Made available in DSpace on 2015-05-14T16:53:13Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-04-08Bitstream added on 2015-05-14T16:59:11Z : No. of bitstreams: 1 000822661.pdf: 3005956 bytes, checksum: aa617124450c9641b6ecb66c3cbbdaa9 (MD5) / Comparou-se a resistência de união (RU) dos cimentos resinosos Panavia F (P) (Kuraray) e RelyX U200 (R) (3M ESPE) à cerâmica zircônia através de três diferentes métodos de tratamento da superfície: 1- silicatização triboquímica (ST) (Rocatec Soft - 3M ESPE); 2- glaze (G) (Akyzent glaze spray- VITA); 3- aplicação de vidro bioativo (VBA). Blocos pré-sinterizados do sistema Zirkonzahn (Zirkonzahn) foram seccionados de modo a produzir 90 blocos menores (5 x 4 x 3 mm). Os blocos foram polidos em Politriz com lixas d’água de granulação fina 1000 e 1200 (3M ESPE) e limpos em banho ultrassônico contendo álcool isopropílico a 96% durante 5 min. Após a sinterização dos blocos cerâmicos, foi realizada a aplicação do tratamento de superfície. O Rocatec Soft foi jateado com 2,8 bar, ângulo de incidência perpendicular e distância padrão de 10 mm por 25 s em movimentos circulares. O Akyzent Glaze Spray foi pulverizado por 2 s e em seguida sinterizado em forno Vacumat (Vita) de acordo com recomendações do fabricante. Após a aplicação de 1 gota do vidro bioativo, procedeu-se a secagem e sinterização a 1200 ºC deste material. Em todos os grupos aplicou-se agente de união silano Monobond-S (Ivoclar Vivadent). Nos grupos 3, 4, 5 e 6 a superfície foi primeiramente condicionada com ácido hidrofluorídrico (HF) a 5% durante 2 min, lavada e depois silanizada. A cimentação foi realizada com um dispositivo (Ultradent), produzindo cilindros de cimento resinoso com 2 x 1mm.! Após 24 h os espécimes foram envelhecidos em termocicladora com 5.000 ciclos com banhos de temperatura entre 5 e 55 ºC e submetidos ao ensaio de cisalhamento na Shear Bond Tester (Bisco). O VBA foi analisado qualitativamente por meio de análise térmica diferencial (DTA), através de difração de raios-x (DRX)(Panalytical) e espectroscopia de energia dispersiva de raio-x (EDS) (Oxford Instruments)... / The bond strength of resin cements Panavia F (P) (Kuraray) and RelyX U200 (R) (3M ESPE) to zirconia using three different surface treatments: 1 - triboquemical silicatization (ST); 2 - glaze (G) 3 - bioactive glass (VBA) was compared. Blocks of Zirkonzahn system were cut producing 90 smaller blocks (5 x 4 x 3 mm). The blocks were polished with water finegrained 1000 and 1200 sandpaper in Politriz and cleaned with 96% isopropyl alcohol for 5 min. The Rocatec Soft was etched with 2.8 bar, in a perpendicular way and a distance of 10 mm for 25 s in a circular motion. The Akyzent Glaze Spray was sprayed by 2s and then sintered in oven Vacumat (Vita) according to manufacturer's recommendations. After application of 1 drop of bioactive glass, the material was dried and sintered at 1200 °C. In all groups was applied silane coupling agent Monobond- S (Ivoclar Vivadent). In groups 3, 4, 5 and 6 the surface was first etched with 5% hydrofluoric acid (HF) and then silanized. The cementing was carried out with a device (Ultradent), producing cured cement cylinders of 2 x 1mm. After 24 h the specimens were aged in thermocycler with 5,000 cycles at a temperature of 5 and 55 ºC and subjected to microshear test on Shear Bond Tester (Bisco). VBA was analyzed by means of DTA, XRD and EDS. Optical profilometry (PO) was performed to obtain roughness. After fracture the samples were analyzed through SEM. It was found that XRD revealed the formation of a glass ceramic film. DTA shows that the temperature of 1200 °C is the most suitable for sintering. DRX showed the formation of a glass ceramic film. According to ANOVA, the interaction effect was significant (p = 0.003 < 0.05). The test for multiple comparison of means, Tukey (5%) showed that the TBS (MPa) for VBA were significantly higher than the other groups (with 26.94 ± 3.50 to P and 28.36 ± 3.32 to R), regardless cement kind used. The lowest result...

Made available in DSpace on 2014-11-10T11:10:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2000-06-30Bitstream added on 2014-11-10T11:57:20Z : No. of bitstreams: 1 000124943.pdf: 2856695 bytes, checksum: d61150204b12b1d758131e6fb0dbf8e1 (MD5) / O propósito deste estudo foi avaliar a rugosidade superficial entre materiais de revestimento estético indiretos (Vita VMK95, Solidex, Artglass, Targis). Para tanto, confeccionaram-se 10 corpos-de-prova nas dimensões de 6mm de comprimento por 6mm de diâmetro de cada material. Uma das superfícies planas recebeu acabamento e polimento, conforme recomendações do fabricante. As amostras concluídas foram submetidas a mensuração, através do rugosímetro Hommel Tester T500. Os valores médios de rugosidade máxima entre os materiais em questão, foram 5,731Jm, 5,151Jm, 6,83 1.1m e 3, 721Jm, respectivamente. A seguir foram submetidos a análise de variância (ANOVA), ao nível de 5%, sendo detectado significância. Concluiu-se que o material Sofidex não apresentou diferença estatisticamente significante entre os grupos, enquanto o Targis apresenta significância estatística em relação ao Artglass e a cerâmica Vita vmk95. / The purpose of this study was to evaluate surface rugosity among indirect esthetic materials (Vita VMK 95, Solidex, Artglass, Targis). Ten samples of each material in the cilindric shape with dimension 6 x 6 mm were manufactured. The surface were submitted to finishing and polishing, according to manufacturer's recommendations. The samples were submitted to measuremenst, using the Hommel Tester T500 device. The average values of maxim surface rugosity among the materiais ín question, were 5, 73pm; 5, 15pm; 6, 83 j.Jm e 3, 72 j.Jm, respectively. Sample were also subjectted to variance analysis- ANOVA (5%), had detected significance. Concluded that the material Solidex did not present significant statistical differences among groups, while Targis presented significant statistical differences in relation to the Artglass and the ceramic Vita vmk95.

Made available in DSpace on 2014-11-10T11:10:01Z (GMT). No. of bitstreams: 0 Previous issue date: 1986Bitstream added on 2014-11-10T11:57:18Z : No. of bitstreams: 1 000023121.pdf: 1889129 bytes, checksum: 7d413d7d31d94f2b417c51acb5fba4e0 (MD5) / O material mais empregado atualmente na construção de modelos é o gesso, que a par de técnica simples reúne condições bastante satisfatórias com relação às propriedades mecânicas, físicas e químicas. Porém, a compatibilidade relativa dos gessos com os materiais de moldagem pode comprometer as qualidades da superfície do modelo. Em nosso trabalho, estudamos a Dureza de dois tipos de gessos: tipo III (gesso pedra) e tipo IV (gesso pedra melhorado), bem como a influência do contacto com três tipos de materiais de moldagem: silicone polimerizada por condensação (Xantopren), polissulfeto (Permlastic) e silicone polimerizada por adição (Provil). Como parâmetro de comparação foi utilizado o gesso reagindo em contacto com uma superfície de vidro...... ( (Resumo completo , clicar acesso eletrônico abaixo) / Currently the most widespread material used in dies is gypsum that together with its simple technique has very satisfactory mechanical, chemical and physical properties. However, its compactibility with the impression materials can compromise the die surface quality. In our work, we studies the hardness of the two gypsum types: Type III (die stone) and type IV (improved die stone), as well as the influence of the contact with three types of impression materials: polymerized silicone for condensation (Xantopren), polysulfide (Permlastic) and polymerized silicone by addition (Provil). As comparison parameter gypsum was used in contact with a glass surface…(Complete abstract click electronic access below)

Made available in DSpace on 2015-01-26T13:21:25Z (GMT). No. of bitstreams: 0 Previous issue date: 1999-06-22Bitstream added on 2015-01-26T13:30:29Z : No. of bitstreams: 1 000124728.pdf: 3630853 bytes, checksum: 0b80fc54b1b28e8603bf29fd818551b0 (MD5) / O propósito deste trabalho foi verificar as reações teciduais em desgastes ósseos cirúrgicos experimentais após a aplicação do adesivo químico, etil cianoacrilato (Super Bonder), em osso parietal de ratos. Investigamos a sua aceitação e a sua interferência no processo de reparo ósseo, mediante estudo microscópico por meio de microscopia de luz. Nesta pesquisa, foram empregados 24 ratos machos e fêmeas brancos (Rattus norvergicus, albinus, Wistar), com peso médio de 250 a 300 gramas, os quais foram divididos em dois grupos, tratado e controle. Após a confecção do desgaste ósseo cirúrgico, no grupo tratado, foi aplicado sobre a superfície óssea o adesivo químico, etil cianoacrilato (Super Bonder). No grupo controle, nenhum material foi aplicado sobre a mesma. Em seguida, procederam-se às suturas do periósteo e da pele. Decorridos 24 horas, três, cinco, sete, trinta e sessenta dias da cirurgia, quatro animais de cada grupo foram sacrificados. As peças contendo os desgastes ósseos foram removidas em bloco, fixadas em formol a 10% por 72 horas e submetidas a análise microscópica por meio de microscopia de luz. Os resultados obtidos possibilitaram concluir que a resposta inflamatória aguda foi mais intensa no grupo tratado do que no grupo controle. O adesivo químico, etil cianoacrilato (Super Bonder), permaneceu sobre a área do desgaste ósseo até o período de observação de sessenta dias e os tecidos adjacentes ao referido material encontravam-se com aspecto de normalidade. O adesivo químico, etil cianoacrilato, não impediu o processo de reparo ósseo / This research objective was to verify the tissues reactions obtained, in surgical experimental bone defect, after the etil cyanoacrylate chemical adhesive application in rats parietal bones. 1t was investigated the acceptance or no acceptance of the tissues surround the bone defect in which was placed the etil cyanoacrylate and the control bone defect. The specimens were submitted to light microscopic analysis. 24 adults rats were used (Rattus norvergicus, albinus, Wistar) with the average weight to 300 gr. and were divided in two groups: treated and control. After the bone defects were realized, etil cyanoacrylate was placed over one of the defects at the parietal bone (treated group). On the other defect nothing was placed and it was used like control group. After 24 hours, 3,5,7,30 and sixty days after surgery, for animals of each group were sacrificed. The bone samples were removed and fixed in 10% formalin during 72 hours and analyzed using light microscopy. The results showed that the acute inflammatory responses was more observed at lhe treated group than the control group. The chemical adhesive was observed until 60 days follow the surgery and the tissues around it present normal appearance. The chemical adhesive, etil cyanaocrylate, did not impede at the bone repair process

Made available in DSpace on 2015-01-26T13:21:31Z (GMT). No. of bitstreams: 0 Previous issue date: 1999-08-16Bitstream added on 2015-01-26T13:30:17Z : No. of bitstreams: 1 000124606.pdf: 3794271 bytes, checksum: 0b7e3cd809f5ce39ab4e03000f54651a (MD5) / Considerando a validade da proposta de remoção químico-mecânica face às vantagens e indicações que o produto Carisolv apresenta e visando a realização de restaurações duradouras, esta pesquisa teve como objetivo comparar o selamento de restaurações adesivas após a remoção químico-mecânica da cárie com Carisolv (Medi Team) e com o método convencional empregando instrumentos rotatórios. Para tanto, foram utilizados sessenta dentes molares humanos cariados que após a remoção da cárie pelas duas técnicas, receberam restaurações com os materiais adesivos Vitremer (3m), Dyract (Dentsply DeTrey) e TPH Spectrum (Dentsply DeTrey). Foi empregada a metodologia para mícroinfiltração com o corante Rodamina B a 0,2% em todos os corpos de prova, que posteriormente foram seccionados em cortadeira especial e avaliados em estereomicroscópio óptico, atribuindo-se escores conforme o grau de microinfiltração observado. A análise estatística constou dos testes não paramétricos de Kruskaii-Wallis e Mann-Whitney cujos resultados evidenciaram que a infiltração marginal ocorreu na maioria das amostras avaliadas; que a diferença entre os escores apresentados pelos materiais não foi significante com a técnica convencional, porém foi significante quando o Carisolv foi empregado; que o Vitremer apresentou os mais altos valores de microinfiltração em ambas as técnicas e que a remoção do tecido cariado pelo método convencional ou químico-mecânico com Carisolv, não influenciou o desempenho selador dos materiais adesivos empregados / The chemo-mechanical removal of carious tissue using Carisolv (MediTeam) presents several advantages and indications, when lasting adhesive fillings are expected. This research proposes to compare the sealing conditions of adhesive restorations placed on teeth submitted either to the chemo-mechanical method using Carisolv or to the traditional bur method of caries removal. Sixty decayed human molars received, after the removal of the carious tissue, adhesive fillings of Vitremer (3M), Dyract (Dentsply DeTrey) e TPH Spectrum (Dentsply DeTrey). The microleakage was observed using the 0,2% Rodamine B dye method in all the samples. The samples were sectioned and examined under optical stereomicroscopy. The statistical analysis using the Kruskall-Wallis and Mann-Whitney non-parametrics tests showed the existence of marginal leakage in most samples; the differences observed in the materials tested were not significant when the traditional method was used but a statistically significant difference existed when Carisolv was employed; the highest levels of microinfiltration occured with Vitremer and the sealing properties of the various adhesive materials were not influenced by the caries removal method applied

Made available in DSpace on 2015-01-26T13:21:31Z (GMT). No. of bitstreams: 0 Previous issue date: 2002-03-15Bitstream added on 2015-01-26T13:30:16Z : No. of bitstreams: 1 000148105.pdf: 6603398 bytes, checksum: b573466a374fbc1a46aedaa48a08fe0f (MD5) / O objetivo deste estudo foi avaliar o grau de microinfiltração marginal em restaurações de resina composta, diante das variáveis remoção ou não do colágeno dentinário após o condicionamento ácido, e utilização ou não de uma camada de resina composta fluida sobre a dentina desproteinizada, alterando-se os seguintes fatores: a)tempo de armazenagem (0, 6 e 12 meses): b) ciclagem térmica (500, 1.500 e 2.500 ciclos). Para tal, 180 dentes bovinos receberam preparos classe V ao nível da junção amelocementária. Eles foram divididos em três grupos: grupo C - foi aplicado o sistema adesivo Single Bond (3M), segundo as recomendações do fabricante, e a seguir procedida a restauração com a resina composta Z250 (3M); grupo H - após o condicionamento ácido foi aplicada uma solução aquosa de NaOCI a 10% por 1 min, e então aplicado o adesivo Single Bond e a resina composta Z250; grupo HF- semelhante ao grupo H, exceto que após a polimerização do adesivo, uma fina camada de resina composta fluída Natural Flow (DFL) foi aplicada e polimerizada, antes da inserção da resina Z250. Todos os espécimes sofreram 500 ciclos ténnicos (5 ±5°C a 55 ±5°C). Os espécimes em cada grupo foram divididos ao acaso em três subgrupos. No primeiro, a microinfiltração marginal foi avaliada após 24h. No segundo, os espécimes permaneceram imersos em água destilada contendo 0,4% de azida sódica em estufa a 37°C por seis meses, sendo que após este período sofreram mais 1.000 ciclos térmicos. No terceiro, os espécimes permaneceram imersos por 12 meses, e receberam mais 1.000 ciclos térmicos a cada 6 meses, totalizando 2.500 ciclos. Após os respectivos períodos de armazenagem, a microinfiltração marginal foi avaliada pelo método do nitrato de prata seguido pela diafanização. Os espécimes foram analisados em estereomicroscópio e receberam escores de 0 a 4. Os dados... / The aim of this study was to evaluate the marginal microleakage in composite resin restorations. under the variables removal or not of the dentin collagen after the acid conditioning, and utilization or not of a flowable composite resin layer on deproteinized dentin, changing the factors: a) storage time (0, 6 and 12 months); b) thermal cycling (500, 1.500 and 2.500 cycles). For this, 180 bovine teeth received class V cavit preparation at cementun-enamel junction. They were assigned to three groups: group C - was applied the Single Bond adhesive system (3M), according to manufacturer instructions, and restored with Z250 composite resin (3M); group H - after the acid conditioning was applied a 10% NaOCI aqueous solution for 1min, and then applied the adhesive and restored with Z250; group HF - like the group H, except that after the adhesive polymerization. a thin layer of a flowable composite resin Natural Flow (DFL) was applied and polimerized, before the placement of Z250. AIl specimens received 500 thermal cycles (5±5'C to 55±5-'C). The specimens in each group were randomly assigned to three subgroups. In the first, the microleakage was evaluated after 24h. In second, the specimens were stored in distillate water containing 0,4% of sodium azide in stove at 37'C, for 6 months, and after this time received more 1.000 thermal cycles. In the third, the specimens were stored for 12 months, and they received more 1.000 thermal cycles for each 6 months. At the end of each storage time, the microleakage was evaluated by the silver nitrate method, followed by cleaning technique. The specimens were analyzed in stereomicroscope and received scores of 0 to 4. The data were submitted to statistical analysis, using the Kruskal Wallis's and Multiple Comparisons tests. After 6 months of storage, the groups H and HF showed falls in microleakage, while the group C didn't showed significant differences

Made available in DSpace on 2015-01-26T13:21:31Z (GMT). No. of bitstreams: 0 Previous issue date: 2002-12-11Bitstream added on 2015-01-26T13:30:16Z : No. of bitstreams: 1 000185829.pdf: 6961073 bytes, checksum: 5b5886f8bdc5cdb65a37f1d7e96773e8 (MD5) / O objetivo deste estudo foi avaliar comparativamente, in vitro, a resistência adesiva ao cisalhamento de sistemas adesivos convencionais come sem a remocão do colágeno com hipoclorito de sódio a 10% e adesivos autocondicionantes. Utilizou-se 48 molares humanos extraídos por indicacão cirúrgica ou ortodôntica que, após a limpeza, foram armazenados em freezer a -18°C. Os dentes foram seccionados em urn plano axial mésio-distal separando-os em duas metades, vestibular e lingual. Após o embutimento em resina acrílica, tiveram as superfícies vestibular e lingual desgastadas com lixa numa sequência de granulacão decrescente para padronizar a smear layer e expor a dentina até a espessura de 2 mm. A área de adesão foi delimitada em 3 mm de diâmetro. Os espécimes foram divididos em seis grupos, de acordo com o sistema adesivo e o tratamento dentinário realizado: OBF - adesivo autocondicionante One-Up Bond F (Tokuyama); CSEB - primer autocondicionante Clearfil SE Bond (Kuraray); SB -Single Bond (3M); SBMP - Scotchbond Multi Uso Plus (3M); SBH – após o condicionamento ácido foi utilizado o hipoclorito de sódio a 10% (AD Gel - Kuraray) durante um minuto e em seguida utilizado o Single Bond; SBMPH - após o condicionamento ácido foi utilizado o hipoclorito de sódio a 10% (AD Gel - Kuraray) durante um minuto e, em seguida, utilizado o Scotchbond Multi Uso Plus. A resina composta Z-100 (3M) foi inserida pela técnica incremental, em matriz metálica, sobre a área preparada. 0 ensaio mecânico de cisalhamento foi realizado em uma máquina lnstron Universal à velocidade de 0,5 mm/min. As superfícies fraturadas foram analisadas em estereomicroscópio (Karl Zeiss). Os dados foram submetidos à análise estatística, empregando-se os testes ANOVA e Tukey. Os resultados demonstraram os seguintes valores em MPa: CSEB - 24,362; SB - 20,956; SBH- 17,825; OBF - 17,355; SBMP - 17,218; SBMPH-14,169. Concluimos que... / The aim of this study was to investigate comparatively in vitro the shear bond strength of conventional adhesive systems with and without collagen removal using 10 % sodium hypochlorite and self-etch adhesives. 48 human's molars were extracted for surgery and orthodontic reasons and after cleaning, they were stored in freezers (-18º C). The teeth were sectioned in an axial plan (mesio-distal), separated in two halves, vestibular and lingual. The teeth were mounted in self-cure resin and the labial and lingual surfaces were ground with sequential abrasive sandpaper to standardize the smear layer and expose the dentin with 2 mm of the thickness. The adhesion surface was delimited in 3 mm of diameter, the specimens were separated into six groups in accordance with adhesive system and dentin treatment: OBF - self-etch adhesive One-Up Bond F (Tokuyama); CSEB- self-etch primer Clearfil SE Bond (Kuraray); SB - Single Bond (3M); SBMP - Scotchbond Multi Uso Plus (3M); SBH - after acid etching was used at 10% sodium hypochlorite (AD Gel - Kuraray) during one minute and then Single Bond was used; SBMPH - after the acid etching sodium hypochlorite at 10% was used (AD GelKuraray) during one minute and then Scotchbond Multi Uso Plus was used. The composite resin Z-100 (3M) was inserted by incremental technique with a metallic matrix on a prepared surface. The shear test was realized in an lnstron Universal machine at 0,5 mm/min speed. The fractured surfaces were classified in stereomicroscopic (Karl Zeiss). The data obtained was analyzed by ANOVA and Tukey tests. The data showed the following values (in MPa): CSEB- 24,362; SB- 20,956; SBH - 17,825; OBF - 17,355; SBMP - 17,218; SBMPH- 14,169. We concluded that self-etch adhesive CSEB showed bond strength significantly higher than OBF and SBMP adhesives; the self-etch adhesive with acidificate primer showed bond strength statistically higher than where...

Orientador: Maria Amélia Máximo de Araújo / Banca: João Candido de Carvalho / Banca: Maria Antonia Pereira / Banca: Savério Mandetta / Banca: Regina Célia Santos Pinto Silva / Resumo: 0 objetivo deste estudo foi avaliar comparativamente, in vitro, a resistência adesiva ao cisalhamento de sistemas adesivos convencionais come sem a remocão do colágeno com hipoclorito de sódio a 10% e adesivos autocondicionantes. Utilizou-se 48 molares humanos extraídos por indicacão cirúrgica ou ortodôntica que, após a limpeza, foram armazenados em freezer a -18°C. Os dentes foram seccionados em urn plano axial mésio-distal separando-os em duas metades, vestibular e lingual. Após o embutimento em resina acrílica, tiveram as superfícies vestibular e lingual desgastadas com lixa numa sequência de granulacão decrescente para padronizar a smear layer e expor a dentina até a espessura de 2 mm. A área de adesão foi delimitada em 3 mm de diâmetro. Os espécimes foram divididos em seis grupos, de acordo com o sistema adesivo e o tratamento dentinário realizado: OBF - adesivo autocondicionante One-Up Bond F (Tokuyama); CSEB - primer autocondicionante Clearfil SE Bond (Kuraray); SB -Single Bond (3M); SBMP - Scotchbond Multi Uso Plus (3M); SBH - após o condicionamento ácido foi utilizado o hipoclorito de sódio a 10% (AD Gel - Kuraray) durante um minuto e em seguida utilizado o Single Bond; SBMPH - após o condicionamento ácido foi utilizado o hipoclorito de sódio a 10% (AD Gel - Kuraray) durante um minuto e, em seguida, utilizado o Scotchbond Multi Uso Plus. A resina composta Z-100 (3M) foi inserida pela técnica incremental, em matriz metálica, sobre a área preparada. 0 ensaio mecânico de cisalhamento foi realizado em uma máquina lnstron Universal à velocidade de 0,5 mm/min. As superfícies fraturadas foram analisadas em estereomicroscópio (Karl Zeiss). Os dados foram submetidos à análise estatística, empregando-se os testes ANOVA e Tukey. Os resultados demonstraram os seguintes valores em MPa: CSEB - 24,362; SB - 20,956; SBH- 17,825; OBF - 17,355; SBMP - 17,218; SBMPH-14,169. Concluimos que... / Abstract: The aim of this study was to investigate comparatively in vitro the shear bond strength of conventional adhesive systems with and without collagen removal using 10 % sodium hypochlorite and self-etch adhesives. 48 human's molars were extracted for surgery and orthodontic reasons and after cleaning, they were stored in freezers (-18º C). The teeth were sectioned in an axial plan (mesio-distal), separated in two halves, vestibular and lingual. The teeth were mounted in self-cure resin and the labial and lingual surfaces were ground with sequential abrasive sandpaper to standardize the smear layer and expose the dentin with 2 mm of the thickness. The adhesion surface was delimited in 3 mm of diameter, the specimens were separated into six groups in accordance with adhesive system and dentin treatment: OBF - self-etch adhesive One-Up Bond F (Tokuyama); CSEB- self-etch primer Clearfil SE Bond (Kuraray); SB - Single Bond (3M); SBMP - Scotchbond Multi Uso Plus (3M); SBH - after acid etching was used at 10% sodium hypochlorite (AD Gel - Kuraray) during one minute and then Single Bond was used; SBMPH - after the acid etching sodium hypochlorite at 10% was used (AD GelKuraray) during one minute and then Scotchbond Multi Uso Plus was used. The composite resin Z-100 (3M) was inserted by incremental technique with a metallic matrix on a prepared surface. The shear test was realized in an lnstron Universal machine at 0,5 mm/min speed. The fractured surfaces were classified in stereomicroscopic (Karl Zeiss). The data obtained was analyzed by ANOVA and Tukey tests. The data showed the following values (in MPa): CSEB- 24,362; SB- 20,956; SBH - 17,825; OBF - 17,355; SBMP - 17,218; SBMPH- 14,169. We concluded that self-etch adhesive CSEB showed bond strength significantly higher than OBF and SBMP adhesives; the self-etch adhesive with acidificate primer showed bond strength statistically higher than where... / Doutor

Orientador: Mario Tanomaru Filho / Banca: Idomeo Bonetti Filho / Banca: Fábio Luiz Camargo Villela Berbert / Banca: Carlos Eduardo Saraiva Miranda / Banca: Celso Luiz Caldeira / Resumo: O Cimento Portland (CP) é um cimento de silicato de cálcio. Modificações em sua composição por meio de aditivos e resinas podem melhorar sua manipulação e presa. Foram avaliados MTA Angelus e diferentes cimentos de silicato de cálcio: puro (CSC), modificado (CSCM), resinoso 1 (CSCR1), resinoso 2 (CSCR2) e resinoso 3 (CSCR3). Dois cimentos foram selecionados para avaliação em associação aos radiopacificadores: óxido de zircônio (ZrO2) ou óxido de nióbio (Nb2O5) micro ou nanoparticulado, tungstato de cálcio (CaWO4) ou óxido de bismuto (Bi2O3). Na primeira etapa (Capítulo 1) foram avaliados tempo de presa, escoamento, resistência à compressão, quantificação de arsênio, radiopacidade e viabilidade celular. Na segunda etapa, os materiais CSCM e CSCR2 associados aos radiopacificadores forma avaliados quanto ao tempo de presa, escoamento, solubilidade, radiopacidade, resistência à compressão, pH, cálcio (capítulo 2); além de superfície, composição química, MTT e apoptose/necrose (capítulo 3). Os dados foram submetidos à análise de variância e teste de Tukey (p˂0,05). Todos os cimentos apresentaram arsênio em níveis compatíveis com o uso clínico, e mostraram biocompatibilidade. O CSCR2 apresentou maior escoamento. As associações do CSCM + CaWO4 e CSCR2 + ZrO2 e Nb2O5 micro ou CaWO4 e o MTA Angelus apresentaram menor tempo de presa, e CSCM e CSCR2 + ZrO2 micro maior escoamento. Todos os cimentos apresentaram baixa solubilidade, pH alcalino e liberaram íons cálcio. Além disso, apresentam partículas de tamanho maior que o MTA, além de cálcio e silício em sua composição e foram biocompatíveis. Concluímos que os cimentos CSCM e CSCR2 apresentam potencial uso clínico quando associado aos radiopacificadores avaliados, destacando-se o ZrO2 e Nb2O5 microparticulados. / Abstract: Portland Cement (PC) is calcium silicate cement. Changes in its composition by additives and resins can improve their handling and setting time. It was evaluated MTA Angelus and different calcium silicate cements: pure (CSC), modified (CSCM), resin 1 (CSCR1), resin 2 (CSCR2) and resin 3 (CSCR3). After selection of two cements, they were associated with radiopacifiers: zirconium oxide (ZrO2) or niobium oxide (Nb2O5) micro or nanoparticulate, calcium tungstate (CaWO4) or bismuth oxide (Bi2O3). In the first fase (Chapter 1), setting time, flow, compressive strength, quantification of arsenic, radiopacity and cell viability were evaluated. In the second study, it were evaluated the setting time, flow, solubility, radiopacity, compressive strength, pH, calcium (Chapter 2), in addition to surface chemical composition, MTT and apoptosis/necrosis (Chapter 3) of cements CSCM and CSCR2 associated to radiopacifiers. Data were subjected to analysis of variance and Tukey test (p˂0.05). All sealers showed arsenic in compatible with clinical use levels, and showed biocompatibility. The CSCR2 showed higher flow. The associations of CSCM + CaWO4 and CSCR2 with ZrO2 or Nb2O5 micro or CaWO4 and MTA Angelus had lower setting time, and CSCM and CSCR2 + ZrO2 micro largest flow. All cements showed low solubility, alkaline and released calcium ions. Also, they have particles larger than the size MTA, calcium and silicon were present in their composition and they were biocompatible. It was concluded that the CSCM and CSCR2 cements have potential clinical use when associated with radiopacifiers reviews, specially the ZrO2 and Nb2O5 microparticulated. / Doutor

Made available in DSpace on 2016-06-07T17:12:20Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-08-13. Added 1 bitstream(s) on 2016-06-07T17:16:59Z : No. of bitstreams: 1 000865267.pdf: 860727 bytes, checksum: 462d816a3edd9a695666266dd28a3c7f (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O presente estudo teve como objetivo avaliar o efeito de diferentes métodos de remoção do excesso de cimento e do polimento na formação de biofilme e micromorfologia na região de margem dente/restauração. A partir de dentes bovinos, foram obtidos 96 blocos de dentina (4 mm x 8 mm x 2 mm) que foram moldados e reproduzidos em gesso tipo IV, sobre os quais foram produzidos 96 blocos prensados de cerâmica (Vita PM9, Vita Zahnfabrik; 4 mm x 8 mm x 2 mm) pela técnica de cera perdida. Os blocos de dentina e seus respectivos blocos cerâmicos foram cimentados com um cimento resinoso auto-adesivo (RelyX U200, 3M ESPE) e o excesso de cimento foi removido utilizando diferentes técnicas: MBr: microbrush e fotoativação, MBr-Pol: microbrush, fotoativação e polimento, Pi: pincel e fotoativação, Pi-Pol: pincel, fotoativação e polimento, Foto- Expl: 5 s de fotoativação inicial, explorador e fotoativação final, Foto-Expl- Pol: 5 s de fotoativação inicial, explorador, fotoativação final e polimento, Foto-Bi: 5 s de fotoativação inicial, bisturi e fotoativação final, Foto-Bi-Pol: 5s de fotoativação inicial, bisturi, fotoativação final e polimento. Após 24 h, a rugosidade da região de margem das amostras foi analisada utilizando um rugosímetro (Mitutoyo SJ-400 Tóquio, Japão; três medições em cada amostra). Análise micromorfológica da região foi obtida por microscópio estereoscópico e MEV. Em seguida, as amostras foram contaminadas em caldo de sacarose com suspensão padronizada com Streptococcus mutans, Staphylococcus aureus e Candida albicans e incubados por um período de 48 h. As amostras foram analisadas quantitativamente para aderência bacteriana na região da margem por microscopia de varredura confocal a laser e contagem das unidades formadoras de colônias (UFC/mL), e analisadas qualitativamente usando MEV. Os dados de rugosidade superficial (Ra) foram submetidos à análise de variância (2- way), teste de Tukey.. / Abstract This study evaluated the effects of excess cement removal techniques, with or without posterior polishing, on the biofilm formation and micromorphology in the marginal region of the tooth/restoration. From bovine teeth, 96 dentin blocks (4 x 8 x 2 mm) were produced, molded and reproduced in type IV gypsum, on which 96 pressed ceramic blocks (Vita PM9 4 mm x 8 mm x 2 mm, Vita Zahnfabrik) were produces via lost wax technique. The dentin blocks and their respective ceramic blocks were cemented with a self-adhesive resin-cement (RelyX U200, 3M ESPE) and cement excess was removed using different techniques, followed by polishing with silicone tips or, in some cases, not polished at all: MBr: microbrush and photoactivation, MBr-Pol: MBr + polishing, Pi: brush and photoactivation, Pi-Pol: PI + polishing, Photo-Expl: 5 s initial photoactivation, explorer and final curing, Photo-Expl-Pol: Photo-Expl + polishing, Photo-Bi: 5 s initial photoactivation, scalpel and final curing, Photo-Bi-Pol: Photo-Bi + polishing. After 24 hours, the samples marginal region roughness was analyzed using a profilometer (Mitutoyo SJ-400 Tokyo, Japan; three measurements on each sample). Micromorphological analyses of the region were performed by stereoscopic microscope and SEM. Then the samples were contaminated with sucrose broth standardized suspension with Streptococcus mutans, Staphylococcus aureus and Candida albicans and incubated for a period of 48 hours. The samples were quantitatively analyzed for bacterial adherence in the marginal region by confocal laser scanning microscopy and counting of colony forming units (CFU/ml), and qualitatively analyzed using SEM. Roughness data (Ra) were submitted to 2-way ANOVA, Tukey test (5%) and Student's-t tests. CFU, Biomass and bio thickness data were analyzed by Kruskal Wallis', Mann-Whitney's e Dunn's tests. The removing technique statistically influenced the roughness (Ra; p ˂ 0.05), when comparing polished and unpolished...