Thesis (M.S.)--University of Michigan, 2003. / Includes bibliographical references.

Thesis (M.S.)--The University of Michigan, 1986. / eContent provider-neutral record in process. Description based on print version record.

Made available in DSpace on 2016-02-05T18:30:10Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-08-28. Added 1 bitstream(s) on 2016-02-05T18:34:20Z : No. of bitstreams: 1 000857869.pdf: 2789826 bytes, checksum: cecfa33b798ebbee35330f861246deea (MD5) / O objetivo do presente estudo foi avaliar o efeito da incorporação do trimetafosfato de sódio (TMP) microparticulado (m) e nanoparticulado (n) ao cimento de ionômero de vidro (CIV) nas propriedades físico-mecânicas e na desmineralização do esmalte. Foram confeccionados corpos-de-prova (n=54) para cada grupo experimental: CIV sem TMP (CIV), CIV com TMPm 3,5%, 7% e 14% e CIV com TMPn 3,5%, 7% e 14%. Seis corposde- prova foram utilizados na determinação da liberação de fluoreto (F) e TMP em soluções de desmineralização e de remineralização durante 15 dias. As propriedades físico-mecânicas avaliadas 24 horas e 7 dias após a confecção foram: resistência à compressão (n=12), resistência à tração diametral (n=12), dureza de superfície do material (n=6) e grau de conversão de monômeros (n=6). Para o estudo da desmineralização do esmalte, corpos-de-prova (n=12) foram adaptados a blocos de esmalte selecionados pelo teste de dureza de superfície inicial (DS1) e submetidos às ciclagens de pH. A seguir, determinou-se a dureza de superfície final (DS2), em secção longitudinal (DSL) e a concentração de F no esmalte. Testes paramétricos e não paramétricos foram realizados, após a verificação da homocedasticidade dos dados (p<0,05). A adição de 14% de TMP levou a maior média de liberação de F (p<0,05) e os demais grupos foram similares ao CIV (p>0,05). Maior liberação de TMP foi observada com 14% microparticulado (p<0,05). A incorporação do TMP ao CIV promoveu uma redução média nas propriedades mecânicas de 21% (tração), 10% (compressão) e 18% (dureza), após 24 horas e em 18%, 23% e 12%, após 7 dias. O grau de conversão foi menor com adição de 14% TMP quando comparado ao CIV após 24 horas (p<0,05); no tempo de 7 dias não houve diferença entre os grupos (p>0,05). A adição de 7% e 14% de... / The aim of this study was to evaluate the effect of addition of sodium trimetaphosphate (TMP) microparticle (m) and nanoparticle (n) to the glass ionomer cement (GIC) on the physico-mechanical properties and demineralization of the enamel. Specimens (n=54) were fabricated from each experimental group: GIC without TMP (GIC), GIC with 3.5%, 7% and 14% TMPm and GIC with 3.5%, 7% and 14% TMPn. To determine the release of fluoride (F) and TMP it was used six specimens immersed into a demineralization and remineralization solution during 15 days. The physico-mechanical properties evaluated 24 hours and 7 days after fabrication were: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=6). For the study of enamel demineralization, specimens (n=12) were attached to enamel blocks selected by the initial surface hardness test (SH1) and submitted to the pH-cycling. Following, final surface (SH2) and cross-sectional (CSH) hardness, as well as enamel F concentration were determined. Parametric and non-parametric tests were performed after checking the data homoscedasticity (p<0.05). The addition of 14% TMP led to higher mean release of F (p<0.05) and the other groups were similar to the GIC (p>0.05). The release of TMP was higher with 14% microparticulate (p<0.05). The addition of TMP at GIC promoted an average reduction of mechanical properties of 21% (tensile), 10% (compressive) and 18% (hardness) after 24 hours and 18%, 23% and 12% after 7 days. The degree of conversion was lower with addition of 14% TMP compared to the GIC after 24 hours (p<0.05); at 7 days there was no difference between groups (p>0.05). Addition of 7% and 14% TMP reduced mineral loss and increased enamel F concentration when compared...

Made available in DSpace on 2014-06-11T19:31:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-07-26Bitstream added on 2014-06-13T20:41:41Z : No. of bitstreams: 1 000737081.pdf: 1574523 bytes, checksum: 5bd18c418b9c0819dc40248db7d21062 (MD5) / O objetivo deste estudo in vitro foi avaliar o efeito da ciclagem de pH erosiva com soluções que simulam a erosão dental, provenientes de fatores extrínsecos ou intrínsecos, na dureza e módulo de elasticidade da dentina restaurada com materiais restauradores contendo fluoretos. Quarenta e cinco blocos de dentina medindo 6 x 6 mm foram restaurados com cinco materiais restauradores: sistema adesivo de condicionamento total Adper Single Bond 2 + resina composta Filtek Z250; sistema adesivo autocondicionante One Up Bond F + resina composta Filtek Z250; sistema adesivo autocondicionante Clearfil SE Protect + resina composta Filtek Z250; cimento de ionômero de vidro convencional Riva Self Cure; cimento de ionômero de vidro resinoso Riva Light Cure. Mensurações da dureza Martens e módulo de elasticidade da dentina subjacente à interface de união (10μm, 30μm, 50μm e 70μm) foram realizadas em ultramicrodurômetro digital antes e após a imersão em soluções de água deionizada, ácido cítrico ou ácido clorídrico. Após a ciclagem, os valores de dureza da dentina diminuíram para todos os materiais. Para a dentina restaurada com Adper Single Bond 2, os menores valores foram encontrados próximo a camada híbrida (10 μm) enquanto que para a dentina restaurada com os sistemas adesivos autocondicionantes (Clearfil SE Protect e One Up Bond F), esses valores foram mantidos em todas as distâncias avaliadas. Para os materiais Riva Self Cure e Riva Light Cure somente nas leituras iniciais a distância foi determinante na dureza, uma vez que quanto maior a distância da interface de união, maiores eram os valores encontrados. Com relação ao módulo de elasticidade, para a dentina restaurada com Adper Single Bond 2, não houve diferença significante em todas as distâncias avaliadas. Já na dentina restaurada com os sistemas adesivos autocondicionantes... / The aim of this study was to evaluate the effect of erosive pH cycling with solutions that simulate dental erosion in the hardness and elastic modulus of dentin restored with fluoride-releasing restorative materials. Forty five bovine dentine slabs (6,0 mm x 6,0 mm) were restored with 5 restorative materials: Adper Single Bond 2 total-etch adhesive system + Filtek Z250 composite resin; One Up Bond F self-etching adhesive system + Filtek Z250 composite resin; Clearfil SE Protect self-etching adhesive system + Filtek Z250 composite resin; Riva Self Cure conventional glass ionomer cement and Riva Light Cure light curing glass ionomer cement. The values of hardness and elastic modulus of dentin (10μm, 30μm, 50μm e 70μm) were evaluated in digital ultramicrohardner tester before and after immersion in solutions of deionized water, citric acid and hydrochloric acid. After cycling, the hardness of dentin decreased for all materials. For dentin restored with Adper Single Bond 2, the lowest values were found close to hybrid layer (10 μm), while for the dentin restored with One Up Bond F and Clearfil SE Protect, the values remained unaltered in all the evaluated distances. For dentin restored with Riva Self Cure and Riva Light Cure only in the initial measurements, the distance had a significant effect in the hardness values, since the greater the distance to the bonding interface, higher values of hardness were found. For the elastic modulus analysis, dentin restored with Adper Single Bond 2 showed no significant difference when distances from bonding interface were compared. Dentin restored with self-etching adhesive system (One Up Bond F and Clearfil SE Protect) and glass ionomer cements (Riva Self Cure and Riva Light Cure) showed a reduction in the elastic modulus values from the bonding interface, but after 30 μm the difference was not significant.

Made available in DSpace on 2015-06-17T19:34:29Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-02-25. Added 1 bitstream(s) on 2015-06-18T12:48:45Z : No. of bitstreams: 1 000830085.pdf: 704356 bytes, checksum: fbb6f56d09478a8adc55d7eb2addad71 (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / O objetivo do presente estudo foi avaliar as propriedades antimicrobianas, físico-mecânicas e de liberação de fluoreto do cimento de ionômero de vidro (CIV) associado ao hexametafosfato de sódio (HMP) microparticulado e nanoparticulado. Inicialmente, foram obtidas soluções de HMP nas concentrações 1, 3, 6, 9 e 12 % e a atividade antibacteriana foi avaliada contra Streptococcus mutans, Lactobacillus acidophilus e Actinomyces israelli por meio do teste de difusão em ágar. A mesma metodologia foi empregada para determinar a atividade antimicrobiana do CIV associado ao HMP nas concentrações de 6, 9 e 12 % microparticulado ou nanoparticulado. Foi determinada a liberação de fluoreto (F) e HMP em soluções de desmineralização e remineralização. Além disso, as resistências à tração diametral e compressão, dureza de superfície e grau de conversão de monômeros foram analisados. Testes paramétricos e não paramétricos foram realizados, após a verificação da homocedasticidade dos dados (p < 0,05). As soluções de 6, 9 e 12 % de HMP apresentaram melhor atividade antimicrobiana contra as bactérias testadas, sendo essas concentrações incorporadas ao CIV. Todas as concentrações de HMP associado ao CIV tiveram atividade antimicrobiana para todas as bactérias. Observou-se uma relação dose-resposta entre concentração de HMP no CIV e a atividade antimicrobiana. Com relação à liberação de F e HMP, os maiores valores ocorreram no primeiro dia em todos os grupos e as maiores médias de liberação ocorreram nos grupos contendo 9 e 12 % de HMP nanoparticulado. Entretanto, a incorporação do HMP ao CIV reduziu as propriedades físico-mecânicas quando comparado ao CIV mostrando uma relação dose-resposta. Concluiu-se que a incorporação de HMP no CIV melhora a atividade antimicrobiana e aumenta a liberação de F, porém reduz suas... / The aim of this study was to evaluate antimicrobial, physico-mechanical and fluoride release properties of the glass ionomer cement (GIC) associated with HMP microparticle and nanoparticle. Initially, solutions of HMP were obtained at concentrations of 1, 3, 6, 9 and 12 %, and the antibacterial activity was evaluated against Streptococcus mutans, Lactobacillus acidophilus and Actinomyces israelli by agar diffusion test. The same methodology was used to determine the antimicrobial activity of GIC associated with HMP at concentrations of 6, 9 and 12 % microparticle or nanoparticle. The release of F and HMP were determined in demineralization and remineralization solutions. Furthermore, the resistance to diametral tensile and compression, surface hardness and the degree of conversion of monomers were measured. Parametric and non-parametric tests were performed, after checking homocedasticity data (p < 0.05). The solutions of 6, 9 and 12 % of HMP showed better antimicrobial activity against all bacteria tested, and these concentrations incorporated into the CIV. All concentrations of HMP incorporated into the GIC had antimicrobial activity for all bacteria. There was a dose-response relationship between concentration of HMP in the GIC and antimicrobial activity. Regarding the release of F and HMP, higher values occurred on the first day in all groups and the highest levels of release occurred in groups containing 9 and 12 % of HMP nanoparticle. However the incorporation of HMP in the GIC reduced values of physical and mechanical tests when compared to the GIC, showing a dose-response relationship. It was concluded that the incorporation of HMP in GIC improves antimicrobial activity and increase the release of fluoride, but reduces its physical and mechanical properties. The reduction of particulate HMP led to better antimicrobial and fluoride release results

Orientador: Paulo Henrique dos Santos / Banca: André Luiz Fraga Briso / Banca: Renato Herman Sundfeld / Banca: Cláudia Batitucci dos Santos Daroz / Banca: Anderson Catelan / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito da ciclagem de pH erosiva com soluções que simulam a erosão dental, provenientes de fatores extrínsecos ou intrínsecos, na dureza e módulo de elasticidade da dentina restaurada com materiais restauradores contendo fluoretos. Quarenta e cinco blocos de dentina medindo 6 x 6 mm foram restaurados com cinco materiais restauradores: sistema adesivo de condicionamento total Adper Single Bond 2 + resina composta Filtek Z250; sistema adesivo autocondicionante One Up Bond F + resina composta Filtek Z250; sistema adesivo autocondicionante Clearfil SE Protect + resina composta Filtek Z250; cimento de ionômero de vidro convencional Riva Self Cure; cimento de ionômero de vidro resinoso Riva Light Cure. Mensurações da dureza Martens e módulo de elasticidade da dentina subjacente à interface de união (10μm, 30μm, 50μm e 70μm) foram realizadas em ultramicrodurômetro digital antes e após a imersão em soluções de água deionizada, ácido cítrico ou ácido clorídrico. Após a ciclagem, os valores de dureza da dentina diminuíram para todos os materiais. Para a dentina restaurada com Adper Single Bond 2, os menores valores foram encontrados próximo a camada híbrida (10 μm) enquanto que para a dentina restaurada com os sistemas adesivos autocondicionantes (Clearfil SE Protect e One Up Bond F), esses valores foram mantidos em todas as distâncias avaliadas. Para os materiais Riva Self Cure e Riva Light Cure somente nas leituras iniciais a distância foi determinante na dureza, uma vez que quanto maior a distância da interface de união, maiores eram os valores encontrados. Com relação ao módulo de elasticidade, para a dentina restaurada com Adper Single Bond 2, não houve diferença significante em todas as distâncias avaliadas. Já na dentina restaurada com os sistemas adesivos autocondicionantes ... / Abstract: The aim of this study was to evaluate the effect of erosive pH cycling with solutions that simulate dental erosion in the hardness and elastic modulus of dentin restored with fluoride-releasing restorative materials. Forty five bovine dentine slabs (6,0 mm x 6,0 mm) were restored with 5 restorative materials: Adper Single Bond 2 total-etch adhesive system + Filtek Z250 composite resin; One Up Bond F self-etching adhesive system + Filtek Z250 composite resin; Clearfil SE Protect self-etching adhesive system + Filtek Z250 composite resin; Riva Self Cure conventional glass ionomer cement and Riva Light Cure light curing glass ionomer cement. The values of hardness and elastic modulus of dentin (10μm, 30μm, 50μm e 70μm) were evaluated in digital ultramicrohardner tester before and after immersion in solutions of deionized water, citric acid and hydrochloric acid. After cycling, the hardness of dentin decreased for all materials. For dentin restored with Adper Single Bond 2, the lowest values were found close to hybrid layer (10 μm), while for the dentin restored with One Up Bond F and Clearfil SE Protect, the values remained unaltered in all the evaluated distances. For dentin restored with Riva Self Cure and Riva Light Cure only in the initial measurements, the distance had a significant effect in the hardness values, since the greater the distance to the bonding interface, higher values of hardness were found. For the elastic modulus analysis, dentin restored with Adper Single Bond 2 showed no significant difference when distances from bonding interface were compared. Dentin restored with self-etching adhesive system (One Up Bond F and Clearfil SE Protect) and glass ionomer cements (Riva Self Cure and Riva Light Cure) showed a reduction in the elastic modulus values from the bonding interface, but after 30 μm the difference was not significant. / Doutor

Orientador: Denise Pedrini / Coorientador: Alberto Carlos Botazzo Delbem / Coorientador: Cristiane Duque / Banca: Débora Barros Barbosa / Banca: Adelisa Rodolfo Ferreira Tiveron / Resumo: O objetivo do presente estudo foi avaliar as propriedades antimicrobianas, físico-mecânicas e de liberação de fluoreto do cimento de ionômero de vidro (CIV) associado ao hexametafosfato de sódio (HMP) microparticulado e nanoparticulado. Inicialmente, foram obtidas soluções de HMP nas concentrações 1, 3, 6, 9 e 12 % e a atividade antibacteriana foi avaliada contra Streptococcus mutans, Lactobacillus acidophilus e Actinomyces israelli por meio do teste de difusão em ágar. A mesma metodologia foi empregada para determinar a atividade antimicrobiana do CIV associado ao HMP nas concentrações de 6, 9 e 12 % microparticulado ou nanoparticulado. Foi determinada a liberação de fluoreto (F) e HMP em soluções de desmineralização e remineralização. Além disso, as resistências à tração diametral e compressão, dureza de superfície e grau de conversão de monômeros foram analisados. Testes paramétricos e não paramétricos foram realizados, após a verificação da homocedasticidade dos dados (p < 0,05). As soluções de 6, 9 e 12 % de HMP apresentaram melhor atividade antimicrobiana contra as bactérias testadas, sendo essas concentrações incorporadas ao CIV. Todas as concentrações de HMP associado ao CIV tiveram atividade antimicrobiana para todas as bactérias. Observou-se uma relação dose-resposta entre concentração de HMP no CIV e a atividade antimicrobiana. Com relação à liberação de F e HMP, os maiores valores ocorreram no primeiro dia em todos os grupos e as maiores médias de liberação ocorreram nos grupos contendo 9 e 12 % de HMP nanoparticulado. Entretanto, a incorporação do HMP ao CIV reduziu as propriedades físico-mecânicas quando comparado ao CIV mostrando uma relação dose-resposta. Concluiu-se que a incorporação de HMP no CIV melhora a atividade antimicrobiana e aumenta a liberação de F, porém reduz suas... / Abstract: The aim of this study was to evaluate antimicrobial, physico-mechanical and fluoride release properties of the glass ionomer cement (GIC) associated with HMP microparticle and nanoparticle. Initially, solutions of HMP were obtained at concentrations of 1, 3, 6, 9 and 12 %, and the antibacterial activity was evaluated against Streptococcus mutans, Lactobacillus acidophilus and Actinomyces israelli by agar diffusion test. The same methodology was used to determine the antimicrobial activity of GIC associated with HMP at concentrations of 6, 9 and 12 % microparticle or nanoparticle. The release of F and HMP were determined in demineralization and remineralization solutions. Furthermore, the resistance to diametral tensile and compression, surface hardness and the degree of conversion of monomers were measured. Parametric and non-parametric tests were performed, after checking homocedasticity data (p < 0.05). The solutions of 6, 9 and 12 % of HMP showed better antimicrobial activity against all bacteria tested, and these concentrations incorporated into the CIV. All concentrations of HMP incorporated into the GIC had antimicrobial activity for all bacteria. There was a dose-response relationship between concentration of HMP in the GIC and antimicrobial activity. Regarding the release of F and HMP, higher values occurred on the first day in all groups and the highest levels of release occurred in groups containing 9 and 12 % of HMP nanoparticle. However the incorporation of HMP in the GIC reduced values of physical and mechanical tests when compared to the GIC, showing a dose-response relationship. It was concluded that the incorporation of HMP in GIC improves antimicrobial activity and increase the release of fluoride, but reduces its physical and mechanical properties. The reduction of particulate HMP led to better antimicrobial and fluoride release results / Mestre

Orientadora: Denise Pedrini Ostini / Coorientador: Alberto Carlos Botazzo Delbem / Banca: Marcelle Danelon / Banca: Adelisa Rodolfo Ferreira Tiveron / Resumo: O objetivo do presente estudo foi avaliar o efeito da incorporação do trimetafosfato de sódio (TMP) microparticulado (m) e nanoparticulado (n) ao cimento de ionômero de vidro (CIV) nas propriedades físico-mecânicas e na desmineralização do esmalte. Foram confeccionados corpos-de-prova (n=54) para cada grupo experimental: CIV sem TMP (CIV), CIV com TMPm 3,5%, 7% e 14% e CIV com TMPn 3,5%, 7% e 14%. Seis corposde- prova foram utilizados na determinação da liberação de fluoreto (F) e TMP em soluções de desmineralização e de remineralização durante 15 dias. As propriedades físico-mecânicas avaliadas 24 horas e 7 dias após a confecção foram: resistência à compressão (n=12), resistência à tração diametral (n=12), dureza de superfície do material (n=6) e grau de conversão de monômeros (n=6). Para o estudo da desmineralização do esmalte, corpos-de-prova (n=12) foram adaptados a blocos de esmalte selecionados pelo teste de dureza de superfície inicial (DS1) e submetidos às ciclagens de pH. A seguir, determinou-se a dureza de superfície final (DS2), em secção longitudinal (DSL) e a concentração de F no esmalte. Testes paramétricos e não paramétricos foram realizados, após a verificação da homocedasticidade dos dados (p<0,05). A adição de 14% de TMP levou a maior média de liberação de F (p<0,05) e os demais grupos foram similares ao CIV (p>0,05). Maior liberação de TMP foi observada com 14% microparticulado (p<0,05). A incorporação do TMP ao CIV promoveu uma redução média nas propriedades mecânicas de 21% (tração), 10% (compressão) e 18% (dureza), após 24 horas e em 18%, 23% e 12%, após 7 dias. O grau de conversão foi menor com adição de 14% TMP quando comparado ao CIV após 24 horas (p<0,05); no tempo de 7 dias não houve diferença entre os grupos (p>0,05). A adição de 7% e 14% de... / Abstract: The aim of this study was to evaluate the effect of addition of sodium trimetaphosphate (TMP) microparticle (m) and nanoparticle (n) to the glass ionomer cement (GIC) on the physico-mechanical properties and demineralization of the enamel. Specimens (n=54) were fabricated from each experimental group: GIC without TMP (GIC), GIC with 3.5%, 7% and 14% TMPm and GIC with 3.5%, 7% and 14% TMPn. To determine the release of fluoride (F) and TMP it was used six specimens immersed into a demineralization and remineralization solution during 15 days. The physico-mechanical properties evaluated 24 hours and 7 days after fabrication were: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=6). For the study of enamel demineralization, specimens (n=12) were attached to enamel blocks selected by the initial surface hardness test (SH1) and submitted to the pH-cycling. Following, final surface (SH2) and cross-sectional (CSH) hardness, as well as enamel F concentration were determined. Parametric and non-parametric tests were performed after checking the data homoscedasticity (p<0.05). The addition of 14% TMP led to higher mean release of F (p<0.05) and the other groups were similar to the GIC (p>0.05). The release of TMP was higher with 14% microparticulate (p<0.05). The addition of TMP at GIC promoted an average reduction of mechanical properties of 21% (tensile), 10% (compressive) and 18% (hardness) after 24 hours and 18%, 23% and 12% after 7 days. The degree of conversion was lower with addition of 14% TMP compared to the GIC after 24 hours (p<0.05); at 7 days there was no difference between groups (p>0.05). Addition of 7% and 14% TMP reduced mineral loss and increased enamel F concentration when compared... / Mestre

Indiana University-Purdue University Indianapolis (IUPUI) / The furanone derivatives and their constructed polymers were synthesized, characterized and formulated into dental glass-ionomer cement (GIC) and resin composite for improved antibacterial properties. Compressive strength (CS) and S. mutans viability were used to evaluate the mechanical strength and antibacterial activity of the restoratives. Fuji II LC cement and P60 were used as control. The specimens were conditioned in distilled water at 37 oC for 24 h prior to testing. The effects of loading, saliva and aging on CS and S. mutans viability were investigated. The antibacterial effect of the furanone derivative on other bacteria was also studied. Chapter 2 describes how we studied and evaluated the formulated antibacterial glass-ionomer cement by incorporating the synthesized furanone derivative-containing polymer into the formulation. The results show that all the formulated furanone-containing cements showed a significant antibacterial activity, accompanying with an initial CS reduction. Increasing loading significantly enhanced antibacterial activity but reduced the initial CS of the formed cements. The derivative showed a broad antibacterial spectrum on bacteria including S. mutans, lactobacillus, S. aureus and S. epidermidis. Human saliva did not affect the antibacterial activity of the cement. The long-term aging study indicates that the cements may have a long-lasting antibacterial function. Chapter 3 describes how we studied and evaluated the formulated antibacterial resin composite by incorporating the synthesized furanone derivative into the basic resin formulations. The results show that the modified resin composites showed a significant antibacterial activity without substantially decreasing the mechanical strengths. With 5 to 30% addition of the furanone derivative, the composite kept its original CS unchanged but showed a significant antibacterial activity with a 16-68% reduction in the S. mutans viability. Further, the antibacterial function of the new composite was not affected by human saliva. The aging study indicates that the composite may have a long-lasting antibacterial function. In summary, we have developed a novel furanone-containing antibacterial system for dental restoratives. Both glass-ionomer cement and resin composite have demonstrated significant antibacterial activities. The modified experimental glass-ionomer cement is a promising system because the reduced strength of the cement with addition of the furanone-containing polymer is still above those demonstrated by original commercial cement Fuji II LC. The modified resin composite shows nearly no reduction in mechanical strength after incorporation of the antibacterial furanone derivative. It appears that both experimental cement and resin composite are clinically attractive dental restoratives that can be potentially used for long-lasting restorations due to their high mechanical strength and permanent antibacterial function.

Orientador: Denise Pedrini / Coorientador: Alberto Carlos Botazzo Delbem / Banca: Marcelle Danelon / Banca: Adelisa Rodolfo Ferreira Tiveron / Resumo: O objetivo do presente estudo foi avaliar o efeito da incorporação do glicerofosfato de cálcio (CaGP) ao cimento de ionômero de vidro (CIV) nas propriedades físicomecânicas e na desmineralização do esmalte. Foram confeccionados corpos-de-prova (n=56) para cada grupo experimental: CIV sem CaGP (CIV), CIV com CaGP 1, 3 e 9%. Seis corpos-de-prova foram utilizados na determinação da liberação de fluoreto (F), cálcio (Ca) e fósforo (P) em soluções de desmineralização e remineralização durante 15 dias. As propriedades físico-mecânicas avaliadas 24 horas e 7 dias após a confecção foram: resistência à compressão (n=12), resistência à tração diametral (n=12), dureza de superfície do material (n=6) e grau de conversão de monômeros (n=8). Para o estudo da desmineralização do esmalte, corpos-de-prova (n=12) foram adaptados a blocos de esmalte selecionados pelo teste de dureza de superfície inicial (DS1) e submetidos às ciclagens de pH. A seguir, foi analisada a dureza de superfície final (DS2) e a concentração de F, Ca e P no esmalte. Os dados foram submetidos a análise de variância seguida pelo teste de Student-Newman-Keuls (p<0,05). A adição de CaGP levou a maior média de liberação de F, Ca e P pelos materiais quando comparado ao CIV (p<0,001). As propriedades mecânicas (tração, compressão e dureza) com a adição de 1% e 3% CaGP apresentaram dentro da variação dos cimentos ionoméricos. O grau de conversão não diferiu entre os grupos nos tempos,... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract : The aim of this study was to evaluate the effect of addition of calcium glycerophosphate glass ionomer cement (GIC) on the physico - mechanical properties and demineralization of the enamel. Specimens (n= 56 ) were fabricated from each ex perimental group : GIC without CaGP (GIC), GIC with 1, 3 and 9% CaGP. To determine the release of fluoride (F), calcium (Ca) and phosphorus (P) w ere used six specimens immersed into a demineralization and remineralization solution s during 15 days. The physico - mechanical properties evaluated 24 hours and 7 days after fabrication were: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n= 8 ). For the study of enamel d emineralization, specimens (n=12) were attached to enamel blocks selected by the initial surface hardness test (SH 1 ) and submitted to the pH - cycling. Following, final surface hardness (SH 2 ) and the concentration of F, Ca and P in enamel were determined . Data were subjected to analysis of variance followed by Student - Newman - Keuls te st (p <0.05 ). The addition of Ca GP led to higher mean release of F, Ca and P by materials compared to the GIC (p <0.001). The mechanical properties ( diametral tensile, compressi ve strength and hardness) were within the range of the ionomer ic cements after addition of 1% and 3% Ca GP. The degree of conversion was not different between gr oups at 24 hours and 7 days (p> 0.43 9). The addition of 3% and 9% Ca GP reduced mineral loss and increased F, Ca and P in the enamel whe n compared to the GIC...(Complete abstract electronic access below) / Mestre