Thesis--Göteborg. / Includes reprints of 10 supporting articles. Also issued as volume 67, Supplement no. 5, 1974 of the Swedish Dental Journal. Includes bibliographical references (p. 66-70).

Thesis--Göteborg. / Includes reprints of 10 supporting articles. Also issued as volume 67, Supplement no. 5, 1974 of the Swedish Dental Journal. Includes bibliographical references (p. 66-70).

Orientador: Wilkens Aurelio Buarque e Silva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T03:30:15Z (GMT). No. of bitstreams: 1 Costa_MarcelodeAlmeida_D.pdf: 2169259 bytes, checksum: 40e31d0384a05e3f5b7c97d6657b6364 (MD5) Previous issue date: 2009 / Resumo: Este trabalho teve como objetivo, avaliar através da extesometria, a resposta de forças aplicadas sobre abutments de infra-estrutruras implanto-retidas fundidas em ligas de cobalto-cromo, pela técnica de monobloco, simulando caso de protocolo mandibular, foram utilizados 06 implantes com distância de 10 mm entre implantes e com extremo livre Cantilever bilateral com tamanho do 20 mm. Em cada abutment foram colados 04 extensometros, fazendo uma ponte de Wheatstone, após apertamento de todos os componentes a peça em monobloco, foi submetido a um ensaio mecânico com cargas compressivas com valores de 150 N/cm, analisando quantitativamente os dados através da extensômetria, permitindo resultados bem precisos. Os referidos resultados foram obtidos usando os maiores valores registrados em cada ponto de força aplicado, ou seja, nos lados: esquerdo e direito ( cantilever bilateralmente), tanto para carga axial ou em 20º, demonstrou pura deflexão, porem quando a aplicação foi entre as fixações( implantes ) P1eP2,P3eP4,P4 eP5, P5eP6, respectivamente, foi obtido nas fixações mais próximas a aplicação da carga um maior grau de compressão (deflexão) e nas fixações mais distantes uma pequena deflexão negativa indo até conseguir uma deflexão positiva, sugerindo movimento de gangorra / Abstract: The objective of this study was evaluate through extensometry the response of implant-suported frameworks in cobalt-chromium submitted to a load by the technique of monoblock, that simulate a case of mandibular protocol with 06 implants with a distance of 10 mm between each implant and a bilateral cantlever of 20 mm. In each abutment were pasted 04 strain gauges, making a bridge of Wheatstone, after squeezing all components of the piece of the monoblock, was submitted to a test with mechanical compressive loads with values of 150 N, quantitatively analyzing the data through extensometry, allowing accurate results. The results were obtained using the highest values recorded at each point of force applied, in the points L and R (cantilever bilaterally) for both axial load or 20, showed pure deflection, but when the load was applyed between p1 and p2, P3eP4, P4 eP5, P5eP6 respectively, was obtained a greater degree of compression (deflection) closer to the application of the load and more dstant to the applicarion of load, a little negative deflection was found by going to a positive deflection, suggesting movement of seesaw / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Resumo: O dióxido de carbono (CO2) é um importante gás de efeito estufa. No entanto, um aumento gradual ameaça substancialmente o clima. Um dos principais desafios do planejamento ambiental é identificar um modelo que vincule todos os fatores do ciclo de carbono, ou seja, oceano - ecossistema terrestre - emissão antropogênica - atmosfera. Princípios básicos de Termodinâmica podem ser aplicados em uma modelagem estatística com bases em séries históricas para obter concentrações de CO2 na atmosfera, possibilitando a construção de cenários para uma melhor tomada de decisões. Por este motivo, foi desenvolvido no trabalho um modelo que interliga todos os fatores do ciclo de carbono, focalizando em quatro zonas térmicas ou climáticas (Boreal, Temperada, Tropical, Polar), para cálculos de armazenamento de CO2 atmosférico. Os resultados mostram que no ano 2100 se atingirá uma concentração de CO2 quatro vezes maior do que antes do período pré-industrial. A zona temperada emite quase a metade de dióxido de carbono à atmosfera na atualidade; para o ano 2100, essa emissão aumentará a quinze vezes mais que a zona tropical. A China será responsável em uma proporção de vinte quatro a onze com relação aos Estados Unidos. A estabilização das concentrações de CO2 na atmosfera será obtida quando as emissões de dióxido de carbono antropogênico tiverem uma diminuição de mais do que trinta e quatro por cento para o ano 2100 na zona temperada. / Abstract: Carbon dioxide (CO2) is the most important greenhouse gas. A gradual increase on its atmospheric concentration threatens significantly the climate. One of the main challenges of environment planning is to identify a model that connects all factors that determine the carbon cycle, that is, ocean - terrestrial ecosystem - anthropogenic emissions - atmosphere. Basic thermodynamic principles can be applied in a statistical modeling with historic time series to obtain atmospheric CO2 concentration, creating the possibility of construction of scenarios that will help decision making. A model that links all carbon cycle factors was developed in this dissertation work, focusing in four thermal of climatic zones (Boreal, Temperate, Tropical, and Polar) for calculations of atmospheric CO2 storage. Results show that in 2100, the atmospheric CO2 concentration will reach a value four times higher than that of the pre-industrial period. The temperate zone already emits almost half of the carbon dioxide to the atmosphere; by 2100, this emission will increase 15 times more than that corresponding to the tropical zone. China will be responsible for emissions in a proportion of 24 to 11 in comparison to that of the United States. Stabilization of CO2 concentrations in the atmosphere will be obtained when the anthropogenic carbon dioxide emissions attain a decrease of at least 34% in 2100 in the temperate zone. / Orientador: Sérgio João Crnkovic / Coorientador: Humberto Lopes Rodrigues / Banca: Antonio Jorge Abdalla / Banca: Marcelo dos Santos Pereira / Banca: Sandra Giacomin Schneider / Banca: Leonardo Gonçalves Cunha / Doutor

Orientador: Lafayette Nogueira Júnior / Banca: Tarcísio José Arruda de Paes Junior / Banca: Argemiro Soares da Silva Sobrinho / Resumo: Esta pesquisa se propôs verificar a manutenção do torque, após fadiga mecânica, de parafusos de pilares protéticos com recobrimento de carbono tipo diamante (DLC) e com dopagem de diamantes (CD-DLC) submetidos ao retorque, em conexões hexagonais externa (HE) e interna (HI). Implantes HE e HI e diferentes tratamentos do parafuso protético foram alocados em grupos experimentais (n = 5): sem tratamento e não submetidos a fadiga (HE-CON) (HI-CON); sem tratamento fadigados (HECONF) (HI-CONF); com DLC fadigado (HE-DLCF) (HI-DLCF) e com CDDLC fadigados (HE-CD-DLCF) (HI-CD-DLCF). Os recobrimentos de DLC e CD-DLC foram depositados a plasma pelo método PECVD. As amostras (implante + parafusos + coroa metálica), que já haviam sido expostas a 1 milhão de ciclos de fadiga, foram retorqueadas com torquímetro digital, com o torque recomendado pelo fabricante 30 N (HE) e 20 N (HI), e submetidos novamente a 1 milhão de ciclos mecânicos. Ao término da fadiga, os parafusos foram destorqueados para verificar a manutenção do torque. Parafusos de cada grupo experimental foram selecionados para observação em MEV. A análise estatística foi realizada pelo teste Anova 2- Fatores (α = 0,05). Não houve interação entre os fatores em estudo (p = 0,765); o tratamento dos parafusos (p = 0,638) e o tipo de conexão (p = 0,615) não apresentaram diferença estatística. Alterações como danos nas roscas do parafuso e remoção do filme foram observados entre os grupos experimentais. Os grupos com revestimento apresentaram pouco ou nenhum dano nas roscas dos parafusos. O revestimento de DLC e CDDLC parece não ter interferido na adaptação do parafuso ao implante. Parafusos protéticos recobertos com DLC e CD-DLC, após o retorque, não elevaram a manutenção do torque / Abstract: The study analyzed the torque maintain of the screw abutments, with coating of diamond-like carbon (DLC) and doping of diamond (CD-DLC), submitted the retorque in external hexagonal (EH) and internal (IH) connections; after mechanical fatigue. HE and HI implants and different treatments of the abutments screws were divided into experimental groups (n = 5): untreated and not subjected to fatigue (EH-CON) (IHICON); fatigued untreatment (EH-CONF) (IH-CONF); fatigued with DLC (EH- DLCF) (IH-DLCF) and fatigued with CD-DLC (EH-CD-DLCF) (IH-CD-DLCF). The DLC and CD-DLC coating was deposited by plasma, PECVD method. Samples (Implant + abutment screew + metal crown), which had been exposed to 1 million fatigue cycles were retorquiadas, digital torque wrench, to the torque recommended by the manufacturer 30 N (HE) and 20 N (HI), and submitted again to 1 million cycles mechanics. At the end of fatigue, the screws were destorquiados to check the maintenance of torque. Screws from each experimental group were selected for observation by SEM. Statistical analysis was performed by ANOVA 2 Factors test (α = 0.05). There was no interaction among the factors studied (p = 0.765); the treatment of screws (p = 0.638) and the connection type (p = 0.615) showed no statistical difference. The microscopy images showed damage the threads and covering the presence of HI connections. Changes such as damage on the screws threads and film removal were observed among the experimental groups. The coating groups showed little or no damage on the screws threads. The DLC and CD-DLC coating did not interfere in the screw adaptation on the implant. Abutments screew coating with DLC and CD-DLC, after retorque, no raised torque maintenance / Mestre

Made available in DSpace on 2014-06-11T19:35:46Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-04-14Bitstream added on 2014-06-13T19:46:48Z : No. of bitstreams: 1 souza_cfln_dr_guara.pdf: 2882302 bytes, checksum: bbab3a7e686dbd0b753b29bbd65b3a74 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O dióxido de carbono (CO2) é um importante gás de efeito estufa. No entanto, um aumento gradual ameaça substancialmente o clima. Um dos principais desafios do planejamento ambiental é identificar um modelo que vincule todos os fatores do ciclo de carbono, ou seja, oceano – ecossistema terrestre – emissão antropogênica – atmosfera. Princípios básicos de Termodinâmica podem ser aplicados em uma modelagem estatística com bases em séries históricas para obter concentrações de CO2 na atmosfera, possibilitando a construção de cenários para uma melhor tomada de decisões. Por este motivo, foi desenvolvido no trabalho um modelo que interliga todos os fatores do ciclo de carbono, focalizando em quatro zonas térmicas ou climáticas (Boreal, Temperada, Tropical, Polar), para cálculos de armazenamento de CO2 atmosférico. Os resultados mostram que no ano 2100 se atingirá uma concentração de CO2 quatro vezes maior do que antes do período pré-industrial. A zona temperada emite quase a metade de dióxido de carbono à atmosfera na atualidade; para o ano 2100, essa emissão aumentará a quinze vezes mais que a zona tropical. A China será responsável em uma proporção de vinte quatro a onze com relação aos Estados Unidos. A estabilização das concentrações de CO2 na atmosfera será obtida quando as emissões de dióxido de carbono antropogênico tiverem uma diminuição de mais do que trinta e quatro por cento para o ano 2100 na zona temperada. / Carbon dioxide (CO2) is the most important greenhouse gas. A gradual increase on its atmospheric concentration threatens significantly the climate. One of the main challenges of environment planning is to identify a model that connects all factors that determine the carbon cycle, that is, ocean – terrestrial ecosystem – anthropogenic emissions – atmosphere. Basic thermodynamic principles can be applied in a statistical modeling with historic time series to obtain atmospheric CO2 concentration, creating the possibility of construction of scenarios that will help decision making. A model that links all carbon cycle factors was developed in this dissertation work, focusing in four thermal of climatic zones (Boreal, Temperate, Tropical, and Polar) for calculations of atmospheric CO2 storage. Results show that in 2100, the atmospheric CO2 concentration will reach a value four times higher than that of the pre-industrial period. The temperate zone already emits almost half of the carbon dioxide to the atmosphere; by 2100, this emission will increase 15 times more than that corresponding to the tropical zone. China will be responsible for emissions in a proportion of 24 to 11 in comparison to that of the United States. Stabilization of CO2 concentrations in the atmosphere will be obtained when the anthropogenic carbon dioxide emissions attain a decrease of at least 34% in 2100 in the temperate zone.

Made available in DSpace on 2016-06-07T17:12:32Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-12-10. Added 1 bitstream(s) on 2016-06-07T17:17:17Z : No. of bitstreams: 1 000865436.pdf: 1601189 bytes, checksum: c34e3709b85d75f0d4c7ed707ac9c2a8 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Esta pesquisa se propôs verificar a manutenção do torque, após fadiga mecânica, de parafusos de pilares protéticos com recobrimento de carbono tipo diamante (DLC) e com dopagem de diamantes (CD-DLC) submetidos ao retorque, em conexões hexagonais externa (HE) e interna (HI). Implantes HE e HI e diferentes tratamentos do parafuso protético foram alocados em grupos experimentais (n = 5): sem tratamento e não submetidos a fadiga (HE-CON) (HI-CON); sem tratamento fadigados (HECONF) (HI-CONF); com DLC fadigado (HE-DLCF) (HI-DLCF) e com CDDLC fadigados (HE-CD-DLCF) (HI-CD-DLCF). Os recobrimentos de DLC e CD-DLC foram depositados a plasma pelo método PECVD. As amostras (implante + parafusos + coroa metálica), que já haviam sido expostas a 1 milhão de ciclos de fadiga, foram retorqueadas com torquímetro digital, com o torque recomendado pelo fabricante 30 N (HE) e 20 N (HI), e submetidos novamente a 1 milhão de ciclos mecânicos. Ao término da fadiga, os parafusos foram destorqueados para verificar a manutenção do torque. Parafusos de cada grupo experimental foram selecionados para observação em MEV. A análise estatística foi realizada pelo teste Anova 2- Fatores (α = 0,05). Não houve interação entre os fatores em estudo (p = 0,765); o tratamento dos parafusos (p = 0,638) e o tipo de conexão (p = 0,615) não apresentaram diferença estatística. Alterações como danos nas roscas do parafuso e remoção do filme foram observados entre os grupos experimentais. Os grupos com revestimento apresentaram pouco ou nenhum dano nas roscas dos parafusos. O revestimento de DLC e CDDLC parece não ter interferido na adaptação do parafuso ao implante. Parafusos protéticos recobertos com DLC e CD-DLC, após o retorque, não elevaram a manutenção do torque / The study analyzed the torque maintain of the screw abutments, with coating of diamond-like carbon (DLC) and doping of diamond (CD-DLC), submitted the retorque in external hexagonal (EH) and internal (IH) connections; after mechanical fatigue. HE and HI implants and different treatments of the abutments screws were divided into experimental groups (n = 5): untreated and not subjected to fatigue (EH-CON) (IHICON); fatigued untreatment (EH-CONF) (IH-CONF); fatigued with DLC (EH- DLCF) (IH-DLCF) and fatigued with CD-DLC (EH-CD-DLCF) (IH-CD-DLCF). The DLC and CD-DLC coating was deposited by plasma, PECVD method. Samples (Implant + abutment screew + metal crown), which had been exposed to 1 million fatigue cycles were retorquiadas, digital torque wrench, to the torque recommended by the manufacturer 30 N (HE) and 20 N (HI), and submitted again to 1 million cycles mechanics. At the end of fatigue, the screws were destorquiados to check the maintenance of torque. Screws from each experimental group were selected for observation by SEM. Statistical analysis was performed by ANOVA 2 Factors test (α = 0.05). There was no interaction among the factors studied (p = 0.765); the treatment of screws (p = 0.638) and the connection type (p = 0.615) showed no statistical difference. The microscopy images showed damage the threads and covering the presence of HI connections. Changes such as damage on the screws threads and film removal were observed among the experimental groups. The coating groups showed little or no damage on the screws threads. The DLC and CD-DLC coating did not interfere in the screw adaptation on the implant. Abutments screew coating with DLC and CD-DLC, after retorque, no raised torque maintenance

Orientador: Tarcisio José de Arruda Paes-Junior / Co-orientador: Fernando Henrique Cristovan / Banca: Alexandre Luiz Souto Borges / Banca: Regina Tamaki / Banca: Marina Amaral / Banca: Lafayette Nogueira Junior / Resumo: O objetivo desta pesquisa foi sintetizar e caracterizar partículas de sílica recobertas com nanopartículas de prata, e avaliar a influência destas quando incorporadas à resina acrílica termicamente ativada e reembasador rígido, em suas características mecânicas e microbiológicas. Uma solução de sílica foi sintetizada pelo método de hidrólise controlada do tetraetilortosilicato (TEOS) em meio alcoólico. Foi adicionada a essa uma solução de nitrato de prata, em duas molaridades (10 mmols e 30 mmols) formando partículas do tipo núcleo-casca. Após centrifugação e secagem, cada pó obtido foi adicionado em duas concentrações: 0.5% e 2%, às resinas analisadas. Foram confeccionadas barras retangulares (n=9) de 30 x 10x 3mm para realização do teste de resistência a flexão de três pontos, rugosidade e ângulo de contato; e 120 amostras em forma de disco (2 mmx10 mm) para análise microbiológica. Como grupo controle teve-se amostras sem nanopartículas. As nanopartículas foram analisadas em microscopia eletrônica de varredura com microanalisador por energia dispersiva de raios-X integrado (EDS), Difratômetro de Raios-X e microscopia eletrônica de transmissão. Uma suspensão de Candida albicans foi utilizada para análise de aderência fúngica, halo de inibição e concentração inibitória mínima. As fotomicrografias mostraram que as nanopartículas de 10 mmols apresentam uma distribuição mais homogênea e menor agregação das nanopartículas de prata na superfície da sílica do que as de 30 mmols. Os resultados indicaram que a resistência a flexão foi afetada negativamente, em ambos materiais, com a adição de 2% de partículas, independente da molaridade. A adição das partículas não alterou a molhabilidade da superfície dos materiais, nem a rugosidade, exceto do grupo de reembasador com partículas de 10mmols, em ambas concentrações. As partículas não apresentaram ação antifúngica para os.... / Abstract: This research aimed to synthesize, characterize, and evaluate the influence of the addition of silica-silver core/shell particles in mechanical and antifungal characteristics of thermally active acrylic resins or hard reliner . Silica solution was produced by controlled hydrolysis method of tetraethylorthosilicate (TEOS) in an alcoholic. It was added a silver nitrate solution in two molarities, 10 and 30 milimols, forming core-shell particles. After centrifugation and drying, each obtained powder was added in two concentrations 0.5% and 2% in the resins analyzed. Rectangular samples (n=9) with 30 x10 x3 mm were made to three point bend test), roughness and contact angle, and 120 samples in disc (2 mmx10 mm) for microbiological analysis Samples without particles were used as control. The nanoparticles were analyzed by scanning electron microscopy with dispersive energy microanalyzer integrated X-rays (EDS), X-ray diffractometer and transmission electron microscopy. Candida albicans suspension was used to adhesion test, inhibition zone and minimum inhibitory concentration. Photomicrograph showed that nanoparticles with 10 milimols show a distribution more uniform and less aggregation of silver nanoparticles on the silica surface than 30 millimols. The Three point bend test results showed that the flexural strength was negatively affected in both materials, with the addition of 2% particles, in both molarity. The addition of the nanoparticles did not change the surface wettability or roughness of the materials, except for except the reliner group with 10mmols, in both concentrations. The nanoparticles showed no antifungal action for the materials tested at any concentration, neither was zone innibition. However, the solution presented minimal inhibitory concentration to 2.000 ppm. We conclude that low concentrations nanoparticles do not affect the mechanical characteristics and surface of ... / Doutor

Orientador: Marcelo Ferraz Mesquita / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:45:55Z (GMT). No. of bitstreams: 1 Botega_DanielaMaffei_D.pdf: 1293355 bytes, checksum: a37a5034b23a6bf25d957f6db83d9d6d (MD5) Previous issue date: 2005 / Resumo: Este trabalho avaliou a resistência à tração e alongamento de amostras de diferentes diâmetros (1,5, 2,0 e 5,0 mm) fundidas em titânio comercialmente puro (Tritan - Dentaurum), submetidas a soldagem a laser em diferentes distâncias de soldagem (0,0 mm e 0,6 mm). Foram confeccionadas 45 amostras, separadas em 9 grupos (n= 5): G1) diâmetro 1,5 mm controle (não submetidas à soldagem); G2) diâmetro 1,5 mm e distância zero; G3) diâmetro 1,5 mm e distância 0,6 mm; G4) diâmetro 2,0 mm (controle); G5) diâmetro 2,0 mm e distância zero; G6) diâmetro 2,0 mm e distância 0,6 mm; G7) diâmetro 5,0 mm (controle); G8) diâmetro 5,0 mm e distância zero; e G9) diâmetro 5,0 mm e distância 0,6 mm. Após a fundição, todas as amostras, exceto as dos grupos controle, foram seccionadas e unidas, utilizando-se resina acrílica autopolimerizável, para a soldagem com as seguintes especificações: 320V / 9 milisegundos (ms) (amostra de 1,5mm), 330V / 9 ms (amostra de 2,0mm) e 350V / 9 ms (amostra de 5,0mm) em um aparelho de soldagem a laser Desktop-F (Dentaurum KG). Após a soldagem, foram submetidas ao ensaio de resistência à tração até a ruptura em máquina servohidráulica (MTS 810) com velocidade de 1mm/min. As superfícies de fratura foram analisadas em microscópio eletrônico de varredura (M.E.V. ¿ JEOL). Os resultados foram submetidos à Análise de Variância e teste de Tukey (p<0,05). Os valores médios de resistência máxima à tração (MPa) revelaram que o grupo controle apresentou valores, para todos os diâmetros, estatisticamente superiores aos grupos experimentais, que não diferiram entre si, exceto para 5,0 mm de diâmetro, onde a distância de 0,6 mm apresentou maiores valores (G1- 595,64; G2- 496,46; G3- 441,04; G4- 516,54; G5- 397,85; G6- 442,15; G7- 560,19; G8- 200,88; e G9- 316,04). Os valores médios de alongamento (mm) para o grupo controle foram estatisticamente superiores aos experimentais nos diâmetros 2,0 e 5,0 mm, não havendo diferença entre os grupos no diâmetro 1,5 mm. Não houve diferença estatística entre os grupos experimentais (G1- 1,68; G2- 1,47; G3- 1,20; G4- 2,61; G5- 1,34; G6- 1,05; G7- 2,51; G8- 0,92; e G9- 1,32). As imagens revelaram eficiente penetração do laser nas amostras de 1,5 e 2,0 mm de diâmetro, e insuficiente nas de 5,0 mm de diâmetro. A resistência à tração para todos os diâmetros e o alongamento para os diâmetros 2,0 e 5,0 mm foram influenciados pela técnica de soldagem a laser de forma significativa. Dentre as amostras de 5,0 mm de diâmetro submetidas à soldagem a laser, aquelas com distância de 0,6 mm entre as partes apresentaram maior alcance do feixe de laser / Abstract: The aim of this study was to evaluate the tensile strength and elongation of commercially pure titanium samples (Tritan - Dentaurum), with 3 diameters (1.5, 2.0 and 5.0 mm of diameter x 42 mm length), submitted to laser welding in 2 distances of soldering (0.0 mm and 0.6 mm). 45 samples were made (dumbbell), divided in 9 groups (5 each): G1) 1.5 mm control (without welding procedures); G2) 1.5 mm and no distance; G3) 1.5 mm and 0.6 mm of distance; G4) 2.0 mm (control); G5) 2.0 mm and no distance; G6) 2.0 mm and 0.6 mm; G7) 5.0 mm (control); G8) 5.0 mm and no distance; G9) 5.0 mm and 0.6 mm of distance. After casting, all the samples, except control groups, were sectioned and joined with self curing acrylic resin for the welding procedures, as follows: 320V/9 miliseconds (ms) (samples of 1.5mm), 330V/9ms (samples of 2.0 mm) and 350V/9ms (samples of 5.0 mm) using a laser welding machine Desktop-F (Dentaurum KG). After soldering, the samples were submitted to tensile test using a servohidraulic machine MTS-810 with speed of 1mm/min. The fractured surfaces were microscopically analyzed (M.E.V. ¿ JEOL). Data were submitted to ANOVA and Tukey¿s test (p<0.05). The tensile strength mean values (MPa) for control group were statistically higher than the experimental groups, which did not differ from each other, except for 5.0 mm group, in which the samples with 0.6 mm of distance had the highest values (G1- 595.64; G2- 496.46; G3- 441.04; G4- 516.54; G5- 397.85; G6- 442.15; G7- 560.19; G8- 200.88 and G9- 316.04). The mean values of elongation (mm) for the control group were statistically higher than experimental groups in the 2.0 and 5.0 mm, having no difference for the groups with 1.5 mm. There was no difference between the experimental groups (G1- 1.68; G2- 1.47; G3- 1.20; G4- 2.61; G5- 1.34; G6- 1.05; G7- 2.51; G8- 0.92; and G9- 1.32). The SEM images showed a good penetration of laser in the samples of 1.5 and 2.0 mm of diameter, and insufficient penetration of laser in the samples of 5.0 mm. Ductile fractures were predominant in all groups with the presence of dimples. Laser welding procedure is an effective method of joining titanium, however, caused a decrease in the values of tensile strength for all diameters and elongation for 2.0 and 5.0 mm. Among the 5.0 mm samples submitted to laser welding procedures, the laser welding was more effective for the samples with distance of 0.6 mm between the parts / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientadores: Altair Antoninha Del Bel Cury, Pedro Luiz Rosalen / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T09:42:20Z (GMT). No. of bitstreams: 1 Silva_WanderJoseda_M.pdf: 3982460 bytes, checksum: cc52755a091670127495a82d48ac39c9 (MD5) Previous issue date: 2005 / Resumo: Na candidose, ou estomatite induzida por prótese, a Candida albicans atua como o patógeno mais importante e mais virulento. A terapêutica indicada no tratamento são os agentes antifúngicos (AA) como Fluconazol (FLU) e Nistatina (NYS) e mais recentemente tem sido indicado soluções a base de própolis. Entretanto, a literatura é escassa sobre os efeitos destes agentes nos materiais utilizados para confecção de bases de próteses. O objetivo deste estudo foi verificar a influência de NYS, FLU, e gel orobase (GO) de própolis sobre a superfície de resinas acrílicas durante período de 14 dias. Água destilada e GO manipulado sem princípio ativo foram utilizadas como grupos controle. Espécimes (3,0 x 2,5 x 0,5 cm) foram fabricados a partir de moldes de cera, com resina acrílica polimerizada em banho de água (Jet Clássico, grupos 1 a 5) ou com energia de microondas (OndaCryl, grupos 6 a 10), ambas processadas de acordo com as instruções dos fabricantes. Após a confecção, os espécimes receberam acabamento e polimento e a rugosidade superficial (RS), ângulo de contato (AC), energia livre de superfície (ELS) e dureza de superfície (DS) foram mensuradas. Os tratamentos de superfície foram feitos com os AA e grupos controles e os espécimes foram escovados com dentifrício e escova macia 3 vezes ao dia durante os 14 dias. Os meios de imersão foram substituídos diariamente. Novas mensurações para as variáveis foram executadas em 3, 7, 10 e 14 dias de exposição. Os compostos dos AA que poderiam ser incorporados à resina acrílica foram mensurados por cromatografia líquida. Os resultados mostraram que a RS aumentou para ambas as resinas acrílicas, mas não diferiram entre si (p>0,05); os grupos G2 e G7, contendo propolis mostraram valores maiores e estatisticamente diferente dos demais agentes nos tempos de T7, T10 e T14 (p<0,05). Também com o passar do tempo os grupos G1, G3, G4 e G8 mostraram valores de rugosidade aumentada e significantemente diferente dos demais tempos (p<0,05, teste de Tukey). Nas análises de cromatografia não foi detectada a presença de FLU ou NYS, assim como não foi detectada diferença entre as resinas acrílicas (p>0,05, teste de Tukey) quanto a compostos do GO. A microscopia eletrônica de varredura mostrou as alterações sobre a superfície dos espécimes após o tratamento. Dentro dos limites deste estudo, é possível concluir que os agentes antifúngicos podem interferir com propriedades da superfície de resina acrílica que são associadas a adesão de Candida sp / Abstract: The high prevalence of candidosis in denture wearers, and its association to Candida spp. as principal pathogen is well established. Besides, there are many studies about candidosis etiology, predisposing factors and its treatment using antifungal agents such as Fluconazole (FLU) and Nystatin (NYS). However, little work has been performed to explore the effects of these antifungal agents on acrylic resin surface. The aim of this study was to verify the influence of NYS, FLU, and propolis orobase gel over surface acrylic resins. Distillate water and orobase gel without any active component were used as control groups. Specimens (3.0 x 2.5 x 0.5 cm) were fabricated from wax moulds using heat cured (HC = Clássico; groups 1 to 5) or microwave cured (MW = Onda Cry; groups 6 to 10) acrylics resin, both processed according to manufacturers¿ instructions. After polymerized the specimens were polished and had their surface roughness (SR), contact angle (CA), surface free energy (SFE) and hardness (HD) measured. The surface treatments were done with antifungal agents and controls. The specimens had their surface toothbrushed 3 times a day during the 14 days of exposure to antifungal agents. The antifungal agents¿ solutions and gels were replaced daily. Measurements to all variables were performed in days 3, 7, 10 and 14. Components from antifungal agents that could be incorporated to acrylic resin measured with liquid chromatography. The results showed that SR increased for both acrylic resins and the treatment with propolis showed higher values and statistically different from the others (p<0.05). No statistical difference (Tukey test, p>0.05) was found regarding CA and SFE. No presence of FLU or NYS were detected in chromatography and no difference (p<0.05) between acrylic resins were detect to orobase gels detection. Scanning electronic microscopy evaluation showed surface alterations after treatment. Within the limits of this study, it is possible to conclude that antifungal agents are able to interfere with the surface properties of acrylic resins that are associated to Candida spp. adhesion / Mestrado / Protese Dental / Mestre em Clínica Odontológica