Thesis (M.S.)--University of Alabama at Birmingham, 2008. / Title from first page of PDF file (viewed Feb. 16, 2009). Includes bibliographical references (p. 49-57).

Thesis (M.S.)--University of Michigan, 2001. / Includes bibliographical references.

O objetivo deste estudo foi analisar a força de retenção de dois cimentos resinosos utilizados na técnica de cimentação passiva para implantes osseointegráveis, Panavia F e RelyX U100, avaliando essa propriedade na sua aplicação em espécimes de três tipos de diferentes metais, NiCr (Verabond 2, Aalba Dental), NiCrTi (Tilite Ômega, Talladium) e Titânio (Ti c.p., grau 2, Realum), submetidos ou não à termociclagem. Noventa e seis cilindros calcináveis (Conexão Sistemas de Próteses) foram encerados de forma padronizada, fundidos (32 cilindros em cada tipo de liga) e cimentados sobre cilindros de titânio (Conexão Sistemas de Próteses). Os corpos-de-prova foram distribuídos em 12 grupos (n = 8) de acordo com o tipo de liga, cimento e ciclagem térmica. Todos os espécimes foram submetidos a imersão em água destilada a 37º C por 24 horas, entretanto apenas metade deles a um ensaio de termociclagem em uma máquina de simulação de ciclos térmicos MSCT-3 por 5000 ciclos durante 30 dias. Todos os corpos-de-prova foram submetidos a ensaios de tração em uma máquina de ensaios mecânicos EMIC-DL2000 (velocidade = 5mm / min e célula de carga = 500 Kgf ). A análise estatística evidenciou resistência de união à tração do cimento RelyX U100 superior ao cimento Panavia F, independente do tipo de metal utilizado, com médias de até 71,18 Kgf e 55,08 Kgf respectivamente. O ensaio de termociclagem não exibiu interferência na resistência de união de ambos cimentos. / The aim of this study was to analyze the bond strength of two resin cements used in the passive cementation technique for osseointegrated implants, Panavia F and RelyX U100, evaluating this property on its application in specimens of three different metal types, NiCr (Verabond 2, Dental Aalba), NiCrTi (Tilite Omega, Talladium) and Titanium (Ti c.p., degree 2, Realum), submitted or not to termocycling assay. Ninety six calcined cylinders (Conexão Sistemas de Próteses) had been waxed of standardized form, casted (32 in each type of league) and cemented on titanium cylinders (Conexão Sistemas de Próteses). The specimens were distributed enter 12 groups (n = 8) in accordance with the type of metal, cement and thermocycling. All specimens were submitted to an immersion in distilled water at 37ºC for 24 hours, however only half of them to a termocycling assay in a simulation thermal cycles machine MSCT-3 for 5000 cycles during 30 days. All specimens were submitted to a tensile test in a mechanical test machine EMIC-DL2000 (speed = 5mm/min and cell load = 500Kgf). The statistics analysis evidenced tensile strength of the RelyX U100 cement greater than Panavia F cement independent of the metal league type used with averages until 71,18 Kgf and 55,08 Kgf respectively. The termocycling assay did not show interference in the tensile strength of both cements.

O objetivo deste estudo foi analisar a força de retenção de dois cimentos resinosos utilizados na técnica de cimentação passiva para implantes osseointegráveis, Panavia F e RelyX U100, avaliando essa propriedade na sua aplicação em espécimes de três tipos de diferentes metais, NiCr (Verabond 2, Aalba Dental), NiCrTi (Tilite Ômega, Talladium) e Titânio (Ti c.p., grau 2, Realum), submetidos ou não à termociclagem. Noventa e seis cilindros calcináveis (Conexão Sistemas de Próteses) foram encerados de forma padronizada, fundidos (32 cilindros em cada tipo de liga) e cimentados sobre cilindros de titânio (Conexão Sistemas de Próteses). Os corpos-de-prova foram distribuídos em 12 grupos (n = 8) de acordo com o tipo de liga, cimento e ciclagem térmica. Todos os espécimes foram submetidos a imersão em água destilada a 37º C por 24 horas, entretanto apenas metade deles a um ensaio de termociclagem em uma máquina de simulação de ciclos térmicos MSCT-3 por 5000 ciclos durante 30 dias. Todos os corpos-de-prova foram submetidos a ensaios de tração em uma máquina de ensaios mecânicos EMIC-DL2000 (velocidade = 5mm / min e célula de carga = 500 Kgf ). A análise estatística evidenciou resistência de união à tração do cimento RelyX U100 superior ao cimento Panavia F, independente do tipo de metal utilizado, com médias de até 71,18 Kgf e 55,08 Kgf respectivamente. O ensaio de termociclagem não exibiu interferência na resistência de união de ambos cimentos. / The aim of this study was to analyze the bond strength of two resin cements used in the passive cementation technique for osseointegrated implants, Panavia F and RelyX U100, evaluating this property on its application in specimens of three different metal types, NiCr (Verabond 2, Dental Aalba), NiCrTi (Tilite Omega, Talladium) and Titanium (Ti c.p., degree 2, Realum), submitted or not to termocycling assay. Ninety six calcined cylinders (Conexão Sistemas de Próteses) had been waxed of standardized form, casted (32 in each type of league) and cemented on titanium cylinders (Conexão Sistemas de Próteses). The specimens were distributed enter 12 groups (n = 8) in accordance with the type of metal, cement and thermocycling. All specimens were submitted to an immersion in distilled water at 37ºC for 24 hours, however only half of them to a termocycling assay in a simulation thermal cycles machine MSCT-3 for 5000 cycles during 30 days. All specimens were submitted to a tensile test in a mechanical test machine EMIC-DL2000 (speed = 5mm/min and cell load = 500Kgf). The statistics analysis evidenced tensile strength of the RelyX U100 cement greater than Panavia F cement independent of the metal league type used with averages until 71,18 Kgf and 55,08 Kgf respectively. The termocycling assay did not show interference in the tensile strength of both cements.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Passivity fit of an implant fixed partial denture (FPD) is one of major factor in treatment success. Among various factors that influence the passive fit of a prostheses is the kind of retained. Thus, the aim of this study was to evaluate, with the aid of linear strain gages (gauges), the tension generated around two implants after installation of a three-unit implant FPD. Five groups were analyzed (n = 5): 1. Control (only the abutments on implants); 2. Cement-retained prosthesis; 3. Screw-retained prosthesis made from plastic cylinders; 4. Screw-retained prosthesis made from Co-Cr machined collar abutments; 5. Hybrid prosthesis (cemented / screwed). For the investigation, homogeneous polyurethane experimental model with two parallel external hexagon implants was used. From this model, transfer impression and one master stone cast was made on which all frameworks were made accompanying a wax pattern. Aiming to measure the tensions, four strain gauges for each implant placed in the mesial, distal, buccal and lingual were glued on the top surface of the experimental block. The tests were performed by installing the samples on the implants according to the characteristics of each group. Five repetitions of readings for each specimen were performed. One-way ANOVA and Tukey test were applied to the average values (p <.05). The mean and standard deviation were obtained: Group 1 (48.71 με ± 0.29), Group 2 (60.03 με ± 22.65) and group 3 (254.15 με ± 46.23), Group 4 (215,42 με ± 30.48), Group 5 (70.05 με ± 13.78). These results showed that the cement-retained prostheses have the ability to produce less stress on the peri-implant area when compared to the screw-retained prosthesis (p≤.05). It was observed that the hybrid group had similar performance to the cement-retained prostheses and the control group (p>.05). Furthermore, the screw-retained prosthesis made from plastic cylinders showed similar performance to the Co-Cr machined collar abutments (p>.05). Finally, these results demonstrated that the generated tension to the peri-implant tissues is directly related to the type of retention. / A passividade de assentamento de uma prótese parcial fixa sobre implantes é um fator primordial para o sucesso no tratamento. Dentre vários fatores que interferem na adaptação passiva de uma prótese está o tipo de retenção utilizado. Desta forma, o objetivo deste estudo foi avaliar, com o auxílio de extensômetros elétricos lineares (strain gauges), a tensão gerada ao redor de dois implantes após assentamento de uma prótese parcial fixa implantossuportada de 3 elementos. Cinco grupos foram analisados (n=5): 1. Controle (apenas os munhões sobre os implantes); 2. Prótese Cimentada; 3. Prótese Parafusada confeccionada com cilindros plásticos; 4. Prótese Parafusada confeccionada com cilindros com base de Co-Cr; 5. Prótese híbrida (cimentada/parafusada). Para a investigação, foi utilizado um modelo experimental homogêneo a base de poliuretano com dois implantes hexágono externo paralelos entre si. Visando medir as tensões, foram colados na superfície superior do bloco experimental quatro strain gauges para cada implante, posicionados nas faces mesial, distal, vestibular e lingual. Os testes foram executados instalando os corpos de prova sobre os implantes de acordo com as características de cada grupo. Realizou-se 5 repetições de leituras para cada corpo de prova. Análise de variância e teste de Tukey foram aplicados sobre os valores médios obtidos, utilizando um nível de significância de 0,05. A média e desvio-padrão obtidos foram: Grupo 1 (48,71 με ± 0,29); Grupo 2 (60,03 με ± 22,65); Grupo 3 (254,15 με ± 46,23), Grupo 4 (215,42 με ± 30,48), Grupo 5 (70,05 με ± 13,78). Esses resultados mostraram que as próteses cimentadas geraram menos tensão à região periimplantar quando comparadas às próteses parafusadas (p=0,0004/p=0,0008). Observou-se que o grupo híbrido teve desempenho semelhante às próteses cimentadas e ao grupo controle (p=0,9540/p=0,3402). Além disso, as próteses parafusadas confeccionadas com cilindros plásticos apresentaram desempenho semelhante às confeccionadas com cilindros com a base de Co-Cr (p=0,1580). Por fim, estes resultados demonstraram que a tensão gerada aos tecidos perimplantares está diretamente relacionada ao tipo de retenção.