) along the gas flow. In addition, no significant variation in the electronic temperature was noted. In this work, spreading effects of the Townsend discharge were highlighted by a simple and quick method of estimating the discharge area. The discharge is initiated at the exit due to a larger population of energy species compared to the entrance. Wrong discharge area estimates lead to poor estimates of capacitance values of the equivalent circuit and thus to incorrect electrical parameters such as discharge current and gas voltage. This can lead to misinterpretations of DBD physics. The proposed method can be applied with or without fractional electrode, and also in the presence of reactive species suitable for thin-film deposition.

The work presented in this thesis consists of two distinct parts. The first years of my work focused on the development and improvement of a new equipment built to study magnetic and electrical properties, particularly applying microwaves in reflection and transmission conditions. The sample space in conventional cryostats with superconducting magnets is usually smaller than 10-mm-diameter. Our equipment consists of a hollow cylindrical cryostat having a 33-mm-diameter hole all along its vertical axis. These characteristics enable the measurement of large samples and the use of big resonant cavities to get to a wider microwave (MW) range, particularly in transmission measurements. The cryostat has a superconducting magnet made of a solenoid that applies a magnetic field from -5 T to 5 T, and a temperature controller that works in the range 1.8 - 300 K. The system is cooled down with nitrogen and helium and the temperature can be controlled with the precision required by each experiment using a heater and a needle valve. Different probes for a wide range of experiments in our cryostat have been developed in order to be as versatile as possible. Following this idea each one has been divided in two halves that can be combined as it is preferred in each experiment. Each probe is made of a 8-to-10-mm-diameter stainless steel tube that is used to protect and give some stiffness to the measuring device. A coaxial cable and different waveguides are added to these stainless steel jackets, so we end up having nine halves, four upper parts that can be combined with five lower parts. There are three waveguides working in the frequency ranges 33-50 GHz (WR22), 50-75 GHz (WR15) and 75-110 GHz (WR10), and a coaxial cable that maintains the fundamental mode at a frequency of 60 GHz. In the extra lower part a 16-pin Fischer connector is added at the bottom in order to be able to perform more resistance experiments. Once the probes have been built, they have been tested to make sure the system is able to reach high vacuum and to be cooled down. Problems found along the way have been solved and at the end all the probes work properly. Different sample holders have been designed and built according to the needs in each experiment. The system has been tested by reproducing experimental results with Mn12-acetate, as quantum tunneling and magnetic avalanches, and by obtaining new results on microwave transmission in thin TiN films. The second part of the thesis focuses on the measurements of thin TiN films in a dilution refrigerator working with a mixture of 3He and 4He that enables experiments at a few tens of millikelvins. The cryostat also contains a superconductor magnet which can apply a magnetic field up to 5 T. Low-temperature transport properties of nanoperforated superconducting TiN films have been experimentally studied. Resistance measurements have been performed in the critical region of the superconductor-insulator transition (SIT), applying the magnetic field perpendicular to the plane of the structure or the dc current through the sample. SIT is a transition from a superconductor to an insulator state by localizing the Cooper pairs. The evolution of the SIT with temperature, magnetic field and dc current has been investigated in detail. Characteristic parameters have been determined for as-cast thin films using the theory of quantum corrections to conductivity. Disorder-driven and field-induced SITs have been measured. Commensurability effects have been observed down to the lowest experimental temperature, and are emphasized in the more disordered samples. The SIT has been observed for a dc current applied across the sample as changes in the curvature at zero bias current. Experiments prove that electronic transport in the nanoperforated samples is mediated by Andreev conversion. Finally, the existence of the superinsulator state has been experimentally proved. / El treball que es presenta en aquesta tesi consta de dues parts ben diferenciades. La primera pretén el desenvolupament d’un equip experimental concebut per a l’estudi de propietats magnètiques i elèctriques en materials diversos i, en especial, el treball amb radiació de microones en condicions de reflexió i transmissió. La segona s’ha centrat en les mesures de transport d’una capa fina superconductora de nitrur de titani (TiN) de 5 nm de gruix en un criòstat de dilució.

This dissertation deals with the study of electric and dielectric properties of composite structures on the base of alkali-activated aluminosilicates with admixtures of various carbon particles. These materials fabricated from alkali-activated blast furnace slag, quarz sand, natrium water glass as alkali activator, water, dispersant and small amount of carbon admixture (carbon black, graphite powder, carbon fibers or carbon nanotubes) to increase electric conductivity may be used for example to construction of snow-melting, deicing and self-monitoring systems. Their current-voltage characteristics and impedance spectra were used for determination of electric and dielectric properties of these structures. The equivalent circuits were used for evaluation of impedance spectra. The results were correlated with thermal properties of these structures.

The thesis is focused on the study of electric and dielectric properties of thin film organic materials that can be used as an active layer of photovoltaic cells. Primarily were studied the properties of the layers on the glass substrates, which consist of a thin active layer of phthalocyanines. On the samples were first measured current-voltage characteristics (in the dark and during the exposure) and the basic parameters of the photovoltaic conversion were determined. Finally were measured frequency dependencies (impedance spectra, in the dark and during the exposure) and the parameters of a model of the structure with organic semiconductor were determined. The obtained results will be used to optimize the properties of photovoltaic cells.

The exact mechanism of the discharge in liquids ignition is not sufficiently known up to now. Although during the last years was achieved the great progress and overloading which some of them are written in this theoretical part of thesis. This thesis is divided into two experimental parts. When the first part deals with diagnostics of diaphragm discharge in electrolyte solutions and the second part is focused on its use for uncoiling (higher homogenization) of carbon nanotubes in solutions. In experiment 1, three different sized (4 l, 100 ml, 50 ml) diaphragm discharge configurations were used to diagnose diaphragm discharge in electrolyte solutions. Diagnostics is done through current and voltage waveforms with the addition of synchronized ICCD camera images that have been connected to a four-channel oscilloscope. The V-A characteristic can be described by three events occurring in the electrolyte solution with a gradual increase in voltage. Slowly increasing of the voltage in the solution leads first to electrolysis. The next phase is the formation of microbubbles or bubbles, which is characteristic of the curve by a slight decrease in the increase of the current passing between electrodes. The sudden increase in the current flow is characteristic of the last phase, namely the discharge phase. The distance of the electrodes from the diaphragm does not significantly affect the V-A characteristic. The higher diameter of the pin hole, therefore, has a higher voltage, but this does not affect the origin of bubble generation or breakdown. The higher thickness of diaphragm, the higher voltage is needed to the beginning of the bubbles generation, and consequently the discharge breakdown. Comparison of the voltage of the start generation of the bubbles and breakdown for PET diaphragms and diaphragms from the ceramic there was no mark able difference. One of the most important parameters is the conductivity of the electrolyte solution. The lower voltage is needed for the start generation of the bubbles at the higher solution conductivity, and also the discharge generation is observed at a lower breakdown voltage. The second experimental part is focused on the study of the diaphragm discharge effect on carbon nanotubes. A specially designed U-shaped reactor is used to modify carbon nanoparticles. Tap water and aqueous solutions of organic compounds are used as the electrolytic solutions. The discharge is generated by a non-pulsed DC high source with a voltage in the range of 0-2.8 kV supplied to platinum electrodes located in the electrolyte solution. The experimental results have shown that the diaphragm discharge has positive effects on the disintegration of clusters and agglomerates of carbon nanotubes. The primary effect on disintegration is probably the shock waves generated by the discharge. It turned out that it depends on the electrode configuration, where the treatment in anode space has far greater effects than the treatment in cathode half of the reactor. Effects of carbon nanotubes disintegration in solution are long-lasting and the treatment effect is not loosed after several months. There were detected no significant changes in the structure of plasma-treated nanotubes by Infra-red spectroscopy.